CN203864098U - Double-layer structured compound knitting lace fabric - Google Patents

Double-layer structured compound knitting lace fabric Download PDF

Info

Publication number
CN203864098U
CN203864098U CN201420182439.6U CN201420182439U CN203864098U CN 203864098 U CN203864098 U CN 203864098U CN 201420182439 U CN201420182439 U CN 201420182439U CN 203864098 U CN203864098 U CN 203864098U
Authority
CN
China
Prior art keywords
fabric
double
top layer
fiber
lace fabric
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201420182439.6U
Other languages
Chinese (zh)
Inventor
谭托
卞文生
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
FUJIAN BAIKAI WARP KNITTING INDUSTRIAL Co Ltd
Original Assignee
FUJIAN BAIKAI WARP KNITTING INDUSTRIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by FUJIAN BAIKAI WARP KNITTING INDUSTRIAL Co Ltd filed Critical FUJIAN BAIKAI WARP KNITTING INDUSTRIAL Co Ltd
Priority to CN201420182439.6U priority Critical patent/CN203864098U/en
Application granted granted Critical
Publication of CN203864098U publication Critical patent/CN203864098U/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

The utility model relates to a double-layer structured compound knitting lace fabric. The double-layer structured compound knitting lace fabric comprises a surface layer and a bottom layer, wherein the surface layer is connected with the bottom layer through a knitting manner; the thickness ratio between the surface layer and the bottom layer is 1:1-5; the bottom layer is formed knitting warps and wefts; the warps are made of polylactic acid fibers; the wefts are made of triangular polyester tea carbon fibers. According to double-layer structured compound knitting lace fabric provided by the utility model, triangular cross sections of the triangular polyester tea carbon fibers provide maximum light absorption area, so that the light absorption efficiency is improved; moreover, the triangular polyester tea carbon fibers are provided with optical properties of flash effect and the like and provide various gloss for the fabric, so as to enable to fabric to have favorable gloss effect.

