CN201507034U - Heat preservation system in heat preservation plate outer wall - Google Patents
Heat preservation system in heat preservation plate outer wall Download PDFInfo
- Publication number
- CN201507034U CN201507034U CN 200920048239 CN200920048239U CN201507034U CN 201507034 U CN201507034 U CN 201507034U CN 200920048239 CN200920048239 CN 200920048239 CN 200920048239 U CN200920048239 U CN 200920048239U CN 201507034 U CN201507034 U CN 201507034U
- Authority
- CN
- China
- Prior art keywords
- heat preservation
- wall
- bottom layer
- plate
- thermal insulation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model relates to a heat preservation system in a heat preservation plate outer wall, which includes adhesive mortar applied on a substrate wall body, a heat preservation plate adhered onto the adhesive mortar, a bottom layer gypsum plaster applied onto the heat preservation plate, a fiberglass mesh fabric embedded in the bottom layer gypsum plaster, a surface layer applied on the bottom layer gypsum plaster, and a finishing coat applied on the surface layer, wherein two side surfaces of the heat preservation plate are printed with surfactant. Through treating the surfaces of a phenolic aldehyde foaming plate, that is applying the surfactant, the bonding performance of the phenolic aldehyde foaming plate with matched materials are enhanced; and the utility model has low cost, convenient construction and stable performance, thereby ensuring the safety and the economy of the inner heat preservation structure of the phenolic aldehyde plate outer wall.
Description
Technical field
The utility model relates to building engineering field, relates in particular to a kind of internal thermal insulation system of thermal insulation board exposed wall.
Background technology
Phenol formaldehyde foam is insulation of new generation, fire prevention, sound insulation materials; have the mechanical strength height, dimensional stability is good, Applicable temperature is wide (60～150 ℃), ageing resistance is good; do not contain freon and help environmental protection; particularly under 1000 ℃ of high temperature, do not burn, do not melt, do not shrink, no poison gas, no dense smoke, do not have drippage, be other heat insulating materials can not compare.The phenolic board internal insulation structure for exterior wall generally is made up of tack coat, insulation layer, the overcoat of plastering, finish coat, if wherein the phenolic board surface is not carried out interface processing or is only carried out texturing and handle, can cause phenolic board and supplementary material adhesive property relatively poor, be prone to come off, quality problems such as hollowing, even also there are shortcomings such as cost is too high, rate of drying slow, contraction is big in bonding, coating material that preparation is special-purpose.
The utility model content
The technical problems to be solved in the utility model is: provide a kind of adhesive property good, cost is low, easy construction, the warming plate exterior wall heat-preserving system of stable performance.
In order to overcome the defective that exists in the background technology, the technical scheme that its technical problem that solves the utility model adopts is: a kind of internal thermal insulation system of thermal insulation board exposed wall, comprise the adhesive mortar that is coated on basic unit's body of wall, be attached on the warming plate on the adhesive mortar, be applied in the bottom layer brushing gypsum of warming plate, be embedded in the glass fiber reticular cloth on bottom layer brushing gypsum top layer, be painted on the surface layer brushing gypsum on the bottom layer brushing gypsum, be painted on the finish coat of surface layer brushing gypsum, the brushing of wherein said warming plate both side surface has interfacial agents.
According to another embodiment of the present utility model, internal thermal insulation system of thermal insulation board exposed wall comprises that further described warming plate is the phenolic aldehyde heat preserving plate.
The utility model has solved the defective that exists in the background technology, by the interfacial agents of promptly constructing is handled on the phenolic foam board surface, strengthened the adhesive property of phenolic foam board and supplementary material, and the utility model cost is low, easy construction, stable performance, thus the safety of phenolic board internal insulation structure for exterior wall, economy guaranteed.
Description of drawings
Below in conjunction with drawings and Examples the utility model is further specified.
Fig. 1 is the structural representation of the preferred embodiments of the present invention;
Among the figure: 1, basic unit's body of wall, 2, adhesive mortar, 3, warming plate, 4, bottom layer brushing gypsum, 5, glass fiber reticular cloth, 6, the surface layer brushing gypsum, 7, finish coat, 8, interfacial agents.
The specific embodiment
With preferred embodiment the utility model is described in further detail in conjunction with the accompanying drawings now.These accompanying drawings are the schematic diagram of simplification, basic structure of the present utility model only is described in a schematic way, so it only show the formation relevant with the utility model.
