CN203925297U - The high carcass geological drill bit of welded type - Google Patents
The high carcass geological drill bit of welded type Download PDFInfo
- Publication number
- CN203925297U CN203925297U CN201420255561.1U CN201420255561U CN203925297U CN 203925297 U CN203925297 U CN 203925297U CN 201420255561 U CN201420255561 U CN 201420255561U CN 203925297 U CN203925297 U CN 203925297U
- Authority
- CN
- China
- Prior art keywords
- tooth
- high carcass
- mouth
- drill bit
- carcass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model discloses the high carcass geological drill bit of a kind of welded type, comprise that high carcass bores tooth, mouth of a river piece and steel body.High carcass bore tooth and the independent sinter molding of mouth of a river piece again closely connect into brill crown, bore crown laser weld on steel body; High carcass bores tooth by the work tooth layer containing broken rock abrasive particle, containing the transition tooth layer of abrasive particle and do not form containing the welding tooth layer of abrasive particle, and it is 15mm～35mm that high carcass bores tooth overall height; Mouth of a river piece can adopt simple substance powder, various metals powder or alloyed powder sintering to make.The utility model is owing to adopting high carcass to bore tooth independence sintering, and designed self adaptation wearing and tearing mouth of a river piece, sintering temperature reduces greatly, damnification of diamond grits reduces, brill tooth height improves, all have obtained in the drilling efficiency of drill bit, application life increasing substantially, can significantly reduce in geological drilling the drill bit number of times that makes a trip, be particularly suitable in 1000 meters of following deep well drilling engineerings.
Description
(1) technical field:
The utility model relates to geological prospecting drilling technology, is specially the high carcass geological drill bit of a kind of welded type.
(2) background technology:
At present, solid mineral reserve exploratory drilling enters in engineering mostly still to adopt diamond core bit, and diamond core bit manufacturing technology is through the development of many decades, aspect structure design, drilling technology, there iing certain progress, but, slower development generally speaking, strength of technical renovation is inadequate.
Diamond core bit product comprises the integral sintered method geological drill bit of intermediate frequency, galvanoplastic geological drill bit at present.
The integral sintered method geological drill bit of intermediate frequency is to adopt the manufacture of intermediate-frequency hot-pressing sintering machine, manufacture process is first the mixture of diamond and metal dust to be poured in the graphite jig of required size, then will be placed on powder through being processed to form the steel body of serrated face, by intermediate frequency electromagnetic, respond to heat and the upper downforce producing, the brill tooth of sinter molding and steel body are combined.The diamond bit sintering temperature that this method is produced is high, bores tooth interior solid degree poor, bores tooth strong not with steel body adhesion, so brill tooth height is low, and drilling efficiency, application life are all lower.
The diamond core bit > > at the people's such as Sun Youhong the renewable mouth of a river of < < (application number is 200810051152.9) patent of invention has proposed to have carried out appropriate design from structure, realize the multiple stratification of boring tooth and the mouth of a river, and guarantee that every one deck gate surface is long-pending than reaching 15%～35%, but this patent still adopts the integral sintered method manufacture of intermediate frequency, sintering temperature is high, brill tooth sintered density is low, and complex structure, manufacture difficulty is large, and mould consumption is large.
Galvanoplastic diamond core bit is at the steel body surface after surfacing, directly to plate the composite bed of metal matrix and diamond particles, and metal matrix is that valence bond is combined with steel body, so bond strength is higher; The geological drill bit metal matrix that galvanoplastic are made to diamond have than commonsense method higher control intensity, and diamond is without high-temperature damage, drill bit drilling efficiency is high; Yet it is long to electroplate drill bit Production Time, and cost is high, and carcass height is higher, and Production Time is longer, and drilling life of bit is often lower.
The manufacture method > > of a < < high-efficiency diamond geological drills of Xiao Yunjie (application number is 201110008431.9) patent of invention has proposed to adopt method for laser welding to manufacture the concept of diamond core bit for the first time, but just the simple conventional laser welding product that imitates, will bore tooth and realize and being connected with steel body.Because diamond abrasive grain content in geological drill bit brill tooth is conventionally higher, brill tooth intensity is also often lower, along with boring the increase of tooth height, bores the possibility increase of tooth fracture, and therefore, conventional bit brill tooth height is lower than 8mm, and bit life is very limited.
