CN1970829A - Method for manufacturing nontoxic tablewares, tea set, and medical vessels by using binary method and products therefrom - Google Patents
Method for manufacturing nontoxic tablewares, tea set, and medical vessels by using binary method and products therefrom Download PDFInfo
- Publication number
- CN1970829A CN1970829A CN 200510032446 CN200510032446A CN1970829A CN 1970829 A CN1970829 A CN 1970829A CN 200510032446 CN200510032446 CN 200510032446 CN 200510032446 A CN200510032446 A CN 200510032446A CN 1970829 A CN1970829 A CN 1970829A
- Authority
- CN
- China
- Prior art keywords
- silver
- pattern
- silvered film
- technology
- silver layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a manufacturing method of gas-mask tableware, tea set and medical utensil through combining method of vacuum magnetic control splashing silver depositing technique and macromolecular solidifying technique, which comprises the following steps: 1. sputtering silver layer through vacuum magnet; loading tableware, tea set and medical utensil in the vacuum magnetic control sputtering machine; aerating argon; bombarding silver target; sputtering silver layer on the surface with thickness at 2-5um of tableware, tea set and medical utensil; spraying a layer of colorless transparent tempering coating; removing mould with pattern; reserving protective function of silver on the projected silver layer without tempering coating.
Description
Technical field
The present invention relates to a kind of method and product that adopts binary method production gas defence tableware, tea set and medical vessels, particularly a kind of vacuum magnetic-control sputtering silvered film technology and macromolecular material curing technology the combine method and product of production gas defence tableware, tea set and medical vessels of adopting.
Background technology
Silverware of the prior art has the gas defence function, contains food with silverware, in case food is poisonous, the surface of silver will variable color, and people will find that food is poisonous.But silver is a kind of precious metal, and the tableware of full silver costs an arm and a leg, and can not generally use in daily life.And vacuum magnetic-control sputtering silvered film technology and macromolecular material curing technology all are very sophisticated prior aries, but also have no talent these two technology are combined production gas defence tableware, tea set and medical vessels.
Summary of the invention
The purpose of this invention is to provide a kind of vacuum magnetic-control sputtering silvered film technology and macromolecular material curing technology the combine method and product of production gas defence tableware, tea set and medical vessels of adopting.
Technical scheme of the present invention is: a kind of combine method of production gas defence tableware, tea set and medical vessels of vacuum magnetic-control sputtering silvered film technology and macromolecular material curing technology that adopts, it mainly comprises the steps:
One, vacuum magnetic-control sputtering silvered film
A, tableware, tea set and medical vessels are cleaned up with liquid, carry out drying treatment then, can seasoning, also can use kiln dried;
B, with dried tableware, tea set and the medical vessels vacuum magnetic-control sputtering coating equipment of packing into, charge into argon gas, under the action of a magnetic field, bombard silver-colored target with argon ion, at the surface sputtering silvered film of tableware, tea set and medical vessels, plate the silver layer of one deck 2-5 micron thickness;
C, silver layer coated tableware, tea set and medical vessels are cleaned up, carry out drying treatment then, can seasoning, also can use kiln dried.
Two, macromolecular material solidifies
A, stick the template that has pattern at the internal surface that has plated the dried tableware of silver layer, tea set and medical vessels, the surfaces externally and internally at tableware, tea set and medical vessels all sprays the water white toughened paint layer of last layer then;
B, the template that will have a pattern are taken away, tableware, tea set and the medical vessels that will spray toughened paint then carry out drying treatment, can seasoning, also can use kiln dried, like this, just remain with the silver layer that has pattern of protruding dew at the internal surface of tableware, tea set and medical vessels, on the silver layer that has pattern of protruding dew by the spraying toughened paint, to keep the gas defence function of silver.
The present invention has following characteristics:
1, adopt vacuum magnetic-control sputtering silvered film technology and macromolecular material curing technology combine production gas defence tableware, tea set and medical vessels, its technical maturity, low cost of manufacture is fit to produce in batches.
2, adopt vacuum magnetic-control sputtering silvered film technology and macromolecular material curing technology combine production gas defence tableware, tea set and medical vessels, have and prevent that people from poisoning by food and the function of drug intoxication.
In order to be illustrated more clearly in the present invention, enumerate following examples.
