CN203141938U

CN203141938U - Veneer decorative plate

Info

Publication number: CN203141938U
Application number: CN 201120397481
Authority: CN
Inventors: 罗坚立
Original assignee: Individual
Current assignee: Individual
Priority date: 2011-10-18
Filing date: 2011-10-18
Publication date: 2013-08-21
Anticipated expiration: 2021-10-18

Abstract

A utility model of veneer decorative plate with total thickness of between 0.6 and 5mm, is a combination of a flame resistant layer, a veneer decorative layer, a flame resistant layer, a wooden veneer layer, one or more than one groups of combinations each comprising a frame resistant layer and a wooden layer arranged in order, wherein the flame resistant layer is a flame resistant layer provided with a surface made from melamine impregnated paper and the refractory layer of aluminum oxide, and the veneer decorative layer is a natural veneer or a recombinant veneer of all wood species with a thickness of between 0.1 and 2mm, and the wooden veneer layer has a thickness of between 0.5 and 3.5mm, and the flame resistant layer, veneer decorative layer, flame resistant layer, wooden veneer layer, one or more than one groups of combinations each comprising a flame resistant layer and a wooden veneer layer are sequentially, orderly stacked to be once molded under high temperature and pressure. the veneer decorative plate can avoid and reduce fire, and has characteristics of simple and practical structure, natural beauty, good texture, distinct layer, beautiful appearance, endurance, wear resistance, water resistance, dry heat resistance, high temperature resistance, pressure resistance, weather resistance and paint-free property, reduced in-site procedures and low-carbon and environment-friendly industrial production, etc.

Description

A kind of utility model wood leather jacket plaque

Affiliated technical field

The utility model relates to a kind of utility model wood leather jacket plaque, and not only fire-resistant but also wear-resisting utility model wood leather jacket plaque belong to architectural decoration material field and can be applicable to wooden surface layer floor, cabinet plate, decorative panel, furniture-plates, difficult combustion version, wallboard.

Background technology

Has plenty of common difficulty combustion plate in the market, texture, decoration, poor effect; Be difficult to satisfy people's diversification, higher esthetic requirement.

Summary of the invention

The utility model designs a kind of utility model wood leather jacket plaque and satisfies people's diversification, higher esthetic requirement.The utility model wood leather jacket plaque decorative layer adopts be natural wooden skin or scientific and technological wooden leatherware have simple and practical, natural attractive in appearance, texture good, well arranged, attractive in appearance durable, and wear-resisting, water-fast, dry heat resistance, high temperature resistant, withstand voltage, weather-proof, exempt from paint, reduce the field procedure batch production and produce the low-carbon environment-friendly characteristics.

The technical scheme that its technical problem that solves the utility model adopts is: a kind of utility model wood leather jacket plaque, gross thickness is 0.6 ~ 5mm, by the difficulty combustion layer that sets gradually, wood skin decorative layer, difficult combustion layer, Wooden veneer layer and the combustion of the difficulty more than a group or group layer and Wooden veneer layer combine, it is characterized in that: the surface that described difficult combustion layer is set to melamine impregnated paper adds the difficulty combustion layer of alundum (Al, the scientific and technological wooden skin that the natural wooden skin that all wood that described wooden skin decorative layer is thickness 0.1 ~ 2mm are planted or all wood are planted, described Wooden veneer layer is set to the Wooden veneer layer of 0.5 ~ 3.5mm, described difficult combustion layer, wood skin decorative layer, difficult combustion layer, Wooden veneer layer and a group or more difficulty combustion layer and Wooden veneer layer stack neat through the HTHP moulding of producing once in order.Its surface can be mute light, Gao Guang, pitted skin, pearl, wire drawing, modelled after an antique utility model wood leather jacket plaque.

Described wooden skin decorative layer is set to natural wooden skins that all wood through seamless spliced or whole of thickness 0.1 ~ 2mm plant and contains wooden skin decorative layers dyeing or the scientific and technological wooden skins that all wood are planted and contain dyeing.

