CN203999327U - The producing device of Glass tubing for a kind of LED electricity-saving lamp - Google Patents
The producing device of Glass tubing for a kind of LED electricity-saving lamp Download PDFInfo
- Publication number
- CN203999327U CN203999327U CN201420465675.9U CN201420465675U CN203999327U CN 203999327 U CN203999327 U CN 203999327U CN 201420465675 U CN201420465675 U CN 201420465675U CN 203999327 U CN203999327 U CN 203999327U
- Authority
- CN
- China
- Prior art keywords
- runway
- material road
- melting furnace
- glass tubing
- saving lamp
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The producing device that the utility model discloses a kind of LED electricity-saving lamp Glass tubing, comprises connected successively mixer, charging machine, melting furnace, trombone slide shaped device and verifying attachment, and melting furnace bottom or sidewall are provided with molybdenum electrode; Trombone slide shaped device comprises material road, material road is divided into bottom level material road, vertically rises and expect road and upper level material road, upper level material road is connected with feed basin, in feed basin, be provided with and blow bar, the lower end of feed basin is connected with air cushion runway, air cushion runway, vacuum runway, temperature regulate runway to be connected successively, and temperature regulates the exit end of runway to be connected with tractor; Temperature regulates between runway and tractor and is also provided with laser automatic tester; Verifying attachment comprises connected successively cutting machine, carding machine and verifying bench, and cutting machine is connected with tractor.Excellent, durable, the nondiscoloration of the Glass tubing steady quality coefficient of expansion that the utility model is made, without coating, direct production sizing, acidproof, alkaline-resisting, high temperature resistant with corrode, security is good, pollution-free.
Description
Technical field
The utility model relates to the producing device of a kind of LED electricity-saving lamp Glass tubing, belongs to glasswork Recipe and manufacture technology field.
Background technology
LED is as novel energy-conserving light source, compared with traditional set lights, has the advantages such as energy-saving and environmental protection, the life-span is long, volume is little, developed to domestic light application place by open air.Current, the tubing of LED energy-saving lamp tube adopts " partly moulding half aluminium " structure more, and tubing is made up of aluminium alloy and PC cover, and " prolate bar shaped " driving power is placed in aluminium alloy semicircular cavity, and the light of LED lamp plate covers ejaculation by PC.But there is following problem in the LED energy-saving lamp tube of this structure: (1) efficiency of assembling is low: when assembling, need that " prolate bar shaped " driving power is added to insulating protective layer and fill in aluminium alloy semicircular cavity again, aluminium alloy and PC cover also need to be assembled together; (2) poor safety performance: only have insulation layer as thin as a wafer between the aluminium base of lamp plate and the aluminium alloy of lamp housing as isolation, touching load has the danger of electric shock, is difficult for by CE and UL certification; (3) transmittance of PC cover is lower, and whiteness is poor, and unfavorable output of using up is used the easy variable color of fluorescent tube, resistant, poor corrosion resistance for a long time; (4) cost of tubing is higher.
Along with growing and scientific and technical the advancing by leaps and bounds of LED industry, the particularly requirement of country to LED product in recent years, the environmental requirement of especially outer encapsulation is more and more higher.Utilize LED illuminating lamp shade and the fluorescent tube that frosting and dusting glass material are made also to occur, LED illuminating lamp shade and the fluorescent tube assembling process of glass material are simple thereupon, and safety performance is good, and the cost of tubing is low, and use properties is good; But the rare earth powder in mat glass and dusting glass desired raw material and the easy contaminate environment of part rare metal, the coating of dusting glass very easily variable color with come off.
On the other hand, at present LED with the making employing of Glass tubing be the method for traditional danner process fuel traditional heating, temperature measuring gauge measured temperature error is large, and can be serious by the erosion of high temp glass immersion, temperature shows ineffective, and the investment of equipment is large, and the construction period is long, energy consumption is large, it is also large to pollute.
