CN204435727U - A kind of compound resin decorative panel - Google Patents

A kind of compound resin decorative panel Download PDF

Info

Publication number
CN204435727U
CN204435727U CN201420753068.2U CN201420753068U CN204435727U CN 204435727 U CN204435727 U CN 204435727U CN 201420753068 U CN201420753068 U CN 201420753068U CN 204435727 U CN204435727 U CN 204435727U
Authority
CN
China
Prior art keywords
layer
resin
decorative panel
bed
ornament
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201420753068.2U
Other languages
Chinese (zh)
Inventor
陈志远
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangmen City Hundred Million Fine Horse Ornament Materials Co Ltd
Original Assignee
Jiangmen City Hundred Million Fine Horse Ornament Materials Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangmen City Hundred Million Fine Horse Ornament Materials Co Ltd filed Critical Jiangmen City Hundred Million Fine Horse Ornament Materials Co Ltd
Priority to CN201420753068.2U priority Critical patent/CN204435727U/en
Application granted granted Critical
Publication of CN204435727U publication Critical patent/CN204435727U/en
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The utility model discloses a kind of compound resin decorative panel, this decorative panel comprises substrate layer, middle sticky glutinous layer and surface decoration layer, the sticky glutinous layer in described centre adopts epoxyn to make, and described surface decoration layer is made up of hyaline layer, the ornament bed of material and back cover layer.The utility model has the toughness of good bonding ability and appropriateness, effectively can solve the problem on deformation that resin plate causes because expanding and shrink gravitation, and the scope of application is wide, and diversity is strong, and anti-wear performance is good, and practical, is worthy to be popularized.

