CN201671630U - Double-metal structural pick - Google Patents
Double-metal structural pick Download PDFInfo
- Publication number
- CN201671630U CN201671630U CN2010200461378U CN201020046137U CN201671630U CN 201671630 U CN201671630 U CN 201671630U CN 2010200461378 U CN2010200461378 U CN 2010200461378U CN 201020046137 U CN201020046137 U CN 201020046137U CN 201671630 U CN201671630 U CN 201671630U
- Authority
- CN
- China
- Prior art keywords
- pick
- head
- alloy steel
- tooth head
- conical tooth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
A double-metal structural pick belongs to the technical field of metal material and geotechnical engineering research of mining machinery, and particularly relates to a pick which is applied for coal mining machines and heading machines. The double-metal structural pick is characterized in that a pick body is made of two metals, the top end of a pick head which is easily worn is made of purpose-made alloy steel, and a pick handle and the lower end of the pick head which are not easily worn are made of medium carbon alloy steel. The top end of the pick head is downwards provided with a plurality of annular grooves, a partition layer is arranged between each two adjacent annular grooves, the insides of the annular grooves are welded sufficiently by aid of purpose-made alloy steel welding strips, and as the partition layers are extremely thin, the top end of the pick head forms complete wear-resistant purpose-made alloy steel. The double-metal structural pick is simple in structure, novel in design, strong in practicality, convenient in manufacturing and fine in anti-corrosion property, and is hard, wear-resistant and anti-impact. Industrial tests prove that the service life of the double-metal structural pick is prolonged by 20-30 times compared with a national pick, thereby being capable of saving large quantities of alloy steel for nations, and reducing coal mining cost.
Description
Technical field
The pick of a kind of bimetal structure of the utility model belongs to mining machinery metal material and geotechnical study technical field, and being specifically related to a kind of be applied on coal-winning machine, the development machine can the cut coal seam and the pick of rock stratum.
Background technology
Coal industry production both at home and abroad, all extensive use coal-winning machine, development machine exploitation.The different size of installing on coal-winning machine, development machine, the pick of varying number are its indispensable spare and accessory parts easy to wear.The cylindrical portion of pick is divided into the tooth handle, and conical portion is divided into the tooth head, and tooth handle and tooth head are collectively referred to as denticle, and tooth crown end is welded with hard alloy head, and denticle and hard alloy head constitute a complete pick.Pick has very high requirement to the hardness of denticle, impact toughness, flexural strength, corrosion resistance etc., but the performance requirement to tooth handle and tooth head has tangible different, the tooth handle requires to have certain intensity and toughness, and tooth crown end requires to have high strength, high rigidity, high abrasion and corrosion resistance.Existing denticle extensively adopts single steel to make, this has just sacrificed high rigidity, high abrasion and the corrosion resistance of tooth crown end, thereby in mining work, cause very quick-wearing of tooth crown end, expose the hard alloy head welding portion, make hard alloy head lose parcel and rely on and be thrown out of, cause pick to be scrapped.As seen hard alloy head is the very important part of pick, have only the abrasion resistance and the impact resistance that improve tooth crown end, could guarantee that hard alloy head can not be worn and throws away because of tooth crown end, finally give full play to its maximum efficiency, then pick can reach maximum life.
The abrasion resistance and the representational way of impact resistance of present domestic raising tooth crown end mainly contain three kinds.First kind of way is: tooth crown end is welded with hard alloy head, tooth crown end adopts wear-resisting alloy steel, tooth handle and tooth head remainder adopt high strength alloy steel, wear-resisting alloy steel and high strength alloy steel are respectively after Overheating Treatment, link together by welding and seam, and then carry out lonneal.Pick the time bears very big impact force in work, and weld seam is connected with seam and is difficult to guarantee enough flexural strengths, can cause separating of tooth crown end and denticle remainder; The welding stress of junction can be eliminated though lonneal is handled, the flexural strength that weld seam is connected with seam can not be improved.Second kind of way is: tooth crown end is welded with hard alloy head; the tooth head surface utilizes the powder metallurgical technique roasting that hard alloy layer is arranged; though this layer has abrasion resistance preferably; but because pick is when work; radial force is big; can produce bigger flexural stress, tooth head and hard alloy layer strength difference cause it to come off greatly, make hard alloy head lose protection.The third way is: tooth crown end does not weld hard alloy head, but tooth crown end is made the pointed hard alloy head that replaces, and tooth handle and tooth head use commaterial to make one, at the wearing layer of 0.5～1 millimeter of tooth head surface covering and through Overheating Treatment.Though this layer has higher hardness can resist wearing and tearing, because tooth head and wearing layer exist aspect mechanical property than big-difference, the lining is soft outer hard, and wearing layer peels off because of impact resistance is not enough; Owing to there is not hard alloy head, tooth crown end is not enough to keep long application life only according to this thin wearing layer direct cut coal seam and rock stratum in addition.
