CN201962204U - 可异地加工的单银低辐射镀膜玻璃 - Google Patents
可异地加工的单银低辐射镀膜玻璃 Download PDFInfo
- Publication number
- CN201962204U CN201962204U CN2011200541358U CN201120054135U CN201962204U CN 201962204 U CN201962204 U CN 201962204U CN 2011200541358 U CN2011200541358 U CN 2011200541358U CN 201120054135 U CN201120054135 U CN 201120054135U CN 201962204 U CN201962204 U CN 201962204U
- Authority
- CN
- China
- Prior art keywords
- layer
- glass
- protective layer
- dielectric medium
- sliver
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
本实用新型公开了一种可异地加工的单银低辐射镀膜玻璃,包括基板玻璃和镀膜层,镀膜层包括以基板玻璃为基础层向外依次镀覆的第一电介质层、第一保护层、Ag层、第二保护层和第二电介质层,其中第一电介质层和第二电介质层的材料为Si3N4,所述的第一保护层的材料为AZO,而第二保护层的材料为ZrO。本实用新型通过采用AZO和ZrO材料分别作为保护层分镀在银层前后两侧,使得产品的耐磨性及抗氧化性能得到了很大的提高,能够承受长途运输、预加工处理(如切割、洗磨),甚至是高温处理(如钢化、热弯),在此过程中,其外观和性能均不会受到影响,并且具有很高的透过率,其热功性能优于普通的单银低辐射玻璃,且非常易于长期储存。
Description
技术领域
本实用新型涉及一种镀膜玻璃,尤其是涉及一种可异地加工的单银低辐射镀膜玻璃。
背景技术
目前市场上普通单银低辐射镀膜产品,随着国产设备性能的提升及大批量的投入使用,市场进一步被蚕食、压缩,这对于大型的玻璃深加工企业来说,其为了保持与小型加工厂在竞争中的竞争优势,就必须利用自身国外设备性能的优势,来提高生产效率,因此,就出现了可异地加工的单银低辐射镀膜玻璃,利用高效的生产效率和降低成本来提升产品的竞争力,然而目前市场上的可异地加工单银低辐射镀膜玻璃,经常由于膜层硬度不够,抗氧化能力较差,在预处理过程中造成划伤、擦伤,且储存时间稍长便会出现氧化的问题。
发明内容
为了克服现有技术的不足,本实用新型的目的在于提供一种性能稳定、耐磨、抗氧化性能好,且能提供透光率的可异地加工的单银低辐射镀膜玻璃。
本实用新型是通过以下技术方案来实现的:
一种可异地加工的单银低辐射镀膜玻璃,包括基板玻璃和镀膜层,镀膜层包括以基板玻璃为基础层向外依次镀覆的第一电介质层、第一保护层、Ag层、第二保护层和第二电介质层,其中第一电介质层和第二电介质层的材料为Si3N4,其特征在于,所述的第一保护层的材料为AZO,而第二保护层的材料为ZrO。
本实用新型的有益效果是:本实用新型通过采用AZO材料和ZrO材料分别作为保护层分镀在银层的前后两侧,使得产品本身的耐磨性及抗氧化性能得到了很大的提高,能够承受长途运输、预加工处理(如切割、洗磨),甚至是高温处理(如钢化、热弯),在此过程中,其外观和性能均不会受到影响,并且具有很高的透过率,其热功性能优于普通的但银低辐射玻璃,且非常易于长期储存。
附图说明
图1为本实用新型一实施例的结构示意图。
图中主要附图标记含义为:
1、基板玻璃 2、第一电介质层 3、第一保护层
