CN203192532U - Salt-corrosion-resistant torsion-resistant communication cable for offshore wind power - Google Patents
Salt-corrosion-resistant torsion-resistant communication cable for offshore wind power Download PDFInfo
- Publication number
- CN203192532U CN203192532U CN 201320141346 CN201320141346U CN203192532U CN 203192532 U CN203192532 U CN 203192532U CN 201320141346 CN201320141346 CN 201320141346 CN 201320141346 U CN201320141346 U CN 201320141346U CN 203192532 U CN203192532 U CN 203192532U
- Authority
- CN
- China
- Prior art keywords
- cable
- low
- nonwoven fabrics
- resistant
- sheath
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model relates to a salt-corrosion-resistant torsion-resistant communication cable for offshore wind power. Each insulating core is formed by uniformly extruding a salt-corrosion-resistant torsion-resistant rubber insulating layer from a stranded copper conductor, the insulating cores are stranded pairwise to form twisted cable pairs, flame-retardant non-hygroscopic fiber filling cores are filled into gap of each twisted cable pair, and multiple twisted cable pairs are stranded to form a cable core, wherein twisting pitches of different twisted cable pairs are different; the cable core is wrapped in a low-strength non-woven-fabric longitudinal wrapping; and a sheath is extruded from the low-strength non-woven-fabric longitudinal wrapping. The appearance of the low-strength non-woven-fabric longitudinal wrapping is completely matched with that of the insulating cores, so that gap between the low-strength non-woven-fabric longitudinal wrapping and the insulating cores is eliminated, flame is prevented from spreading inwards during combustion, and resistance to dipping of humidity can be enhanced; and at the same time the low-strength non-woven-fabric longitudinal wrapping ensures that the sheath is not adhesive to the insulating cores, so that when the sheath is stripped during construction, the insulating cores are not damaged.
Description
Technical field
The utility model relates to a kind of telecommunication cable, and particularly a kind of ocean wind-powered electricity generation is with the rotten anti-telecommunication cable that reverses of salt tolerant.
Background technology
The maturation of following landing to utilize with wind-powered electricity generation, country begins to advance ocean wind-powered electricity generation utilization, but still do not have at present and can satisfy ocean wind-powered electricity generation applying working condition fully to be exclusively used in ocean wind-powered electricity generation electricity consumption cable supporting with it, and be mostly former supporting for the ocean wind-powered electricity generation with the cable of wind-powered electricity generation for the land, or adopt the cable that possesses certain required performance of ocean wind-powered electricity generation electricity consumption cable.But the land is not considered the particular surroundings of ocean wind-powered electricity generation with wind-powered electricity generation with cable performance, does not especially possess to stand the many salt in ocean, acid, caustic corrosion, greasy dirt corrosion and the moist saturating machine of sea water resistance for a long time.Be easy to break down when reversing in sea wind generating, reduction of service life, cause engineering cost to increase even shelve.
Granted publication number discloses a kind of offshore wind energy plant spcific power cable for the utility model patent of CN 201725624U, this cable adopts 105 ℃ of irradiation crosslinking types ethylene propylene rubber insulated, possesses salt spray resistance, but cross-linking radiation ethylene-propylene rubber material is very hard, the softness that is unfavorable for the wind-powered electricity generation requirement, it does not possess ocean wind-powered electricity generation electricity consumption cable simultaneously needs the anti-moist impregnability of sea wind seawater that stands for a long time, causing insulation to make moist easily to reduce insulation resistance to cause and using potential safety hazard, reducing cable useful life.
Granted publication number discloses a kind of flexible cable for offshore wind generating for the utility model patent of CN 201904120U, this cable stranding adopts polypropylene rope to fill, conductor is provided with internal shield and outer shielding layer outward, external shield is provided with the copper wire braiding outward, the polypropylene rope packing material has very big morphotropism and structural instability, filling is not accomplished closely knit, there is the slit between sheath and the core, cable cable core when reversing is unfixing, radial displacement can take place cause local bulge, even the sheath breakage, seawater takes place to be soaked into, cause the use accident.The internal shield of She Zhiing, outer shielding layer and copper wire braiding simultaneously makes the outside diameter of cable very big, and metal knitted meeting reduces cable flexion torsion performance.
