CN204983530U - Fire -retardant antibiotic floor of photocatalyst - Google Patents
Fire -retardant antibiotic floor of photocatalyst Download PDFInfo
- Publication number
- CN204983530U CN204983530U CN201520511512.4U CN201520511512U CN204983530U CN 204983530 U CN204983530 U CN 204983530U CN 201520511512 U CN201520511512 U CN 201520511512U CN 204983530 U CN204983530 U CN 204983530U
- Authority
- CN
- China
- Prior art keywords
- layer
- photocatalyst
- flame
- wood shavings
- floor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model relates to a fire -retardant antibiotic floor of photocatalyst belongs to functional type environmental protection floor field. Fire -retardant antibiotic floor of photocatalyst, for the lamellar structure including the substrate layer, its characterized in that: the formaldehyde emission on fire -retardant antibiotic floor < the 0.3mgL that limits the quantity of, antibiotic rate >= 90%, surface abrasion -resistant <= 0.08g100r, the substrate layer is the oriented wood chipboard layer, the oriented wood chipboard layer include with the glue mixing wood shavings according to its fiber direction longitudinal arrangement's upper epidermis, down the top layer, with the glue mixing wood shavings according to its fiber direction transverse arrangement's sandwich layer wood shavings layer, set up on the first fire -retardant layer between upper epidermis and the sandwich layer wood shavings layer and set up fire -retardant layer of the second between top layer and the sandwich layer wood shavings layer down, substrate layer top is according to apart from substrate layer decorative layer, wear -resisting priming paint layer and the antibiotic layer of covering or decorate with paint of photocatalyst of including at least in proper order from near and far, the substrate layer below is including balanced layer. The utility model discloses the floor has high environmental protection and antibacterial function, intensity is high, the wearability is good, the feel is comfortable.
Description
Technical field
The utility model relates to a kind of photocatalyst flame-proof antibiotic floor, belongs to field, functional form environment protection health floor.
Background technology
In the dwelling environment of people, there is various volatile organic matter and harmful microorganism, directly affect the physical and mental health of people.In living environment, most of pathogenic bacteria are toward contact to aspects such as ground dirt and pets, and the microorganism growing germ and bacterium directly and human contact, is easilier passed to human body by floor.The antimildew and antibacterial agent of past people chemicals is sprayed at the surrounding in room, solve the air quality problems in room by this, and the toxicity of common antimildew and antibacterial agent is comparatively large, heat-resisting, endurance quality is poor, be sprayed at floor and surface of decorative plate easily makes its variable color and affects attractive in appearance.Along with the requirement of people to domestic environment is more and more higher, the demand on the health environment-friendly floor of functional form is brought into schedule.First very high to the environmental protection class requirement on floor itself, reach without aldehyde level.Next requires floor to have to purify air and antibacterial functions.
CN202467086U(2012-2-29) disclose a kind of photo-catalytic antibacterial floor, but the structure on this floor and performance thereof still have much room for improvement.
Utility model content
The purpose of this utility model be to provide a kind of have high-environmental and antibacterial functions, intensity is high, abrasion resistance good, the photocatalyst flame-proof antibiotic floor of comfortable foot feeling.
Above-mentioned technical purpose of the present utility model is achieved by the following technical programs:
A kind of photocatalyst flame-proof antibiotic floor, is the layer structure comprising substrate layer, it is characterized in that: the Form aldehyde release limitation < 0.3mg/L on described flame-proof antibiotic floor; Antibiotic rate >=90%; Surface abrasion resistance≤0.08g/100r;
Described substrate layer is oriented shaving flaggy;
Described oriented shaving flaggy comprise by glue mixing wood shavings by the upper epidermis of its machine direction longitudinal arrangement, layer, by glue mixing wood shavings by the transversely arranged sandwich layer wood shavings layer of its machine direction, the second flame-retardant layer of being arranged on the first flame-retardant layer between upper epidermis and sandwich layer wood shavings layer and being arranged between layer and sandwich layer wood shavings layer; Layer is covered or decorate with paint according to apart from described substrate layer decorative layer, wear-resistant primer layer and the photo-catalytic antibacterial of comprising at least successively near and far above described substrate layer;
Balance layer is comprised below described substrate layer.