Summary of the invention
The purpose of this utility model is to provide the producing device of a kind of LED electricity-saving lamp Glass tubing, adopts all-electric melting furnace Vello process to draw, manufacture craft advanced person, and labour intensity is little, save the energy, safety, efficiency is high, cost is low.
For achieving the above object, the utility model adopts following technical scheme:
A producing device for Glass tubing for LED electricity-saving lamp, comprises connected successively mixer, charging machine, melting furnace, trombone slide shaped device and verifying attachment, and described melting furnace bottom or sidewall are provided with molybdenum electrode; Described trombone slide shaped device comprises material road, described material road is divided into three sections, be followed successively by bottom level material road, vertically rise and expect road and upper level material road, wherein bottom level material road is connected with melting furnace, vertically rise and expect that the stage casing in road is provided with molybdenum electrode, upper level material road is connected with the feed basin for refining, in described feed basin, be provided with and blow bar perpendicular to feed basin horizontal plane, the lower end of feed basin is connected with air cushion runway, air cushion runway, vacuum runway, temperature regulate runway to be connected successively, and temperature regulates the exit end of runway to be connected with tractor; Described temperature regulates between runway and tractor and is also provided with laser automatic tester; Described verifying attachment comprises connected successively cutting machine, carding machine and verifying bench, and described cutting machine is connected with tractor.
Described melting furnace is T-shaped all-electric melting furnace, and kiln body is hexagon.
The molybdenum electrode of described melting furnace is divided into 6 of starting electrodes, inserts on melting furnace bottom or sidewall; 18 of main electrodes, are evenly arranged in melting furnace surrounding bottom.
In described melting furnace bottom and top, bottom level material road, vertical rise material road, upper level material road and feed basin, be equipped with temperature measurement-control instrument.
Described temperature measurement-control instrument is platinum rhodium thermopair.
The length of described air cushion runway is 1200mm, and the length of vacuum runway is 6000mm, and it is 20000mm that temperature regulates the length of runway.
Described verifying bench comprises meter ruler and wall thickness measurer.
This LED electricity-saving lamp Glass tubing, made by the starting material of following weight part:
Quartz sand 100-120 part, borax 20-30 part, boric acid 6-10 part, aluminium hydroxide 5-8 part, sodium-chlor 0.2-0.3 part, calcium phosphate 5-8 part, magnesium oxide 3-6 part, glass cullet 60-80 part, pigment 0-0.1 part;
In described quartz sand, SiO
2quality percentage composition>=99.3%, Fe
2o
3quality percentage composition≤0.03%;
In described borax, B
2o
3quality percentage composition>=47%, Na
2quality percentage composition>=21% of O, Fe
2o
3quality percentage composition≤0.005%;
In described boric acid, B
2o
3quality percentage composition>=56%, Fe
2o
3quality percentage composition≤0.01%;
In described aluminium hydroxide, calculate Al by wet basis
2o
3quality percentage composition>=62%, Fe
2o
3quality percentage composition≤0.03%;
In described calcium phosphate, Ca
3(PO
4)
2quality percentage composition>=98%;
In described magnesium oxide, quality percentage composition >=99.9% of MgO, quality percentage composition≤0.005% of Fe;
The piece footpath of described glass cullet is 0.2-3cm.
Described pigment is cobalt oxide or cupric oxide.
Preferably, described LED electricity-saving lamp Glass tubing, made by the starting material of following weight part:
110 parts of quartz sands, 25 parts of boraxs, 8 parts of boric acid, 6 parts, aluminium hydroxide, 0.25 part, sodium-chlor, 6 parts, calcium phosphate, 5 parts, magnesium oxide, 70 parts of glass cullet, 0.05 part of pigment.
Wherein, boric acid and borax can form boron trioxide, in glass, jointly form structural network with silicon-oxy tetrahedron, can effectively reduce the coefficient of expansion, can also improve burn-off rate.
Sodium-chlor can play clarification, under chemical reaction, bubble is got rid of smoothly;
The glass cullet of certain piece footpath size can improve melting rate, accelerate glass melting, also help clarification and homogenization, make glass metal quality more stable, and bubble can be effectively controlled.