Publication number is that the utility model patent of CN 101531781A discloses a kind of sheath rubber for wind electric power generation cable, formed with other raw materials are mixing by neoprene and butadiene rubber, in the time of-50 ℃, can significantly not lose flexibility, elasticity and generation cracking, but it does not possess sea water resistance salt air corrosion and the moist saturating machine of sea water resistance, is unsuitable for the oceanic winds electrical environment.
Publication number is that the utility model patent of CN101838424A discloses a kind of distortion-resistance wind power generation cable sheath materials and cable, it is former gum base materials that sheath adopts haloflex, possess low temperature resistant-60 ℃ of torsional resistances, but do not possess the moist saturating machine of sea water resistance salt, acid, caustic corrosion and sea water resistance, be unsuitable for the oceanic winds electrical environment; This cable insulation and sheath double-layer coextrusion simultaneously, cable socket insulation and sheath separates when being unfavorable for construction and installation.
The utility model content
The purpose of this utility model is, overcome problems of the prior art, provide a kind of ocean wind-powered electricity generation with the rotten anti-telecommunication cable that reverses of salt tolerant, production technology is simple, cost is lower, external diameter is little, in light weight, soft pliable is bent, be convenient to construction and installation, possess anti-ly reverse, sea water resistance salt air corrosion and the moist saturating machine of sea water resistance.
For realizing above purpose, a kind of ocean provided by the utility model wind-powered electricity generation is with the rotten anti-telecommunication cable that reverses of salt tolerant, the twisted copper conductors periphery evenly is extruded with the rotten anti-rubber insulation that reverses of salt tolerant and constitutes insulated wire cores, insulated wire cores stranded formation twisted pair wire in twos is right, the right slit of described twisted pair wire is filled with fire-retardant non-hygroscopic fiber and fills out core, the twisting pitch that each described twisted pair wire has nothing in common with each other to employing, the described twisted pair wire strand of many groups constitutes cable core, the periphery of described cable core is enclosed with the vertical covering of low-intensity nonwoven fabrics, and the periphery of the vertical covering of described low-intensity nonwoven fabrics is extruded with sheath.
With respect to prior art, the utility model has been obtained following beneficial effect: cable of the present utility model adopts the vertical covering of low-intensity nonwoven fabrics, the characteristics of vertical bag can only be that the nonwoven fabrics with certain width is divided into some sections, connect one section parcel along one section of telecommunication cable cable core axis direction, the vertical covering of low-intensity nonwoven fabrics is very little at the tension force of circumferencial direction, be easy to when extruding sheath the vertical covering of low-intensity nonwoven fabrics is pressed in communication cable insulating core outer surface, the shape profile complete and the communication cable insulating core that is the vertical covering of low-intensity nonwoven fabrics matches, eliminated the space between the vertical covering of low-intensity nonwoven fabrics and the communication cable insulating core, be convenient to stop under the burning condition flame to the continuous transmission of inside, and can strengthen the dipping of resisting moisture; Simultaneously the vertical covering of low-intensity nonwoven fabrics can be guaranteed adhesion between sheath and the communication cable insulating core, does not injure the communication cable insulating core when being convenient to work progress and divesting sheath.
As preferred version of the present utility model, the thickness of the vertical covering of described low-intensity nonwoven fabrics is 0.05 ~ 0.1mm, overlap vertical bag successively along telecommunication cable cable core axis direction, the width of every section vertical covering of described low-intensity nonwoven fabrics is 3.5 ~ 3.8 times of telecommunication cable cable core diameter.
Description of drawings
Fig. 1 for the utility model ocean wind-powered electricity generation with the anti-structural representation that reverses telecommunication cable of salt tolerant corruption.
Among the figure: 1. insulated wire cores; 1a. twisted copper conductors; 1b. the rotten anti-rubber insulation that reverses of salt tolerant; 2. fire-retardant non-hygroscopic fiber is filled out core; 3. the low-intensity nonwoven fabrics is indulged covering; 4. sheath.
