CN204154114U - Ironmaking stove - Google Patents
Ironmaking stove Download PDFInfo
- Publication number
- CN204154114U CN204154114U CN201420546518.0U CN201420546518U CN204154114U CN 204154114 U CN204154114 U CN 204154114U CN 201420546518 U CN201420546518 U CN 201420546518U CN 204154114 U CN204154114 U CN 204154114U
- Authority
- CN
- China
- Prior art keywords
- stove
- ironmaking
- tack claw
- utility
- sheet metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model discloses a kind of ironmaking stove, comprise: stove sheet metal shell, reasonable Arrangement be welded in the good refractory metal of heat conductivility inside stove sheet metal shell or nonmetallic heat conduction tack claw, and ramming the amorphous refractory material be consolidated on this tack claw.Stove housing adopts the sheet metal that mechanical strength is large; Because heat conduction tack claw adds heat conductivility and the heat impact strength of amorphous refractory lining, thus the water-cooled protective effect of stove liner is strengthened.Further, also easily form stable dross layer on the surface of liner, thus make the liner of stove obtain more effectively protecting.The most important thing is due to the heat conduction tack claw of the present utility model material not affecting molten steel quality, even if therefore in the use latter stage of ironmaking stove, also can normally use.
Description
Technical field
The utility model relates to metallic iron or ferroalloy field of metallurgy, especially relates to flash ironmaking stove.
Background technology
The in-furnace temperature such as blast furnace and flash iron-smelting furnace can up to 1550 DEG C, and the solution usually adopted at present is in refractory brick marshalling, inlay expensive copper water cooling wall or copper water jacket.Although fine copper heat conductivility is good, fusing point only 1083 DEG C, if it is careless slightly therefore to supply water, water-cooled protection element melts rapidly, and this is the major reason that various ironmaking stove copper water-cooling wall or Copper Water Jacket leakage accident happen occasionally.Copper water cooling element can peel off because of high temperature corrosion inevitably in running on the other hand, causes the hot metal composition of output defective because of cupric time serious.Seek that cost is low, security of operation, easily construction and the ironmaking stove liner repaired and be the common requirement of steel industry.
Utility model content
Given this, the utility model provides a kind of ironmaking stove.
Ironmaking stove has blast furnace and various non-blast furnace ironmaking stove.Described ironmaking stove comprises: stove sheet metal shell, reasonable Arrangement be welded in the good refractory metal of heat conductivility inside stove sheet metal shell or nonmetallic heat conduction tack claw, and ramming the amorphous refractory material member be consolidated on this tack claw.Meanwhile, one circle spray pipe and corresponding raggle are at least set in stove hull outside.Stove housing adopts the metallic plate that mechanical strength is large; Spray pipe and corresponding raggle are fixed on the outside of described stove housing, and spray pipe to the direct continual even water spray in top of stove hull outside, and forms uniform moisture film in stove hull outside face, and is finally discharged by raggle; Because heat conduction tack claw adds heat conductivility and the heat impact strength of amorphous refractory lining, thus the water-cooled protective effect of stove liner is strengthened.Further, also easily form stable dross layer on the surface of liner, thus make the liner of stove obtain more effectively protecting.The most important thing is because heat conduction tack claw of the present utility model belongs to the material not affecting molten steel quality, even if therefore in the use latter stage of ironmaking stove, also can normally use.
In the technique scheme of this ironmaking with stove, can avoid adopting expensive high refractory brick and fine copper water-cooling wall or water jacket, thus significantly reduce the cost of ironmaking stove.Further, the ironmaking stove that the utility model provides is without copper liner and construction method, and construction is simple, and easy spray repair is repaired, simultaneously low to water quality requirement, and safety.
According to an embodiment of the present utility model, described ironmaking stove is 2000m
3blast furnace.In-furnace temperature is 1550 DEG C, produces the pig iron 1,600,000 tons per year.
According to an embodiment of the present utility model, described ironmaking stove is the flash iron-smelting furnace of reduction tower internal diameter 3 meters, high 7 meters.In-furnace temperature is 1200 DEG C, produces the pig iron 400,000 tons per year.
According to another embodiment of the present utility model, described High-temp. kiln is the flash iron-smelting furnace of reduction tower internal diameter 10 meters, high 7 meters.In-furnace temperature is 1200 DEG C, produces the pig iron 1,300 ten thousand tons per year.
According to an embodiment of the present utility model, described iron-smelting furnace kiln shell body adopts the manufacture of Boiler Metallic plate; Arranged outside 2 layers of spray pipe of stove housing and corresponding raggle; Described tack claw, adopts the manufacture of regular screw threads metal, and adopts welding manner to be vertically fixed on the inner side of described stove housing.
According to an embodiment of the present utility model, described tack claw length is 70mm.
The aspect that the utility model is additional and advantage will part provide in the following description, and part will become obvious from the following description, or be recognized by practice of the present utility model.
Accompanying drawing explanation
Fig. 1 is the schematic diagram of the ironmaking flash iron-smelting furnace according to the utility model embodiment;
Fig. 2 is the tack claw schematic diagram of the amorphous refractory lining of ironmaking stove according to the utility model embodiment.
Detailed description of the invention
Be described below in detail embodiment of the present utility model, the example of described embodiment is shown in the drawings, and wherein same or similar label represents same or similar element or has element that is identical or similar functions from start to finish.Be exemplary below by the embodiment be described with reference to the drawings, be intended to for explaining the utility model, and can not be interpreted as restriction of the present utility model.
1-accompanying drawing 2 illustrates the structure of the reduction tower amorphous fire proofed wood section liner according to ironmaking flash iron-smelting furnace of the present utility model below with reference to accompanying drawings.
