CN203726928U - Heat-seal foil-overlaid glass cotton product - Google Patents
Heat-seal foil-overlaid glass cotton product Download PDFInfo
- Publication number
- CN203726928U CN203726928U CN201320888948.6U CN201320888948U CN203726928U CN 203726928 U CN203726928 U CN 203726928U CN 201320888948 U CN201320888948 U CN 201320888948U CN 203726928 U CN203726928 U CN 203726928U
- Authority
- CN
- China
- Prior art keywords
- heat
- sealed foil
- glass wool
- hot melt
- goods
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
The utility model provides a heat-seal foil-overlaid glass cotton product. The heat-seal foil substrate of the product is high-strength paper or pure aluminum, and the surface of the substrate is uniformly coated with a hot melt adhesive. The product is molded on a production line by means of one-time hot-press compounding and is produced continuously. The product has a flat and smooth heat-seal foil surface, has high insulating performance, has a large bonding area between a foil and a cotton plate (felt), high bonding strength and can avoid peeling.
Description
Technical field
The utility model relates to take microglass fiber goods as base material, and surface recombination is pasted decorative cover and formed both novel heat-sealed foil veneer mineral wool goods that strengthen product surface intensity, tear-resistant, anti-separation attractive in appearance.
Background technology
Traditional foliation mineral wool goods, adopt hand paste under line conventionally, and production efficiency is low, and the waste product waste material cut, modification, glue spraying, hot pressing producing is more, artificial, energy consumption is larger.Also have some to adopt on production line with putting or the mode of line bonds after spraying adhesive, but adhesion strength is low, bond area is limited, and paper tinsel and cotton plate (felt) easily come off, and adhesive causes environmental pollution in spraying process.
Summary of the invention
For improving the deficiency in above-mentioned technology, the purpose of this utility model is to provide a kind of heat-sealed foil veneer mineral wool goods, and the surfacing of goods heat-sealed foil is bright and clean, and thermal insulation is good, paper tinsel and cotton plate (felt) bond area is large, adhesion strength is high, be difficult for peeling off.
For achieving the above object, the utility model goods are once pressure composite molding hot in nature and generating continuously on production line, have production scale large, without cutting, modify that waste product produces, production specification variation, produce feature timely easy to adjust.
The preparation method of the utility model heat-sealed foil veneer mineral wool goods is that heat-sealed foil is lifted into heat-sealed foil conveying device, adjust heat-sealed foil running tension device to adapt to conveying requirement, heat-sealed foil is drawn through heat-sealed foil adjusting device, hot melt warm-up mill to block of glass wool (felt), by heat seal pressure roller, carry out pressing, generate heat-sealed foil veneer mineral wool goods.
The preparation technology of the utility model heat-sealed foil veneer mineral wool goods is specifically in the following ways:
A. according to production specification, set the heating-up temperature of hot melt warm-up mill, hot melt warm-up mill heating-up temperature is set according to line speed and is carried out automatic constant-temperature control.
B. according to product of production line speed of production, the linear velocity of hot melt warm-up mill is adjusted into and product of production line speed of production automatic synchronization state.
C. regulate adjusting device to set the hot melt adhesive length (heat-sealed foil outer surface and hot melt warm-up mill contact-making surface length) that needs heating, guaranteeing can hot melt under the design temperature of hot melt warm-up mill.
D. press the selected heat-sealed foil of production specification, heat-sealed foil is lifted into heat-sealed foil conveying device, adjust heat-sealed foil running tension device to adapt to conveying requirement, by heat-sealed foil traction through heat-sealed foil adjusting device, hot melt warm-up mill to block of glass wool (felt), by heat seal pressure roller, carry out pressing.
E. regulate heat-sealed foil adjusting device to guarantee the justified margin of heat-sealed foil and block of glass wool (felt).
Described hot melt heating roller temperature be 200 ℃～350 ℃ adjustable, preferably 220 ℃～260 ℃ are adjustable.
Described hot melt heating roller temperature when preparation heat-sealed foil veneer blanket of glass wool more preferably 230 ℃～240 ℃ adjustable; When preparation heat-sealed foil veneer block of glass wool more preferably 250 ℃～260 ℃ adjustable.
