CN1986471A - Sandwiched glass making process - Google Patents
Sandwiched glass making process Download PDFInfo
- Publication number
- CN1986471A CN1986471A CN 200510045594 CN200510045594A CN1986471A CN 1986471 A CN1986471 A CN 1986471A CN 200510045594 CN200510045594 CN 200510045594 CN 200510045594 A CN200510045594 A CN 200510045594A CN 1986471 A CN1986471 A CN 1986471A
- Authority
- CN
- China
- Prior art keywords
- glass
- pattern
- manufacture craft
- laminated glass
- baking
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The sandwiched glass making process includes the following steps: 1. drawing and making plate in a computer; 2. cutting glass into required size, washing and air drying; 3. drawing patterns on the surface of the glass based on the template and drying naturally; 4. perforating glass; 5. compounding glass plates with patterns and holes and adhering edges with adhesive tape; 6. setting inside mold and baking at 800-920 deg.c for 3-4.5 hr; 7. naturally cooling and annealing at 500-600 deg.c in a low temperature for 2-3 hr; and 8. water washing. The sandwiched glass is molten into one integral without produced bubble and no exposure of harmful matter in the pigment.
Description
Technical field
The present invention relates to a kind of making method of glass, be specifically related to the manufacture craft of laminated glass.
Background technology
Present domestic and international widely used laminated glass, bubble is more, and middle color variable color, blackout, a dirt be not through the high temperature baking, objectionable impuritiess such as leaded, chromium attached to the glassy product surface or be the baking of two-layer incomplete eclipsed glass together, and all do not have stereoscopic sensation.
Summary of the invention
Technical problem to be solved by this invention is in order to overcome above-mentioned defective, provides a kind of bubble seldom and the manufacture craft of the laminated glass that has pattern that fuses into one.
In order to solve the problems of the technologies described above, the technical solution adopted in the present invention is: a kind of manufacture craft of laminated glass, it comprises the following steps:
(1) determines that the pattern that will draw carries out computer graphics, makes a plate then;
(2) determine the glass size that will make, and excision forming, clean up then, dry;
(3) draw a design at glass surface according to model, dry naturally the back of completing;
(4) punching in the middle of glass;
(5) glass that will have pattern and a hole combines, and justified margin cements with adhesive tape;
(6) be put on the mould, alignment aligns, under 800-920 ℃ high temperature baking 3-4.5 hour;
(7) glass of high temperature baking moulding is steadily placed, made its naturally cooling, in 500-600 ℃ low temperature oven, annealed 2-3 hour then;
(8) the product water that will finish operation cleans up;
The manufacture craft of described laminated glass, the diameter in its hole are 1-3mm;
The manufacture craft of described laminated glass, the available coloured pigment hand drawing pattern of its step (3);
The manufacture craft of described laminated glass, the available coloured pigment of its step (3) is combined into pattern;
The manufacture craft of described laminated glass, its step (3) can adopt in the middle of glass and piece together pattern with the stained glass sheet;
The manufacture craft of described laminated glass, its step (3) add the method for pressing from both sides film in the middle of can adopting glass;
The manufacture craft of described laminated glass adds the folder film promptly at the film that has pattern that sticks on glass in the middle of its glass, baking formed pattern in 2-3 hour under 500-600 ℃ temperature.
Check through Zibo Entry-Exit Inspection and Quarantine Bureau with the laminated glass that technology of the present invention is produced, reach FDA (FDA (Food and Drug Adminstration)) standard.
The beneficial effect that compared with prior art the present invention had is: in the technology of this invention glass punching made and ventilate between the glass, prevented the generation of bubble effectively, the high temperature baking has avoided pigment at product surface, objectionable impurities in the pigment can't be revealed, thereby reached the infringement that prevents harmful element, this technology fuses into one glass in addition.The present invention can make laminated glass multiple multi color patterns such as monochromatic pattern, double-side different color pattern, folder mirror pattern.