Described difficult combustion layer melts bonding wooden skin decorative layer, wooden skin decorative layer and Wooden veneer layer, Wooden veneer layer and Wooden veneer layer through HTHP.

Described Wooden veneer layer is the veneer of all 0.5 wooden ~ 3.5mm, contains import, homemade.

Described HTHP temperature 100 ℃ ~ 160 ℃ with 150 ~ 220MPa pressurize 1 minute ~ 80 minutes, the template construct that is placed on hot press becomes various utility models wood leather jacket plaques.

Of the present utility modelly resultfully be: can avoid, reduce fire and take place, simple and practical, natural attractive in appearance, texture good, well arranged, attractive in appearance durable, and wear-resisting, water-fast, dry heat resistance, high temperature resistant, withstand voltage, weather-proof, exempt from paint, reduce characteristics such as field procedure suitability for industrialized production low-carbon environment-friendly.

Description of drawings

Fig. 1 is structural representation of the present utility model.

1---difficult combustion layer, 2---wooden skin decorative layer, 3---Wooden veneer layer.

The specific embodiment

Below in conjunction with drawings and Examples the utility model is further specified.

A kind of utility model wood leather jacket plaque, gross thickness is 0.6 ~ 5mm, by the difficulty combustion layer 1 that sets gradually, wood skin decorative layer 2, difficult combustion layer 1, Wooden veneer layer 3 and the combustion of the difficulty more than a group or group layer 1 and Wooden veneer layer 3 combine, described difficult combustion layer 1 surface that is set to melamine impregnated paper adds the difficulty combustion layer 1 of alundum (Al, the scientific and technological wooden skin that the natural wooden skin that all wood that described wooden skin decorative layer 2 is thickness 0.1 ~ 2mm are planted or all wood are planted, described Wooden veneer layer 3 is set to the Wooden veneer layer 3 of 0.5 ~ 3.5mm, described difficult combustion layer 1, wood skin decorative layer 2, difficult combustion layer 1, Wooden veneer layer 3 and a group or more difficulty combustion layer 1 and Wooden veneer layer 3 stack neat through the HTHP moulding of producing once in order, and its surface can be mute light, Gao Guang, pitted skin, pearl, wire drawing, modelled after an antique utility model wood leather jacket plaque.

Described wooden skin decorative layer 2 is set to natural wooden skins that all wood through seamless spliced or whole of thickness 0.1 ~ 2mm plant and contains wooden skin decorative layers 2 dyeing or the scientific and technological wooden skins that all wood are planted and contain dyeing.

Described difficult combustion layer 1 melts bonding wooden skin decorative layer 2, wooden skin decorative layer 2 and Wooden veneer layer 3, Wooden veneer layer 3 and Wooden veneer layer 3 through HTHP.

Described Wooden veneer layer 3 is the veneer of all 0.5 wooden ~ 3.5mm, contains import, homemade.

Method (one): at first with difficult combustion layer 1, wooden skin decorative layer 2, difficult combustion layer 1, Wooden veneer layer 3 among Fig. 1; On the neat mute optical mode plate that is placed on hot press,, be cooled to the following ejecting plate of normal temperature and be made into wooden leather jacket plaque embryonic plate 100 ℃ ~ 160 ℃ pressurizes 1 minute ~ 80 minutes with 150 ~ 220MPa, temperature successively; After cutting edge, with the sander abrasive band difficulty of wooden leather jacket plaque is fired layer 1 and carry out the fixed thick wooden leather jacket plaque that forms mute light face of sanding.

Method (two): at first with difficult combustion layer 1, wooden skin decorative layer 2, difficult combustion layer 1, Wooden veneer layer 3 among Fig. 1; On the neat high optical mode plate that is placed on hot press,, be cooled to the following ejecting plate of normal temperature and be made into wooden leather jacket plaque embryonic plate 100 ℃ ~ 160 ℃ pressurizes 1 minute ~ 80 minutes with 150 ~ 220MPa, temperature successively; After cutting edge, with the sander abrasive band difficulty of wooden leather jacket plaque is fired layer 1 and carry out the fixed thick wooden leather jacket plaque that forms high light face of sanding.