Embodiment
Embodiment one
As shown in Figure 1, ocean of the present utility model wind-powered electricity generation is with the rotten anti-telecommunication cable that reverses of salt tolerant, may further comprise the steps successively: twisted copper conductors 1a periphery evenly extrudes the rotten anti-rubber insulation 1b that reverses of salt tolerant and constitutes insulated wire cores 1, insulated wire cores 1 stranded formation twisted pair wire in twos is right, the right slit of twisted pair wire is filled with fire-retardant non-hygroscopic fiber and fills out core 2, the twisting pitch that each twisted pair wire has nothing in common with each other to employing, many group twisted pair wire strands constitute cable core, indulge covering 3 at the periphery parcel low-intensity nonwoven fabrics of cable core then, periphery at the vertical covering 3 of low-intensity nonwoven fabrics extrudes sheath 4 at last, and sheath 4 closely is squeezed in the vertical covering 3 of low-intensity nonwoven fabrics on the insulated wire cores 1.The thickness of the vertical covering 3 of low-intensity nonwoven fabrics is 0.05mm, overlaps vertical bag successively along telecommunication cable cable core axis direction, and the width of every section vertical covering of low-intensity nonwoven fabrics is 3.5 times of telecommunication cable cable core diameter.Sheath 4 employing oxygen indexs are not less than 32 flexibility high flame retardant protective cover material.
Wherein, the rotten anti-preparation process of reversing the used electro-insulating rubber of rubber insulation of salt tolerant is as follows: (1) prepares raw material, ethylene propylene diene rubber Keltan 5508:8 part by following component and weight content; Ethylene propylene diene rubber Dutral TER4044:12 part; Particle ethylene elastomer rubber EP-20:5 part; Vulcanizing agent cumyl peroxide (vulcanizing agent DCP): 0.5 part; Co-vulcanization agent triallylcyanurate (co-vulcanization agent TAC): 0.3 part; Antiscorching agent N, a N '-penylene bismaleimides (antiscorching agent HVA-2): 0.2 part; Age resistor 2,2,4-trimethyl-1,2-dihyaroquinoline condensate (anti-aging agent RD): 0.2 part; Age resistor 2 mercapto benzimidazole (antioxidant MB): 0.2 part; Silane coupler gamma-aminopropyl-triethoxy-silane (silane resin acceptor kh-550): 0.2 part; Fire retardant hydration zinc borate: 2.1 parts; Fire retardant antimonous oxide: 1 part; Flame retardant filler aluminium hydroxide (Al
2O
33H
2The O hydrated alumina): 25 parts; Activator lead orthoplumbate: 0.8 part; Activator stearic acid: 0.5 part; Activator nano zine oxide: 1.5 parts; Plasticizer Sunpar 2280 paraffin oils: 2 parts; Plasticizer chlorinated paraffin-52: 0.5 part; Reinforcing agent hydrated SiO 2: 1 part.
(2) earlier the banbury temperature is risen to 160 ℃, then add ethylene propylene diene rubber Keltan 5508, mixing 1.5 minutes of ethylene propylene diene rubber Dutral TER4044 and particle ethylene elastomer rubber EP-20, add above-mentioned flame retardant filler aluminium hydroxide more successively, the activator lead orthoplumbate, the activator nano zine oxide, antiscorching agent N, a N '-penylene bismaleimides, the reinforcing agent hydrated SiO 2, the silane coupler gamma-aminopropyl-triethoxy-silane, plasticizer Sunpar 2280 paraffin oils, the plasticizer chlorinated paraffin-52, the fire retardant hydration zinc borate, the fire retardant antimonous oxide, the activator stearic acid, age resistor 2,2,4-trimethyl-1,2-dihyaroquinoline condensate and age resistor 2 mercapto benzimidazole, carry out discharging after mixing 7 minutes, dry in the air in the space of dried and clean and put more than 24 hours; It is on 80 ℃ the banbury mixing 2 minutes again that sizing material is knocked down temperature, and added vulcanizing agent cumyl peroxide and co-vulcanization agent triallylcyanurate in the end 30 seconds, three-roller open mill on the mixing materials is carried out thin-pass, the roll spacing of three-roller open mill is 1.5mm, and slice is standby after playing the triangle bag and just wrapping each four times.
Rubber extruding machine adopted cold feeding manner when described electro-insulating rubber was extruded, screw slenderness ratio is 15:1, body temperature is 55 ℃, 90 ℃ of head temperatures, mold temperature is 120 ℃, the rubber extruding machine screw rod type of cooling is water cooling, and it is 1:1 with the ratio of extruding external diameter that the core rod of extrusion die holds line length, and the die sleeve land length is 2mm.