Description

A kind of double-deck compound knitted lace fabric
[technical field]
The utility model relates to weaving production technical field, specifically, is a kind of double-deck compound knitted lace fabric.
[background technology]
Fabric, according to the mode of the mode of production and knitted fabric formation, is divided into weft-knitted fabric and the large class of warp-knitted fabric two.Weft-knitted fabric is that yarn feeds successively along broadwise on the eedle of knitting machine, successively crooked lopping mutually go here and there cover with old coil and the knitted fabric that forms.(group) yarn can form a row, thereby has higher extensibility along broadwise.Warp-knitted fabric is the warp thread being arranged in parallel by a group or several groups, feeds lopping on all knitting needles of knitting machine and the knitted fabric that forms simultaneously.Yarn only forms one or two coil in each line on the same group, then transfers in next line, in another stringer lopping, thereby makes stringer contact in flakes.The coil of every group of yarn formation configures along fabric warp-wise.Same group of formed coil of warp thread regularity of distribution on knitted fabric is different and form various warp knitting fabrics.WARP-KNITTING have be difficult for decoherencing, extensibility is less than weft-knitted fabric, the good feature of dimensional stability.Be commonly used for compensation underwear and house decorative material and work, agriculture, doctor field.Warp-knitted fabric is used for coat expects, its performance approaches tatting and expects.
The kind of lace is a lot, as roses and lace, tricot lace, elastic force lace, without the limit of fluffing cotton, add bone lace, embroidery lace, water-soluble lace etc., according to the fabric of lace, can divide as follows:
Cotton type fabric: refer to cotton or fabric cotton and that cotton type chemical mixed yarn line is made into.Its good permeability, good hygroscopicity, comfortable and easy to wear, be practical popular fabric.The large class of blending two that can be divided into textile goods, cotton.This is subject to liking of consumer very much.
Silk type fabric: be the high-grade variety in textile.Mainly refer to the fabric that is primary raw material by mulberry silk, tussah silk, artificial silk, filament of synthetic fibre.It has advantages of thin light, soft, smooth, graceful, magnificent, comfortable.It is noble that this fabric seems.
Wool fabrics: be to take the fabric that wool, the rabbit hair, camel hair, wool type chemical fibre make as primary raw material, generally take wool as living, it is high-grade fabric throughout the year, the advantage such as have that good springiness, crease-resistant, well-pressed, strong to stand up to hard wear, warmth retention property are strong, Comfortable attractive, color and luster are pure, is subject to consumer's welcome deeply.Be used for making sweater.
Linen look fabric: the pure linen being formed by weaving by flaxen fiber and fiber crops and other fiber blend or the fabric interweaving are referred to as linen look fabric.The common feature of linen look fabric is hard tough, rough stiffening, the cool and comfortable of quality, good hygroscopicity, is desirable summer clothes fabric, and linen look fabric can be divided into pure spinning and blending two classes.
Pure chemical & blended fabric: chemical fiber plus material is large with its fastness, good springiness, well-pressed, wear-resisting washable, easy keeping collection and be subject to liking of people.Pure chemical & blended fabric is the fabric being formed by pure chemistry fibrous woven.Its characteristic is decided by the characteristic of its chemical fibre itself.Chemical fibre can be processed into certain length according to different needs, and is made into the fabrics such as imitative silk, imitative cotton, imitative fiber crops, elastic force simulate wool, middle long simulate wool by different technique.
[utility model content]
The purpose of this utility model is to overcome the deficiencies in the prior art, and a kind of double-deck compound knitted lace fabric is provided.
The purpose of this utility model is achieved through the following technical solutions:
A double-deck compound knitted lace fabric, it comprises top layer and bottom, and the mode by braiding between top layer and bottom connects, and wherein, the Thickness Ratio of top layer and bottom is 1: 1~5; Described bottom is mutually woven and forms by warp and parallel, and wherein, warp consists of acid fiber by polylactic, and parallel consists of triangle polyester tea charcoal fiber.
Described top layer and the Thickness Ratio of bottom are 1: 1~4.
Described top layer and the Thickness Ratio of bottom are 1: 3.
Described bottom is mutually woven and forms by warp and parallel, and wherein, warp consists of acid fiber by polylactic, and parallel consists of triangle polyester tea charcoal fiber.Acid fiber by polylactic is 1: 1 with the braiding ratio of triangle polyester tea charcoal fiber.
Described top layer is polyster fibre, the blended yarn weaved fabric that cotton fiber and nylon fibre form, and by polyster fibre, three kinds of raw material blending of cotton fiber and nylon fibre form, and the braiding ratio of three kinds of raw materials is 3: 1: 1.
Compared with prior art, good effect of the present utility model is:
The fiber of the triangle tee section of triangle polyester tea charcoal fiber provides maximized light absorption area, has improved the efficiency of light absorption, and triangle fiber has the optical properties such as flash effect, provides fabric different gloss; Make fabric there is good gloss effect.
[accompanying drawing explanation]
Fig. 1 structural representation of the present utility model;
Being labeled as in accompanying drawing: 1 top layer, 2 bottoms.
[specific embodiment]
The specific embodiment of a kind of double-deck compound knitted lace fabric of the utility model is below provided.
Embodiment 1
Refer to accompanying drawing 1, a kind of double-deck compound knitted lace fabric, it comprises top layer and bottom, and the mode by braiding between top layer and bottom connects, and wherein, top layer 1 is 1: 1 with the Thickness Ratio of bottom 2;
Described bottom is mutually woven and forms by warp and parallel, and wherein, warp consists of acid fiber by polylactic, and parallel consists of triangle polyester tea charcoal fiber.Acid fiber by polylactic is 1: 1 with the braiding ratio of triangle polyester tea charcoal fiber.
Described top layer is polyster fibre, the blended yarn weaved fabric that cotton fiber and nylon fibre form, and by polyster fibre, three kinds of raw material blending of cotton fiber and nylon fibre form, and the braiding ratio of three kinds of raw materials is 3: 1: 1.
Embodiment 2
Refer to accompanying drawing 1, a kind of double-deck compound knitted lace fabric, it comprises top layer and bottom, and the mode by braiding between top layer and bottom connects, and wherein, the Thickness Ratio of top layer and bottom is 1: 2;
Described bottom is mutually woven and forms by warp and parallel, and wherein, warp consists of acid fiber by polylactic, and parallel consists of triangle polyester tea charcoal fiber.Acid fiber by polylactic is 1: 1 with the braiding ratio of triangle polyester tea charcoal fiber.
Described top layer is polyster fibre, the blended yarn weaved fabric that cotton fiber and nylon fibre form, and by polyster fibre, three kinds of raw material blending of cotton fiber and nylon fibre form, and the braiding ratio of three kinds of raw materials is 3: 1: 1.
Embodiment 3
Refer to accompanying drawing 1, a kind of double-deck compound knitted lace fabric, it comprises top layer and bottom, and the mode by braiding between top layer and bottom connects, and wherein, the Thickness Ratio of top layer and bottom is 1: 3;
Described bottom is mutually woven and forms by warp and parallel, and wherein, warp consists of acid fiber by polylactic, and parallel consists of triangle polyester tea charcoal fiber.Acid fiber by polylactic is 1: 1 with the braiding ratio of triangle polyester tea charcoal fiber.
Described top layer is polyster fibre, the blended yarn weaved fabric that cotton fiber and nylon fibre form, and by polyster fibre, three kinds of raw material blending of cotton fiber and nylon fibre form, and the braiding ratio of three kinds of raw materials is 3: 1: 1.
Embodiment 4
Refer to accompanying drawing 1, a kind of double-deck compound knitted lace fabric, it comprises top layer and bottom, and the mode by braiding between top layer and bottom connects, and wherein, the Thickness Ratio of top layer and bottom is 1: 4;
Described bottom is mutually woven and forms by warp and parallel, and wherein, warp consists of acid fiber by polylactic, and parallel consists of triangle polyester tea charcoal fiber.Acid fiber by polylactic is 1: 1 with the braiding ratio of triangle polyester tea charcoal fiber.
Described top layer is polyster fibre, the blended yarn weaved fabric that cotton fiber and nylon fibre form, and by polyster fibre, three kinds of raw material blending of cotton fiber and nylon fibre form, and the braiding ratio of three kinds of raw materials is 3: 1: 1.
Embodiment 5
Refer to accompanying drawing 1, a kind of double-deck compound knitted lace fabric, it comprises top layer and bottom, and the mode by braiding between top layer and bottom connects, and wherein, the Thickness Ratio of top layer and bottom is 1: 5;
Described bottom is mutually woven and forms by warp and parallel, and wherein, warp consists of acid fiber by polylactic, and parallel consists of triangle polyester tea charcoal fiber.Acid fiber by polylactic is 1: 1 with the braiding ratio of triangle polyester tea charcoal fiber.
Described top layer is polyster fibre, the blended yarn weaved fabric that cotton fiber and nylon fibre form, and by polyster fibre, three kinds of raw material blending of cotton fiber and nylon fibre form, and the braiding ratio of three kinds of raw materials is 3: 1: 1.
The above is only preferred embodiment of the present utility model; it should be pointed out that for those skilled in the art, without departing from the concept of the premise utility; can also make some improvements and modifications, these improvements and modifications also should be considered as in protection domain of the present utility model.