As shown in Figure 1, a kind of internal thermal insulation system of thermal insulation board exposed wall of the present invention, comprise the adhesive mortar 2 that is coated on basic unit's body of wall 1, be attached on the warming plate 3 on the adhesive mortar 2, smear bottom layer brushing gypsum 4 at warming plate 3, be embedded in the glass fiber reticular cloth 5 on bottom layer brushing gypsum 4 top layers, be painted on the surface layer brushing gypsum 6 on the bottom layer brushing gypsum 4, be painted on the finish coat 7 of surface layer brushing gypsum 6, wherein said warming plate 3 both side surface brushings have interfacial agents 8.Wherein, the thickness of bottom layer brushing gypsum 4 is preferably 6mm, and the thickness of surface layer brushing gypsum 6 is preferably 2mm, in addition the warming plate 3 preferred phenolic aldehyde heat preserving plates that adopt.
Wherein, internal thermal insulation system of thermal insulation board exposed wall interfacial agents 8, it is mixed and made into by emulsion, coalescents, dispersing agent, defoamer, mould inhibitor, mould inhibitor, thickener, pH value conditioning agent and filler, and each raw material component by weight is: emulsion 20-40 part, coalescents 0-1 part, dispersing agent 0.05-0.15 part, defoamer 0.3-1 part, mould inhibitor 0.5-1.0 part, thickener 0.1-0.3 part, pH value conditioning agent 0-0.5 part, filler 30-50 part, water 20-30 part.
Emulsion is benzene emulsion, pure-acrylic emulsion or VAE emulsion.
Coalescents is ethylene glycol or propane diols.
Dispersing agent is poly carboxylic acid series water reducer or melamine based water reducer.
Defoamer is phosphoric acid ester defoamer, mineral oil defoaming agent or silicone based defoamer.
Thickener is hydroxyethylcellulose, methylcellulose or association thickener.
Filler is calcite powder, French chalk or wollastonite in powder.
And internal thermal insulation system of thermal insulation board exposed wall is as follows with the preparation method of interfacial agents 8:
In container, successively thickener 0.1-0.3 part, pH value conditioning agent 0-0.5 part, defoamer 0.2-0.6 part, mould inhibitor 0.5-1.0 part, dispersing agent 0.05-0.15 part, filler are added in the water of 20-30 part by weight with (400-500) rev/min mixing speed, after leaving standstill 5-10 minute, add defoamer 0.1-0.4 part again, emulsion 20-40 part stirs with (150-250) rev/min mixing speed, promptly makes internal thermal insulation system of thermal insulation board exposed wall with interfacial agents 8.
In addition, the work progress of internal thermal insulation system of thermal insulation board exposed wall is as follows:
(1) on basic unit's body of wall 1, applies adhesive mortar 2;
(2) the both side surface brushing there is the phenolic aldehyde heat preserving plate 3 of interfacial agents 8 be affixed on the adhesive mortar 2;
(3) smear bottom layer brushing gypsum 4 in the outside of phenolic aldehyde heat preserving plate 3, bottom layer brushing gypsum 4 thickness are 6mm;
(4) embedded glass fiber reticular cloth 5;
(5) be coated with float coat brushing gypsum 6, thickness is 2mm;
(6) further, after the dry tack free, brushing finish coat 7 on surface layer brushing gypsum 6.
Test by experiment, data are as follows:
By the interfacial agents of promptly constructing is handled on the phenolic foam board surface, strengthened the adhesive property of phenolic foam board and supplementary material, and cost of the present invention is low, easy construction, stable performance, thus guaranteed the safety of phenolic board internal insulation structure for exterior wall, economy.
With above-mentioned foundation desirable embodiment of the present utility model is enlightenment, and by above-mentioned description, the related work personnel can carry out various change and modification fully in the scope that does not depart from this utility model technological thought.The technical scope of this utility model is not limited to the content on the manual, must determine its technical scope according to the claim scope.
Claims (2)
1. internal thermal insulation system of thermal insulation board exposed wall, it is characterized in that: comprise the adhesive mortar that is coated on basic unit's body of wall, be attached on the warming plate on the adhesive mortar, be applied in the bottom layer brushing gypsum of warming plate, be embedded in the glass fiber reticular cloth on bottom layer brushing gypsum top layer, be painted on the surface layer brushing gypsum on the bottom layer brushing gypsum, be painted on the finish coat of surface layer brushing gypsum, the brushing of wherein said warming plate both side surface has interfacial agents.
2. internal thermal insulation system of thermal insulation board exposed wall as claimed in claim 1 is characterized in that: described warming plate is the phenolic aldehyde heat preserving plate.