Described line speed is generally 6～50 ms/min.
Described line speed when preparation heat-sealed foil veneer blanket of glass wool preferably 40～50 ms/min; When preparation heat-sealed foil veneer block of glass wool preferably 10～20 ms/min.
Described hot melt warm-up mill speed is generally 6～50 ms/min.
Described hot melt warm-up mill speed when preparation heat-sealed foil veneer blanket of glass wool preferably 40～50 ms/min; When preparation heat-sealed foil veneer block of glass wool preferably 10～20 ms/min.
Described heat-sealed foil outer surface and hot melt warm-up mill contact-making surface length be 1000～3500 millimeters adjustable, preferably 1500～2500 millimeters adjustable.
Described heat-sealed foil outer surface and hot melt warm-up mill contact-making surface length when preparation heat-sealed foil veneer blanket of glass wool more preferably 2000～2200 millimeters adjustable; When preparation heat-sealed foil veneer block of glass wool more preferably 2400～2500 millimeters adjustable.
Described heat-sealed foil running tension is 20～50 kilograms, preferably 30～35 kilograms.
Described heat-sealed foil running tension more preferably 30 kilograms when preparation heat-sealed foil veneer blanket of glass wool; More preferably 35 kilograms when preparation heat-sealed foil veneer block of glass wool.
Described heat seal pressure roller pressing pressure is generally 0.015～0.15 kilogram/square centimeter.
Described heat seal pressure roller pressing pressure preferred 0.015～0.025 kilogram/square centimeter when preparation heat-sealed foil veneer blanket of glass wool; Preferred 0.1～0.15 kilogram/square centimeter when preparation heat-sealed foil veneer block of glass wool.
Described heat-sealed foil veneer mineral wool goods are heat-sealed foil veneer block of glass wool or heat-sealed foil veneer blanket of glass wool.
Described heat-sealed foil matrix is high-strength paper or fine aluminium, and the hot melt adhesive of different performance is evenly coated in stromal surface.
Described block of glass wool, blanket of glass wool width are 1000～1200 millimeters.
Described heat-sealed foil width is generally 1000～1200 millimeters when producing block of glass wool.
Described heat-sealed foil width is generally 1000～1300 millimeters when producing blanket of glass wool.Be that blanket of glass wool allows that one-sided or bilateral heat-sealed foil is wide goes out 50 millimeters sometimes, claim solo flight or round trip flight, be beneficial to overlap joint.
On production line, have five rip cutting cut-off knives after heat seal pressure roller, can any width be cut apart by heat-sealed foil veneer block of glass wool (felt), the heat-sealed foil veneer mineral wool goods width finally making is 300～1200 millimeters.
180 ° of peel strengths of the utility model heat-sealed foil veneer blanket of glass wool goods can reach 16N/m; More than 180 ° of peel strengths of heat-sealed foil veneer block of glass wool goods can reach 50N/m.
The utility model heat-sealed foil veneer mineral wool goods viscose fibre area can reach 60～90%.
When the utility model heat-sealed foil veneer mineral wool goods are blanket of glass wool, viscose fibre area is 60～75%; When heat-sealed foil veneer mineral wool goods are block of glass wool, viscose fibre area is 70～90%.
Compared with prior art, advantage of the present utility model is:
1. hot melt adhesive heated length (heat-sealed foil outer surface and hot melt warm-up mill contact-making surface length) is adjusted according to the speed of production separately of different product.
2. the utility model product surface is attractive in appearance and product surface intensity is high, tear-resistant, be difficult for peeling off.Hot melt adhesive and product are planar bonding, and veneer is smooth, corrugationless, firm, not stratified foaming.
3. on production line, adopt the auxiliary material of hot melt equipment complex and heat molten type (heat-sealed foil of coating hot-melt adhesive stick), a hot pressing composite molding, and can be continuously shaped on production line.
Accompanying drawing explanation
Fig. 1 is the utility model heat-sealed foil veneer mineral wool goods preparation flow figure.