As seen the purpose of above structure is that all the hardness and the abrasion resistance that improve pick tooth head part protect hard alloy head; but key issue be this enhancing part with former denticle metal material because the tangible interface of the bigger existence of performance difference; two kinds of different metal material do not have transitional region; really do not fuse into one in the junction with the denticle metal material; under strong impact, be easy to rupture or peel off; thereby cause hard alloy head to lose parcel and rely on and be thrown out of, final pick is scrapped.Therefore, rational pick structure of design science and preparation technology can guarantee that hard alloy head brings into play usefulness to greatest extent, have crucial meaning this application life for abundant raising pick.
Summary of the invention
The pick of a kind of bimetal structure of the utility model, purpose is to solve the problems of the technologies described above, a kind of long service life is provided, saves alloy steel products, reduces mining costs, economical and practical being applied on coal-winning machine, the development machine, the technical scheme of pick that constitutes by two kinds of metals and preparation method thereof.
The pick of a kind of bimetal structure of the utility model, it is characterized in that pick is made up of denticle and hard alloy head, denticle comprises cylin-drical tooth handle 2 and conical tooth head 4, denticle is made of two kinds of metals, cylin-drical tooth handle 2 and conical tooth head 4 lower ends are medium carbon alloy steel, conical tooth head 4 tops are special alloy steel, be drilled with axial circular hole on conical tooth head 4 tops, hard alloy head 9 is put into axial circular hole and is welded together by copper weld layer 17 and conical tooth head 4,3 diameter is greater than the diameter of cylin-drical tooth handle 2 at the bottom of the conical tooth head, secondly offer cannelure from top to bottom along the taper seat of its conical tooth head 4, the width of cannelure is 7～9 millimeters, conical tooth head 4 tops first cannelure D8 degree of depth downwards are 5.5～6.0 millimeters, all the other cannelure degree of depth are deepened to 8～9 millimeters with conical increase of tooth head, between adjacent two cannelures 1.5～2.0 millimeters interlayer is arranged, that 3 distances are minimum at the bottom of the conical tooth head of distance is cannelure A5, its distance is not more than 1/2nd of conical tooth head 4 length, is 8～12 millimeters apart from the distance of hard alloy head 9 bottom surfaces.
The pick of above-mentioned a kind of bimetal structure is characterized in that described special alloy steel tightly surrounds the welding portion of hard alloy head 9, and the scope of special alloy steel is greater than the welding portion of hard alloy head 9, and extends 8～12 millimeters to hard alloy head 9 bottom surfaces.
The pick of above-mentioned a kind of bimetal structure is characterized in that described special alloy steel is air quenching steel HRC55～60, and its chemical analysis percentage by weight is, C:0.46～0.58, Cr:4.0～6.0, W:6.0～11.0, Mo:2.3～3.0, V:0.6～1.3, Si:0.18～0.20, Mn:0.17～0.19, Ni:0.50～0.60, S:0.030～0.035, P:0.028～0.030.
