CN202559046U - Basalt composite nonwoven material - Google Patents
Basalt composite nonwoven material Download PDFInfo
- Publication number
- CN202559046U CN202559046U CN2011205692570U CN201120569257U CN202559046U CN 202559046 U CN202559046 U CN 202559046U CN 2011205692570 U CN2011205692570 U CN 2011205692570U CN 201120569257 U CN201120569257 U CN 201120569257U CN 202559046 U CN202559046 U CN 202559046U
- Authority
- CN
- China
- Prior art keywords
- basalt
- web layer
- nonwoven material
- composite nonwoven
- equipment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model discloses a basalt composite nonwoven material which comprises at least one basalt fiber web layer and at least two common fiber web layers, wherein the basalt fiber web layer is sandwiched between the two common fiber web layers. The utility model also discloses a preparation method of the basalt composite nonwoven material. Compared with the conventional basalt composite nonwoven material, the basalt composite nonwoven material of the application is superior in overall characteristics, such as high production efficiency, low cost, filter property, high temperature resistance, noise reduction by absorption, skid prevention by water absorption, heat insulation property, and air humidity conditioning capability. In the preparation method of the basalt composite nonwoven material of the application, the operation of mechanically drawing basalt to form basalt fibers prior to weaving is not needed, and the basalt is directly subjected to melt-spinning and high pressure air drawing to form the web. The production process is simple, the production difficulty is greatly reduced, and the production efficiency is increased.
Description
Technical field
The utility model relates to the composite nonwoven material field, particularly relates to a kind of basalt composite nonwoven material and preparation method thereof.
Background technology
Volcanic rock is the porous shape stone material that forms after the volcano eruption, is of great rarity.Basalt is to develop down from molten form to form as a kind of igneous rock, contains mineral matters such as abundant sodium, magnesium, aluminium, silicon, calcium, manganese, iron, phosphorus, nickel, cobalt.Because of its surface evenly is covered with pore, antique, and have characteristics such as electrical conductivity is little, "dead", will never fade; And weathering resistance, high temperature resistant, sqouynd absorption lowering noise, the anti-skidding resistance heat of suction, regulate air humidity, function such as improve the ecological environment.The Paul Dhe of France is that first wants to utilize basalt to extrude the people of basalt fibre.
Basalt fibre is to continue similar in appearance to the way manufacturing of glass wire drawing to form at present.At first, demand stops the basalt of exploiting out to break and destroy to dispose and wash; Pack into then with feed bin that batch charger links to each other in, by batch charger raw material is put into the melting end with the kiln of natural gas heating, for example patent ZL97199852.3, ZL200410101966.0 are to utilize this method spinning.But these all are to utilize mechanical stretching to make fiber, utilize the traditional textile method to weave again; Speed of production is slow, and cost is high, and the production difficulty is also bigger.
Summary of the invention
The purpose of the utility model provides a kind of new basalt composite nonwoven material and preparation method thereof.
To achieve these goals, the utility model has adopted following technical scheme:
The application discloses a kind of basalt composite nonwoven material, comprises one deck basalt web layer and two-layer at least web layer at least, and the basalt web layer is located between the two-layer web layer.It is pointed out that the basalt web layer is located between the two-layer web layer, is not the qualification of the basalt composite nonwoven material number of plies among the application, is a kind of structure; That is to say that the basalt composite nonwoven material among the application can have multilayer basalt web layer, and each layer basalt web layer is located between the web layer formation sandwich structure respectively.
Further, the basalt web layer adopts the basalt melt spinning directly to become net through the high pressure draught drawing-off.It is pointed out that in the utility model that the basalt web layer directly adopts the fusion lapping to be shaped, rather than traditional basalt fibre of preparation earlier, be woven into net through basalt fibre again; Therefore, improve production efficiency greatly, also reduced production cost.
Further, the angle of high pressure draught and fiber is between the level downward 5 °-85 °.
Among the application, it is compound fixed that basalt web layer and web layer adopt wherein a kind of in acupuncture, water thorn, ultrasonic wave, the hot calendering bonding to carry out.
Further, common web layer adopts fiber carding or filature fleece formation.
Among the application, the material of preferred common web layer comprises at least a in polyester, polypropylene, polyethylene, the polyamide.
Preferably, the fineness of basalt melt-spinning fiber is 1-5d.