In figure: 1-heat seal pressure roller; 2-block of glass wool (felt); 3-production line transmitting device; 4-hot melt warm-up mill; 5-heat-sealed foil; 6-heat-sealed foil adjusting device; 7-heat-sealed foil conveying device.
Fig. 2 is the utility model heat-sealed foil veneer mineral wool goods schematic diagrames.
In figure: 8-article cross sections; 9-hot melt adhesive; 10-heat-sealed foil matrix.
Wherein, Fig. 2 is Figure of abstract.
The specific embodiment
Below be only preferred embodiment of the present utility model, can not limit scope of the present utility model with this.The equalization generally done according to the utility model claim changes and modifies, and all should still belong in the scope that the utility model patent contains.
Embodiment 1
The heating-up temperature of setting hot melt warm-up mill 4 is 240 ℃, and carries out automatic constant-temperature control, and setting product of production line speed of production is 43 ms/min, the linear velocity of hot melt warm-up mill 4 is adjusted into 43 ms/min, with product of production line speed of production automatic synchronization.Regulate adjusting device 6 to set needing the hot melt adhesive length of heating is 2000 millimeters, and guaranteeing can hot melt under the design temperature of hot melt warm-up mill.Press the selected fine aluminium heat-sealed foil of production specification, fine aluminium heat-sealed foil is lifted into heat-sealed foil conveying device 7, adjusting heat-sealed foil running tension is 30 kilograms, to adapt to conveying requirement, heat-sealed foil is drawn through heat-sealed foil adjusting device 6, hot melt warm-up mill 4 to blanket of glass wool 2, by heat seal pressure roller 1, carry out pressing, heat seal pressure roller pressing pressure is 0.02 kilogram/square centimeter.Regulate heat-sealed foil adjusting device 6 to guarantee the justified margin of heat-sealed foil 5 and blanket of glass wool 2.
Making heat-sealed foil veneer blanket of glass wool goods width is 1200 millimeters.The physical property of product detects data and lists in table one, and contrasts and list in table one with common foliation felt physical property.
Embodiment 2
The heating-up temperature of setting hot melt warm-up mill 4 is 230 ℃, and carries out automatic constant-temperature control, and setting product of production line speed of production is 41 ms/min, the linear velocity of hot melt warm-up mill 4 is adjusted into 41 ms/min, with product of production line speed of production automatic synchronization.Regulate adjusting device 6 to set needing the hot melt adhesive length of heating is 2100 millimeters, and guaranteeing can hot melt under the design temperature of hot melt warm-up mill.Press the selected fine aluminium heat-sealed foil of production specification, fine aluminium heat-sealed foil is lifted into heat-sealed foil conveying device 7, adjusting heat-sealed foil running tension is 30 kilograms, to adapt to conveying requirement, heat-sealed foil is drawn through heat-sealed foil adjusting device 6, hot melt warm-up mill 4 to blanket of glass wool 2, by heat seal pressure roller 1, carry out pressing, heat seal pressure roller pressing pressure is 0.02 kilogram/square centimeter.Regulate heat-sealed foil adjusting device 6 to guarantee the justified margin of heat-sealed foil 5 and blanket of glass wool 2.
Making heat-sealed foil veneer blanket of glass wool goods width is 1200 millimeters.The physical property of product detects data and lists in table one, and contrasts and list in table one with common foliation felt physical property.
Table one
Note: viscose fibre area refers to that heat-sealed foil veneer blanket of glass wool goods peel off the area of the blanket of glass wool that post heat-seal paper tinsel bonds from production line.