(3) utility model content:
For this reason, the utility model provides a kind of welded type high carcass geological drill bit, is intended to solve that mineral product geology exploration is crept in engineering, particularly 1000 meters of following deeps are crept into that middle drill bit drilling efficiency is low, application life is short and caused the drill bit problems such as frequency is high, probing overall efficiency is low, boring is easy to subside that make a trip.
The high carcass geological drill bit of welded type that can solve the problems of the technologies described above, comprise that high carcass bores tooth, mouth of a river piece and steel body, described high carcass bores tooth circumference uniform distribution on steel body, described mouth of a river piece is located at adjacent high carcass and is bored on the steel body between tooth, difference is that described high carcass brill tooth comprises the work tooth layer containing broken rock abrasive particle, the welding tooth layer that does not contain the transition tooth layer of abrasive particle and do not contain abrasive particle, it is 15mm～35mm that high carcass bores tooth overall height, wherein, described work tooth layer height is 12mm～29mm, described transition tooth layer height is 1mm～3mm, described welding tooth layer height is 2mm～3mm, be matched with high carcass and bore tooth height, described mouth of a river tile height is 5mm～15mm.
According to rock drilling object, the further setting to mouth of a river tile height: when described high carcass brill tooth overall height is chosen as 15mm～20mm, described mouth of a river tile height is chosen as 5mm～10mm; When described high carcass brill tooth height is chosen as 20mm～35mm, described mouth of a river tile height is chosen as 10mm～15mm.
Abundant for guaranteeing drilling regional water supply, interior tank and external flume are offered respectively in the inside and outside both sides (diametric(al)) of described mouth of a river piece, and the described inside and outside tank degree of depth is 1mm～5mm according to creeping into Object Selection.
For common rock drilling, generally do not need to add glomerocryst and carry out bit gauge protection, but for strong abrasive layer, described high carcass bores the inside and outside surface of tooth need inlay glomerocryst, glomerocryst mosaic site is work tooth layer or for transition tooth layer or be work tooth layer and transition tooth layer.
The broken rock abrasive particle comprising in described work tooth layer is diamond, and during hard in rock drilling is, soft formation, the mixture that the broken rock abrasive particle comprising in work tooth layer is diamond and broken glomerocryst, is realized and being crept into by volumetric fracture mode, can greatly improve drilling efficiency.
The beneficial effects of the utility model:
1, in the high carcass geological drill bit of the utility model welded type structure, high carcass bores and in toothing, welds that tooth layer has been guaranteed and the bonding strength of steel body, and transition tooth layer plays the effect of linking work tooth layer and welding tooth layer, can ensure the bulk strength of high carcass brill tooth; In preparation method, adopt advanced laser welding technology manufacture to there is large brill tooth height, can guarantee to bore the geological drill bit that tooth intensity is unlikely to fracture, this kind geological drill bit brill tooth intensity is high, drilling efficiency is high, high life, thereby greatly reduced the number of times that drill bit makes a trip, greatly improve the probing efficiency of rig-month, reduced the generation of collapse hole accident.
2, the utlity model has and bore that tooth sintered density is high, diamond fire damage is little, carcass size advantages of higher, thereby more conventional geological drill bit has much higher life-span and the higher drilling efficiency of creeping into, greatly reduced the frequency that makes a trip of drill bit, can promote greatly and creep into engineering efficiency.
(4) accompanying drawing explanation:
Fig. 1 is the three-dimensional structure diagram of a kind of embodiment of the utility model.
Fig. 2 (a) is the three-dimensional structure diagram of short teeth drill bit in Fig. 1 embodiment.
Fig. 2 (b) is the three-dimensional structure diagram of middle teeth drill bit in Fig. 1 embodiment.
Fig. 2 (c) is the three-dimensional structure diagram of high teeth drill bit in Fig. 1 embodiment.
Fig. 3 is that in Fig. 1 embodiment, high carcass bores the three-dimensional structure diagram that tooth and mouth of a river piece form brill crown.
