CN201112340Y - Lamp tube - Google Patents
Lamp tube Download PDFInfo
- Publication number
- CN201112340Y CN201112340Y CNU2007200075249U CN200720007524U CN201112340Y CN 201112340 Y CN201112340 Y CN 201112340Y CN U2007200075249 U CNU2007200075249 U CN U2007200075249U CN 200720007524 U CN200720007524 U CN 200720007524U CN 201112340 Y CN201112340 Y CN 201112340Y
- Authority
- CN
- China
- Prior art keywords
- fluorescent tube
- exposed conduit
- silver
- layer
- titanium dioxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model discloses a lighting tube which comprises an exposed conduit. The outside of the exposed conduit is compounded with a layer of titanium dioxide film and a layer of silver film, or the outside of the exposed conduit is compounded with a film layer that is formed by mixing titanium dioxide and silver. The lighting tube has the advantages that: when nano Ag-antibacterial material and nano TiO2 photocatalyst are organically combined, under the excitation of a light source or natural light, the continuous and long-term effective performances of disinfection, sterilization and decomposition of organic pollutants can be provided, with the effectiveness higher than a TiO2 photocatalyst lighting tube (the activity of degradation formaldehyde is improved by 5-30 percent in an intermittent photocatalysis evaluation system).
Description
Technical field
The utility model relates to a kind of fluorescent tube.
Background technology
A kind of fluorescent tube in the existing known technology, it comprises an exposed conduit, this exposed conduit is compounded with the layer of titanium dioxide rete outward.Be the patent of invention of " uviol lamp that is used for air cleaner " as the denomination of invention of announcing on June 8th, 2002 in the United States Patent (USP) database, its patent No. is 6,336,998.This uviol lamp exposed conduit outer wrapping the glass fabric that dip-coating has titanium oxide film layer, excite down at ultraviolet source or natural daylight, though a kind of ability with disinfection and decomposing organic pollutant can be provided, but the ultraviolet ray of its emission has side effect to human body, and continuous, long-term air-cleaning function can not be provided; And the denomination of invention in China's patent database is " a photocatalyst of titanium dioxide light source ", and its patent No. is 03259494,1.This luminous element outer surface spraying layer of titanium dioxide coating, its thickness is 0.1~5mm, and does not have curing process, must cause coating adhesion poor, the deficiency of disinfection and decomposing organic matter pollutant power inefficiency.
The utility model content
The utility model provides a kind of fluorescent tube, and it has overcome the existing disinfection of existing fluorescent tube and the power inefficiency of decomposing organic pollutant and the deficiency of using described in the background technology.
The technical scheme that its technical problem that solves the utility model adopts is: a kind of fluorescent tube, and it comprises an exposed conduit, described exposed conduit is compounded with layer of titanium dioxide rete and one deck silver film outward.
In one preferred embodiment of present technique originating party case, described titanium oxide film layer is the nano titanium dioxide film layer, and described silver film is the Nano Silver rete.
In one preferred embodiment of present technique originating party case, described titanium oxide film layer is compound in outside the exposed conduit, and described silver film is compound in outside the titanium oxide film layer.
In one preferred embodiment of present technique originating party case, described silver film is compound in outside the exposed conduit, and described titanium oxide film layer is compound in outside the silver film.
In one preferred embodiment of present technique originating party case, described titanium dioxide film layer thickness is 100~400nm.
In one preferred embodiment of present technique originating party case, described silver film thickness is 20~150nm.
The technical scheme that its technical problem that solves the utility model adopts is: a kind of fluorescent tube, and it comprises an exposed conduit, described exposed conduit is compounded with the rete that one deck is mixed with silver by titanium dioxide outward.
In one preferred embodiment of present technique originating party case, described thicknesses of layers is 100~500nm.
The beneficial effect of the technical program is: with nanometer Ag anti-biotic material and nano-TiO
2Photocatalyst organically combines, and excites down at light source or natural daylight, can provide a kind of continuous, permanently effective,, compare TiO
2The photocatalyst lamp pipe has the ability (in step light-catalyzed reaction appraisement system, the activity of degradation of formaldehyde has improved 5~30%) of disinfection and decomposing organic pollutant more efficiently.
Description of drawings
Below in conjunction with drawings and Examples the utility model is further specified.
Fig. 1 has illustrated the partial cutaway schematic of the fluorescent tube of present embodiment one.
Fig. 2 has illustrated the partial cutaway schematic of the fluorescent tube of present embodiment two.
Label declaration: 10 exposed conduits, 20 titanium oxide film layer, 30 silver films, 40 mixed membranous layers.
Embodiment
Embodiment one
Please refer to Fig. 1, Fig. 1 has illustrated the partial cutaway schematic of the fluorescent tube of present embodiment one.The multi-functional fluorescent tube of a kind of photocatalysis automatically cleaning (as ultraviolet lamp tube), it comprises an exposed conduit 10, the described exposed conduit 10 outer pure nano titanium dioxide film layer 20 of one deck and one deck simple-substance nano silvery retes 30 of being compounded with.Titanium oxide film layer 20 is compound in outside the exposed conduit 10, and its thickness is about 100,200,300 or 400nm; Silver film 30 is compound in outside the titanium oxide film layer 20, and its thickness is about 20,50,100 or 150nm.
