CN202766470U - Special device for producing adhesion agent for stainless steel plate flocking - Google Patents
Special device for producing adhesion agent for stainless steel plate flocking Download PDFInfo
- Publication number
- CN202766470U CN202766470U CN 201220438236 CN201220438236U CN202766470U CN 202766470 U CN202766470 U CN 202766470U CN 201220438236 CN201220438236 CN 201220438236 CN 201220438236 U CN201220438236 U CN 201220438236U CN 202766470 U CN202766470 U CN 202766470U
- Authority
- CN
- China
- Prior art keywords
- steel plate
- stainless steel
- flocking
- special device
- adhesion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model discloses a special device for producing an adhesion agent for stainless steel plate flocking. The special device comprises a high temperature reaction tank, a cooling reaction tank, a high speed stirring kettle and a mixing reaction kettle. The special device is characterized in that a technological process and related devices for producing the adhesion agent for the stainless steel plate flocking sequentially include the high temperature reaction tank, the cooling reaction tank, the high speed stirring kettle and the mixing reaction kettle, the maximum rotating speed of the high speed stirring kettle can reach to 8000 revolutions per minute, and particles with particle size of 0.01micrometer can be prepared. According to products produced by the special device, the storage life is long, and the normal temperature sealing storage life can reach more than one year; the adhesion strength is high, and the adhesion stress strength for the stainless steel plate and polypropylene fiber villus is high; the waterproofing performance is good, and the flocking stainless steel plate can be used in various environments; the flexibility is moderate, the adhesion joint strength of the flocking stainless steel plate is guaranteed, and simultaneously various processing requirements can be met; and the anti-corrosion and weather resisting performances are good, during long-term usage of the flocking stainless steel plate, the stainless steel plate can be protected from being corroded, and enduring adhesion strength can be guaranteed.
Description
Technical field
The utility model relates to a kind of equipment that tackiness agent is used in the metallic substance flocking of producing, and is specially a kind of isolated plant that tackiness agent is used in the stainless steel plate flocking of producing.
Background technology
The flocking steel plate is a kind of high performance material of implementing static flocking continuously and make on the starting material coiled material.The flocking steel plate has unique excellent performance as a kind of comparatively novel implanted article.The flocking steel plate is made substrate with stainless steel plate, any decorative pattern of wanting on villous surface can also be planted.Produce this flocking stainless steel plate, tackiness agent is had many requirements: at first, adhesive therefor must have remarkable base plate bonding power, and can not peel off as the bonding mode of porous plastics and glass fibre propping material; The second, require tackiness agent can satisfy wearing quality and the long-term safety of flocking stainless steel plate; The 3rd, the flocking stainless steel plate needs to stand the multiple process operations such as rolling forming processing, punch process, spiral processing, plasma cutting, seam is folding in the course of processing, and this just requires tackiness agent that good snappiness can be arranged.In addition, for satisfying the life-time service of flocking stainless steel plate production and construction, tackiness agent need have certain fungicidal properties and package stability, and meets the environmental requirement of modern society.
Because the flocking stainless steel plate is type material, the domestic market does not have the professional production stainless steel plate flocking equipment of tackiness agent now, commercially available Flock Adhesive is used on the flocking stainless steel plate enough binding strengths can not be provided, and water resistance and ageing-resistant performance are not good.
Summary of the invention
The purpose of this utility model is to overcome above-mentioned weak point, thereby provide a kind of and produce the stainless steel plate flocking with the isolated plant of tackiness agent, the over-all properties such as ageing-resistant and processing characteristics that the tackiness agent of its production satisfies shelf-stable, bonding is firm, anti-corrosion is good.
The technical solution of the utility model is: a kind of isolated plant of producing stainless steel plate flocking usefulness tackiness agent, comprise pyroreaction tank, cooling retort, high-speed stirring still, hybrid reactor, it is characterized in that: the flocking of production stainless steel plate is followed successively by pyroreaction tank, cooling retort, high-speed stirring still, hybrid reactor with technological process and the relevant device of tackiness agent.Described high-speed stirring still, maximum speed reach 8000 rev/mins, can be prepared into the particle of particle diameter 0.01um.
Compared with the prior art the utility model has the following advantages: the product that the utility model is produced, and the shelf lives is long, and the normal temperature sealed storage phase is more than 1 year; Cohesive strength is high, and stainless steel plate and polypropylene fibre fine hair are all had high-intensity cohesive force; Water resistance is good, guarantees the use of flocking stainless steel plate in multiple environment; Snappiness is moderate, can satisfy various processing requests again when guaranteeing flocking stainless steel plate Joint strength; Anti-corrosion good weatherability can protect stainless steel plate not to be corroded in the life-time service of flocking stainless steel plate, can guarantee again lasting cohesive strength and other performance.
Description of drawings
Fig. 1 is device structure schematic diagram of the present utility model.
Among the figure, 1. the pyroreaction tank 2. cools off retort, 3. high-speed stirring still, 4. hybrid reactor.
Embodiment:
Below in conjunction with accompanying drawing the utility model is further described.