Description

A kind of compound resin decorative panel
Technical field
The utility model relates to a kind of compound resin decorative panel.
Background technology
Traditional man-made stone and various types of resins decorative panel (as artificial transparent stone, transparent resin decorative panel etc.) are widely used in the field such as all kinds of furniture table-board and lamp decoration, bathroom, wall, stringcourse.
But, no matter be that general artificial slabstone is (with aluminium hydrate powder, Shi Li, stone flour and beads, pigment etc. are filler), or transparent resin decorative sheet is (with dried flower hay, cobble, conch, starfish, shell, sea sand etc. are as built-in materials), its main component is all unsaturated polyester resin, all inevitably there is following shortcoming: first, it has unsurmountable thermal expansion and cold events gravitation, this causes general man-made stone to hold yielding main cause, because general man-made stone and resin plate are more than temperature 50-60 DEG C, less than 10-15 DEG C just there will be metaboly, the second, traditional artificial slabstone is all opaque, clearly can not manifest the 3 D stereo of insert, just has very large limitation like this to Modern Decorative sheet material, 3rd, general resin decorative sheet, its surface is not wear-resisting, and hardness Barcol only has 58-62.
Utility model content
The utility model, in order to solve the above-mentioned deficiency of prior art, proposes a kind of compound resin decorative panel production technology.
In order to solve the problems of the technologies described above, the utility model is by the following technical solutions: a kind of compound resin decorative panel, comprise the substrate layer being located at bottom, the sticky glutinous layer in the centre be located on substrate layer, be located at the surface decoration layer on middle sticky glutinous layer, the sticky glutinous layer in described centre adopts epoxyn to make and upper and lower two surfaces bond described substrate layer and surface decoration layer respectively; Described surface decoration layer is made up of hyaline layer, the ornament bed of material and back cover layer, described back cover layer adopts transparent resin or opaque resin to make, the described ornament bed of material is embedded to be fixed in transparent resin by multiple material and is formed, the described ornament bed of material be cast in back cover layer above and pour into an integrated entity simultaneously, described hyaline layer adopts transparent pure resin to make, and described hyaline layer cast is bonded in the upper surface of the described ornament bed of material.
Described substrate layer is stone plate, Ceramic Tiles embryonic plate, glass magnesium plate, moist-proof board, aluminum honeycomb panel, clamping plate or medium density fiberboard.
Compared with prior art, the utility model has the following advantages, the first, the base material anti-deformation force rate due to selected is stronger, and middle sticky glutinous layer adopts epoxyn to make, there is the toughness of firmly binding ability and appropriateness, effectively can solving the problem on deformation that resin plate causes because expanding and shrink gravitation; The second, material is embedded in transparent resin material, produce lifelike transparent resin dalle, more various layout can be changed, improve use diversity of the present utility model; Three, in order to improve the anti-scratch mill ability on the utility model surface, we are coated on resin board surface with the UV resin of the high grade of transparency and high rigidity, and effects on surface carries out ultraviolet light polymerization process, and make its surface abrasion resistance degree better, hardness Barcol reaches more than 90.
Accompanying drawing explanation
Fig. 1 is structural representation of the present utility model;
Fig. 2 is the structural representation of surface decoration layer of the present utility model.
Detailed description of the invention
Below in conjunction with drawings and Examples, utility model is described in detail.
As shown in Figure 1, 2, the compound resin decorative panel that the utility model proposes, comprise the substrate layer 1 being located at bottom, be located at the sticky glutinous layer 2 in centre on substrate layer 1, be located at the surface decoration layer 3 on middle sticky glutinous layer 2, middle sticky glutinous layer 2 adopts epoxyn to make and upper and lower two surfaces bond described substrate layer 1 and surface decoration layer 3 respectively; Surface decoration layer 3 is made up of hyaline layer 31, the ornament bed of material 32 and back cover layer 33, back cover layer 33 adopts transparent or opaque resin to make, the ornament bed of material 32 is embedded to be fixed in transparent resin by multiple material and is formed, the ornament bed of material 32 be cast in back cover layer 33 above and become to be integrated, hyaline layer 31 adopts transparent pure resin to make, and hyaline layer 31 cast is bonded in the upper surface of the described ornament bed of material 32.The surface of hyaline layer 31 also coating one deck high grade of transparency high rigidity UV resin and carry out ultraviolet light polymerization process.
Transparent and the opaque resin that surface decoration layer 3 adopts in the utility model is all unsaturated polyester resin, and its effect mainly improves the ornamental of sheet material.Unsaturated polyester resin, English formal name used at school: Unsaturated Polyester Resin (UPR).The sticking flowable unsaturated polyester resin of tool, exist at initator (being commonly called as curing compound) and catalyzer (being commonly called as accelerator) and issue raw free radical copolymerization, thus the process generating the three-dimensional-structure of stable performance is called the solidification of unsaturated polyester resin.Because different material will be embedded in resin plate, so prepare resin plate [i.e. above-mentioned surface decoration layer (3)] usually will divide following step:
1, according to the resin plate size of required preparation, with the aluminum alloy bar of glass bar or tabular, corresponding size is gone out at the glass table top upper ledge with better levelness.(consider the factor of resin shrinkage rate, the size that usual frame goes out is larger than actual needs size)
2, first floor is hyaline layer 31 (pure resin), and thickness is advisable with 1-1.5mm.Be container with Plastic Drum, by curing compound and unsaturated polyester resin according to 4 ‰ ratio allocate, with mixer by resin agitating evenly and put into vacuum tank pump drainage bubble.Then by resin-cast to glass table top, and to strike off with the resin of plastic wipers by liquid state, guarantee all places in resin coating cover frame.
3, the second layer is the ornament bed of material 32 (transparent resin+material), and the thickness of this layer of resin is advisable with 2mm.After first floor cast about 1 hour (different because of season and variations in temperature), curing compound ratio in 3 ‰ also presses the deployed resin of above step, be poured on glass table top, then by even with rational density dispenser to cobble, shell, little conch, the broken and extra large sand of shell or the material such as dried flower, Radix Glycyrrhizae.
4, third layer is back cover layer 33 (transparent or opaque resin).The about 2 little times after second layer resin-cast, then the opaque resin poured into a mould layer of transparent resin or be mixed with inserts (pigment or stone flour, Shi Li etc.) carries out back cover, this layer thickness is depending on actual conditions.
5, about 8-12 hour after back cover layer resin-cast, resin plate just can the demoulding.With sander or thicknessing machine, resin plate is processed into 3-6mm thickness (depending on material thickness), requires that resin plate thickness is after processing even, positive and negative all must be smooth.
Two, middle sticky glutinous layer 2 is epoxyn.Its effect is bonded surface course (unsaturated polyester resin plate) and base material.
Epoxyn is primarily of epoxy resin (component A) and curing compound (B component) composition, and A:B ratio is generally 2:1, suitably can adjust proportioning according to different environment temperatures, humidity and different base materials.
For reaching different effective utilizations, also often add colorant, flexibilizer, thinner, filler, accelerator and coupling agent etc.Deployed adhesive must be finished in 2 hours, otherwise can condensation cure.
Three, substrate layer 1 is the smooth plate object of unlike material.Its effect is the physical property improving surface course, mainly strengthens its load-bearing and non-deformability.
According to the different purposes of composite board, the materials such as stone material, Ceramic Tiles embryo, moist-proof board, glass magnesium plate, aluminum honeycomb panel, clamping plate, medium density fiberboard can be selected for the base material closed with unsaturated-resin plate holder.
Four, bind and process.By deployed epoxy resin adhesive uniform application on base material, then resin plate (surface decoration layer 3) is placed on base material gently, and puts into hydraulic platen machine and carry out pressurization clamping.After 4-6 hour, with regard to removably and carry out polishing, the Surface Finishing such as polishing or UV process and cut, the processing such as edging, edge sealing.
Of the present utility model of many uses, resin sheet and ceramic tile compound, can as flower sheet, and background wall brick, stringcourse, baseboard and indoor floor use, and also can cut into the particle of different size and shape, be combined into mosaic.Be base material with lithotome, can be used as all kinds of furniture table-board and use (as cabinet, tea table, dinner table, washbasin, TV cabinet etc.).With moist-proof board or cellular board for base material, sliding door, screen, partition can be made, and so on.
Above-mentioned example only have expressed several embodiment of the present utility model, describes comparatively concrete and detailed, but therefore can not be interpreted as the restriction to the utility model the scope of the claims.It should be pointed out that for the person of ordinary skill of the art, without departing from the concept of the premise utility, can also make some distortion and improvement, these all belong to protection domain of the present utility model.Therefore, the utility model patent and protection domain should be as the criterion with appended claims.

