CN204298441U - A kind of system utilizing metallurgy sintered blast furnace harmless treatment electroplating sludge - Google Patents
A kind of system utilizing metallurgy sintered blast furnace harmless treatment electroplating sludge Download PDFInfo
- Publication number
- CN204298441U CN204298441U CN201420799765.1U CN201420799765U CN204298441U CN 204298441 U CN204298441 U CN 204298441U CN 201420799765 U CN201420799765 U CN 201420799765U CN 204298441 U CN204298441 U CN 204298441U
- Authority
- CN
- China
- Prior art keywords
- electroplating sludge
- ball
- equipment
- balling
- coated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Utilize the system of metallurgy sintered blast furnace harmless treatment electroplating sludge, it comprises electroplating sludge core system, ball is pre-coated wraps up in system, secondary compound ball manufacturing system, half way reduction and detoxication system and blast furnace system.It utilizes secondary material compound pelletizing technology, makes in core system in colter mixing, and electroplating sludge and reductibility metallurgical waste gravitational dust collection ash form the ball of suitable particle size.Wrapping up in technique pre-coated, be the pre-coated object wrapping up in material is guarantee that electroplating sludge does not produce secondary pollution with dedusting ash.Pre-coated wrap up in after enter into conventional balling equipment and carry out electroplating sludge secondary compound pelletizing, then be transported to metallurgy sintered and blast furnace and thoroughly detoxify and comprehensive utilization of resources.This system does not thoroughly produce new objectionable impurities to electroplating sludge removing toxic substances; Construction cost is few, and working cost is low; Resource can effectively utilize, for the harmless treatment of electroplating sludge and comprehensive utilization of resources open up a new way.
Description
Technical field
The utility model belongs to dangerous harmful fixed-end forces technical field, is specifically related to pellet production and the innocuity disposal system to electroplating sludge.
Background technology
At present, for electroplating sludge harmless treatment and resource regeneration, each electroplating enterprise does not all have effective technology to solve completely.The method of process electroplating sludge is roughly following four kinds: 1) curing/stabilizing technology; 2) thermochemical treatment technology; 3) valuable metal recovery technology; 4) microbiological treatment technology; 5) materialized technology.Have plenty of in above treatment system that investment is many, working cost is too high, have plenty of process not thoroughly, having plenty of resource can not fully effectively utilize, and has plenty of and takies a large amount of land wastage resource.
Summary of the invention
The utility model thoroughly detoxifies for electroplating sludge and the suitability for industrialized production of utilization of resources and a kind for the treatment of system of developing, and this system does not thoroughly produce new objectionable impurities to electroplating sludge removing toxic substances; Construction cost is few, and working cost is low; Resource can effectively utilize, for the harmless treatment of electroplating sludge and comprehensive utilization of resources open up a new way.
It is as follows that the utility model solves the technical scheme that its technical problem adopts:
Utilize a system for metallurgy sintered blast furnace harmless treatment electroplating sludge, it utilizes secondary material compound pelletizing technology, makes in core system in colter mixing, and electroplating sludge and reductibility metallurgical waste gravitational dust collection ash form the ball of suitable particle size.In pre-coated system, be the pre-coated object wrapping up in material with dedusting ash be guarantee that electroplating sludge does not produce secondary pollution.Pre-coated wrap up in after enter into conventional balling equipment and carry out electroplating sludge secondary compound pelletizing, then be transported to metallurgy sintered and blast furnace and thoroughly detoxify and comprehensive utilization of resources.
Native system is is specifically connected and composed successively by following system:
(1) electroplating sludge core system: adopt colter mixing equipment and balling disc, colter mixing equipment is by conveying belt clutch disk pelletizer and ball is pre-coated wraps up in system, the ball meeting Particle size requirements enters by conveying belt that ball is pre-coated wraps up in system, the ball not meeting Particle size requirements is admitted to balling disc pelletizing again, and balling disc connects by conveying belt that ball is pre-coated wraps up in system.