A kind of isolated plant of producing stainless steel plate flocking usefulness tackiness agent in the utility model, comprise pyroreaction tank 1, cooling retort 2, high-speed stirring still 3, hybrid reactor 4, it is characterized in that: the flocking of production stainless steel plate is followed successively by pyroreaction tank 1 with technological process and the relevant device of tackiness agent, cooling retort 2, high-speed stirring still 3, hybrid reactor 4, described high-speed stirring still 3, maximum speed reach 8000 rev/mins, can be prepared into the particle of particle diameter 0.01um.
Working process of the present utility model is: 200 parts of adipic acid type polyester diol (molecular weight is 1800～2000), 60 parts of isophorone diisocyanates and 0.05 part of dibutyl tin dilaurate are added in the pyroreaction tank 1, mix and blend also is heated to 80 ℃, reacted 1.8 hours, stirring velocity is 1200 rev/mins, makes the polyester polyols alcohol mixture.
Above-mentioned polyester polyols alcohol mixture being added in the cooling retort 2, be cooled to 68 ℃, adds 8 parts of dimethylol propionic acids and 7 parts of N-Methyl pyrrolidone, is to react 3.8 hours under 1200 rev/mins the condition in temperature 70 C, stirring velocity; Be cooled to 35 ℃, add 6 parts of triethylamines, low whipping speed is reaction 20 minutes under 1200 rev/mins the condition; Add 500 parts of deionized waters, low whipping speed is high speed dispersion emulsification 0.8 hour under 3000 rev/mins the condition again; Add at last 6 parts of isophorone diamines, low whipping speed is reaction 50 minutes under 1200 rev/mins the condition, obtains base polyurethane prepolymer for use as.
40 parts of methyl methacrylates and 500 parts of base polyurethane prepolymer for use as are joined in the high-speed stirring still 3, dispersed with stirring is 0.8 hour under the condition of 68 ℃ of temperature, then in 1.6 hours, drip 0.4 part of Diisopropyl azodicarboxylate, stir when dripping, be warming up to 80 ℃ of continuation after being added dropwise to complete and under the condition that stirs, reacted 2.5 hours; Discharging when treating that temperature is down to 45 ℃ namely obtains described acrylic acid modified polyurethane emulsion; Described stirring velocity is 8000 rev/mins.
100 parts of polyaminoester emulsions and 10 parts of filler-silicon dioxides are added in the hybrid reactor 4, add filler-silicon dioxide, to improve the optics of sizing agent, physicals, increase the hardness of sizing agent, and reach the effect that hides substrate, stir after 20 minutes, when stirring, add 0.5 part of defoamer organo-siloxane, 0.04 part antimildew disinfectant isothiazolinone biocide agent, 1 part of wetting agent mersolates and 2 parts of thickening material organobentonites, add the defoamer organo-siloxane and eliminate the bubble that may exist in the sizing agent, prevent from coating procedure, occurring the not blank spot of gluing.Add the agent of mould inhibitor isothiazolinone biocide, prevent that sizing agent and flocking steel plate from occurring going mouldy in placement or use procedure.Add the wetting agent mersolates, to promote sizing agent the sprawling of metallic surface, improve sizing agent in the coating homogeneity of metallic surface.Add the thickening material organobentonite, in order to improve system viscosity, make system keep uniform and stable suspended state or milkiness state, or form gel, have thickening, suspension, emulsification, the several functions such as stable.Continue to stir 15 minutes, stirring velocity is 900 rev/mins; Reduce stirring velocity to 300 rev/min, and add 8 parts of viscosity increaser water-baseds and increase glutinous resin, utilize water-based to increase glutinous resin as viscosity increaser, not only can be adjusted to suitable viscosity but also can be well compatible with emulsion.Stirred 10 minutes, and namely obtained described steel plate flocking tackiness agent.
Take the 0.25mm stainless steel plate as substrate, length 2.5mm polypropylene fibre is as fine hair, tackiness agent coated weight 25g/m
2
As shown in table 1 to the preparation-obtained tackiness agent flocking of embodiment performance evaluation project, test conditions and result.
Flocking performance evaluation project, test conditions and the result of table 1 tackiness agent
This shows, the product that the utility model is produced, the shelf lives is long, and the normal temperature sealed storage phase is more than 1 year; Cohesive strength is high, and stainless steel plate and polypropylene fibre fine hair are all had high-intensity cohesive force; Water resistance is good, guarantees the use of flocking stainless steel plate in multiple environment; Snappiness is moderate, can satisfy various processing requests again when guaranteeing flocking stainless steel plate Joint strength; Anti-corrosion good weatherability can protect stainless steel plate not to be corroded in the life-time service of flocking stainless steel plate, can guarantee again lasting cohesive strength and other performance.
Claims (2)
1. produce the isolated plant that tackiness agent is used in the stainless steel plate flocking for one kind, comprise pyroreaction tank, cooling retort, high-speed stirring still, hybrid reactor, it is characterized in that: the flocking of production stainless steel plate is followed successively by pyroreaction tank, cooling retort, high-speed stirring still, hybrid reactor with technological process and the relevant device of tackiness agent.
2. according to claim 1ly a kind ofly produce the stainless steel plate flocking with the isolated plant of tackiness agent, it is characterized in that: described high-speed stirring still, maximum speed reach 8000 rev/mins, can be prepared into the particle of particle diameter 0.01um.