This LED electricity-saving lamp is adopted with the following method and is made with Glass tubing:
(1) raw-material preparation: take each raw material according to said ratio, send in mixer mixed preparing even;
(2) founding of raw material: the raw material of step (1) mixed preparing is joined in melting furnace, adopt electrically heated, controlled melting pond temperature is 1380-1460 DEG C, and each group of material composition is melted to after fining glass liquid, enters material road;
(3) draw moulding: by the glass metal that flows into material road by refining, scavenger system vertically downward after, level is introduced air cushion runway, glass metal is held up in air cushion runway, forms and suspends; Then by tractor horizontally tracting, successively through making Glass tubing keep stressed uniform vacuum runway, and Glass tubing is lowered the temperature gradually, the temperature of eliminating thermal stresses regulates runway, draws moulding;
(4) test package: the LED electricity-saving lamp of moulding is the cutting through cutting machine with Glass tubing, is transported to verifying bench tests and pack warehouse-in by machine in the wrong.
In step (2), the speed that adds of raw material is 10-15Kg/min.
In step (3), adopt laser automatic tester to detect online the outside dimension of Glass tubing.
The beneficial effects of the utility model:
(1) the glass lamp steady quality that adopts device of the present utility model to make, the coefficient of expansion is excellent, durable, nondiscoloration, without coating, direct production sizing, acidproof, alkaline-resisting, high temperature resistant and corrosion, has solved the coming off of easy to change, potential safety hazard, environmental pollution, painting bisque of PC material, frosting, the coating generation of LED electricity-saving lamp Glass tubing, allochroic problem effectively.
(2) the utility model has solved the volatilization of the material component of traditional kiln fusing generation, the problems such as energy dissipation, manufacture craft advanced person, science, reasonable, feasible, there is labour intensity little, save the energy, efficiency is high, and low cost and other advantages is applicable to make versicolor LED power saving fluorescent lamps glass-tube.
(3) melting furnace of the present utility model adopts the inner heating of molybdenum electrode interpolation type, reduced calorific loss simultaneously, All Electric Melting Furnace is realized its fusing by glass metal self-conductive, it is internal heat type, owing to being vertical fusing, metal level is covered by one deck raw material, and the temperature of upper space only has 100-250 DEG C of left and right; And flame furnace is to realize from surface to conducted inside convection current by the hyperthermia radiation of flame, glass metal upper space temperature is up to 1600 DEG C, and furnace roof heat radiation is very large, even through heat exchanging apparatus, the temperature of waste gas is still very high, and thermo-efficiency can only reach 30%; And glass electric melting thermo-efficiency of the present invention can reach 78% left and right, make the energy consumption of unit weight glass low, the thermo-efficiency of smelting furnace is high.
(4) stage casing in vertical rising material of the present utility model road is provided with molybdenum electrode, makes the glass metal upper level material road of flowing through smoothly.
(5) Glass tubing of the present utility model traction moulding under the affecting of tractor, laser diameter measuring instrument is measured the outside dimension of Glass tubing, forms closed loop with tractor pulling speed, makes product surface trimming, has improved quality product.
Brief description of the drawings
Fig. 1 is of the present utility model for making the apparatus structure schematic diagram of LED electricity-saving lamp Glass tubing;
Wherein, 1-mixer, 2-charging machine, 3-melting furnace, 4-bottom level material road, the 5-material road that vertically rises, 6-upper level material road, 7-feed basin, 8-blows bar, 9-air cushion runway, 10-vacuum runway, 11-temperature regulates runway, 12-laser automatic tester, 13-tractor, 14-cutting machine, 15-carding machine, 16-check-out console.
Embodiment
The utility model is further described in conjunction with the embodiments, should be noted that following explanation is only in order to explain the utility model, does not limit its content.
