CN1978160A - Bamboo material surface nano treatment technology - Google Patents
Bamboo material surface nano treatment technology Download PDFInfo
- Publication number
- CN1978160A CN1978160A CN 200510122957 CN200510122957A CN1978160A CN 1978160 A CN1978160 A CN 1978160A CN 200510122957 CN200510122957 CN 200510122957 CN 200510122957 A CN200510122957 A CN 200510122957A CN 1978160 A CN1978160 A CN 1978160A
- Authority
- CN
- China
- Prior art keywords
- material surface
- bamboo
- bamboo material
- treatment technology
- nanometer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
This invention provides a nanometer process technology on bamboo surfaces by washing, soaking, infrared baking and cooling them by inert gas to get nm surfaces.
Description
Technical field
The invention belongs to the forest product industry technical field, a kind of bamboo material surface nano treatment technology is provided.
Technical background
Nanometer technology is developed rapidly in recent years, the emphasis that most nanometer technologies relate to be nano material manufacturing, obtain and use, owing to special usefulness that nano material had has obtained extensive use in every field.Handle and provide some technical schemes in that the nanometer of timber is strengthened some researchers aspect other material surface nanometer processing.The technology that provides as Chinese patent " method of C N00131599.4 modifying wood with nano material " is for being impregnated into timber earlier in the pre-polymerization liquid that contains Lauxite the improved wood that drying obtains having performances such as superpower, superhard, anticorrosion, waterproof, pest-resistant bacterium again; " C N200510043560.6 Nanolizing method for metal material surface " provides a kind of in the electroplate liquid of electroplanting device, and metal material as the some electrodes in two electrodes, is loaded AC process and forms nanometer layer; The technical scheme of " C N 200410012247.1 fiber surface nano functionalization processing methods " is successively by nano functional liquid, nanometer softening agent with material fiber, emulsifying liquid is handled, and obtains the fibrous material of surface nano functionalization again through PROCESS FOR TREATMENT such as microwave discharge, adjusting pH value dipping, washing, oven dry.
Prior art and patent have related to the nano reinforcement of wood quality and have handled, the Surface Nanocrystalline of metal, fiber, glass, ceramic masses, but the nanometer that does not relate to bamboo material surface handles, and more do not have the effectively technology of maturation.
Summary of the invention
Based on above understanding, the purpose of this invention is to provide a kind of bamboo material surface nano treatment technology, through the processing of this technology, bamboo material surface can obtain certain thickness nanometer layer, thereby utilizes its surface further.For reaching this purpose, the technological means that the present invention takes is for cleaning bamboo timber successively through organic cleaning solvent, and the nano functional material soaks into, and the infrared oven baking is cooled off in inert gas environment at last.The effect of each step and operating instruction are: 1, the purpose of Qing Xiing is to remove grease, lipoids, the itrogenous organic substance of bamboo wood surface, bamboo material surface texture composition is effectively spread simultaneously, and bamboo timber after the cleaning and cleaning fluid are put and reclaimed organic cleaning solvent in the retracting device.2, the purpose of Jin Runing is to soak into to the top layer of bamboo timber with the nano functional material, makes it fully to combine with bamboo timber composition.3, the purpose of infrared ray baking is volatile materials and the moisture content of removing in the size, and functional materials and bamboo wood substance are had an effect simultaneously, forms the surface of nanometer.Should be during baking according to the true form of timber, cooperate operations such as stirrings, rotation, make the bamboo material surface that is soaked into can obtain ultrared direct irradiation, oven temperature is chosen as between 150 ℃～390 ℃, and selection of time continues to toast half an hour-5 hour.4, taking-up bamboo timber was put and is cooled to room temperature in the inert gas environment after baking finished, and inert gas is selected CO
2, N
2In a kind of or two kinds of combinations, can avoid the oxidation of air like this, simultaneously to the formation of nanometer structure with stablize useful to bamboo material surface.
Embodiment
A kind of embodiment of the present invention is: the willow timber of getting the surface of scraping soaks half an hour in cleaning agent, take out, recovery sticks to the cleaning agent in wood surface and the cleaning raffinate, then timber is immersed in the size, soak into taking-up in 2 hours, put in 250 ℃ of infrared-ray ovens and toasted 10 hours, place one to be full of N then
2Closed container in be cooled to room temperature.
Claims (3)
1, a kind of bamboo material surface nano technology is characterized in that its technical process is: bamboo timber is through surface clean, infiltration, infrared ray baking, inert gas environment cooling.
2, nanometer technology as claimed in claim 1 is characterized in that, it is 150 ℃～390 ℃ that described infrared ray toasts selected temperature range, and the time is half an hour-5 hour.
3, nanometer technology as claimed in claim 1 is characterized in that described inert gas is CO
2, N
2In a kind of or two kinds mixture.