CN201031490Y - Decoration flooring - Google Patents
Decoration flooring Download PDFInfo
- Publication number
- CN201031490Y CN201031490Y CNU2006201566972U CN200620156697U CN201031490Y CN 201031490 Y CN201031490 Y CN 201031490Y CN U2006201566972 U CNU2006201566972 U CN U2006201566972U CN 200620156697 U CN200620156697 U CN 200620156697U CN 201031490 Y CN201031490 Y CN 201031490Y
- Authority
- CN
- China
- Prior art keywords
- finishing
- levelling
- middle level
- moulding
- utility
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The utility model discloses a flooring for decoration, which consists of a leveling bottom layer, a modeling middle layer and a wear-resistant transparent layer. The material has the advantages of safety and environmental protection, no seam exists, variable models, easy renewing and quick construction.
Description
Technical field
The utility model relates to a kind of novel finishing material, and is relevant with the structure of ground surface material for finishing.
Background technology
The house ornamentation earth material is many based on ceramic tile, stone material, wood flooring now.The power consumption height was gapped because of splicing during finishing when ceramic tile was produced, and as shown in Figure 1, needed to mend the ditch seam afterwards; The stone decoration material is (see figure 2) except that the splicing problem is arranged equally, and the unhealthful anxiety of radioactive radon gas is still arranged; Wood flooring need be cut down the woods, sprays possibility remaining waste gas (toluene, dimethylbenzene) through solvent based coating in the making, and fits up many pieces, as shown in Figure 3.In addition, above-mentioned material all can only be made variation in moulding in limited range, lacks individuality, and during the renovation of in the future old back, because the original ground material is thick, must be earlier with the old finishing again of rooting out again, otherwise directly the finishing back influences floor height on former basis, so the renovation construction is difficult for.In a word, all there is a little deficiency in above-mentioned house ornamentation earth material, remains really to be reformed.
The utility model content
The purpose of this utility model is to provide a kind of ground surface material for finishing, and it has safety and environmental protection, no seam, moulding ten thousand changes, renovation is easy and the advantage fast of constructing.
To achieve these goals, solution of the present utility model is:
Ground surface material for finishing is made up of levelling bottom, moulding middle level and wear-resisting transparent surface layer.
Wherein, described levelling bottom is formed by the height self-leveling mortar that flows, and the high self-leveling mortar that flows is modulated by following substances in percentage by weight and formed: portland cement 52.5R 20-25%, high alumina cement 5-10%, incremental dose of 1-2%, calcium carbonate (50-100 micron) 15-25%, silica sand (0.1-0.5 millimeter) 30-50%, early strength admixture 0.5-1%, retarding agent 0.5-1%, quicklime 1-3%, dispersed latex powder 2-4%, water-loss reducer 0.5-1%, defoamer 0.5-1% again.
Described incremental dose is high sclerosis melamine.
Described early strength admixture is calcium acetate.
Described water-loss reducer is a cellulose ether.
Described retarding agent is a disodium citrate.
The thickness of described levelling bottom is the 3-10 millimeter.
Described moulding middle level is water soluble acrylic acid or water-base epoxy colored paint.
Described wear-resisting transparent surface layer is mixed by solvent-free epoxy resin and the curing compound percentage by weight by 2: 1, and wherein solvent-free epoxy resin is formulated by 83.33%828 epoxy resin, 12.5% reactive diluent, 0.25% defoamer, 0.5% levelling agent, 3.42% visbreaking agent.
Described curing compound is alicyclic.
After adopting said structure, the utility model is made up of three layer construction, and this three layer construction all can be selected environment-friendly materials for use, formaldehydeless, toluene, dimethylbenzene, no radon gas, so, the product safety environmental protection, and thickness can make thinner.During finishing, but wear-resisting transparent surface layer full wafer be formed on the moulding middle level, do not have seam, convenient, fast construction.Various patterns, decorative pattern and color can need be made according to design in the moulding middle level, and moulding ten thousand becomes more personalized.During as if the renovation of old back, can old layer not rooted out, and on old layer basis, directly fit up, also little to the influence of floor height, so the renovation finishing is quicker.
Description of drawings
Fig. 1 is the structural representation with ceramic tile finishing ground;
Fig. 2 is the structural representation with stone material finishing ground;
Fig. 3 is the structural representation with wood flooring finishing ground;
Fig. 4 is the structural representation with the utility model finishing ground;
Fig. 5 is the structural representation with the utility model renovation ground.