The preparation method of the pick of above-mentioned a kind of bimetal structure is characterized in that: the concrete steps of this method are:
I, press deposited metal chemical analysis percentage by weight C:0.46～0.58, Cr:4.0～6.0, W:6.0～11.0, Mo:2.3～3.0, V:0.6～1.3, Si:0.18～0.20, Mn:0.17～0.19, Ni:0.50～0.60, S:0.030～0.035, P:0.028～0.030 made special alloy steel welding rod, 240～260 ℃ of oven dry 2.0～2.5 hours;
It is the pick denticle that cylin-drical tooth handle 2 and conical tooth head 4 constitute that II, employing medium carbon alloy steel are machined to structure;
III, some cannelures are driven on conical tooth head 4 tops of the denticle that obtains at above-mentioned II downwards, be generally 3～5 cannelures, the clear span of cannelure is 7～9 millimeters, interlayer between the two adjacent cannelures is 1.5～2.0 millimeters, conical tooth head 4 tops first cannelure degree of depth downwards are 5.5～6.0 millimeters, all the other annular groove depths are deepened to 8～9 millimeters with conical increase of tooth head, the scope of offering cannelure is greater than 8～12 millimeters of the bottom surfaces of hard alloy head 9, conical tooth head 4 tops downwards last cannelure A 5 distance of 3 at the bottom of the conical tooth head be not more than conical tooth head 4 long 1/2nd;
IV, with denticle preheating 1.0～1.5 hours in 350～400 ℃ of temperature, use the full cannelure of the special alloy steel welding rod of above-mentioned I built-up welding then, because interlayer is very thin, tooth crown end forms complete above-mentioned special alloy steel, and special alloy steel and medium carbon alloy steel have constituted the matrix of bimetal structure pick jointly;
The denticle of V, bimetal structure that above-mentioned IV is obtained was with 140～160 ℃ of destressing tempering 2.0～2.5 hours;
The denticle of VI, the bimetal structure that above-mentioned V obtained according to conventional method grinds fine finishining;
An axial circular hole is bored on conical tooth head 4 tops of the denticle of VII, the bimetal structure that obtains at above-mentioned VI, brazing sheet and solder flux are put into circular hole, then conical tooth head 4 tops and hard alloy head 9 are placed and be heated to 950～1050 ℃ in the superaudio induction coil, hard alloy head promptly welds together by copper weld layer and conical tooth head 4.
The pick of a kind of bimetal structure of the utility model, its advantage is:
1. the utility model modern design, utilize the built-up welding of special alloy steel welding rod to form special alloy steel by offering cannelure, because the high temperature that produces during built-up welding has formed the Mixed Zone changeover portion of two kinds of steel at the binding site of special alloy steel and medium carbon alloy steel, although be two kinds of different alloy steels of hardness but do not have tangible interface, the chemical analysis of changeover portion does not have bimetallic obvious like that, but between two kinds of steel, performance is also between two kinds of steel, has good hardness and toughness, organically fuse as a whole, satisfy the bond strength of special alloy steel and medium carbon alloy steel, after the destressing temper, greatly improved the abrasion resistance and the impact resistance of tooth crown end.
2. the utility model is rational in infrastructure, the scope of special alloy steel is greater than the welding portion of hard alloy head, the axial circular hole and the special alloy steel of welding hard alloy head join, special alloy steel welds together securely by copper weld layer and hard alloy head, special alloy steel is from axially still radially all closely wrapping up hard alloy head, so just guarantee that by the abrasion resistance that improves the tooth crown end hard alloy head gives full play to task performance, can hard alloy head be thrown out of, greatly improve the application life of pick because of the too early wearing and tearing of tooth crown end.
3. the utility model is practical, and special alloy steel is because its special chemical analysis makes it have the ability of dielectric corrosions such as antiacid preferably, alkali, salt.
4. commerical test proves, the bimetal structure pick has good intensity, abrasion resistance and corrosion resistance, is applicable to the driving and the exploitation of various coal seams and medium ground, and improved 20～30 times than homemade pick application life, approaching with the import pick, can save a large amount of alloy steel products for country.
5. owing to the prolongation in application life, reduced the time of maintenance and replacing number of times greatly, thereby improved 15～20 times coal mining efficient.
The raising of the efficient of 6. mining has reduced working strength of workers and labour hour, has reduced mining costs.