Claims (6)

1. a double-deck compound knitted lace fabric, it comprises top layer and bottom, and the mode by braiding between top layer and bottom connects, and it is characterized in that, and the Thickness Ratio of top layer and bottom is 1: 1~5; Described bottom is mutually woven and forms by warp and parallel, and wherein, warp consists of acid fiber by polylactic, and parallel consists of triangle polyester tea charcoal fiber.
2. a kind of double-deck compound knitted lace fabric as claimed in claim 1, is characterized in that, described top layer and the Thickness Ratio of bottom are 1: 1~4.
3. a kind of double-deck compound knitted lace fabric as claimed in claim 1, is characterized in that, described top layer and the Thickness Ratio of bottom are 1: 3.
4. a kind of double-deck compound knitted lace fabric as claimed in claim 1, is characterized in that, the acid fiber by polylactic of described bottom is 1: 1 with the braiding ratio of triangle polyester tea charcoal fiber.
5. a kind of double-deck compound knitted lace fabric as claimed in claim 1, is characterized in that, described top layer is polyster fibre, the blended yarn weaved fabric that cotton fiber and nylon fibre form.
6. a kind of double-deck compound knitted lace fabric as claimed in claim 1, is characterized in that, described top layer is polyster fibre, and the braiding ratio of cotton fiber and nylon fibre is 3: 1: 1.
CN201420182439.6U 2014-04-15 2014-04-15 Double-layer structured compound knitting lace fabric Expired - Fee Related CN203864098U (en)