Embodiment one
(1) pattern that will draw carries out computer graphics, makes a plate then;
(2) glass that will make is determined size, and excision forming, cleans up then, dries;
(3) according to model at glass surface coloured pigment hand drawing pattern, complete the back dry naturally;
(4) in the middle of glass, beat the hole that diameter is 1mm;
(5) glass that will have pattern and a hole combines, and justified margin cements with adhesive tape;
(6) be put on the mould, alignment aligns, and baking is 4.5 hours under 800 ℃ high temperature;
(7) glass of high temperature baking moulding is steadily placed, made its naturally cooling, in 500 ℃ low temperature oven, annealed 3 hours then;
(8) the product water that will finish operation cleans up;
Embodiment two
(1) pattern that will draw carries out computer graphics, makes a plate then;
(2) glass that will make is determined size, and excision forming, cleans up then, dries;
(3) be combined into pattern at glass surface with coloured pigment according to model, dry naturally the back of completing;
(4) in the middle of glass, beat the hole that diameter is 3mm;
(5) glass that will have pattern and a hole combines, and justified margin cements with adhesive tape;
(6) be put on the mould, alignment aligns, and baking is 3 hours under 920 ℃ high temperature;
(7) glass of high temperature baking moulding is steadily placed, made its naturally cooling, in 600 ℃ low temperature oven, annealed 2 hours then;
(8) the product water that will finish operation cleans up;
Embodiment three
(1) pattern that will draw carries out computer graphics, makes a plate then;
(2) glass that will make is determined size, and excision forming, cleans up then, dries;
(3) piece together pattern with the stained glass sheet according to model in the middle of glass, dry naturally the back of completing;
(4) in the middle of glass, beat the hole that diameter is 2mm;
(5) glass that will have pattern and a hole combines, and justified margin cements with adhesive tape;
(6) be put on the mould, alignment aligns, and baking is 3.5 hours under 860 ℃ high temperature;
(7) glass of high temperature baking moulding is steadily placed, made its naturally cooling, in 550 ℃ low temperature oven, annealed 2.5 hours then;
(8) the product water that will finish operation cleans up;
Embodiment four
(1) glass that will make is determined size, and excision forming, cleans up then, dries;
(2) at the film that has pattern that sticks on glass, baking formed pattern in 3 hours under 500 ℃ temperature, dried naturally after finishing;
(3) in the middle of glass, beat the hole that diameter is 1.5mm;
(4) glass that will have pattern and a hole combines, and justified margin cements with adhesive tape;
(5) be put on the mould, alignment aligns, and baking is 3.4 hours under 900 ℃ high temperature;
(6) glass of high temperature baking moulding is steadily placed, made its naturally cooling, in 560 ℃ low temperature oven, annealed 2.4 hours then;
(7) the product water that will finish operation cleans up;
Embodiment five
(1) glass that will make is determined size, and excision forming, cleans up then, dries;
(2) at the film that has pattern that sticks on glass, baking formed pattern in 2 hours under 600 ℃ temperature, dried naturally after finishing;
(3) in the middle of glass, beat the hole that diameter is 2.5mm;
(4) glass that will have pattern and a hole combines, and justified margin cements with adhesive tape;
(5) be put on the mould, alignment aligns, and baking is 3.8 hours under 830 ℃ high temperature;
(6) glass of high temperature baking moulding is steadily placed, made its naturally cooling, in 520 ℃ low temperature oven, annealed 2.8 hours then;
(7) the product water that will finish operation cleans up;
Embodiment six
(1) glass that will make is determined size, and excision forming, cleans up then, dries;
(2) at the film that has pattern that sticks on glass, baking formed pattern in 2.5 hours under 550 ℃ temperature, dried naturally after finishing;
(3) in the middle of glass, beat the hole that diameter is 1.8mm;
(4) glass that will have pattern and a hole combines, and justified margin cements with adhesive tape;
(5) be put on the mould, alignment aligns, and baking is 3.2 hours under 880 ℃ high temperature;
(6) glass of high temperature baking moulding is steadily placed, made its naturally cooling, in 570 ℃ low temperature oven, annealed 2.2 hours then;
(7) the product water that will finish operation cleans up;
The laminated glass of above-mentioned production reaches FDA (FDA (Food and Drug Adminstration)) standard through the check of Zibo Entry-Exit Inspection and Quarantine Bureau.
Claims (7)
1, a kind of manufacture craft of laminated glass is characterized in that comprising the following steps:
(1) determines that the pattern that will draw carries out computer graphics, makes a plate then;
(2) determine the glass size that will make, and excision forming, clean up then, dry;
(3) draw a design at glass surface according to model, dry naturally the back of completing;
(4) punching in the middle of glass;
(5) glass that will have pattern and a hole combines, and justified margin cements with adhesive tape;
(6) be put on the mould, alignment aligns, under 800-920 ℃ high temperature baking 3-4.5 hour;
(7) glass of high temperature baking moulding is steadily placed, made its naturally cooling, in 500-600 ℃ low temperature oven, annealed 2-3 hour then;
(8) the product water that will finish operation cleans up.
2, the manufacture craft of laminated glass according to claim 1 is characterized in that: the diameter in hole is 1-3mm.
3, the manufacture craft of laminated glass according to claim 1 and 2 is characterized in that: the available coloured pigment hand drawing pattern of step (3).
4, the manufacture craft of laminated glass according to claim 1 and 2 is characterized in that: the available coloured pigment of step (3) is combined into pattern.
5, the manufacture craft of laminated glass according to claim 1 and 2 is characterized in that: step (3) can adopt in the middle of glass and piece together pattern with the stained glass sheet.
6, the manufacture craft of laminated glass according to claim 1 and 2 is characterized in that: step (3) adds the method for pressing from both sides film in the middle of can adopting glass.
7, the manufacture craft of laminated glass according to claim 6 is characterized in that: add the folder film in the middle of the glass promptly at the film that has pattern that sticks on glass, baking formed pattern in 2-3 hour under 500-600 ℃ temperature.