Fig. 4 (a) is for boring the structural representation of crown in resin circle banding Fig. 3.
Fig. 4 (b) is the A-A cut-away view in Fig. 4 (a).
Figure number sign: 1, high carcass bores tooth; 1-1, work tooth layer; 1-2, transition tooth layer; 1-3, welding tooth layer; 2, mouth of a river piece; 3, bore crown; 4, steel body; 5, external flume; 6, interior tank; 7, resin circle.
(5) specific embodiment:
Below in conjunction with accompanying drawing illustrated embodiment, the technical solution of the utility model is described further.
The high carcass geological drill bit of the utility model welded type comprises the brill crown 3 on the top being connected and the steel body 4 of bottom, described brill crown 3 comprises that high carcass bores tooth 1 and mouth of a river piece 2, described high carcass bores tooth 1 circumference uniform distribution on steel body 4, and piece 2 intervals, the described mouth of a river are located at adjacent high carcass and are bored on the steel body 4 between tooth 1, described high carcass bores tooth 1 and comprises, in, lower three parts, be respectively top containing the work tooth layer 1-1 of broken rock abrasive particle, middle part does not contain the transition tooth layer 1-2 of abrasive particle, bottom does not contain the welding tooth layer 1-3 of abrasive particle, it is 15mm～35mm that high carcass bores tooth 1 overall height, according to different drilling conditions, the height of described work tooth layer 1-1 is selected between 12mm～29mm, described transition tooth layer 1-2 height is selected between 1mm～3mm, the height of described welding tooth layer 1-3 is selected between 2mm～3mm, in order to match with the overall height of high carcass brill tooth 1, the height of described mouth of a river piece 2 is selected between 5mm～15mm, described mouth of a river piece 2 inside and outside both sides radially offer respectively interior tank 6 and external flume 5, the degree of depth of described inside and outside tank 6,5 is chosen between 1mm～5mm according to drilling condition, as shown in Figure 1, Figure 2 shown in (a), Fig. 2 (b), Fig. 2 (c), Fig. 3.
In said structure, described transition tooth layer 1-2 plays linking work tooth layer 1-1 and the effect of welding tooth layer 1-3, ensures the anti-breaking strength of boring tooth integral body; Welding tooth layer 1-3 is that laser weld special powder sintering forms, and has higher densified sintering product and anti-scorification loss ability, guarantees to bore after tooth 3 hats weld with steel body 4 to have higher bonding strength.
The effect of described mouth of a river piece 2 is to support high carcass to bore tooth 1, improve its anti-tangential breaking strength and radial fragmentation intensity, the height that the height of described mouth of a river piece 2 bores tooth 1 according to high carcass designs: the height that bores tooth 1 when high carcass is between 15mm～20mm time, and the height of mouth of a river piece 2 is 5～10mm; When the height of high carcass brill tooth 1 is 20mm～35mm, the height of mouth of a river piece 2 is 10mm～15mm.
According to drilling condition needs, described high carcass bores the inside and outside surface inserting glomerocryst of tooth 1, and glomerocryst mosaic site is work tooth layer 1-1 or for transition tooth layer 1-2 or be work tooth layer 1-1 and transition tooth layer 1-2; The broken rock abrasive particle comprising in described work tooth layer 1-1 is diamond, or is the mixture of diamond and broken glomerocryst, as shown in Figure 1, Figure 2, Figure 3 shows.
The manufacture method of the high carcass geological drill bit of the utility model welded type:
1, make and bore crown 3.
1., described high carcass bores tooth 1, mouth of a river piece 2 independent sinter molding respectively, fits together to sinter an integral body into and bore crown 3, bonding agent composition is the PM sintered materials of the simple substance such as WC, Co, Cu, Sn, Ni or alloy, as shown in Figure 3.
When described high carcass bores tooth 1, the independent sinter molding of mouth of a river piece 2 difference, can first adopt respectively the punching block idiosome of colding pressing, then be assembled in respectively in carbon mould, adopt vacuum resistance pressing sintering to carry out sintering, in making, become in crown 3 processes, the high carcass that needs to cold pressing respectively bores the idiosome of colding pressing of tooth 1, mouth of a river piece 2, and the idiosome of then colding pressing is assembled in carbon mould and sinters ring into.