Embodiment two
As shown in Figure 1, ocean of the present utility model wind-powered electricity generation is with the rotten anti-telecommunication cable that reverses of salt tolerant, may further comprise the steps successively: twisted copper conductors 1a periphery evenly extrudes the rotten anti-rubber insulation 1b that reverses of salt tolerant and constitutes insulated wire cores 1, insulated wire cores 1 stranded formation twisted pair wire in twos is right, the right slit of twisted pair wire is filled with fire-retardant non-hygroscopic fiber and fills out core 2, the twisting pitch that each twisted pair wire has nothing in common with each other to employing, many group twisted pair wire strands constitute cable core, indulge covering 3 at the periphery parcel low-intensity nonwoven fabrics of cable core then, periphery at the vertical covering 3 of low-intensity nonwoven fabrics extrudes sheath 4 at last, and sheath 4 closely is squeezed in the vertical covering 3 of low-intensity nonwoven fabrics on the insulated wire cores 1.The thickness of the vertical covering 3 of low-intensity nonwoven fabrics is 0.08mm, overlaps vertical bag successively along telecommunication cable cable core axis direction, and the width of every section vertical covering of low-intensity nonwoven fabrics is 3.7 times of telecommunication cable cable core diameter.Sheath 4 employing oxygen indexs are not less than 32 flexibility high flame retardant protective cover material.
Wherein, the rotten anti-preparation process of reversing the used electro-insulating rubber of rubber insulation of salt tolerant is as follows: (1) prepares raw material, ethylene propylene diene rubber Keltan 5508:8 part by following component and weight content; Ethylene propylene diene rubber Dutral TER4044:12 part; Particle ethylene elastomer rubber EP-20:6 part; Vulcanizing agent cumyl peroxide: 0.6 part; Co-vulcanization agent triallylcyanurate: 0.4 part; Antiscorching agent N, a N '-penylene bismaleimides: 0.3 part; Age resistor 2,2,4-trimethyl-1,2-dihyaroquinoline condensate: 0.3 part; Age resistor 2 mercapto benzimidazole: 0.3 part; Silane coupler gamma-aminopropyl-triethoxy-silane: 0.3 part; Fire retardant hydration zinc borate: 2.3 parts; Fire retardant antimonous oxide: 1.2 parts; Flame retardant filler aluminium hydroxide: 30 parts; Activator lead orthoplumbate: 1.0 parts; Activator stearic acid: 0.8 part; Activator nano zine oxide: 1.7 parts; Plasticizer Sunpar 2280 paraffin oils: 2.5 parts; Plasticizer chlorinated paraffin-52: 0.8 part; Reinforcing agent hydrated SiO 2: 2 parts.
(2) earlier the banbury temperature is risen to 170 ℃, then add ethylene propylene diene rubber Keltan 5508, mixing 1.8 minutes of ethylene propylene diene rubber Dutral TER4044 and particle ethylene elastomer rubber EP-20, add above-mentioned flame retardant filler aluminium hydroxide more successively, the activator lead orthoplumbate, the activator nano zine oxide, antiscorching agent N, a N '-penylene bismaleimides, the reinforcing agent hydrated SiO 2, the silane coupler gamma-aminopropyl-triethoxy-silane, plasticizer Sunpar 2280 paraffin oils, the plasticizer chlorinated paraffin-52, the fire retardant hydration zinc borate, the fire retardant antimonous oxide, the activator stearic acid, age resistor 2,2,4-trimethyl-1,2-dihyaroquinoline condensate and age resistor 2 mercapto benzimidazole, carry out discharging after mixing 7.5 minutes, dry in the air in the space of dried and clean and put more than 24 hours; It is on 90 ℃ the banbury mixing 2.5 minutes again that sizing material is knocked down temperature, and added vulcanizing agent cumyl peroxide and co-vulcanization agent triallylcyanurate in the end 30 seconds, three-roller open mill on the mixing materials is carried out thin-pass, the roll spacing of three-roller open mill is 1.8mm, and slice is standby after playing the triangle bag and just wrapping each four times.
Rubber extruding machine adopted cold feeding manner when described electro-insulating rubber was extruded, screw slenderness ratio is 18:1, body temperature is 60 ℃, 95 ℃ of head temperatures, mold temperature is 125 ℃, the rubber extruding machine screw rod type of cooling is water cooling, and it is 1:1.1 with the ratio of extruding external diameter that the core rod of extrusion die holds line length, and the die sleeve land length is 3mm.