Material prevents material from building bridge by the anti-bl bridge layer of the broken arch of colter mixing equipment, fall into equipment smoothly, by the colter structure of this equipment, fragmentation is carried out to electroplating sludge, and in mixing of materials process, by being constantly mixed into by reductibility metallurgical waste gravitational dust collection ash, the moisture of electroplating sludge is reduced simultaneously, form mutual NA particle, namely form electroplating sludge ball.The ball meeting Particle size requirements enters by conveying belt that ball is pre-coated wraps up in system, and the ball not meeting Particle size requirements is admitted to balling disc, adds binding liquid and is again entered that ball is pre-coated wraps up in system after pelletizing again by conveying belt.
(2) ball is pre-coated wraps up in system: adopt balling disc, and its opening for feed connects the discharging conveyor belts of electroplating sludge core system, electroplating sludge ball is sent into balling disc, is provided with feed bin above balling disc, dress reductibility metallurgical waste.
Electroplating sludge ball is sent into balling disc by the discharging conveyor belts of electroplating sludge core system, reductibility metallurgical waste is filled in the feed bin of balling disc, reductibility metallurgical waste is synchronously sent in the disk of balling disc and mix with electroplating sludge ball, one deck screening can is wrapped to form to electroplating sludge ball, prevent the secondary pollution of electroplating sludge and create hexavalent chrome reduction reaction good condition.
(3) secondary compound ball manufacturing system: comprise spherical shell material deposit feed proportioning system, Preblend system PBS, material buffer storehouse, active reduction compound sticking integrated system, secondary material compound balling-up system, composite pellet surge bunker.
described spherical shell material deposit feed proportioning system has sulfate slag feed bin, gravitational dust collection ash feed bin and metallurgical dedusting ash feed bin and feeding belt, and the outlet of each feed bin all aims at feeding belt, and material synchronously falls into feeding belt in proportion, and the end of feeding belt connects Preblend system PBS.
Described Preblend system PBS adopts double-spiral mixer, and its discharge end connects material surge bunker by transfer roller.
Buffering to material, storage effect are played in described material buffer storehouse, and it is arranged in, and ball is pre-coated to be wrapped up in above the material conveyer belt that is connected between the discharge end of system and the feed end of secondary material compound balling-up system.
Described active reduction compound sticking integrated system comprises the head tank, adhering liquid Preparation equipment and the container for storing liquid that connect successively.Head tank is for storing binding agent raw material, and binding liquid Preparation equipment is high speed dispersion reactor, and for preparing binding liquid, container for storing liquid, for storing the binding liquid configured, provides preparation for producing.Transfer roller is had between head tank and binding liquid Preparation equipment, raw material in head tank passes through baby conveyor feeding in binding liquid Preparation equipment, binding liquid to be transported in container for storing liquid by pump and to store by the binding liquid prepared, container for storing liquid and each pelletizing system are again by pipeline and high-pressure pump equipment connection, and the binding liquid in container for storing liquid is delivered in each pelletizing system by high-pressure pump equipment carries out pelletizing.
Described secondary material compound balling-up system adopts balling disc, by pre-coated wrap up in rear electroplating sludge ball with sulfate slag and gravitational dust collection ash mixed pelletizing under the effect of active reduction compound sticking liquid, formation secondary material composite pellet.
Described composite pellet surge bunker is arranged in the discharge end of secondary material compound balling-up system, composite pellet is played to the effect of buffer reservoir, transhipment.
(4) half way reduction and detoxication system
Described half way reduction and detoxication Operation system setting is at the discharge end of composite pellet surge bunker, comprise a set of transfer roller and sinter machine, secondary material composite pellet is sent in sintering mixing material as agglomerate raw material by transfer roller, in sinter machine, carry out roasting form meltbility agglomerate, in roasting process, secondary material composite pellet inside generates reducing atmosphere, is trivalent chromium, plays the effect of half way reduction and detoxication by hexavalent chrome reduction.
(5) blast furnace system (omnidistance reduction and detoxication and resource comprehensive utilization system), is arranged on transfer roller end;
Half way reduction and detoxication system is connected by transfer roller, by the reduction of half way containing trivalent chromium agglomerate in blast furnace in strongly reducing atmosphere reduction obtain nickel-chromium pig iron, complete the harmless treatment of electroplating sludge and the regeneration of metallurgical waste, improve the metallurgical performance of sintering mixing material simultaneously.
Electroplating sludge core system more than the utility model, ball be pre-coated wraps up in system and secondary compound ball manufacturing system is arranged in airtight environment.