Claims (3)

1. a compound resin decorative panel, it is characterized in that: comprise the substrate layer (1) being located at bottom, the sticky glutinous layer (2) in the centre be located on substrate layer (1), be located at the surface decoration layer (3) on middle sticky glutinous layer (2), the sticky glutinous layer (2) in described centre adopts epoxyn to make and upper and lower two surfaces bond described substrate layer (1) and surface decoration layer (3) respectively; Described surface decoration layer (3) is made up of hyaline layer (31), the ornament bed of material (32) and back cover layer (33), described back cover layer (33) adopts transparent resin or opaque resin to make, the described ornament bed of material (32) is bumped into be fixed in transparent resin by multiple material and is formed, the described ornament bed of material (32) be cast in back cover layer (33) above and pour into an integrated entity simultaneously, described hyaline layer (31) adopts transparent pure resin to make, and described hyaline layer (31) cast is bonded in the upper surface of the described ornament bed of material (32).
2. compound resin decorative panel as claimed in claim 1, is characterized in that: described substrate layer (1) is stone plate, Ceramic Tiles embryonic plate, moist-proof board, glass magnesium plate, aluminum honeycomb panel, clamping plate or medium density fiberboard.
3. compound resin decorative panel as claimed in claim 1, is characterized in that: the surface of described hyaline layer (31) is also provided with the UV glue coating of the high grade of transparency and carries out ultraviolet light polymerization process.
CN201420753068.2U 2014-12-03 2014-12-03 A kind of compound resin decorative panel Expired - Fee Related CN204435727U (en)