Embodiment three
As shown in Figure 1, ocean of the present utility model wind-powered electricity generation is with the rotten anti-telecommunication cable that reverses of salt tolerant, may further comprise the steps successively: twisted copper conductors 1a periphery evenly extrudes the rotten anti-rubber insulation 1b that reverses of salt tolerant and constitutes insulated wire cores 1, insulated wire cores 1 stranded formation twisted pair wire in twos is right, the right slit of twisted pair wire is filled with fire-retardant non-hygroscopic fiber and fills out core 2, the twisting pitch that each twisted pair wire has nothing in common with each other to employing, many group twisted pair wire strands constitute cable core, indulge covering 3 at the periphery parcel low-intensity nonwoven fabrics of cable core then, periphery at the vertical covering 3 of low-intensity nonwoven fabrics extrudes sheath 4 at last, and sheath 4 closely is squeezed in the vertical covering 3 of low-intensity nonwoven fabrics on the insulated wire cores 1.The thickness of the vertical covering 3 of low-intensity nonwoven fabrics is 0.1mm, overlaps vertical bag successively along telecommunication cable cable core axis direction, and the width of every section vertical covering of low-intensity nonwoven fabrics is 3.8 times of telecommunication cable cable core diameter.Sheath 4 employing oxygen indexs are not less than 32 flexibility high flame retardant protective cover material.
Wherein, the rotten anti-preparation process of reversing the used electro-insulating rubber of rubber insulation of salt tolerant is as follows: (1) prepares raw material, ethylene propylene diene rubber Keltan 5508:8 part by following component and weight content; Ethylene propylene diene rubber Dutral TER4044:12 part; Particle ethylene elastomer rubber EP-20:7 part; Vulcanizing agent cumyl peroxide: 0.7 part; Co-vulcanization agent triallylcyanurate: 0.5 part; Antiscorching agent N, a N '-penylene bismaleimides: 0.4 part; Age resistor 2,2,4-trimethyl-1,2-dihyaroquinoline condensate: 0.4 part; Age resistor 2 mercapto benzimidazole: 0.4 part; Silane coupler gamma-aminopropyl-triethoxy-silane: 0.4 part; Fire retardant hydration zinc borate: 2.5 parts; Fire retardant antimonous oxide: 1.5 parts; Flame retardant filler aluminium hydroxide: 40 parts; Activator lead orthoplumbate: 1.2 parts; Activator stearic acid: 1 part; Activator nano zine oxide: 2 parts; Plasticizer Sunpar 2280 paraffin oils: 5 parts; Plasticizer chlorinated paraffin-52: 1 part; Reinforcing agent hydrated SiO 2: 3 parts.
(2) earlier the banbury temperature is risen to 180 ℃, then add ethylene propylene diene rubber Keltan 5508, mixing 2 minutes of ethylene propylene diene rubber Dutral TER4044 and particle ethylene elastomer rubber EP-20, add above-mentioned flame retardant filler aluminium hydroxide more successively, the activator lead orthoplumbate, the activator nano zine oxide, antiscorching agent N, a N '-penylene bismaleimides, the reinforcing agent hydrated SiO 2, the silane coupler gamma-aminopropyl-triethoxy-silane, plasticizer Sunpar 2280 paraffin oils, the plasticizer chlorinated paraffin-52, the fire retardant hydration zinc borate, the fire retardant antimonous oxide, the activator stearic acid, age resistor 2,2,4-trimethyl-1,2-dihyaroquinoline condensate and age resistor 2 mercapto benzimidazole, carry out discharging after mixing 8 minutes, dry in the air in the space of dried and clean and put more than 24 hours; It is on 100 ℃ the banbury mixing 3 minutes again that sizing material is knocked down temperature, and added vulcanizing agent cumyl peroxide and co-vulcanization agent triallylcyanurate in the end 30 seconds, three-roller open mill on the mixing materials is carried out thin-pass, the roll spacing of three-roller open mill is 2mm, and slice is standby after playing the triangle bag and just wrapping each four times.