Further, electroplating sludge pretreatment system can also be set, comprise filtering equipment, handling equipment, test set and watch-dog; Described filtering equipment adopts high-pressure machinery metal plate-and-frame filter press to dewater, and press filtration pressure can reach 50kgf/cm
2, after portion of water is sloughed in electroplating sludge pre-treatment, enter electroplating sludge core system through handling equipment again.Filtering equipment connects described electroplating sludge core system by handling equipment, and test set and watch-dog carry out signal with filtering equipment and be connected.
Adopt above system, by colter mixing equipment by electroplating sludge and the effectively mixing of reductibility metallurgical waste gravitational dust collection ash, airtight particle diameter of producing is (3 ~ 6) mm ball, pre-coatedly system is wrapped up in through ball shielding, one deck dedusting ash is wrapped in ball outside, recycle conventional balling equipment, adopt secondary material be combined into playing skill art ball and sulfate slag, metallurgical waste are made particle diameter for the secondary material composite pellet of (3 ~ 12) mm enters metallurgy sintered with blast furnace in carry out harmless treatment.In whole treating processes, the region producing ball is totally closed operation system, prevent electroplating sludge from forming secondary pollution, simultaneously, in the process of follow-up secondary material compound pelletizing, a large amount of use sulfate slag and metallurgical waste carry out secondary material compound pelletizing to the ball containing electroplating sludge, both electroplating sludge secondary pollution had been avoided, make use of metallurgical waste in a large number again, compound ball after removing toxic substances can be used as the Ni and Cr contained pig iron raw material produced and have higher economic worth through comprehensive utilization of resources, reach the object of resource regeneration.
The electroplating sludge composite pellet utilizing native system to produce need reach following performance requriements:
(1) physicals
A, electroplating sludge secondary compound ball granularity are the ratio of (3-12) mm: >=85%;
Ball water ratio in b, electroplating sludge secondary compound ball: 15 ~ 25%;
The dropping strength of c, electroplating sludge secondary compound ball is: >=8 times/balls;
The ultimate compression strength of d, electroplating sludge secondary compound ball is: >=5N/ ball.
(2) chemical property
Require that the basicity of the secondary compound ball made is 1.5 ~ 2.0.
Adopt native system, realize secondary material compound ball---metallurgy sintered, blast furnace technology technology line, electroplating sludge is thoroughly detoxified and carries out harmless treatment and comprehensive utilization of resources, compared to other process system process electroplating sludge, this process system advanced technology is feasible, technical process is simple, and does not need to set up new high-temperature detoxification equipment, less investment; Secondary compound ball processing line next-door neighbour metallurgy sintered, raw material (electroplating sludge, metallurgical waste) and compound ball haul distance short, faces replacement coordinate facilitate, working expense is low; Compound ball roasting does not affect existing metallurgy sintered technological process; The alternative a certain amount of raw materials for metallurgy of compound ball.Therefore this process economics and social benefit are significantly.
Accompanying drawing explanation
Fig. 1 is the structured flowchart of native system;
Fig. 2 is the technological process block-diagram of system.
Embodiment
Treatment system described in the utility model makes ball for pretreated electroplating sludge and dedusting ash, reductive agent are made mixing in core system at batch mixing, then after adding that dedusting ash is pre-coated and wrapping up in, be transported to secondary balling equipment again, add sulfate slag and metallurgical waste produces electroplating sludge secondary composite pellet.
See Fig. 1, utilize that the system of metallurgy sintered blast furnace harmless treatment electroplating sludge includes electroplating sludge core system, ball is pre-coated wraps up in system, secondary compound ball manufacturing system and a few part of blast furnace sinter system, they are connected by transfer limes successively, and first three system is arranged in airtight environment.
Its operational path is: electroplating sludge, reductive agent and dedusting ash make ball by electroplating sludge core system (nuclear equipment made by colter batch mixing), then entering the pre-coated treatment system of wrapping up in of ball shielding makes ball outside surface cover the harmless dedusting ash of one deck, again with laid in sulfate slag that feed proportioning system adds and metallurgical waste by spherical shell material and enter secondary compound ball manufacturing system and make composite pellet, then enter metallurgy sintered system and smelt further and reach electroplating sludge harmless treatment and comprehensive utilization of resources.Its major ingredient is electroplating sludge, sulfate slag and metallurgical waste, and the electroplating sludge composite pellet produced through this process system can complete electroplating sludge and thoroughly detoxify after sintering is smelted.