The preparation technology of fluorescent tube: earlier exposed conduit 10 outer surfaces are cleaned; Then adopt high pressure airless spraying apparatus, plate a layer thickness and be about 100,200,300 or the pure nano titanium dioxide film layer 20 of 400nm; After spray-dried; Then plate a layer thickness again and be about 20,50,100 or the simple-substance nano silvery rete 30 of 150nm; After ultraviolet ray or infra-red heat curing, can form Ag-TiO then
2Composite film, curing temperature are 50~250 ℃.Nanometer Ag anti-biotic material and nano-TiO
2The organic combination of photocatalyst excites down at light source or natural daylight, provide a kind of continuous, permanently effective, compare TiO
2The photocatalyst lamp pipe has the ability (in step light-catalyzed reaction appraisement system, the activity of degradation of formaldehyde has improved 5~30%) of disinfection and decomposing organic pollutant more efficiently.Wherein, titanium oxide film layer 20 is that spray-dried again back formed after pure nano titanic oxide sol plated, and this pure nano titanic oxide sol comprises nano-TiO
2And water, TiO
2Weight content is 1~20wt%, and grain size is 6~10nm, and all the other are water.
Embodiment two
Please refer to Fig. 2, Fig. 2 has illustrated the partial cutaway schematic of the fluorescent tube of present embodiment two.The multi-functional fluorescent tube of a kind of photocatalysis automatically cleaning (as ultraviolet lamp tube), it comprises an exposed conduit 10, described exposed conduit 10 outer one decks that are compounded with are by titanium dioxide and the silver-colored mixed membranous layer 40 that mixes.Mixed membranous layer 40 thickness are about 100,200,300,400 or 500nm.
The preparation technology of fluorescent tube: earlier exposed conduit 10 outer surfaces are cleaned; Then adopt high pressure airless spraying apparatus, plate a layer thickness be about 100,200,300,400 or 500nm by titanium dioxide and the mixed membranous layer 40 that mixes of silver; After spray-dried; Solidify to form Ag-TiO through ultraviolet ray or infra-red heat then
2Composite film, curing temperature are 50~250 ℃.Nanometer Ag anti-biotic material and nano-TiO
2The organic combination of photocatalyst excites down at light source or natural daylight, provide a kind of continuous, permanently effective, compare TiO
2The photocatalyst lamp pipe has the ability (in step light-catalyzed reaction appraisement system, the activity of degradation of formaldehyde has improved 5~30%) of disinfection and decomposing organic pollutant more efficiently.Wherein, mixed membranous layer 40 comprise TiO 2 sol and in the colloidal sol adding weight content be 0.05~5% AgNO
3, fully behind the mixing, be plated on exposed conduit 10 outer surfaces.This pure nano titanic oxide sol comprises nano-TiO
2And water, TiO
2Weight content is 1~20wt%, and grain size is 6~10nm, and all the other are water.
Embodiment three
Present embodiment and embodiment two differences are: mixed membranous layer 40 comprise TiO 2 sol and in the colloidal sol adding molar concentration be 10
-6~10
-1The nano silver colloidal sol of mol/L is mixed with nanometer Ag-TiO
2Complex sol plates nanometer Ag-TiO through airless spraying and spray drying equably at the fluorescent tube outer surface
2Laminated film; Then through ultraviolet ray or hot curing Ag-TiO
2Composite film.
The above, it only is the utility model preferred embodiment, so can not limit the scope that the utility model is implemented with this, i.e. the equivalence of doing according to the utility model claim and description changes and modifies, and all should still belong in the scope that the utility model patent contains.
Claims (8)
1. fluorescent tube, it comprises an exposed conduit, it is characterized in that: described exposed conduit is compounded with layer of titanium dioxide rete and one deck silver film outward.
2. a kind of fluorescent tube according to claim 1 is characterized in that: described titanium oxide film layer is the nano titanium dioxide film layer, and described silver film is the Nano Silver rete.
3. a kind of fluorescent tube according to claim 1 and 2 is characterized in that: described titanium oxide film layer is compound in outside the exposed conduit, and described silver film is compound in outside the titanium oxide film layer.
4. a kind of fluorescent tube according to claim 1 and 2 is characterized in that: described silver film is compound in outside the exposed conduit, and described titanium oxide film layer is compound in outside the silver film.
5. a kind of fluorescent tube according to claim 1 and 2 is characterized in that: described titanium dioxide film layer thickness is 100~400nm.
6. a kind of fluorescent tube according to claim 1 and 2 is characterized in that: described silver film thickness is 20nm~150nm.
7. fluorescent tube, it comprises an exposed conduit, it is characterized in that: described exposed conduit is compounded with the rete that one deck is mixed by titanium dioxide and silver outward.
8. a kind of fluorescent tube according to claim 7 is characterized in that: described thicknesses of layers is 100~500nm.