Description of drawings
Accompanying drawing 2 is the vertical view of accompanying drawing 1;
Accompanying drawing 3 is the partial enlarged drawing in the accompanying drawing 1
Accompanying drawing 4 is the structural representation of plate;
Accompanying drawing 5 is the vertical view of accompanying drawing 4;
Accompanying drawing 6 is the partial enlarged drawing in the accompanying drawing 4;
The spoon structural representation that accompanying drawing 7 is;
Accompanying drawing 8 is the upward view of accompanying drawing 7;
Accompanying drawing 9 is the partial enlarged drawing in the accompanying drawing 8;
Accompanying drawing 10 is the structural representation of lunch box;
Accompanying drawing 11 is the partial enlarged drawing in the accompanying drawing 10;
Accompanying drawing 12 is the vertical view of box body 13 in the accompanying drawing 10;
Accompanying drawing 13 is the upward view of lid 16 in the accompanying drawing 10;
Accompanying drawing 14 is the structural representation of cup;
Accompanying drawing 15 is the partial enlarged drawing in the accompanying drawing 14;
Accompanying drawing 16 is the A-A sectional view in the accompanying drawing 14;
Accompanying drawing 17 is the vertical view of accompanying drawing 14;
Accompanying drawing 18 is the structural representation of medical vessels;
Accompanying drawing 19 is the vertical view of accompanying drawing 18;
Accompanying drawing 20 is the partial enlarged drawing in the accompanying drawing 18.
Embodiment
Embodiment 1: prevent the bowl of poisoning by food, shown in accompanying drawing 1,2,3, it comprises a bowl 1 of containing food, the material of bowl 1 is the same with prior art, can be metallic substance, also can be non-metallic material (as pottery, glass, plastics etc.), in the whole surfaces externally and internally employing vacuum magnetic-control sputtering technology of bowl 1, plate the silvered film 2 of one deck 2-5 micron thickness, be coated with the water white toughened paint layer 3 of one deck on the surface of silvered film 2.In the inside of bowl, remain with the silver layer 4 that has pattern of protruding dew, do not sprayed toughened paint on the silver layer 4 that has pattern of protruding dew, to keep the gas defence function of silver.
Embodiment 2: prevent the plate of poisoning by food, shown in accompanying drawing 4,5,6, it comprises a plate 5 of containing food, the material of plate 5 is the same with prior art, can be metallic substance, also can be non-metallic material (as pottery, glass, plastics etc.), in the whole surfaces externally and internally employing vacuum magnetic-control sputtering technology of plate 5, plate the silvered film 6 of one deck 2-5 micron thickness, be coated with the water white toughened paint layer 7 of one deck on the surface of silvered film 6.In the inside of plate 5, remain with the silver layer 8 that has pattern of protruding dew, do not sprayed toughened paint on the silver layer 8 that has pattern of protruding dew, to keep the gas defence function of silver.
Embodiment 3: prevent the spoon of poisoning by food, shown in accompanying drawing 7,8,9, it comprises the spoon 9 of a dining usefulness, the material of spoon 9 is the same with prior art, can be metallic substance, also can be non-metallic material (as pottery, plastics etc.), adopts vacuum magnetic-control sputtering technology on the whole surface of spoon 9, plate the silvered film 10 of one deck 2-5 micron thickness, be coated with the water white toughened paint layer 11 of one deck on the surface of silvered film 10.In the inside of spoon 9, remain with the silver layer 12 that has pattern of protruding dew, do not sprayed toughened paint on the silver layer 12 that has pattern of protruding dew, to keep the gas defence function of silver.
Embodiment 4: prevent the lunch box of poisoning by food, shown in accompanying drawing 10,11,12,13, it comprises a box body 13 and a lid 16 of containing food, the material of lunch box is the same with prior art, employing is a metallic substance, the whole surfaces externally and internally of lunch box adopts vacuum magnetic-control sputtering technology, plates the silvered film 14 of one deck 2-5 micron thickness, is coated with the water white toughened paint layer 15 of one deck on the surface of silvered film 14.In the inside of box body 13 and lid 16, remain with the silver layer 17 that has pattern of protruding dew, do not sprayed toughened paint on the silver layer 17 that has pattern of protruding dew, to keep the gas defence function of silver.
Embodiment 5: prevent the cup that liquid is poisoned, shown in accompanying drawing 14,15,16,17, it comprises the cup 18 of a holding liquid, the material of cup 18 is the same with prior art, can be metallic substance, also can be non-metallic material (as pottery, glass, plastics etc.), in the whole surfaces externally and internally employing vacuum magnetic-control sputtering technology of cup 18, plate the silvered film 19 of one deck 2-5 micron thickness, be coated with the water white toughened paint layer 20 of one deck on the surface of silvered film 19.In the inside of cup 18, remain with the silver layer 21 that has pattern of protruding dew, do not sprayed toughened paint on the silver layer 21 that has pattern of protruding dew, to keep the gas defence function of silver.
Embodiment 6: prevent the medical vessels that Chinese medicinal materials is poisoned, shown in accompanying drawing 18,19,20, it comprises a medical vessels 22 of containing Chinese medicinal materials, the material of medical vessels 22 is the same with prior art, can be metallic substance, also can be non-metallic material (as pottery, glass, plastics etc.), in the whole surfaces externally and internally employing vacuum magnetic-control sputtering technology of medical vessels 22, plate the silvered film 23 of one deck 2-5 micron thickness, be coated with the water white toughened paint layer 24 of one deck on the surface of silvered film 23.In the inside of medical vessels, remain with the silver layer 25 that has pattern of protruding dew, do not sprayed toughened paint on the silver layer 25 that has pattern of protruding dew, to keep the gas defence function of silver.