Disclosed herein as well is a kind of preparation method of basalt composite nonwoven material, comprise the steps,
A. first web layer becomes net: adopt carding or filature fleece formation;
B. the basalt web layer becomes net: carry out the drawing-off of basalt melt spinning high pressure draught on first web layer and become net, form and be layed in the basalt web layer on first web layer;
C. second web layer becomes net: on the basalt web layer, carry out carding or filature fleece formation, form and be layed in second web layer on the basalt web layer;
D is compound fixed: first fibrage, basalt web layer and second web layer is compound fixed.
Among the application's the preparation method, compound fixed wherein a kind of in fixed of acupuncture, water thorn, ultrasonic wave, hot calendering bonding that be.
Further, the material of first web layer and second web layer comprises at least a in polyester, polypropylene, polyethylene, the polyamide respectively.
In the application's the embodiment, the drawing-off of basalt melt spinning high pressure draught becomes netting gear body process to comprise: basalt fusion, screw rod extruding, measuring pump metering, melt distribute, spinnerets sprays silk, cold air high pressure draught drawing-off lapping.
Because adopt above technical scheme, the beneficial effect of the utility model is:
The application's basalt composite nonwoven material is compared with traditional basalt fiber composite material; Production efficiency is high; Cost is low, and overall characteristic is strong, and is hot like filterability, heat-resisting quantity, sqouynd absorption lowering noise property, the anti-skidding resistance of suction, regulate air humidity ability characteristics etc.
Among the application's the basalt composite nonwoven material preparation method; Need not carry out weaving after mechanical commutation draft forms basalt fibre to basalt; But directly adopt the basalt melt spinning to become net through the high pressure draught drawing-off; Production technology is simple, has reduced the production difficulty greatly, has improved production efficiency.
Description of drawings
Fig. 1 is the structural representation of the basalt composite nonwoven material for preparing among the utility model embodiment;
Fig. 2 is the structural representation of the production equipment of preparation basalt composite nonwoven material among the utility model embodiment;
Fig. 3 is the structural representation of the production equipment of preparation basalt composite nonwoven material among another embodiment of the utility model.
The specific embodiment
In traditional basalt fiber composite material, the basalt web layer is woven into net by basalt fibre, and promptly earlier mechanical drawing-off forms basalt fibre, utilizes basalt fibre to weave then.In the application's the basalt composite nonwoven material; The basalt web layer is located between two-layer common (referring to non-basalt web layer) web layer; And; The basalt web layer adopts the basalt melt spinning directly to become net through the high pressure draught drawing-off, and the angle of high pressure draught and fiber is between downward 5 °-85 ° of the level.Wherein the material of common web layer comprises at least a in polyester, polypropylene, polyethylene, the polyamide.
Preparation method at the application's basalt composite nonwoven material comprises:
A. first web layer becomes net: adopt carding or filature fleece formation;
B. the basalt web layer becomes net: carry out the drawing-off of basalt melt spinning high pressure draught on first web layer and become net, form and be layed in the basalt web layer on first web layer;
C. second web layer becomes net: on the basalt web layer, carry out carding or filature fleece formation, form and be layed in second web layer on the basalt web layer;
D is compound fixed: first fibrage, basalt web layer and second web layer is compound fixed.
Among the application, compoundly fixedly be selected from but be not limited only to a kind of in fixed of acupuncture, water thorn, ultrasonic wave, hot calendering bonding.Wherein, acupuncture is fixed to be to have the pricker that stings hook through acupuncture apparatus to move up and down, and the thorn ditch drives the part fiber and interts up and down, tangles mutually and embraces knot, forms fixed; Water thorn is fixed to be to move up and down through the fine water flow drives fiber of high pressure, and it is fixed to tangle obvolvent; Ultrasonic wave is fixed to be to utilize ultrasonic wave that the part high polymer fibre is melt bonded fixed; Hot calendering bonding is fixed to be to push up and down through hot roll, makes the bond vitrified of part high polymer fibre fixed.
The application provides a kind of production line of basalt composite nonwoven material, comprises at least two the high polymer lapping equipment, at least one basalt filature fleece formation equipment and the compound consolidation device that are arranged at the guipure top; Wherein basalt filature fleece formation equipment interval formula is installed between the high polymer lapping equipment successively; Compound consolidation device is installed on the end of guipure direction of transfer.Be that guipure passes through high polymer lapping equipment, basalt filature fleece formation equipment, high polymer lapping equipment, basalt filature fleece formation equipment, high polymer lapping equipment, basalt filature fleece formation equipment successively ... high polymer lapping equipment, compound consolidation device.