Method (three): at first with difficult combustion layer 1, wooden skin decorative layer 2, difficult combustion layer 1, Wooden veneer layer 3 among Fig. 1; On the neat pitted skin template that is placed on hot press,, be cooled to the following ejecting plate of normal temperature and be made into wooden leather jacket plaque embryonic plate 100 ℃ ~ 160 ℃ pressurizes 1 minute ~ 80 minutes with 150 ~ 220MPa, temperature successively; After cutting edge, with the sander abrasive band difficulty of wooden leather jacket plaque is fired layer 1 and carry out the fixed thick wooden leather jacket plaque that forms pitted skin of sanding.

Method (four): at first with difficult combustion layer 1, wooden skin decorative layer 2, difficult combustion layer 1, Wooden veneer layer 3 among Fig. 1; On the neat pearl face die plate that is placed on hot press,, be cooled to the following ejecting plate of normal temperature and be made into wooden leather jacket plaque embryonic plate 100 ℃ ~ 160 ℃ pressurizes 1 minute ~ 80 minutes with 150 ~ 220MPa, temperature successively; After cutting edge, with the sander abrasive band difficulty of wooden leather jacket plaque is fired layer 1 and carry out the fixed thick wooden leather jacket plaque that forms the pearl face of sanding.

Method (five): at first with difficult combustion layer 1, wooden skin decorative layer 2, difficult combustion layer 1, Wooden veneer layer 3 among Fig. 1; On the neat wire drawing face die plate that is placed on hot press,, be cooled to the following ejecting plate of normal temperature and be made into wooden leather jacket plaque embryonic plate 100 ℃ ~ 160 ℃ pressurizes 1 minute ~ 80 minutes with 150 ~ 220MPa, temperature successively; After cutting edge, with the sander abrasive band difficulty of wooden leather jacket plaque is fired layer 1 and carry out the fixed thick wooden leather jacket plaque that forms wire drawing face of sanding.

Method (six): at first with difficult combustion layer 1, wooden skin decorative layer 2, difficult combustion layer 1, Wooden veneer layer 3 among Fig. 1; On the neat face die plate modelled after an antique that is placed on hot press,, be cooled to the following ejecting plate of normal temperature and be made into wooden leather jacket plaque embryonic plate 100 ℃ ~ 160 ℃ pressurizes 1 minute ~ 80 minutes with 150 ~ 220MPa, temperature successively; After cutting edge, with the sander abrasive band difficulty of wooden leather jacket plaque is fired layer 1 and carry out the fixed thick wooden leather jacket plaque that forms modelled after an antique of sanding.

Claims

1. utility model wood leather jacket plaque, gross thickness is 0.6～5mm, by the difficulty combustion layer that sets gradually, wood skin decorative layer, difficult combustion layer, Wooden veneer layer and the combustion of the difficulty more than a group or group layer and Wooden veneer layer combine, it is characterized in that: the surface that described difficult combustion layer is set to melamine impregnated paper adds the difficulty combustion layer of alundum (Al, the scientific and technological wooden skin that the natural wooden skin that all wood that described wooden skin decorative layer is thickness 0.1～2mm are planted or all wood are planted, described Wooden veneer layer is set to the Wooden veneer layer of 0.5～3.5mm, described difficult combustion layer, wood skin decorative layer, difficult combustion layer, Wooden veneer layer and a group or more difficulty combustion layer and Wooden veneer layer stack neat through the HTHP moulding of producing once in order.

2. a kind of utility model wood leather jacket plaque according to claim 1 is characterized in that: described wooden skin decorative layer is set to the wooden skin decorative layer of the scientific and technological wooden skins that natural wooden skins that all wood through seamless spliced or whole of thickness 0.1～2mm plant or all wood plants.

3. a kind of utility model wood leather jacket plaque according to claim 1, it is characterized in that: described difficult combustion layer melts bonding wooden skin decorative layer, wooden skin decorative layer and Wooden veneer layer, Wooden veneer layer and Wooden veneer layer through HTHP.