Below subsystems is described in detail:
1, core system is made in electroplating sludge core system 6(and colter mixing)
Native system adopts colter mixing equipment 601 and balling disc 602, and colter mixer 601 is primarily of compositions such as grab bucket, the anti-bl bridge layer of feed broken arch, colter mechanism, discharge mechanism and electric instrument robots.Electroplating sludge after pretreatment enters colter mixing through handling equipment and makes nuclear machinery, prevent material from building bridge by the anti-bl bridge layer of the broken arch of colter mixing equipment, fall into equipment smoothly, by the colter structure of this equipment, fragmentation is carried out to electroplating sludge, and simultaneously in mixing of materials process by mixing with the dedusting ash of drying, reductive agent the electroplating sludge ball made in nuclear machinery and form suitable particle size at colter by technique determination proportioning.Therefore the colter batch mixing in this process system is not singly batch mixing function, also has granulation concurrently.The ball meeting Particle size requirements enters by conveying belt that ball is below pre-coated wraps up in system 7, and the ball not meeting Particle size requirements is admitted to balling disc 602, adds binding liquid and is again entered that ball is pre-coated wraps up in system 7 after pelletizing again by conveying belt.
2, ball shielding is pre-coated wraps up in system 7
Native system adopts balling disc, has fly-ash separator by metallurgical waste feed bin 701(storehouse heading tape), metering outfit, double-spiral mixer 702, test set, watch-dog etc. form.The electroplating sludge ball made and dedusting ash enter ball shielding and pre-coatedly wrap up in equipment, dedusting ash is covered and is rolled on electroplating sludge ball, form one deck screen layer.Employing shielding is pre-coated wraps up in mode, can prevent ball from making and produce the diffuse pollution of electroplating sludge secondary in material transportation process, and pre-coated the wrapping up in of ball shielding adopts dedusting ash to be wrapped up by electroplating sludge, makes hexavalent chrome reduction have better reaction environment condition, detoxifies more thorough.
3, secondary compound ball manufacturing system
Native system comprises spherical shell material deposit feed proportioning system 3, Preblend system PBS 5, material buffer storehouse 8, active reduction compound sticking integrated system 10, secondary material compound balling-up system 9, composite pellet surge bunker 10.
3.1, spherical shell material deposit feed proportioning system 3
Native system is made up of feed bin, metering outfit, test set and watch-dog.Feed bin has three, is sulfate slag feed bin 301, gravitational dust collection ash feed bin 302 and metallurgical dedusting ash feed bin 303 respectively.Sulfate slag delivers to sulfate slag ground blanking by transport trolley in advance to cheat in 1, and being then sent to through delivery system 2 is in sulfate slag feed bin 301.Metallurgical waste is directly delivered in feed bin by metallurgical waste transport trolley 4.In each feed bin, material synchronously falls into feeding belt in proportion, and the double-spiral mixer sent in Preblend system PBS 5 by feeding belt carries out batch mixing.
3.2, Preblend system PBS 5
Preblend system PBS adopts double-spiral mixer, and its discharge end connects material surge bunker 8 by conveyor.Buffering to material, storage effect are played in material buffer storehouse 8, and it is arranged in, and ball is pre-coated to be wrapped up in above the material conveyer belt that is connected between the discharge end of system 7 and the feed end of secondary material compound balling-up system 9.
3.3, active reduction compound sticking integrated system 10
Comprise head tank 101, adhering liquid Preparation equipment 102, container for storing liquid 103, head tank is for storing binding agent raw material, binding liquid Preparation equipment is mainly high speed dispersion reactor for preparing binding liquid, and container for storing liquid, for storing the binding liquid configured, provides preparation for producing.Raw material in head tank is by baby conveyor feeding in binding liquid Preparation equipment, and binding liquid to be transported in container for storing liquid by pump and to store by the binding liquid prepared, and the binding liquid in container for storing liquid is delivered in each pelletizing system by high-pressure pump equipment again carries out pelletizing.In such a system, prepare online binding liquid, possess bonding in the short period of time active, the reduction characteristic had makes electroplating sludge composite pellet increase reductibility in roasting environment, and balling property meets the technical requirements of pellet sintering.