Embodiment 3
The heating-up temperature of setting hot melt warm-up mill 4 is 250 ℃, and carries out automatic constant-temperature control, and setting product of production line speed of production is 10 ms/min, the linear velocity of hot melt warm-up mill 4 is adjusted into 10 ms/min, with product of production line speed of production automatic synchronization.Regulate adjusting device 6 to set needing the hot melt adhesive length of heating is 2400 millimeters, and guaranteeing can hot melt under the design temperature of hot melt warm-up mill.Press the selected fine aluminium heat-sealed foil of production specification, fine aluminium heat-sealed foil is lifted into heat-sealed foil conveying device 7, adjusting heat-sealed foil running tension is 35 kilograms, to adapt to conveying requirement, heat-sealed foil is drawn through heat-sealed foil adjusting device 6, hot melt warm-up mill 4 to block of glass wool 2, by heat seal pressure roller 1, carry out pressing, heat seal pressure roller pressing pressure is 0.12 kilogram/square centimeter.Regulate heat-sealed foil adjusting device 6 to guarantee the justified margin of heat-sealed foil 5 and block of glass wool 2.
Making heat-sealed foil veneer block of glass wool goods width is 1200 millimeters.The physical property of product detects data and lists in table two, and lists in table two with common foliation plate physical property contrast.
Embodiment 4
The heating-up temperature of setting hot melt warm-up mill 4 is 260 ℃, and carries out automatic constant-temperature control, and setting product of production line speed of production is 15 ms/min, the linear velocity of hot melt warm-up mill 4 is adjusted into 15 ms/min, with product of production line speed of production automatic synchronization.Regulate adjusting device 6 to set needing the hot melt adhesive length of heating is 2500 millimeters, and guaranteeing can hot melt under the design temperature of hot melt warm-up mill.Press the selected fine aluminium heat-sealed foil of production specification, fine aluminium heat-sealed foil is lifted into heat-sealed foil conveying device 7, adjusting heat-sealed foil running tension is 35 kilograms, to adapt to conveying requirement, heat-sealed foil is drawn through heat-sealed foil adjusting device 6, hot melt warm-up mill 4 to block of glass wool 2, by heat seal pressure roller 1, carry out pressing, heat seal pressure roller pressing pressure is 0.12 kilogram/square centimeter.Regulate heat-sealed foil adjusting device 6 to guarantee the justified margin of heat-sealed foil 5 and block of glass wool 2.
Making heat-sealed foil veneer block of glass wool goods width is 1200 millimeters.The physical property of product detects data and lists in table two, and lists in table two with common foliation plate physical property contrast.
Table two
Note: viscose fibre area refers to that heat-sealed foil veneer block of glass wool goods peel off the area of the block of glass wool that post heat-seal paper tinsel bonds from production line.
Claims (9)
1. heat-sealed foil veneer mineral wool goods, for heat-sealed foil veneer block of glass wool or blanket of glass wool, is characterized in that, heat-sealed foil matrix is high-strength paper or fine aluminium, and hot melt adhesive is evenly coated in stromal surface.
2. heat-sealed foil veneer mineral wool goods according to claim 1, is characterized in that, block of glass wool, blanket of glass wool width are 1000～1200 millimeters.
3. according to heat-sealed foil veneer mineral wool goods described in claim 1 or 2, it is characterized in that, heat-sealed foil width is 1000～1200 millimeters when producing block of glass wool.
4. according to heat-sealed foil veneer mineral wool goods described in claim 1 or 2, it is characterized in that, heat-sealed foil width is 1000～1300 millimeters when producing blanket of glass wool.
5. according to heat-sealed foil veneer mineral wool goods described in claim 1 or 2, it is characterized in that, mineral wool goods viscose fibre area is 60～90%.
6. according to heat-sealed foil veneer mineral wool goods described in claim 1 or 2, it is characterized in that, when heat-sealed foil veneer mineral wool goods are block of glass wool, viscose fibre area is 70-90%.
7. heat-sealed foil veneer mineral wool goods according to claim 3, is characterized in that, when heat-sealed foil veneer mineral wool goods are block of glass wool, viscose fibre area is 70-90%.
8. according to heat-sealed foil veneer mineral wool goods described in claim 1 or 2, it is characterized in that, when heat-sealed foil veneer mineral wool goods are blanket of glass wool, viscose fibre area is 60～75%.
9. heat-sealed foil veneer mineral wool goods according to claim 4, is characterized in that, when heat-sealed foil veneer mineral wool goods are blanket of glass wool, viscose fibre area is 60～75%.