CN203729542U - Wire glass used for building decoration - Google Patents
Wire glass used for building decoration Download PDFInfo
- Publication number
- CN203729542U CN203729542U CN201420020442.8U CN201420020442U CN203729542U CN 203729542 U CN203729542 U CN 203729542U CN 201420020442 U CN201420020442 U CN 201420020442U CN 203729542 U CN203729542 U CN 203729542U
- Authority
- CN
- China
- Prior art keywords
- glass
- wire
- glass plate
- architectural decoration
- gauze
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model discloses wire glass used for building decoration and belongs to the technical field of building decoration material. The wire glass is good in decoration, safety and weather fastness. According to the wire glass used for building decoration, a metal wire net is arranged between an upper glass plate and a lower glass plate, the metal wire net are stuck to the upper glass plate and the lower glass plate through a sticking layer which is a SGP middle film. The wire glass has the beautifying decoration effect. The color of the wire net is selected freely. The wire glass is high in safety and anti-theft performance. Even if the glass is broken, broken pieces will not fall off, and meanwhile the metal wire net still plays a part in the process. The SGP film is adopted as the middle film of the wire glass and can be combined better compared with common PVB, and the defects of a glue failure, air bubble generation and others are not prone to being generated. The edges of the wire glass are double sealed through a Dow sealant, and therefore it is avoided that because water vapor enters, the glass is ineffective, and the metal wire net is corroded.
Description
Technical field
The utility model relates to a kind of wire glass for architectural decoration, and this wire glass possesses ornamental, safety preferably and weatherability.Belong to technical field of construction and decoration materials.
Background technology
Laminated glass is by a sheet glass and one or more pieces glass or plastics, the glass component that is bonded together with one or more layers intermediate layer.The performance such as safety, impact resistance that laminated glass possesses with it, firmly gets people's favor.Along with safety, the ornamental further demand of people to glass, color laminated glass progressively enters in the middle of people's life.The plurality of advantages of laminated glass, makes it aspect building curtain wall and home decoration, have a large amount of uses, and has obtained good effect.The appearance of wire glass, can meet people to the demand of decorating, and has possessed again higher safety and theftproof.
Utility model content
For realize decorative effect, high security and the theftproof of cladding glass and household glass simultaneously, the utility model provides a kind of wire glass for architectural decoration, it is characterized in that: in the middle of upper and lower two glass sheets, wire gauze is set, between wire gauze and upper and lower two glass sheets, all bond by tack coat, described tack coat is SGP intermediate coat.The structure of this wire glass is followed successively by: glass plate/SGP intermediate coat/wire gauze/SGP intermediate coat/glass plate.
The thickness of described glass plate is 6mm-19mm; Glass plate is float glass, and tempered glass or semi-tempered glass can be colourless or mass colourings;
The thickness of described SGP intermediate coat is not less than 0.89mm.
Wire gauze can adopt copper mesh or gauze wire cloth, and mesh can be square, rectangle or hexagon etc., and wire gauze thickness is not more than 1.5mm.
The limit portion of wire glass adopts Tao Shi edge sealing agent double sealing, and SGP intermediate coat is non-directly exposed.
The preparation method of above-mentioned architectural decoration wire glass, comprises the following steps:
(1) preparation of glass plate and cleaning
Select certain thickness glass plate, glass plate is cleaned up.Cleaning process adopts deionized water.
(2) wire glass close sheet
By specific order, material is combined to glass plate/intermediate coat/wire lath/intermediate coat/glass plate.The undersized of wire lath is in glass size, guarantees that metal selvage portion do not expose.Close sheet process, operating personnel should wear gloves and mouth mask, avoid intermediate coat, wire lath and glass plate contaminated.
(3) vacuum exhaust
Be positioned in vacuum bag closing the glass that sheet completes, carry out vacuumizing and exhausting.
(4) autoclave process
Glass is positioned over to the exhaust of autoclave mesohigh.
(5) edge sealing processing
Adopt Tao Shi edge sealing agent to carry out double sealing.
Step can be selected common float glass in (1), carries out the chamfered edge processing of limit portion, and for follow-up edge sealing process, the inner side edge contacting with intermediate coat adopts 2*45 ° of large chamfered edge.Water for cleaning is RO water.
The beneficial effects of the utility model are:
1. this wire glass has decorative effect attractive in appearance.
2. wire lath possesses the selective arbitrarily of color effects, as silver color gauze wire cloth, red metal silk screen, brass wire mesh etc.
3. this wire glass has higher safety and theftproof.Even glass breaking, fragment also can not fall down, and wire gauze also in action simultaneously.
4. this wire glass intermediate coat adopts SGP film, can be than the better combination of common PVB, be not easy to occur coming unglued and producing the defects such as bubble.
5. wire glass limit portion carries out Tao Shi sealant double sealing, has avoided glass inefficacy and wire gauze that entering of steam causes to be corroded.
Brief description of the drawings
Accompanying drawing 1 is the structural representation of the wire glass for architectural decoration of the present utility model;
Number in the figure:
1-glass plate; 2-intermediate coat; 3-wire lath; 4-intermediate coat; 5-glass plate.