The utility model antibiotic rate performs LY/T1926-2010 antibacterial wood (bamboo) quality plate, and surface abrasion resistance performs GB/T18103-2013 flame-proof antibiotic floor.
Nanoscale TiO
2photocatalyst material, produces similar photosynthetic catalytic reaction, the oxygen in air and hydrone is excited under the irradiation of sunshine or visible ray, forms the extremely strong hydroxyl free radical of oxidation capacity and active oxygen.The extremely strong free radical of these oxidation capacities can catch and kill the planktonic bacteria in air, and removes that cigarette is smelly, rubbish is smelly, mud is smelly, and organic pollution is constantly degraded into free of contamination water and carbon dioxide etc., thus reaches the object of environment purification and air.For improving TiO
2the photocatalytic activity of photocatalyst, adopts Nano Silver as active catalyst.Silver in inorganic nano-silver is noble metal, can improve nanoscale TiO by surface deposition
2the photocatalytic activity of photocatalyst material, improves the effect that it is antibacterial.Nano Silver itself has antibacterial action, and silver ion has raising nanoscale TiO simultaneously
2the photocatalysis of photocatalyst material, makes TiO
2photocatalyst material just can produce stronger activity under the visible ray that wavelength is longer, improves the utilization rate of luminous energy.The environment protection health composite antibacterial floor with photo-catalytic antibacterial function made by flame-proof antibiotic ground laminin plate after wear-resistant primer, photocatalyst surface are covered or decorate with paint.
As preferably, it is nanoscale TiO that described photo-catalytic antibacterial covers or decorate with paint layer
2the mixture layer that photocatalyst material, Nano Silver and UV scratch-resistant finish paint form.
As preferably, described decorative layer is the wood floors fabric of thickness 0.6-4.0mm.
As preferably, described decorative layer is rotary-cut material, slicing material or sawn timber.
As preferably, described balance layer is the veneer of thickness 0.3-1.2mm.
As preferably, described balance layer is rotary-cut material.
As preferably, described wear-resistant primer layer is optical curing of UV prime coat, one side coating weight 30-40g/m
2.
As preferably, it is photocuring antimicrobial paint surface layer that described photo-catalytic antibacterial covers or decorate with paint layer, and one side coating weight is 10-14g/m
2.
As preferably, described oriented shaving flaggy comprises living beings rubber made from soybean cake adhesion coating.
By the specific substrate layer of the utility model, contribute to the overall anti-microbial property playing flame-proof antibiotic floor.By adopting living beings rubber made from soybean cake as special adhesive, guarantee the high-environmental of ground laminin plate, intensity and antibiotic property.
In sum, the utility model has following beneficial effect:
By setting up photo-catalytic antibacterial layer on the surface on floor, making floor surface have killing and suppressing the function of multiple harmful bacteria.The composite board that the base material that this floor uses simultaneously is adhesive for employing rubber made from soybean cake, its Form aldehyde release limitation reaches completely without aldehyde level, accomplishes abundant environmental protection.For occupants provides good living environment, thus the generation of minimizing disease of improving the quality of living.
Accompanying drawing explanation
Fig. 1 is the structural representation on the utility model photocatalyst flame-proof antibiotic floor;
Fig. 2 is the utility model substrate layer structural representation.
Detailed description of the invention
Below in conjunction with accompanying drawing, the utility model is described in further detail.