In the application's the production line; Basalt filature fleece formation equipment comprises basalt stone breaker and melt spinning device; The outlet of basalt stone breaker is communicated with the inlet of melt spinning device, and the basalt stone entering melt spinning device after the fragmentation sprays silk, cold air high pressure draught drawing-off lapping through screw rod extruding, measuring pump metering, melt distribution, spinnerets after the fusion; The spinnerets orifice diameter is 6-100 μ m, and spinneret orifice density is 500-7000/m.The outlet of basalt stone breaker is provided with screen pack, and the aperture of filter screen is less than or equal to 2cm.
In the application's the production line, high polymer lapping equipment is selected from one or both in fiber carding equipment and the filature fleece formation equipment.Preferred spinning product equipment is melt spinning device.
In the application's the production line, compound consolidation device is selected from but is not limited only to a kind of in acupuncture apparatus, water thorn equipment, ultrasonic equipment, the hot calendering bonding consolidation device.
Further, compound fixed after, in the application's the production line, adopt take up roll that the basalt composite nonwoven material is reeled.
Among the application's the embodiment, the production line of basalt composite nonwoven material comprises, two high polymer lapping equipment, a basalt filature fleece formation equipment and compound consolidation device.And two high polymer lapping equipment are fiber carding equipment.Technological process comprises that the high polymer short fiber forms first web layer through first fiber carding equipment carding; Then, first web layer is sent to basalt filature fleece formation equipment below through guipure, and drawing-off becomes net to basalt with high pressure draught through melt spinning, forms to be layed in the basalt web layer on first web layer; Then; The web layer (first web layer and basalt web layer) that two superimposed is laid is sent to second fiber carding equipment below through guipure again; On the basalt web layer, lay second web layer, form the basalt web layer and be sandwiched in first web layer and the middle sandwich structure of second web layer.At last, guipure is sent to compound consolidation device place with three layers of fibre web of this sandwich structure, and it is compound fixed, forms the described basalt composite nonwoven material of the application.
Among another embodiment of the application, the production line of basalt composite nonwoven material comprises, two high polymer lapping equipment, a basalt filature fleece formation equipment and compound consolidation device.And two high polymer lapping equipment are the melt spinning web-forming equipment.In the production technology, first web layer all adopts melt spinning to become net with second web layer, and remainder is identical with above-mentioned technological process.
The application's basalt composite nonwoven material is compared with traditional basalt fiber composite material; Production efficiency is high; Cost is low, and overall characteristic is strong, and is hot like filterability, heat-resisting quantity, sqouynd absorption lowering noise property, the anti-skidding resistance of suction, regulate air humidity ability characteristics etc.
Among the application's the basalt composite nonwoven material preparation method; Need not carry out weaving after mechanical commutation draft forms basalt fibre to basalt; But directly adopt the basalt melt spinning to become net through the high pressure draught drawing-off; Production technology is simple, has reduced the production difficulty greatly, has improved production efficiency.
Below through specific embodiment and combine accompanying drawing that the utility model is done further explain.Following examples are only further explained the utility model, should not be construed as the restriction to the utility model.
Embodiment one
In this example, the basalt composite nonwoven material is made up of three layers of fibre web, and is as shown in Figure 1, be respectively first web layer 2 and second web layer 4 and be sandwiched in first web layer 2 and second web layer 4 between basalt web layer 3.Wherein first web layer 2 and second web layer 4 are the polyester web layer.
In this example; The production line of basalt composite nonwoven material comprises; As shown in Figure 2; Be set in turn in the first short fiber carding equipment 12, basalt filature fleece formation equipment 13, the second short fiber carding equipment 14 and the acupuncture consolidation device 15 of guipure 11 tops, and the take up roll 16 that is arranged at acupuncture consolidation device 15 outputs.Wherein, basalt filature fleece formation equipment 13 comprises basalt stone breaker and melt spinning device (not drawing), and the outlet of basalt stone breaker is communicated with the inlet of melt spinning device; Basalt stone after the fragmentation gets into melt spinning device, and the spinnerets orifice diameter is 15-25 μ m, and the outlet of basalt stone breaker is provided with screen pack; The aperture of filter screen is less than or equal to 2cm, and the about 7.3m of spinnerets fabric width slightly is wider than the product fabric width; The about 7m of product fabric width, 3000/m of spinnerets spinneret orifice.The basalt melt-spinning technology comprises, sprays silk, cold air high pressure draught drawing-off lapping through screw rod extruding, measuring pump metering, melt distribution, spinnerets after the basalt fusion; Wherein, 10 seconds melting times, 1450 ℃ of melt temperatures, the air pressure 10000pa of high pressure draught, gas flow temperature between 10 ℃-15 ℃, average fiber fineness 2 Denier (2d) in the basalt web layer of acquisition.