Rubber extruding machine adopted cold feeding manner when described electro-insulating rubber was extruded, screw slenderness ratio is 20:1, body temperature is 65 ℃, 100 ℃ of head temperatures, mold temperature is 130 ℃, the rubber extruding machine screw rod type of cooling is water cooling, and it is 1:1.2 with the ratio of extruding external diameter that the core rod of extrusion die holds line length, and the die sleeve land length is 4mm.
Measuring mechanical property result such as table 1 before aging to electro-insulating rubber among the embodiment one to embodiment three:
Table 1
To measuring mechanical property result such as the table 2 behind the electro-insulating rubber oven ageing among the embodiment one to embodiment three, aging condition: 135 ± 2 ℃ of temperature, time: 168h.
Table 2
To measuring mechanical property result such as the table 3 behind the electro-insulating rubber air bomb aging among the embodiment one to embodiment three, aging condition: 127 ± 1 ℃ of temperature, time 40h, pressure 56 N/mm2.
Table 3
As shown in table 4 to the insulation resistance of electro-insulating rubber among the embodiment one to embodiment three (20 ℃ time) test result.
Table 4
To ac capacitor increment rate test result such as table 5 behind 50 ℃ of water of electro-insulating rubber immersion among the embodiment one to embodiment three.The numerical value that records in the table be respectively the 14th day with the 1st day, the 7th day difference.
Table 5
The finished cable that electro-insulating rubber among the embodiment one to embodiment three is made carries out sea water resistance salt air corrosion performance, sea water resistance moisture saturating machine and the test of anti-twisting property.
Finished cable sea water resistance salt air corrosion performance requirement: with three long be that 30 ± 1 ℃ saliferous (NaCl) mass concentration is that 20% solution soaked 40 days for the finished cable sample of 1.1m places temperature.Cable adopts U-shaped bending, sample two ends respectively to have 30cm to surface when soaking; Soaking end back cable can be by the withstand voltage test of AC7kV/5min; Cable is wrapped on the circular shaft that diameter is 9 times of cable sample external diameters, requires insulating surface not have the range estimation visible crack, and insulation is not peeled off situation from cable in said process.
Finished cable sea water resistance moisture saturating machine requires: it is that 75 ℃ water soaks that the dielectric constant of insulation is not more than 6 after 1 day that cable is placed temperature, the ac capacitor gaining rate that soaks between the 14th day end and the 1st day end is not more than 5, the ac capacitor gaining rate that soaks between the 14th day end and the 7th day end is not more than 3, the stability factor of soaking after 14 is not more than 1, soaks that the requirement of insulation resistance constant is not less than 3670M Ω Km after 84 days.
The anti-twisting property of finished cable requires: under-40 ℃ of low temperature, finished cable is according to reversing 360 ° clockwise, return to nature then, reverse identical angle more counterclockwise, returning to nature subsequently again is one-period, regulation is carried out the test in 11000 cycles, and reverse speed is 720 °～1080 °/min.The thermal cycling test that carries out energising heating in 8 hours therebetween simultaneously and cooled off naturally in 16 hours during the energising, makes conductor temperature be stabilized in the cable maximum operating temperature, carries out 14 thermal cycling tests altogether.Require the cable appearance not chap after the end, insulation resistance satisfies the requirement of IEC 60092-351.
The finished cable that electro-insulating rubber among the embodiment one to embodiment three is made and sea water resistance salt air corrosion performance, sea water resistance moisture saturating machine and the anti-twisting property of prior art ethylene propylene rubber insulated cable are tested by above-mentioned requirements, and result of the test is relatively as table 6.