Embodiment one
As depicted in figs. 1 and 2, photocatalyst flame-proof antibiotic floor is the layer structure comprising substrate layer 1, the Form aldehyde release limitation < 0.3mg/L on flame-proof antibiotic floor; Antibiotic rate >=90%; Surface abrasion resistance≤0.08g/100r; Substrate layer 1 is oriented shaving flaggy; Substrate layer is oriented shaving flaggy, comprise by glue mixing wood shavings by the upper epidermis 11 of its machine direction longitudinal arrangement, layer 13, by glue mixing wood shavings by the transversely arranged sandwich layer wood shavings layer 12 of its machine direction, the second flame-retardant layer 15 of being arranged on the first flame-retardant layer 14 between upper epidermis and sandwich layer wood shavings layer and being arranged between layer and sandwich layer wood shavings layer.Bond by living beings rubber made from soybean cake adhesion coating between each layer of oriented shaving flaggy.Layer 4 is covered or decorate with paint according to apart from substrate layer 1 decorative layer 2, wear-resistant primer layer 3 and the photo-catalytic antibacterial of comprising successively near and far above substrate layer 1; Balance layer 0 is comprised below substrate layer 1.Photo-catalytic antibacterial covers or decorate with paint layer 4 for nanoscale TiO
2the mixture layer that photocatalyst material, Nano Silver and UV scratch-resistant finish paint form.Decorative layer 2 is the wood floors fabric of thickness 0.6mm.Decorative layer 2 is rotary-cut material.Balance layer 0 is the veneer of thickness 0.3-1.2mm.Balance layer 0 is rotary-cut material.Wear-resistant primer layer 3 is optical curing of UV prime coat, one side coating weight 30g/m
2.Photo-catalytic antibacterial covers or decorate with paint layer 4 for photocuring antimicrobial paint surface layer, and one side coating weight is 10g/m
2.
Embodiment two
As depicted in figs. 1 and 2, photocatalyst flame-proof antibiotic floor is the layer structure comprising substrate layer 1, the Form aldehyde release limitation < 0.3mg/L on flame-proof antibiotic floor; Antibiotic rate >=90%; Surface abrasion resistance≤0.08g/100r; Substrate layer 1 is Multilayer Structure; Layer 4 is covered or decorate with paint according to apart from substrate layer 1 decorative layer 2, wear-resistant primer layer 3 and the photo-catalytic antibacterial of comprising successively near and far above substrate layer 1; Balance layer 0 is comprised below substrate layer 1.Photo-catalytic antibacterial covers or decorate with paint layer 4 for nanoscale TiO
2the mixture layer that photocatalyst material, Nano Silver and UV scratch-resistant finish paint form.Decorative layer 2 is the wood floors fabric of thickness 4.0mm.Decorative layer 2 is slicing material.Balance layer 0 is the veneer of thickness 1.2mm.Balance layer 0 is rotary-cut material.Wear-resistant primer layer 3 is optical curing of UV prime coat, one side coating weight 40g/m
2.Photo-catalytic antibacterial covers or decorate with paint layer 4 for photocuring antimicrobial paint surface layer, and one side coating weight is 14g/m
2.Substrate layer 1 is oriented shaving flaggy; Substrate layer is oriented shaving flaggy, comprise by glue mixing wood shavings by the upper epidermis 11 of its machine direction longitudinal arrangement, layer 13, by glue mixing wood shavings by the transversely arranged sandwich layer wood shavings layer 12 of its machine direction, the second flame-retardant layer 15 of being arranged on the first flame-retardant layer 14 between upper epidermis and sandwich layer wood shavings layer and being arranged between layer and sandwich layer wood shavings layer.Bond by living beings rubber made from soybean cake adhesion coating between each layer of oriented shaving flaggy.