In this example, the preparation method of basalt composite nonwoven material carries out on this routine above-mentioned production line, specifically comprises:
A. first web layer becomes net: the polyester staple fibers raw material adopts the first short fiber carding machine equipment, 12 cardings to form first web layer 2;
B. the basalt web layer becomes net: first web layer 2 is sent to basalt filature fleece formation equipment 13 belows through guipure 11; Basalt filature fleece formation equipment 13 directly carries out the drawing-off of basalt melt spinning high pressure draught and becomes net on first web layer 2, form to be layed in the basalt web layer 3 on first web layer 2;
C. second web layer becomes net: the second short fiber carding machine equipment 14 is that raw material carries out the fiber carding on basalt web layer 3 with the polyester staple fibers, forms and is layed in second web layer 4 on the basalt web layer 3;
D is compound fixed: first fibrage 2, basalt web layer 3 and 4 acupunctures of second web layer that will superpose successively are fixed.
Wherein, the fibre fineness of polyester staple fibers is 0.5-3.5d.Promptly obtain this routine described basalt composite nonwoven material through above-mentioned three steps, last, adopt take up roll 16 to reel and collect.
Embodiment two
In this example, the basalt composite nonwoven material is made up of three layers of fibre web, and is as shown in Figure 1, be respectively first web layer 2 and second web layer 4 and be sandwiched in first web layer 2 and second fibre web 4 between basalt web layer 3.Wherein first web layer 2 and second fibre web 4 are the polypropylene web layer.
In this example; The production line of basalt composite nonwoven material comprises; As shown in Figure 3; Be set in turn in the first spunbond spinning lapping equipment 22, basalt filature fleece formation equipment 23, the second spunbond spinning lapping equipment 24 and the acupuncture consolidation device 25 of guipure 21 tops, and the take up roll 26 that is arranged at acupuncture consolidation device 25 outputs.Wherein, basalt filature fleece formation equipment 23 comprises basalt stone breaker and melt spinning device (not drawing), and the outlet of basalt stone breaker is communicated with the inlet of melt spinning device; Basalt stone after the fragmentation gets into melt spinning device, and the spinnerets orifice diameter is 5-15 μ m, and the outlet of basalt stone breaker is provided with screen pack; The aperture of filter screen is less than or equal to 2cm, and the about 3.2m of spinnerets fabric width slightly is wider than the product fabric width; The about 3m of product fabric width, 5000/m of spinnerets spinneret orifice.Basalt melt spinning high pressure draught drawing-off net-forming process comprises, sprays silk, cold air high pressure draught drawing-off lapping through screw rod extruding, measuring pump metering, melt distribution, spinnerets after the basalt fusion; Wherein, 8 seconds melting times, 1650 ℃ of melt temperatures, the about 20000pa of the air pressure of high pressure draught, gas flow temperature between 10 ℃-15 ℃, average fiber fineness 1.5 Denier (1.5d) in the basalt web layer of acquisition.
In this example, the preparation method of basalt composite nonwoven material carries out on this routine above-mentioned production line, specifically comprises:
A. first web layer becomes net: pp material adopts first spunbond spinning lapping equipment 22 melt spinnings to become net to form first web layer 2;
B. the basalt web layer becomes net: first web layer 2 is sent to basalt filature fleece formation equipment 23 belows through guipure 21; Basalt filature fleece formation equipment 23 directly carries out the drawing-off of basalt melt spinning high pressure draught and becomes net on first web layer 2, form to be layed in the basalt web layer 3 on first web layer 2;
C. second web layer becomes net: the second spunbond spinning lapping equipment 24 is that raw material carries out melt spinning and becomes net with the polypropylene on basalt web layer 3, forms and is layed in second web layer 4 on the basalt web layer 3;
D is compound fixed: first fibrage 2, basalt web layer 3 and 4 acupunctures of second web layer that will superpose successively are fixed.
Wherein, fibre fineness is 0.5-3.5d in the polypropylene web layer of melt spinning formation.Promptly obtain this routine described basalt composite nonwoven material through above-mentioned three steps, last, adopt take up roll 26 to reel and collect.