Table 6
Among the embodiment one to embodiment three, ethylene propylene diene rubber Keltan 5508 selects the product of Dutch DSM N. V. for use; Ethylene propylene diene rubber Dutral TER4044 selects the product of Italian ENI company for use; Particle ethylene elastomer rubber EP-20 adopts the speed WanFlowTM particle ethylene elastomer rubber EP-20 of production of Cheng Huagong industry and trade Co., Ltd of Shanghai; Vulcanizing agent cumyl peroxide (vulcanizing agent DCP) can select for use the permanent promise Chemical Industry Science Co., Ltd in Yantai or Shanghai Fang Rui to reach chemicals Co., Ltd product; Co-vulcanization agent triallylcyanurate (co-vulcanization agent TAC) can select for use the permanent promise Chemical Industry Science Co., Ltd in Yantai or Shanghai Fang Rui to reach chemicals Co., Ltd product; Antiscorching agent N, N '-penylene bismaleimides (antiscorching agent HVA-2) can be selected the product of emerging Hua Daming chemical industry Co., Ltd of the Huangyan East Sea, Taizhou chemical industry Co., Ltd or Changzhou for use; Age resistor 2 mercapto benzimidazole (antioxidant MB) can be selected special promise commerce and trade Co., Ltd of Shanghai rubber chemicals Co., Ltd., Factory or Qingdao product for use; Age resistor 2,2,4-trimethyl-1,2-dihyaroquinoline condensate (anti-aging agent RD) can be selected the product of friendly auxiliary agent chemical industry Co., Ltd of Jiangsu Hai'an Petrochemical Plant or Nanjing for use; Silane coupler gamma-aminopropyl-triethoxy-silane (silane resin acceptor kh-550) can be selected the product of the long brave chemical industry Co., Ltd in Nanjing or Jiangsu Chenguang Coincident Dose Co., Ltd. for use; The fire retardant hydration zinc borate can be selected the product of Shandong Bo Ao Industrial Co., Ltd. for use; The fire retardant antimonous oxide can be selected the product of the mayor pool, Yiyang antimony industry Co., Ltd or Loudi, Hunan China star antimony industry Co., Ltd for use; Flame retardant filler aluminium hydroxide (Al
2O
33H
2The O hydrated alumina) can select the product of Shijiazhuang prosperous source chemical industry Co., Ltd or the Hong Taiji of Shenzhen Industrial Co., Ltd. for use; The activator lead orthoplumbate can select for use Xinxiang to raise the product of great birch chemical industry Co., Ltd of chemical industry Co., Ltd far away or Guangzhou; The activator stearic acid can be selected the product of Shanghai Xu Ya Industrial Co., Ltd. or the Shanghai prosperous chemical industry of letter Co., Ltd for use; The particle diameter of activator nano zine oxide can be selected the product of Qinyang City zincaluminite chemical industry Co., Ltd or Zhuzhou Zhongle Chemical Industry Co., Ltd. for use between the 1-100 nanometer; Plasticizer Sunpar 2280 paraffin oils are selected U.S. NATROCHEM company or Holly Refining ﹠amp for use; Marketing – Tulsa, the product of LLC company; The plasticizer chlorinated paraffin-52 can be selected the product of Shanghai east thunder petrochemical industry Co., Ltd or Lvshunkou District Jiangxi, Daliang City chemical engineering industry parent company for use.The reinforcing agent hydrated SiO 2 can be selected the product of Guangzhou Science and Technology Ji Sheng Industrial Co or Taicang glad great chemical industry Co., Ltd for use.The utility model is raw materials used, except above producer, all can select other satisfactory like product on the market for use.
The above only is the preferable possible embodiments of the utility model, and is non-so limit to scope of patent protection of the present utility model.In addition to the implementation, the utility model can also have other execution modes.All employings are equal to the technical scheme of replacement or equivalent transformation formation, all drop in the protection range of the utility model requirement.
Claims (2)
1. an ocean wind-powered electricity generation is with the rotten anti-telecommunication cable that reverses of salt tolerant, it is characterized in that: the twisted copper conductors periphery evenly is extruded with the rotten anti-rubber insulation that reverses of salt tolerant and constitutes insulated wire cores, insulated wire cores stranded formation twisted pair wire in twos is right, the right slit of described twisted pair wire is filled with fire-retardant non-hygroscopic fiber and fills out core, the twisting pitch that each described twisted pair wire has nothing in common with each other to employing, the described twisted pair wire strand of many groups constitutes cable core, the periphery of described cable core is enclosed with the vertical covering of low-intensity nonwoven fabrics, and the periphery of the vertical covering of described low-intensity nonwoven fabrics is extruded with sheath.
2. ocean according to claim 1 wind-powered electricity generation is with the rotten anti-telecommunication cable that reverses of salt tolerant, it is characterized in that, the thickness of the vertical covering of described low-intensity nonwoven fabrics is 0.05 ~ 0.1mm, overlap vertical bag successively along telecommunication cable cable core axis direction, the width of every section vertical covering of described low-intensity nonwoven fabrics is 3.5 ~ 3.8 times of telecommunication cable cable core diameter.