Description of drawings
Fig. 1 is the outline drawing of pick of the present invention
Fig. 2 is a pick sectional view of the present invention
Among the above-mentioned figure:
1---at the bottom of the conical tooth head of elastic collar 2---cylin-drical tooth handle 3---
4---conical tooth head 5---cannelure A 6---cannelure B
7---cannelure C 8---cannelure D 9---hard alloy heads
10---interlayer i 11---interlayer ii 12---interlayer iii
13---the special alloy steel III of special alloy steel I 14---special alloy steel II 15---
16---special alloy steel IV 17---copper weld layer
The specific embodiment
Describe the specific embodiment of this pick in detail below in conjunction with embodiment and accompanying drawing thereof, but the specific embodiment of this pick is not limited to following embodiment.What Fig. 1 and Fig. 2 described is the bimetal structure pick, realizes by following concrete steps:
Embodiment one:
I, press deposited metal chemical analysis percentage by weight C:0.46, Cr:4.0, W:6.0, Mo:2.3, V:0.6, Si:0.18, Mn:0.17, Ni:0.50, S:0.030, P:0.028 made special alloy steel welding rod, 240 ℃ of oven dry 2.5 hours;
It is the denticle that cylin-drical tooth handle 2 and conical tooth head 4 constitute that II, employing medium carbon alloy steel are machined to structure;
3 cannelures are driven on conical tooth head 4 tops of III, the denticle that obtains at above-mentioned II downwards, the clear span of cannelure is 7 millimeters, interlayer between the two adjacent cannelures is 1.5 millimeters, conical tooth head 4 tops first cannelure degree of depth downwards are 5.5 millimeters, all the other annular groove depths are deepened to 8 millimeters with conical increase of tooth head, the scope of offering cannelure is greater than 8 millimeters of the bottom surfaces of hard alloy head 9, conical tooth head 4 tops downwards last cannelure A 5 distance of 3 at the bottom of the conical tooth head be not more than conical tooth head 4 long 1/2nd;
IV, denticle that above-mentioned III is obtained preheating 1.5 hours in 350 ℃ of temperature, use the full cannelure of the special alloy steel welding rod of above-mentioned I built-up welding then, because interlayer is very thin, tooth crown end forms complete above-mentioned special alloy steel, and special alloy steel and medium carbon alloy steel have constituted the denticle of bimetal structure pick jointly;
V, bimetal structure denticle that above-mentioned IV is obtained were with 140 ℃ of destressing tempering 2.5 hours;
VI, the bimetal structure denticle that above-mentioned V obtains is ground fine finishining according to conventional method;
An axial circular hole is bored on conical tooth head 4 tops of VII, the bimetal structure denticle that obtains at above-mentioned VI, brazing sheet and solder flux are put into circular hole, then conical tooth head 4 tops and hard alloy head 9 are placed and be heated to 950 ℃ in the superaudio induction coil, hard alloy head 9 promptly welds together by copper weld layer 17 and conical tooth head 4.
Embodiment two:
I, press deposited metal chemical analysis percentage by weight C:0.52, Cr:5.0, W:8.5, Mo:2.65, V:0.95, Si:0.19, Mn:0.18, Ni:0.55, S:0.0325, P:0.029 made special alloy steel welding rod, 250 ℃ of oven dry 2.25 hours;
It is the denticle that cylin-drical tooth handle 2 and conical tooth head 4 constitute that II adopts medium carbon alloy steel to be machined to structure;
4 cannelures are driven on conical tooth head 4 tops of III, the denticle that obtains at above-mentioned II downwards, the clear span of cannelure is 8 millimeters, interlayer between the two adjacent cannelures is 1.75 millimeters, conical tooth head 4 tops first cannelure degree of depth downwards are 5.75 millimeters, all the other annular groove depths are deepened to 8.5 millimeters with conical increase of tooth head, the scope of offering cannelure is greater than 10 millimeters of the bottom surfaces of hard alloy head 9, conical tooth head 4 tops downwards last cannelure A 5 distance of 3 at the bottom of the conical tooth head be not more than conical tooth head 4 long 1/2nd;
IV, denticle that above-mentioned III is obtained preheating 1.25 hours in 375 ℃ of temperature, use the full cannelure of the special alloy steel welding rod of above-mentioned I built-up welding then, because interlayer is very thin, tooth crown end forms complete above-mentioned special alloy steel, and special alloy steel and medium carbon alloy steel have constituted the denticle of bimetal structure pick jointly;
V, bimetal structure denticle that above-mentioned IV is obtained were with 150 ℃ of destressing tempering 2.25 hours;
VI, the bimetal structure denticle that above-mentioned V obtains is ground fine finishining according to conventional method;
An axial circular hole is bored on conical tooth head 4 tops of VII, the bimetal structure denticle that obtains at above-mentioned VI, brazing sheet and solder flux are put into circular hole, then conical tooth head 4 tops and hard alloy head 9 are placed and be heated to 1000 ℃ in the superaudio induction coil, hard alloy head 9 promptly welds together by copper weld layer 17 and conical tooth head 4.