Figure 1 shows the schematic diagram producing the ironmaking flash iron-smelting furnace 100 of the pig iron 1,300 ten thousand tons of embodiments according to of the present utility model every year.As shown in FIG., according to an embodiment of the present utility model, this ironmaking flash iron-smelting furnace 100 comprises: cavity showy reduction tower 1, for bearing the preliminary reduction chemical reaction of iron ore concentrate.Reductive coke molten bath 2, the bottom being arranged on described reduction tower 1 of integration, for accepting the melt that reduction tower produces.Vertical waste heat boiler 3, integrated setting at the afterbody in described molten bath 2, for discharging the flash iron-smelting furnace coal gas containing carbon monoxide and hydrogen, and the waste heat in gas recovery.Reduction tower shell, adopts the boiler plate manufacture of thickness 25mm.Spray pipe and raggle (scheming not shown), be arranged on the outside of reaction tower housing, totally 2 layers.Tack claw 7, adopts regular screw threads steel making, diameter 15mm, height 70mm, and adopts welding manner to be fixed on the inner side of described reduction tower shell, as shown in Figure 2.Amorphous refractory lining is High-Alumina and silicon carbide, ramming thickness 70mm.Cooling water temperature rise about 10 DEG C.
Alternatively, the shape of cross section of tack claw 7 is circular, oval, square or flat etc., and the surface of tack claw 7 is flank, male and fomale(M&F) or light face etc.It is to be appreciated that the concrete shape of tack claw 7 can be arranged according to actual requirement, to strengthen the water-cooled protective effect of stove liner.
Alternatively, the sectional area of tack claw 7 is 0.2 ~ 7cm
2, the length of tack claw 7 is 2 ~ 30cm.It should be noted that, the size of tack claw 7 can be arranged according to actual requirement, to meet actual requirement better.
Further, a circle or multi-turn spray pipe and corresponding raggle is had in stove sheet metal shell arranged outside.When the direct continual even water spray in the described top to stove hull outside, can form uniform moisture film in stove hull outside face, the water flowed down can be discharged by raggle.
Wherein, during construction, tack claw 7 should clean in advance, and surface should without oil stain or other dirt, and stand-by tack claw 7 should straight nothing bend, and vertically firmly should be fixed on the inner side of stove steel plate housing during welding, perpendicularity deviation should be less than 2 degree, and position deviation should be less than 3mm.
According to above-described embodiment of the present utility model, it should be noted that, the utility model is not limited thereto, and the described cavity reduction tower 1 that floats can be configured for other stove mode.Above-described ironmaking flash iron-smelting furnace embodiment is also the object being only limitted to illustrate, instead of in order to limit protection domain of the present utility model.
In description of the present utility model, it will be appreciated that, term " " center ", " transverse direction ", " length ", " on ", D score, " left side ", " right side ", " vertically ", " level ", " top ", " end " " interior ", " outward ", orientation or the position relationship of the instruction such as " circumference " are based on orientation shown in the drawings or position relationship, only the utility model and simplified characterization for convenience of description, instead of indicate or imply that the device of indication or element must have specific orientation, with specific azimuth configuration and operation, therefore can not be interpreted as restriction of the present utility model.In description of the present utility model, the implication of " multiple " is two or more, unless otherwise expressly limited specifically.
In the utility model, unless otherwise clearly defined and limited, the term such as term " installation ", " being connected ", " connection ", " fixing " should be interpreted broadly, and such as, can be fixedly connected with, also can be removably connect, or integral; Can be directly be connected, also indirectly can be connected by intermediary, can be the connection of two element internals or the interaction relationship of two elements.For the ordinary skill in the art, the concrete meaning of above-mentioned term in the utility model can be understood as the case may be.
In the description of this description, specific features, structure, material or feature that the description of reference term " embodiment ", " some embodiments ", " example ", " concrete example " or " some examples " etc. means to describe in conjunction with this embodiment or example are contained at least one embodiment of the present utility model or example.In this manual, to the schematic representation of above-mentioned term not must for be identical embodiment or example.And the specific features of description, structure, material or feature can combine in one or more embodiment in office or example in an appropriate manner.In addition, when not conflicting, the feature of the different embodiment described in this description or example and different embodiment or example can carry out combining and combining by those skilled in the art.
Although illustrate and described embodiment of the present utility model above, be understandable that, above-described embodiment is exemplary, can not be interpreted as restriction of the present utility model, those of ordinary skill in the art can change above-described embodiment, revises, replace and modification in scope of the present utility model.
Claims (7)
1. an ironmaking stove, is characterized in that, comprising:
Stove sheet metal shell;
Be welded in the tack claw inside described stove sheet metal shell; And
Ramming the amorphous refractory material member be consolidated on described tack claw.
2. ironmaking stove according to claim 1, is characterized in that, described tack claw is metal tack claw or nonmetal tack claw.
3. ironmaking stove according to claim 1, is characterized in that, the shape of cross section of described tack claw is circular, oval, square or flat, and surface is flank, male and fomale(M&F) or light face.
4. ironmaking stove according to claim 3, is characterized in that, the sectional area of described tack claw is 0.2 ~ 7cm
2, length is 2 ~ 30cm.
5. ironmaking stove according to claim 1, is characterized in that, has a circle or multi-turn spray pipe and corresponding raggle in described stove sheet metal shell arranged outside.
6. ironmaking stove according to claim 1, is characterized in that, the straight nothing of described tack claw bends, and be vertically fixed on the inner side of described stove sheet metal shell during welding, perpendicularity deviation should be less than 2 degree, and position deviation should be less than 3mm.
7. ironmaking stove according to claim 1, is characterized in that, described ironmaking stove is blast furnace or non-blast furnace ironmaking stove.