Embodiment 1
As shown in Figure 1, for making the device of LED electricity-saving lamp Glass tubing, comprise connected successively mixer 1, charging machine 2, melting furnace 3, trombone slide shaped device and verifying attachment, described melting furnace 3 bottoms or sidewall are provided with molybdenum electrode, described trombone slide shaped device comprises material road, described material road is divided into three sections, be followed successively by bottom level material road 4, material road 5 and upper level material road 6 vertically rise, wherein bottom level material road 4 is connected with melting furnace 3, vertically rise and expect that the stage casing in road 5 is provided with molybdenum electrode, upper level material road 6 is connected with the feed basin 7 for refining, in described feed basin 7, be provided with and blow bar 8 perpendicular to feed basin horizontal plane, the lower end of feed basin 7 is connected with air cushion runway 9, air cushion runway 9, vacuum runway 10, temperature regulates runway 11 to be connected successively, temperature regulates the exit end of runway 11 to be connected with tractor 13, the length of described air cushion runway is 1200mm, the length of vacuum runway is 6000mm, it is 20000mm that temperature regulates the length of runway, described temperature regulates between runway 11 and tractor 13 and is also provided with laser automatic tester 12, described verifying attachment comprises connected successively cutting machine 14, carding machine 15 and verifying bench 16, and described cutting machine 14 is connected with tractor 13.Wherein, be transformed into T-shaped All Electric Melting Furnace by horseshoe type flame kiln, kiln body, by 45 squares of original rectangles, is transformed into 18 squares, hexagon, and refractory materials consumption reduces greatly, has saved cost.The molybdenum electrode of melting furnace is divided into 6 of starting electrodes, inserts on melting furnace bottom or sidewall; 18 of main electrodes, are evenly arranged in melting furnace surrounding bottom.Melting furnace bottom and top, bottom level material road, vertical material road, upper level material road and the feed basin of rising are equipped with platinum rhodium thermopair.Described verifying bench comprises meter ruler and wall thickness measurer.
This LED electricity-saving lamp Glass tubing, made by the starting material of following weight part:
110 kilograms of quartz sands, 25 kilograms of boraxs, 8 kilograms of boric acid, 6 kilograms, aluminium hydroxide, 0.25 kilogram, sodium-chlor, 6 kilograms, calcium phosphate, 5 kilograms, magnesium oxide, 70 kilograms of glass cullet, 0.05 kilogram of cobalt oxide.
Wherein, in quartz sand, SiO
2quality percentage composition>=99.3%, Fe
2o
3quality percentage composition≤0.03%; In borax, B
2o
3quality percentage composition>=47%, Na
2quality percentage composition>=21% of O, Fe
2o
3quality percentage composition≤0.005%; In boric acid, B
2o
3quality percentage composition>=56%, Fe
2o
3quality percentage composition≤0.01%; In aluminium hydroxide, calculate Al by wet basis
2o
3quality percentage composition>=62%, Fe
2o
3quality percentage composition≤0.03%; In calcium phosphate, Ca
3(PO
4)
2quality percentage composition>=98%; In magnesium oxide, quality percentage composition>=99.9% of MgO, quality percentage composition≤0.005% of Fe; The piece footpath of glass cullet is 1.5cm.
This LED electricity-saving lamp is adopted with the following method and is made with Glass tubing:
(1) raw-material preparation: adopt computer control weighing precision and batch mixing uniformity coefficient, by after each raw material accurate weighing, enter in mixer mixed preparing even according to said ratio;
(2) founding of raw material: the raw material of step (1) mixed preparing is joined in melting furnace with the speed of per minute 10Kg, adopt molybdenum electrode mode to carry out electrically heated, power is controlled at 1475KW, controlling melting furnace temperature is 1380 ± 10 DEG C, each group of material composition is melted to after fining glass liquid, through the bottom level material road being communicated with melting furnace, glass metal flows into the material road that vertically rises and is cooled to after 1300 DEG C, flows into subsequent processing;
(3) draw moulding: by the glass metal that flows into material road by refining, scavenger system vertically downward after, level is introduced air cushion runway, glass metal is held up in air cushion runway, forms and suspends; Then by tractor horizontally tracting, successively through making Glass tubing keep stressed even, avoid occurring the vacuum runway of oval tube or inclined to one side wall thickness, and Glass tubing is lowered the temperature gradually, eliminate the insulation runway of thermal stresses, adopt the outside dimension of the online detection Glass tubing of laser automatic tester, draw moulding;
(4) test package: the LED electricity-saving lamp of moulding is the cutting through cutting machine with Glass tubing, is transported to verifying bench tests and pack warehouse-in by machine in the wrong.