Detailed description of the invention
The following examples can make those skilled in the art more fully understand the utility model, but limit never in any form the utility model.
Embodiment 1
A kind of wire glass for architectural decoration of the present embodiment arranges wire gauze in the middle of upper and lower two glass sheets, between wire gauze and upper and lower two glass sheets, all bonds by tack coat, and described tack coat is SGP intermediate coat.The structure of this wire glass is followed successively by: glass plate/SGP intermediate coat/wire gauze/SGP intermediate coat/glass plate.
The thickness of described upper and lower two glass sheets is 10mm; Glass plate is float glass, and tempered glass or semi-tempered glass can be colourless or mass colourings;
Wire gauze adopts 0.5mm red metal silk screen, and mesh is square, and intermediate coat adopts 1.52mm water white transparency SGP film.The physical characteristic of SGP intermediate coat is in table 1.
The physical characteristic of table 1SGP intermediate coat
| Physical parameter | Measured value |
| Young's modulus of elasticity | 300Mpa |
| Shear strength | 50MJ/m 3 |
| Tensile strength | 34.5Mpa |
| Elongation at break | 400% |
| Density | 0.95g/cm 3 |
| Bending modulus (23 DEG C) | 345Mpa |
| Heat deflection temperature (HDT) (0.46Mpa) | 43℃ |
| Fusing point | 94℃ |
| Coefficient of thermal expansion (20 DEG C～32 DEG C) | 10～15×10 -3cm/cm℃ |
The preparation method of above-mentioned architectural decoration wire glass, step is as follows:
(1) preparation of glass plate and cleaning
Select as required the glass plate of specific thicknesses, glass plate is carried out to preprocessing processing, change and cut size, edging, tempering, according to the needs of follow-up edge sealing, glass plate inside edge (face contacting with intermediate coat) carried out to 2*45 ° of chamfered edge.While needing tempering as glass plate, must strictly control the planeness (arc and waveform) of tempered glass and the goodness of fit of two glass sheets.
Adopt horizontal cleaning machine to clean glass plate, water for cleaning is RO water.
(2) wire glass close sheet
By specific order, material is combined to glass plate/SGP intermediate coat/wire gauze/SGP intermediate coat/glass plate.The undersized of wire gauze is in glass size, guarantees that wire selvage portion do not expose.Close sheet process, operating personnel should wear gloves and mouth mask, avoid intermediate coat, wire gauze and glass plate contaminated.
(3) vacuum exhaust
Be positioned in vacuum bag closing the glass that sheet completes, carry out vacuumizing and exhausting.Vacuum is in 10mbar left and right, and the pumpdown time is not less than 2 hours.
(4) autoclave process
Glass is positioned in autoclave.The insulation of autoclave is not less than 135 DEG C, and temperature retention time is not less than 60min, operating pressure 12～14bar.
(5) edge sealing processing
SGP film unnecessary glass edge portion is cut off, and edge trimming is clean.First brush one deck Tao Shi 5500 edge sealing agents, guarantee that coating covers whole glass edge portion, then apply one deck Tao Shi BATASEAL glass cement, edge sealing adhesive apply should be continuously without neat hole without omitting without interrupting.
By above-mentioned example, prepared wire glass, the associativity of film condensation material and glass plate and wire gauze and firmness are good, and limit portion double sealing technique stops the erosion of steam in glass edge portion, weather-proof effective.
The above; it is only preferably detailed description of the invention of the utility model; but protection domain of the present utility model is not limited to this; any be familiar with those skilled in the art the utility model disclose technical scope in; the variation that can expect easily or replacement, within all should being encompassed in protection domain of the present utility model.Therefore, protection domain of the present utility model should be as the criterion with the protection domain of claim.
Claims (9)
1. the wire glass for architectural decoration, it is characterized in that: in the middle of upper and lower two glass sheets, wire gauze is set, between wire gauze and upper and lower two glass sheets, all bond by tack coat, described tack coat is SGP intermediate coat, this wire glass limit portion double sealing.
2. the wire glass for architectural decoration according to claim 1, is characterized in that: the structure of this wire glass is followed successively by: glass plate/SGP intermediate coat/wire gauze/SGP intermediate coat/glass plate.
3. the wire glass for architectural decoration according to claim 1, is characterized in that: the thickness of described glass plate is 6mm-19mm.
4. the wire glass for architectural decoration according to claim 1, is characterized in that: described glass plate is float glass tempered glass or semi-tempered glass.
5. the wire glass for architectural decoration according to claim 1, is characterized in that: described glass plate is colourless or mass colouring.
6. the wire glass for architectural decoration according to claim 1, is characterized in that: the thickness of described SGP intermediate coat is not less than 0.89mm.
7. the wire glass for architectural decoration according to claim 1, is characterized in that: described wire gauze adopts copper mesh or gauze wire cloth.
8. the wire glass for architectural decoration according to claim 1, is characterized in that: described wire gauze mesh is square, rectangle or hexagon.
9. the wire glass for architectural decoration according to claim 1, is characterized in that: described wire gauze thickness is not more than 1.5mm.