Embodiment three
As depicted in figs. 1 and 2, photocatalyst flame-proof antibiotic floor is the layer structure comprising substrate layer 1, the Form aldehyde release limitation < 0.3mg/L on flame-proof antibiotic floor; Antibiotic rate >=90%; Surface abrasion resistance≤0.08g/100r; Substrate layer 1 is Multilayer Structure; Layer 4 is covered or decorate with paint according to apart from substrate layer 1 decorative layer 2, wear-resistant primer layer 3 and the photo-catalytic antibacterial of comprising successively near and far above substrate layer 1; Balance layer 0 is comprised below substrate layer 1.Photo-catalytic antibacterial covers or decorate with paint layer 4 for nanoscale TiO
2the mixture layer that photocatalyst material, Nano Silver and UV scratch-resistant finish paint form.Decorative layer 2 is the wood floors fabric of thickness 2.0mm.Decorative layer 2 is rotary-cut material, slicing material or sawn timber.Balance layer 0 is the veneer of thickness 0.9mm.Balance layer 0 is rotary-cut material.Wear-resistant primer layer 3 is optical curing of UV prime coat, one side coating weight 35g/m
2.Photo-catalytic antibacterial covers or decorate with paint layer 4 for photocuring antimicrobial paint surface layer, and one side coating weight is 12g/m
2.Substrate layer 1 is oriented shaving flaggy; Substrate layer is oriented shaving flaggy, comprise by glue mixing wood shavings by the upper epidermis 11 of its machine direction longitudinal arrangement, layer 13, by glue mixing wood shavings by the transversely arranged sandwich layer wood shavings layer 12 of its machine direction, the second flame-retardant layer 15 of being arranged on the first flame-retardant layer 14 between upper epidermis and sandwich layer wood shavings layer and being arranged between layer and sandwich layer wood shavings layer.Bond by living beings rubber made from soybean cake adhesion coating between each layer of oriented shaving flaggy.This specific embodiment is only to explanation of the present utility model; it is not to restriction of the present utility model; those skilled in the art can make to the present embodiment the amendment not having creative contribution as required after reading this manual, as long as but be all subject to the protection of Patent Law in right of the present utility model.
Claims (8)
1. a photocatalyst flame-proof antibiotic floor, is the layer structure comprising substrate layer, it is characterized in that: the Form aldehyde release limitation < 0.3mg/L on described flame-proof antibiotic floor; Antibiotic rate >=90%; Surface abrasion resistance≤0.08g/100r;
Described substrate layer is oriented shaving flaggy;
Described oriented shaving flaggy comprise by the glue mixing wood shavings upper epidermis of its machine direction longitudinal arrangement, glue mixing wood shavings layer, by the transversely arranged sandwich layer wood shavings layer of its machine direction, the second flame-retardant layer of being arranged on the first flame-retardant layer between glue mixing wood shavings upper epidermis and sandwich layer wood shavings layer and being arranged between glue mixing wood shavings layer and sandwich layer wood shavings layer;
Layer is covered or decorate with paint according to apart from described substrate layer decorative layer, wear-resistant primer layer and the photo-catalytic antibacterial of comprising at least successively near and far above described substrate layer;
Balance layer is comprised below described substrate layer.
2. a kind of photocatalyst flame-proof antibiotic floor according to claim 1, is characterized in that: described decorative layer is the wood floors fabric of thickness 0.6-4.0mm.
3. a kind of photocatalyst flame-proof antibiotic floor according to claim 2, is characterized in that: described decorative layer is rotary-cut material, slicing material or sawn timber.
4. a kind of photocatalyst flame-proof antibiotic floor according to claim 3, is characterized in that: described balance layer is the veneer of thickness 0.3-1.2mm.
5. a kind of photocatalyst flame-proof antibiotic floor according to claim 4, is characterized in that: described balance layer is rotary-cut material.
6. a kind of photocatalyst flame-proof antibiotic floor according to claim 5, is characterized in that: described wear-resistant primer layer is optical curing of UV prime coat, one side coating weight 30-40g/m
2.
7. a kind of photocatalyst flame-proof antibiotic floor according to claim 6, is characterized in that: it is photocuring antimicrobial paint surface layer that described photo-catalytic antibacterial covers or decorate with paint layer, and one side coating weight is 10-14g/m
2.
8. a kind of photocatalyst flame-proof antibiotic floor according to claim 7, is characterized in that: described oriented shaving flaggy comprises living beings rubber made from soybean cake adhesion coating.