Embodiment 2
Use the device of Glass tubing with embodiment 1 for the preparation of this LED electricity-saving lamp.
This LED electricity-saving lamp Glass tubing, made by the starting material of following weight part:
Quartz sand double centner, 30 kilograms of boraxs, 6 kilograms of boric acid, 8 kilograms, aluminium hydroxide, 0.2 kilogram, sodium-chlor, 8 kilograms, calcium phosphate, 3 kilograms, magnesium oxide, 80 kilograms of glass cullet, 0.05 kilogram of cupric oxide.
Wherein, in quartz sand, SiO
2quality percentage composition>=99.3%, Fe
2o
3quality percentage composition≤0.03%; In borax, B
2o
3quality percentage composition>=47%, Na
2quality percentage composition>=21% of O, Fe
2o
3quality percentage composition≤0.005%; In boric acid, B
2o
3quality percentage composition>=56%, Fe
2o
3quality percentage composition≤0.01%; In aluminium hydroxide, calculate Al by wet basis
2o
3quality percentage composition>=62%, Fe
2o
3quality percentage composition≤0.03%; In calcium phosphate, Ca
3(PO
4)
2quality percentage composition>=98%; In magnesium oxide, quality percentage composition>=99.9% of MgO, quality percentage composition≤0.005% of Fe; The piece footpath of glass cullet is 0.2cm.
This LED electricity-saving lamp is adopted with the following method and is made with Glass tubing:
(1) raw-material preparation: adopt computer control weighing precision and batch mixing uniformity coefficient, by after each raw material accurate weighing, enter in mixer mixed preparing even according to said ratio;
(2) founding of raw material: the raw material of step (1) mixed preparing is joined in melting furnace with the speed of per minute 15Kg, adopt molybdenum electrode mode to carry out electrically heated, power is controlled at 1570KW, controlling melting furnace temperature is 1460 ± 10 DEG C, each group of material composition is melted to after fining glass liquid, through the bottom level material road being communicated with melting furnace, glass metal flows into the material road that vertically rises and is cooled to after 1300 DEG C, flows into subsequent processing;
(3) draw moulding: by the glass metal that flows into material road by refining, scavenger system vertically downward after, level is introduced air cushion runway, glass metal is held up in air cushion runway, forms and suspends; Then by tractor horizontally tracting, successively through making Glass tubing keep stressed even, avoid occurring the vacuum runway of oval tube or inclined to one side wall thickness, and Glass tubing is lowered the temperature gradually, eliminate the insulation runway of thermal stresses, adopt the outside dimension of the online detection Glass tubing of laser automatic tester, draw moulding;
(4) test package: the LED electricity-saving lamp of moulding is the cutting through cutting machine with Glass tubing, is transported to verifying bench tests and pack warehouse-in by machine in the wrong.
Embodiment 3
Use the device of Glass tubing with embodiment 1 for the preparation of this LED electricity-saving lamp.
This LED electricity-saving lamp Glass tubing, made by the starting material of following weight part:
120 kilograms of quartz sands, 20 kilograms of boraxs, 10 kilograms of boric acid, 5 kilograms, aluminium hydroxide, 0.3 kilogram, sodium-chlor, 5 kilograms, calcium phosphate, 6 kilograms, magnesium oxide, 60 kilograms of glass cullet, 0.1 kilogram of cobalt oxide.