4、Ag层 5、第二保护层 6、第二电介质层。
具体实施方式
下面将结合附图,详细说明本实用新型的具体实施方式:
图1为本实用新型一实施例的结构示意图。
如图1所示:可异地加工的单银低辐射镀膜玻璃,包括基板玻璃1和镀膜层,其中,镀膜层包括以基板玻璃为基础层向外依次镀覆的第一电介质层2、第一保护层3、Ag层4、第二保护层5和第二电介质层6,其中第一电介质层2和第二电介质层6的材料为Si3N4,而所述的第一保护层3的材料为AZO,第二保护层5的材料为ZrO。
此外,本实用新型的生产工艺为:首先选用新鲜的基板玻璃1,然后通过清洗机清洗达到要求后,干燥,经过预真空过渡后,按顺序依次镀制第一电介质层2、第一保护层3、Ag层4、第二保护层5和第二电介质层6。
更为具体的是:其中的第一电介质层2和第二电介质层6是通过旋转交流阴极的硅铝靶在氮、氩氛围中溅射形成,其中Si:Al=92:8,其作用为:a、在银层和电解质层之间提供吸附力;b、保护整个膜层结构,减少其氧化,提高其物理和化学性能;c、控制膜系的光学性能和颜色。
银层,通过直流平面阴极的银靶在氩气氛围中溅射,其作用是:银层作为主要功能层,降低了辐射率,以起到隔热、保温的效果。
而第一保护层3通过旋转交流阴极AZO靶在氧、氩氛围中溅射,作用是:a、保护银层不被氧化;b、增加银层同其它膜层的结合力;c、为银层成膜做好铺垫,并能保证复合膜的透过率。
第二保护层5通过直流平面阴极Zr靶在氧、氩氛围中溅射,作用是:a、加强对银层的保护;b、增加银层同其它膜层的结合力。
本实用新型使用德国冯.阿登纳的磁控溅射镀膜机,采用表1列出工艺参数,使用7个交流旋转双阴极,4个直流平面阴极,制出本实用新型使用新材料的可异地加工低辐射单银镀膜玻璃,其工艺参数和靶的位置列表如下:
表1:使用新型材料的可异地加工单银低辐射镀膜玻璃靶位及工艺参数
产品说明
1、用上述工艺参数制出的玻璃,按如下加工要求(或建议),就可生产出完全符合国标要求的产品:
a、切割,无特殊要求,切割后要及时洗磨;
b、洗磨(关键工序),建议砂带打磨,若上机磨,则应放低压轮且每隔一段距离增加一个喷淋管,洗片机毛刷采用质地较软的且水加热后,开始清洗,清洗使用去离子水;
c、钢化(或热弯),采用对流式钢化炉,在相同厚度的普通白玻基础上,适当降低钢化温度,延长加热时间;
d、中空,使用去离子水,且边部除膜。
2、用上述工艺参数制出的玻璃,钢化前、后光学性能及颜色数据漂移(变化)情况如下:
(其中Rg表示可见光玻璃面反射率;Rf表示可见光膜面反射率;Tr表示可见光透过率;a*表示红绿色坐标;b*表示黄蓝色坐标;R。表示面电阻)
鉴于以上数据漂移情况,建议单一使用钢化前、钢化后数据分别作为一种产品的光学性能及颜色标准,并加以控制,勿钢前、钢后混用,以避免产生色差(目前国内大多数可钢单银LOW-E产品均采用此方式)
产品光学性能如下(单片钢化后):
玻璃可见光透过率T=88.2%
可见光玻璃面反射率=6.2%
可见光玻璃面色坐标a*值=-2.0
可见光玻璃面色坐标b*值=-2.2
可见光膜面反射率=3.4%
可见光膜面色坐标a*=-2.2
可见光膜面色坐标b*=0.6
玻璃辐射率E=0.08
可通过调节各膜层厚度,得到客户满意的光学性能和颜色外观。
以上已以较佳实施例公开了本实用新型,然其并非用以限制本实用新型,凡采用等同替换或者等效变换方式所获得的技术方案,均落在本实用新型的保护范围之内。
Claims (1)
1.一种可异地加工的单银低辐射镀膜玻璃,包括基板玻璃和镀膜层,镀膜层包括以基板玻璃为基础层向外依次镀覆的第一电介质层、第一保护层、Ag层、第二保护层和第二电介质层,其中第一电介质层和第二电介质层的材料为Si3N4,其特征在于,所述的第一保护层的材料为AZO,而第二保护层的材料为ZrO。