The specific embodiment
As shown in Figure 4, the ground surface material for finishing that the utility model discloses is made up of levelling bottom 1, moulding middle level 2 and wear-resisting transparent surface layer 3.
Wherein, levelling bottom 1 can be formed by the mobile self-leveling mortar of height, and dispersed latex powder, 0.5-1% water-loss reducer, 0.5-1% defoamer (percentage by weight) modulation form the high self-leveling mortar that flows again by 20-25% portland cement 52.5R, 5-10% high alumina cement, incremental dose of 1-2%, 15-25% calcium carbonate (50-100 micron), 30-50% silica sand (0.1-0.5 millimeter), 0.5-1% early strength admixture, 0.5-1% retarding agent, 1-3% quicklime, 2-4%.Particularly, select high sclerosis melamine for incremental dose, early strength admixture is selected calcium acetate, and water-loss reducer is selected cellulose ether, and retarding agent is selected disodium citrate.Like this, the high self-leveling mortar that flows has from levelling early strong, and easy construction is characteristics fast.The physical strength standard of the mobile self-leveling mortar of this height is as follows:
| But the engineering time | 40 minutes |
| Thickness | The 3-10 millimeter |
| Abrasion resistance | ≤ 1.8 milligrams |
| Compressive strength | 28 days 〉=43MPa of 7 days 〉=34MPa of 3 days 〉=17MPa |
| Shrinkage | ≤0.03％ |
| Mobile performance | 25±1cm |
Moulding middle level 2 is water soluble acrylic acid or water-base epoxy colored paint, by mould, carries out moulding according to the required pattern of design coating, the coating of at least two roads.
Wear-resisting transparent surface layer 3 is mixed by solvent-free epoxy resin and the curing compound percentage by weight by 2: 1.Wherein: solvent-free epoxy resin is formulated by 83.33%828 epoxy resin, 12.5% reactive diluent, 0.25% defoamer, 0.5% levelling agent, 3.42% visbreaking agent.Curing compound is selected for use alicyclic.Be applied on the moulding middle level 2 through trowel, form high abrasion, glittering and translucent surface layer.Its physical property is as follows:
| Flexural strength (MPa) | ≥60 |
| Compressive strength (MPa) | ≥85 |
| Impact strength (MPa) | ≥50 |
| Abrasion resistance (750kg/500r) | ≤0.02G |
| Adhesive strength (level) | 1 |
| Pencil intensity (H) | ≥3 |
| Anti-gasoline, lubrication oil | 90 days no changes |
| Anti-NaOH (10%) | 56 days no changes |
| Anti-H 2SO 4(10％) | 56 days no changes |
| Anti-NaCl (3%) | 1 year no change |
During with the utility model finishing ground, as shown in Figure 4, irritate plane earth with the high self-leveling mortar that flows earlier, adopt physics from horizontal principle Automatic Levelling, form levelling bottom 1, this levelling bottom 1 is because of being can make from the levelling of flowing enough to approach (3-10 millimeter); Again on the levelling bottom 1 of levelling, use acrylic acid or water-base epoxy colored paint impose painted and moulding is handled, can make pure plain color, imitative bag, wood grain, apply Chinese style, American-European formula, how much graphic or the like serial moulding if add mold, can make moulding middle level 2 effects better, the thickness in this moulding middle level 2 only has 0.5 millimeter usually; At last, trowel cloth solvent-free epoxy resin on moulding middle level 2 forms limpid wear-resisting transparent surface layer 3 (thickness is at the 2-3 millimeter), is used to protect moulding middle level 2, and concrete optional light, half light, dulling material apply, and promptly finish ground surface finishing miscellaneous.Whole construction is because of directly laying, no joint treatment, so, easily and fast, and various shapesization, rich tool individual character.If during old renovation, because can making enough, the utility model approaches, can directly fit up so needn't root out, as shown in Figure 5, even do not use levelling, direct in addition new moulding middle level 2 and wear-resisting transparent surface layer 3, it is quicker to construct.Each layer of the present utility model all selected environment-friendly materials for use, the ground safety and environmental protection behind the finishing.
Claims (3)
1. ground surface material for finishing is characterized in that: arrange compound the composition by levelling bottom, moulding middle level and wear-resisting transparent surface layer by order from bottom to up.
2. ground surface material for finishing as claimed in claim 1 is characterized in that: the thickness of described levelling bottom is the 3-10 millimeter.
3. ground surface material for finishing as claimed in claim 1 is characterized in that: described moulding middle level is water soluble acrylic acid or water-base epoxy colored paint.