Wherein, in quartz sand, SiO
2quality percentage composition>=99.3%, Fe
2o
3quality percentage composition≤0.03%; In borax, B
2o
3quality percentage composition>=47%, Na
2quality percentage composition>=21% of O, Fe
2o
3quality percentage composition≤0.005%; In boric acid, B
2o
3quality percentage composition>=56%, Fe
2o
3quality percentage composition≤0.01%; In aluminium hydroxide, calculate Al by wet basis
2o
3quality percentage composition>=62%, Fe
2o
3quality percentage composition≤0.03%; In calcium phosphate, Ca
3(PO
4)
2quality percentage composition>=98%; In magnesium oxide, quality percentage composition>=99.9% of MgO, quality percentage composition≤0.005% of Fe; The piece footpath of glass cullet is 1.0cm.
This LED electricity-saving lamp is adopted with the following method and is made with Glass tubing:
(1) raw-material preparation: adopt computer control weighing precision and batch mixing uniformity coefficient, by after each raw material accurate weighing, enter in mixer mixed preparing even according to said ratio;
(2) founding of raw material: the raw material of step (1) mixed preparing is joined in melting furnace with the speed of per minute 13Kg, adopt molybdenum electrode mode to carry out electrically heated, power is controlled at 1500KW, controlling melting furnace temperature is 1400 ± 10 DEG C, each group of material composition is melted to after fining glass liquid, through the bottom level material road being communicated with melting furnace, glass metal flows into the material road that vertically rises and is cooled to after 1300 DEG C, flows into subsequent processing;
(3) draw moulding: by the glass metal that flows into material road by refining, scavenger system vertically downward after, level is introduced air cushion runway, glass metal is held up in air cushion runway, forms and suspends; Then by tractor horizontally tracting, successively through making Glass tubing keep stressed even, avoid occurring the vacuum runway of oval tube or inclined to one side wall thickness, and Glass tubing is lowered the temperature gradually, eliminate the insulation runway of thermal stresses, adopt the outside dimension of the online detection Glass tubing of laser automatic tester, draw moulding;
(4) test package: the LED electricity-saving lamp of moulding is the cutting through cutting machine with Glass tubing, is transported to verifying bench tests and pack warehouse-in by machine in the wrong.
Embodiment 4
Use the device of Glass tubing with embodiment 1 for the preparation of this LED electricity-saving lamp.
This LED electricity-saving lamp Glass tubing, made by the starting material of following weight part:
110 kilograms of quartz sands, 25 kilograms of boraxs, 8 kilograms of boric acid, 6 kilograms, aluminium hydroxide, 0.25 kilogram, sodium-chlor, 6 kilograms, calcium phosphate, 5 kilograms, magnesium oxide, 70 kilograms of glass cullet.
Wherein, in quartz sand, SiO
2quality percentage composition>=99.3%, Fe
2o
3quality percentage composition≤0.03%; In borax, B
2o
3quality percentage composition>=47%, Na
2quality percentage composition>=21% of O, Fe
2o
3quality percentage composition≤0.005%; In boric acid, B
2o
3quality percentage composition>=56%, Fe
2o
3quality percentage composition≤0.01%; In aluminium hydroxide, calculate Al by wet basis
2o
3quality percentage composition>=62%, Fe
2o
3quality percentage composition≤0.03%; In calcium phosphate, Ca
3(PO
4)
2quality percentage composition>=98%; In magnesium oxide, quality percentage composition>=99.9% of MgO, quality percentage composition≤0.005% of Fe; The piece footpath of glass cullet is 1.0cm.
This LED electricity-saving lamp is adopted with the following method and is made with Glass tubing:
(1) raw-material preparation: adopt computer control weighing precision and batch mixing uniformity coefficient, by after each raw material accurate weighing, enter in mixer mixed preparing even according to said ratio;
(2) founding of raw material: the raw material of step (1) mixed preparing is joined in melting furnace with the speed of per minute 15Kg, adopt molybdenum electrode mode to carry out electrically heated, power is controlled at 1570KW, controlling melting furnace temperature is 1460 ± 10 DEG C, each group of material composition is melted to after fining glass liquid, through the bottom level material road being communicated with melting furnace, glass metal flows into the material road that vertically rises and is cooled to after 1300 DEG C, flows into subsequent processing;
(3) draw moulding: by the glass metal that flows into material road by refining, scavenger system vertically downward after, level is introduced air cushion runway, glass metal is held up in air cushion runway, forms and suspends; Then by tractor horizontally tracting, successively through making Glass tubing keep stressed even, avoid occurring the vacuum runway of oval tube or inclined to one side wall thickness, and Glass tubing is lowered the temperature gradually, eliminate the insulation runway of thermal stresses, adopt the outside dimension of the online detection Glass tubing of laser automatic tester, draw moulding;
(4) test package: the LED electricity-saving lamp of moulding is the cutting through cutting machine with Glass tubing, is transported to verifying bench tests and pack warehouse-in by machine in the wrong.