3.4, secondary material compound balling-up system 9
Native system is made up of conventional balling equipment (as balling disc), rotary conveyor, dust removal installation and watch-dog.Secondary material is adopted to be combined into playing skill art electroplating sludge ball, sulfate slag and the metallurgical waste after pre-coated for shielding wrapping up in, electroplating sludge composite pellet is made by conventional balling equipment, inner is the ball containing electroplating sludge and dedusting ash, reductive agent, and shell is nontoxic sulfate slag and metallurgical waste.In balling process, the binding liquid of bonding system is sprayed onto on material with vaporific form.The composite pellet made possesses the condition entering sintering and smelt.
The discharge end of secondary material compound balling-up system connects composite pellet surge bunker 10, and composite pellet surge bunker plays buffering and transhipment to finished product composite pellet.
4, half way reduction and detoxication system 11
At the discharge end of composite pellet surge bunker, a set of transfer roller 111 and sinter machine 112 are set, composite pellet is mixed in sintering mixing material, as agglomerate raw material, is sent into by composite pellet in sinter machine, sinter machine carries out roasting, and form meltbility agglomerate, in roasting process, secondary material composite pellet inside generates reducing atmosphere, be trivalent chromium by hexavalent chrome reduction, play the effect of half way reduction and detoxication.
5, blast furnace system 12
Be connected by adhesive tape conveyor with half way reduction and detoxication system 11, adhesive tape conveyor by the reduction of half way containing trivalent chromium agglomerate, to send into thorough for the heavy metals such as nickel chromium triangle reduction and detoxication in blast furnace system 12 in high temperature, strong reducing property atmosphere, and obtain the Ni and Cr contained pig iron, complete the harmless treatment of electroplating sludge and the regeneration of metallurgical waste, improve the metallurgical performance of sintering mixing material simultaneously.
In addition, this production line can also arrange central monitoring management control system, in this system, whole-process control, supervision and management electroplating sludge material transportation, manufacturing process, guarantee whole electroplating sludge transportation, Production Flow Chart is safe and orderly carries out, reach carrying out smoothly of electroplating sludge harmless treatment and comprehensive utilization of resources project.
Because the water content of electroplating sludge is larger, be unfavorable for balling-up, therefore need pre-treatment before use.And in electroplating sludge, there is flocculation agent, the organism that its moisture contained is flocculated mostly is included in molecular structure gap, and existing dewatering (as horizontal centrifugal dehydration, filter press, belt press filtration, high-temperature hot hydrolysis) is all difficult to remove.Therefore the requirement in order to make electroplating sludge meet follow-up disposing technique, has to pass through electroplating sludge pretreatment system and carries out deep dehydration, meet the electroplating sludge after moisture requirement again through handling equipment enter colter mixing make core system.
Therefore process system can also arrange electroplating sludge pretreatment system in front end, and native system adopts high-pressure machinery metal plate-and-frame filter press to dewater primarily of filtering equipment, and press filtration pressure can reach 50kgf/cm
2, handling equipment, the composition such as test set and watch-dog.
See Fig. 2, be below the concrete technology flow process adopting this system:
(1) electroplating sludge ball is made
A adopts electroplating sludge pretreatment system, is the mud cake of water ratio≤60% by electroplating sludge pre-treatment
Pretreated electroplating sludge and gravitational dust collection ash are made mixing in core system 6 at batch mixing and are made the ball of particle diameter for (3 ~ 6) mm by b
(2) enter pre-coated the wrapping up in system 7 equipment of ball shielding and carry out pre-coated wrapping up in
Pre-coated material of wrapping up in is sent into shielding and pre-coatedly to be wrapped up in system by a together with ball
B opens the pre-coated system device of wrapping up in of ball shielding and fully carries out pre-coated wrapping up in electroplating sludge ball
(3) enter in secondary balling-up manufacturing system equipment and carry out secondary pelletizing
Electroplating sludge ball after pre-coated wrapping up in and sulfate slag, metallurgical waste enter secondary balling-up manufacturing system, add appropriate active reduction compoiste adhering liquid make the electroplating sludge compound ball of particle diameter at (3 ~ 12) mm when conventional balling equipment pelletizing.