Embodiment three
In this example, the basalt composite nonwoven material is made up of three layers of fibre web, and is as shown in Figure 1, be respectively first web layer 2 and second web layer 4 and be sandwiched in first web layer 2 and second web layer 4 between basalt web layer 3.Wherein first web layer 2 is the polyethylene fiber stratum reticulare, and second web layer 4 is the polyamide web layer.
In this example; The production line of basalt composite nonwoven material comprises; Be set in turn in short fiber carding machine equipment, basalt filature fleece formation equipment, spunbond spinning lapping equipment and the hot calendering bonding consolidation device of guipure top, and the take up roll that is arranged at hot calendering bonding consolidation device output.Wherein, basalt filature fleece formation equipment comprises basalt stone breaker and melt spinning device, and the outlet of basalt stone breaker is communicated with the inlet of melt spinning device; Basalt stone after the fragmentation gets into melt spinning device, and the spinnerets orifice diameter is 5-15 μ m, and the outlet of basalt stone breaker is provided with screen pack; The aperture of filter screen is less than or equal to 2cm, and the about 3.2m of spinnerets fabric width slightly is wider than the product fabric width; The about 3m of product fabric width, 1000/m of spinnerets spinneret orifice.Basalt melt spinning high pressure draught drawing-off net-forming process comprises, sprays silk, cold air high pressure draught drawing-off lapping through screw rod extruding, measuring pump metering, melt distribution, spinnerets after the basalt fusion; Wherein, 8 seconds melting times, 1650 ℃ of melt temperatures, the about 20000pa of the air pressure of high pressure draught, gas flow temperature between 10 ℃-15 ℃, average fiber fineness 4.5 Denier (4.5d) in the basalt web layer of acquisition.
In this example, the preparation method of basalt composite nonwoven material carries out on this routine above-mentioned production line, specifically comprises:
A. first web layer becomes net: polyethylene short fiber raw material adopts short fiber carding machine equipment carding to form first web layer 2;
B. the basalt web layer becomes net: first web layer 2 is sent to basalt melt spinning web-forming equipment below through guipure; Basalt melt spinning web-forming equipment directly carries out the drawing-off of basalt melt spinning high pressure draught and becomes net on first web layer 2, form to be layed in the basalt web layer 3 on first web layer 2;
C. second web layer becomes net: spunbond spinning lapping equipment is that raw material carries out melt spinning and becomes net with the polyamide on basalt web layer 3, forms and is layed in second web layer 4 on the basalt web layer 3;
D is compound fixed: first fibrage 2, basalt web layer 3 and 4 acupunctures of second web layer that will superpose successively are fixed.
Wherein, the fibre fineness of polyethylene short fiber is 0.5-3.5d; The fibre fineness of the polyamide that melt spinning forms is 0.5-3.5d.Promptly obtain this routine described basalt composite nonwoven material through above-mentioned three steps, last, adopt take up roll to reel and collect.
Above content is the further explain that combines concrete embodiment that the utility model is done, and can not assert that the practical implementation of the utility model is confined to these explanations.For the those of ordinary skill of technical field under the utility model, under the prerequisite that does not break away from the utility model design, can also make some simple deduction or replace, all should be regarded as belonging to the protection domain of the utility model.Such as, first web layer and second web layer can be used carding technology, also can use filature fleece formation, can adopt existing equipment and technologies such as solution spins, molten spinning in the filature fleece formation.
Claims (6)
1. basalt composite nonwoven material, it is characterized in that: comprise one deck basalt web layer and two-layer at least common web layer at least, said basalt web layer is located between the two-layer common web layer.
2. basalt composite nonwoven material according to claim 1 is characterized in that: said basalt web layer adopts the basalt melt spinning directly to become net through the high pressure draught drawing-off.
3. basalt composite nonwoven material according to claim 2 is characterized in that: the angle of said high pressure draught and basalt melt-spinning fiber is between downward 5 °-85 ° of the level.
4. basalt composite nonwoven material according to claim 2 is characterized in that: the fineness of said basalt melt-spinning fiber is 1-5d.
5. according to each described basalt composite nonwoven material of claim 1-4, it is characterized in that: it is compound fixed that said basalt web layer and common web layer adopt wherein a kind of in acupuncture, water thorn, ultrasonic wave, the hot calendering bonding to carry out.
6. according to each described basalt composite nonwoven material of claim 1-4, it is characterized in that: said common web layer adopts fiber carding or filature fleece formation.