Performance test:
LED electricity-saving lamp Glass tubing prepared by the utility model embodiment 1-4 carries out correlated performance test, and adopting quartz glass relative method is measured the coefficient of expansion of Glass tubing, adopts the light transmission rate of 721 type spectrophotometric determination Glass tubings, the results are shown in Table 1.
Table 1 LED electricity-saving lamp Glass tubing the performance test results
| Sample | The coefficient of expansion | Light transmission rate |
| Embodiment 1 | (3.3 scholar 0.1) × 10 -6/K | 94％ |
| Embodiment 2 | (2.9 scholar 0.1) × 10 -6/K | 92％ |
| Embodiment 3 | (3.1 scholar 0.1) × 10 -6/K | 91％ |
| Embodiment 4 | (3.4 scholar 0.1) × 10 -6/K | 95％ |
As can be seen from Table 1: the glass lamp steady quality that adopts device of the present utility model to make, the coefficient of expansion is excellent.
Claims (7)
1. a producing device for Glass tubing for LED electricity-saving lamp, is characterized in that, comprises connected successively mixer, charging machine, melting furnace, trombone slide shaped device and verifying attachment, and described melting furnace bottom or sidewall are provided with molybdenum electrode; Described trombone slide shaped device comprises material road, described material road is divided into three sections, be followed successively by bottom level material road, vertically rise and expect road and upper level material road, wherein bottom level material road is connected with melting furnace, vertically rise and expect that the stage casing in road is provided with molybdenum electrode, upper level material road is connected with the feed basin for refining, in described feed basin, be provided with and blow bar perpendicular to feed basin horizontal plane, the lower end of feed basin is connected with air cushion runway, air cushion runway, vacuum runway, temperature regulate runway to be connected successively, and temperature regulates the exit end of runway to be connected with tractor; Described temperature regulates between runway and tractor and is also provided with laser automatic tester; Described verifying attachment comprises connected successively cutting machine, carding machine and verifying bench, and described cutting machine is connected with tractor.
2. the producing device of Glass tubing for LED electricity-saving lamp as claimed in claim 1, is characterized in that, described melting furnace is T-shaped all-electric melting furnace, and kiln body is hexagon.
3. the producing device of Glass tubing for LED electricity-saving lamp as claimed in claim 1, is characterized in that, the molybdenum electrode of described melting furnace is divided into starting electrode and main electrode, and wherein starting electrode inserts on melting furnace bottom or sidewall; Main electrode is evenly arranged in melting furnace surrounding bottom.
4. the producing device of Glass tubing for LED electricity-saving lamp as claimed in claim 3, is characterized in that, the quantity of described starting electrode is 6, and the quantity of main electrode is 18.
5. the producing device of Glass tubing for LED electricity-saving lamp as claimed in claim 1, is characterized in that, in described melting furnace bottom and top, bottom level material road, vertical rise material road, upper level material road and feed basin, is equipped with temperature measurement-control instrument.
6. the producing device of Glass tubing for LED electricity-saving lamp as claimed in claim 5, is characterized in that, described temperature measurement-control instrument is platinum rhodium thermopair.
7. the producing device of Glass tubing for LED electricity-saving lamp as claimed in claim 1, is characterized in that, the length of described air cushion runway is 1200mm, and the length of vacuum runway is 6000mm, and it is 20000mm that temperature regulates the length of runway.