Because boring tooth 1, high carcass adopts individual resistors hot pressed sintering, the integral sintered method of intermediate frequency with respect to conventional bit, sintering temperature reduces greatly, thereby reduced adamantine strength damage, also reduced the fire damage of sintering mold, sintering efficiency promotes greatly, and carcass density, intensity etc. have all obtained significantly promoting, thereby the drilling efficiency of drill bit, drilling footage number have also obtained and increased substantially.
2., described high carcass bores the cold moudling separately that is made as of tooth 1 and mouth of a river piece 2, high carcass brill tooth 1 after moulding and mouth of a river piece 2 fit together and are sintered into whole brill crown 3 separately, bonding agent composition is the PM sintered materials of the simple substance such as WC, Co, Cu, Sn, Ni or alloy, as shown in Figure 3.
3., described high carcass bore tooth 1 adopt first cold pressing after heat pressing process, the idiosome density of colding pressing is 50%～70%, and hot pressing adopts vacuum electric resistive hot pressed sintering, and sintering temperature is 750 ℃～900 ℃, temperature retention time 3min～8min, maximum moulding pressure is 20MPa～30MPa; Described mouth of a river piece 2 adopts simple substance powder or various metals powder or alloyed powder sintering to form, sintered density is 50%～100%, the composition of mouth of a river piece 2, according to character (comprising abrasiveness, hardness, the intensity etc.) design of creeping into rock stratum, is generally the mixture of the metallic elements such as Fe, Co, Cu.
It is by 2 compressions of mouth of a river piece with the mode that mouth of a river piece 2 is connected to become whole brill crown 3 that high carcass bores tooth 1, by horizontal squeezing action power, make itself and high carcass bore tooth 1 and realize mechanical build-in, or adopt method for brazing welding (welding material adopts weld tabs or welding wire or soldering paste etc.), or adopt infusion process realization to squeegee and combination.
2, with method for laser welding, the brill crown 3 that 1., 2., 3. method is made is respectively welded on steel body 4, as shown in Figure 1, Figure 2 shown in (a), Fig. 2 (b), Fig. 2 (c).
Before welding, use resin circle 7 lock rings as shown in Fig. 4 (a), Fig. 4 (b) firmly to bore crown 3, adopting plain grinding equipment to bore crown 3 bottoms polishes and bright and clean processing, then brill crown 3 and steel body 4 are arranged on respectively on special fixture, utilize laser-beam welding machine to complete welding sequence, welding wall thickness is typically chosen in 6mm～15mm according to drill bit inside/outside diameter size, welding method can connect welding for laser straight, also can be laser melting coating welding etc., more than weld strength requires to reach 800MPa, welding requirements weld seam is full, tight.After having welded, can carry out temper to drill bit, to reduce the fire damage of welding, improve weld strength, temperature is 250 ℃～350 ℃, and temperature retention time is 4 hours.
Complete after welding sequence, the manufacture craft of geology drill bit, further carries out the machine of drill bit routinely, is included in mouth of a river piece 2 positions and processes external flume 5 and interior tank 6, and steel body 4 is according to required size car inside and outside circle processed, chamfering, screw thread processing etc.
Use of the present utility model:
Drill bit shown in (a), Fig. 2 (b), Fig. 2 (c) is as shown in Figure 1, Figure 2 arranged on the drilling rod of geological drilling rig, by the High Rotation Speed of drilling rod, and pass into drilling fluid in well, high carcass on drill bit bores tooth 1 and realizes creeping into rock stratum, supporting role due to mouth of a river piece 2, high carcass bores tooth 1 and has higher anti-breaking strength, has ensured that high carcass bores the normal use of tooth 1; Particular design due to formula composition, mouth of a river piece 2 also has the function of synchronous wearing and tearing when high carcass bores tooth 1 wearing and tearing, therefore can guarantee that drill bit all exists the mouth of a river in the process of all working tooth layer 1-1 consumption, drilling liquid flow is clear and coherent smooth, realizes the effect of cooling and chip removal.