Embodiment three:
I, press deposited metal chemical analysis percentage by weight C:0.58, Cr:6.0, W:11.0, Mo:3.0, V:1.3, Si:0.20, Mn:0.19, Ni:0.60, S:0.035, P:0.030 made special alloy steel welding rod, 260 ℃ of oven dry 2.0 hours;
It is the denticle that cylin-drical tooth handle 2 and conical tooth head 4 constitute that II, employing medium carbon alloy steel are machined to structure;
5 cannelures are driven on conical tooth head 4 tops of III, the denticle that obtains at above-mentioned II downwards, the clear span of cannelure is 9 millimeters, interlayer between the two adjacent cannelures is 2.0 millimeters, conical tooth head 4 tops first cannelure degree of depth downwards are 6.0 millimeters, all the other annular groove depths are deepened to 9 millimeters with conical increase of tooth head, the scope of offering cannelure is greater than 12 millimeters of the bottom surfaces of hard alloy head 9, conical tooth head 4 tops downwards last cannelure A 5 distance of 3 at the bottom of the conical tooth head be not more than conical tooth head 4 long 1/2nd;
IV, denticle that above-mentioned III is obtained preheating 1.0 hours in 400 ℃ of temperature, use the full cannelure of the special alloy steel welding rod of above-mentioned I built-up welding then, because interlayer is very thin, tooth crown end forms complete above-mentioned special alloy steel, and special alloy steel and medium carbon alloy steel have constituted the denticle of bimetal structure pick jointly;
V, bimetal structure denticle that above-mentioned IV is obtained were with 160 ℃ of destressing tempering 2.0 hours;
VI, the bimetal structure denticle that above-mentioned V obtains is ground fine finishining according to conventional method;
An axial circular hole is bored on conical tooth head 4 tops of VII, the bimetal structure denticle that obtains at above-mentioned VI, brazing sheet and solder flux are put into circular hole, then conical tooth head 4 tops and hard alloy head 9 are placed and be heated to 1050 ℃ in the superaudio induction coil, hard alloy head 9 promptly welds together by copper weld layer 17 and conical tooth head 4.
The diameter of above embodiment tooth handle 2 is 35 millimeters, and the length of tooth handle 2 is 94 millimeters, and 3 diameter is 55 millimeters at the bottom of the tooth head, and 31 millimeters of the top end diameter of tooth head 4, the length of tooth head 4 are 90 millimeters, and the diameter of hard alloy head 9 is 18 millimeters.
Claims (2)
1. the pick of a bimetal structure, it is characterized in that pick is made up of denticle and hard alloy head, denticle comprises cylin-drical tooth handle (2) and conical tooth head (4), denticle is made of two kinds of metals, cylin-drical tooth handle (2) and conical tooth head (4) lower end are medium carbon alloy steel, conical tooth head (4) top is special alloy steel, be drilled with axial circular hole on conical tooth head (4) top, hard alloy head (9) is put into axial circular hole and is welded together by copper weld layer (17) and conical tooth head (4), the diameter of (3) is greater than the diameter of cylin-drical tooth handle (2) at the bottom of the conical tooth head, secondly offer cannelure from top to bottom along the taper seat of its conical tooth head (4), the width of cannelure is 7～9 millimeters, conical tooth head (4) top first cannelure D (8) degree of depth downwards is 5.5～6.0 millimeters, all the other cannelure degree of depth are deepened to 8～9 millimeters with conical increase of tooth head, between adjacent two cannelures 1.5～2.0 millimeters interlayer is arranged, what (3) distance was minimum at the bottom of the conical tooth head of distance is cannelure A (5), its distance is not more than 1/2nd of conical tooth head (4) length, is 8～12 millimeters apart from the distance of hard alloy head (9) bottom surface.
2. according to the pick of the described a kind of bimetal structure of claim 1, it is characterized in that described special alloy steel tightly surrounds the welding portion of hard alloy head (9), the scope of special alloy steel is greater than the welding portion of hard alloy head (9), and extends 8～12 millimeters to hard alloy head (9) bottom surface.