A sulfate slag and metallurgical waste enter spherical shell material deposit feed proportioning system 3 after pretreatment, then enter Preblend system PBS 5;
Electroplating sludge ball is sent in secondary balling-up manufacturing system 9 by b, synchronously adds mixed sulfate slag and metallurgical waste;
C adds suitable active reduction compoiste adhering liquid, starts secondary balling-up manufacturing system 9 and ball and sulfate slag and metallurgical waste are made the compound ball that particle diameter is (3 ~ 12) mm
(4) by the electroplating sludge secondary composite pellet that above-mentioned process system prepares, directly send half way reduction and detoxication system 11 to as product and carry out metallurgy sintered, finally enter blast furnace system 12 and complete Detoxified treatment.
Claims (2)
1. utilize a system for metallurgy sintered blast furnace harmless treatment electroplating sludge, it is characterized in that, connected and composed successively by following system:
(1) electroplating sludge core system: adopt colter mixing equipment and balling disc, colter mixing equipment is by conveying belt clutch disk pelletizer and ball is pre-coated wraps up in system, the ball meeting Particle size requirements enters by conveying belt that ball is pre-coated wraps up in system, the ball not meeting Particle size requirements is admitted to balling disc pelletizing again, and balling disc connects by conveying belt that ball is pre-coated wraps up in system;
(2) ball is pre-coated wraps up in system: adopt balling disc, and its opening for feed connects the discharging conveyor belts of electroplating sludge core system, electroplating sludge ball is sent into balling disc, is provided with feed bin above balling disc, dress reductibility metallurgical waste;
(3) secondary compound ball manufacturing system: comprise spherical shell material deposit feed proportioning system, Preblend system PBS, material buffer storehouse, active reduction compound sticking integrated system, secondary material compound balling-up system, composite pellet surge bunker;
Described spherical shell material deposit feed proportioning system has sulfate slag feed bin, gravitational dust collection ash feed bin and metallurgical dedusting ash feed bin and feeding belt, and the outlet of each feed bin all aims at feeding belt, and the end of feeding belt connects Preblend system PBS;
Described Preblend system PBS adopts double-spiral mixer, and its discharge end connects material surge bunker by transfer roller;
Described material buffer storehouse is arranged in that ball is pre-coated to be wrapped up in above the material conveyer belt that is connected between the discharge end of system and the feed end of secondary material compound balling-up system;
Described active reduction compound sticking integrated system comprises the head tank, adhering liquid Preparation equipment and the container for storing liquid that connect successively, head tank is for storing binding agent raw material, binding liquid Preparation equipment is high speed dispersion reactor, and for preparing binding liquid, container for storing liquid is for storing the binding liquid configured; Transfer roller is had between head tank and binding liquid Preparation equipment, raw material passes through transfer roller feeding in binding liquid Preparation equipment, binding liquid Preparation equipment is connected by pipeline and pump with between container for storing liquid, the binding liquid prepared is by storing in pump delivery to container for storing liquid, container for storing liquid and each pelletizing system are again by pipeline and high-pressure pump equipment connection, and the binding liquid in container for storing liquid is delivered in each pelletizing system by high-pressure pump equipment carries out pelletizing;
Described secondary material compound balling-up system adopts balling disc;
Described composite pellet surge bunker is arranged in the discharge end of secondary material compound balling-up system;
(4) half way reduction and detoxication system
Described half way reduction and detoxication Operation system setting, at the discharge end of composite pellet surge bunker, comprises transfer roller and sinter machine;
(5) blast furnace system: be arranged on transfer roller end;
Above electroplating sludge core system, ball be pre-coated wraps up in system and secondary compound ball manufacturing system is arranged in airtight environment.
2. the system utilizing metallurgy sintered blast furnace harmless treatment electroplating sludge according to claim 1, is characterized in that, be also provided with electroplating sludge pretreatment system, comprise filtering equipment, handling equipment, test set and watch-dog; Described filtering equipment adopts high-pressure machinery metal plate-and-frame filter press, and dewater to electroplating sludge, press filtration pressure reaches 50kgf/cm
2, filtering equipment connects described electroplating sludge core system by handling equipment, and test set and watch-dog carry out signal with filtering equipment and be connected.