Brill crown 3 in the utility model structure can be made by the conventional dimension of inner and outer diameters of geological drill bit, as φ 36.5/ φ 21.5, φ 59/ φ 36.5, φ 75/ φ 47.5, φ 96/63.5 etc.
The drill bit that the diameter of take is φ 36.5/ φ 21.5 is example, the height that designs high carcass brill tooth 1 is 16mm, the height of mouth of a river piece 2 is 5mm, piece 2 width in the mouth of a river are 5mm, design mouth of a river quantity is 5, rock drilling drillability rank is 7 grades, medium abrasive, designing high carcass brill tooth 1 formula is WC, Co, Cu, Sn, Ni etc., diamond concentration is 70%, granularity is 40/45, piece 2 formulas in the mouth of a river are Co, Cu etc., powder is reburned after cold moudling respectively and forms high carcass and bore tooth 1 and mouth of a river piece 2, sintering temperature is 860 ℃, total head is 25MPa, insulation 6min, bore crown 3 demouldings take out after through deburring, polishing is processed, with resin circle 7 lock rings, become circular, adopt flat-grinding machine that weld layer position is polished whole, then by laser, realize the welding of boring crown 3 and steel body 4, pass through again machine, spray paint, detect, realize the making of the high carcass geological drill bit of welded type.
The drill bit that the diameter of take is φ 75/ φ 47.5 is example, designing high carcass brill tooth 1 is highly 25mm, mouth of a river piece 2 is highly 10mm, piece 2 width in the mouth of a river are 8mm, 6 of design mouth of a river quantity, rock drilling drillability rank is 8 grades, strong abrasiveness, it is high WC base that tooth formula is bored in design, diamond concentration is 100%, granularity is 40/45, 45/50, 50/60 combination granularity, mouth of a river piece formula is Fe, Co, Cu etc., powder is assembled into ring-type after cold moudling respectively again, put into graphite jig and carry out sintering, sintering temperature is 880 ℃, total head is 30MPa, insulation 8min, brill crown 3 after sintering polishes processing by weld layer, adopt welding special fixture that brill crown 3 and steel body 4 are arranged on laser-beam welding machine, according to debugging, regulate laser power, realize the welding of boring crown 3 and steel body 4, carry out again machine, spray paint, detect, complete the making of the high carcass geological drill bit of welded type.
Claims (4)
1. the high carcass geological drill bit of welded type, comprise that high carcass bores tooth (1), mouth of a river piece (2) and steel body (4), described high carcass bores the upper circumference uniform distribution of tooth (1) Yu Gangti (4), described mouth of a river piece (2) is located at adjacent high carcass and is bored on the steel body (4) between tooth (1), it is characterized in that: described high carcass bores tooth (1) and comprises the work tooth layer (1-1) containing broken rock abrasive particle, the welding tooth layer (1-3) that does not contain the transition tooth layer (1-2) of abrasive particle and do not contain abrasive particle, it is 15mm～35mm that high carcass bores tooth (1) overall height, wherein, described work tooth layer (1-1) is highly 12mm～29mm, described transition tooth layer (1-2) is highly 1mm～3mm, described welding tooth layer (1-3) is highly 2mm～3mm, be matched with high carcass and bore tooth (1) highly, described mouth of a river piece (2) is highly 5mm～15mm.
2. the high carcass geological drill bit of welded type according to claim 1, is characterized in that: it is 15mm～20mm that described high carcass bores tooth (1) overall height, and described mouth of a river piece (2) is highly 5mm～10mm; It is highly 20mm～35m that described high carcass bores tooth (1), and described mouth of a river piece (2) is highly 10mm～15mm.
3. the high carcass geological drill bit of welded type according to claim 1 and 2, it is characterized in that: the inside and outside both sides of described mouth of a river piece (2) offer respectively interior tank (9) and external flume (8), described inside and outside tank (9, the 8) degree of depth is 1mm～5mm.
4. the high carcass geological drill bit of welded type according to claim 1 and 2, it is characterized in that: described high carcass bores the inside and outside surface inserting glomerocryst of tooth (1), glomerocryst mosaic site is work tooth layer (1-1) or for transition tooth layer (1-2) or be work tooth layer (1-1) and transition tooth layer (1-2).