Claims (7)
1, a kind of combine method of production gas defence tableware, tea set and medical vessels of vacuum magnetic-control sputtering silvered film technology and macromolecular material curing technology that adopts is characterized in that:
One, vacuum magnetic-control sputtering silvered film
A, tableware, tea set and medical vessels are cleaned up with liquid, carry out drying treatment then, can seasoning, also can use kiln dried;
B, with dried tableware, tea set and the medical vessels vacuum magnetic-control sputtering coating equipment of packing into, charge into argon gas, under the action of a magnetic field, bombard silver-colored target with argon ion, at the surface sputtering silvered film of tableware, tea set and medical vessels, plate the silver layer of one deck 2-5 micron thickness;
C, silver layer coated tableware, tea set and medical vessels are cleaned up, carry out drying treatment then, can seasoning, also can use kiln dried;
Two, macromolecular material solidifies
A, stick the template that has pattern at the internal surface that has plated the dried tableware of silver layer, tea set and medical vessels, the surfaces externally and internally at tableware, tea set and medical vessels all sprays the water white toughened paint layer of last layer then;
B, the template that will have a pattern are taken away, tableware, tea set and the medical vessels that will spray toughened paint then carry out drying treatment, can seasoning, also can use kiln dried, like this, just remain with the silver layer that has pattern of protruding dew at the internal surface of tableware, tea set and medical vessels, on the silver layer that has pattern of protruding dew by the spraying toughened paint, to keep the gas defence function of silver.
2, according to claim 1 a kind of adopt vacuum magnetic-control sputtering silvered film technology and macromolecular material curing technology to combine to produce prevent the bowl of poisoning by food, it is characterized in that it comprises a bowl 1 of containing food, the material of bowl 1 is the same with prior art, it can be metallic substance, also can be that non-metallic material are (as pottery, glass, plastics etc.), whole surfaces externally and internally at bowl 1 adopts vacuum magnetic-control sputtering technology, plate the silvered film 2 of one deck 2-5 micron thickness, be coated with the water white toughened paint layer 3 of one deck on the surface of silvered film 2, the inside at bowl, remain with the silver layer 4 that has pattern of protruding dew, do not sprayed toughened paint on the silver layer 4 that has pattern of protruding dew, to keep the gas defence function of silver.
3, according to claim 1 a kind of adopt vacuum magnetic-control sputtering silvered film technology and macromolecular material curing technology to combine to produce prevent the plate of poisoning by food, it is characterized in that it comprises a plate 5 of containing food, the material of plate 5 is the same with prior art, it can be metallic substance, also can be that non-metallic material are (as pottery, glass, plastics etc.), whole surfaces externally and internally at plate 5 adopts vacuum magnetic-control sputtering technology, plate the silvered film 6 of one deck 2-5 micron thickness, be coated with the water white toughened paint layer 7 of one deck on the surface of silvered film 6, the inside at plate 5, remain with the silver layer 8 that has pattern of protruding dew, do not sprayed toughened paint on the silver layer 8 that has pattern of protruding dew, to keep the gas defence function of silver.
4, according to claim 1 a kind of adopt vacuum magnetic-control sputtering silvered film technology and macromolecular material curing technology to combine to produce prevent the spoon of poisoning by food, it is characterized in that it comprises the spoon 9 of a dining usefulness, the material of spoon 9 is the same with prior art, it can be metallic substance, also can be that non-metallic material are (as pottery, plastics etc.), vacuum magnetic-control sputtering technology is adopted on whole surface at spoon 9, plate the silvered film 10 of one deck 2-5 micron thickness, be coated with the water white toughened paint layer 11 of one deck on the surface of silvered film 10, the inside at spoon 9, remain with the silver layer 12 that has pattern of protruding dew, do not sprayed toughened paint on the silver layer 12 that has pattern of protruding dew, to keep the gas defence function of silver.
5, according to claim 1 a kind of adopt vacuum magnetic-control sputtering silvered film technology and macromolecular material curing technology to combine to produce prevent the lunch box of poisoning by food, it is characterized in that it comprises a box body 13 and a lid 16 of containing food, the material of lunch box is the same with prior art, employing is a metallic substance, the whole surfaces externally and internally of lunch box adopts vacuum magnetic-control sputtering technology, plate the silvered film 14 of one deck 2-5 micron thickness, be coated with the water white toughened paint layer 15 of one deck on the surface of silvered film 14, the inside at box body 13 and lid 16, remain with the silver layer 17 that has pattern of protruding dew, do not sprayed toughened paint on the silver layer 17 that has pattern of protruding dew, to keep the gas defence function of silver.
6, according to claim 1 a kind of adopt vacuum magnetic-control sputtering silvered film technology and macromolecular material curing technology to combine to produce prevent the cup of poisoning by food, it is characterized in that it comprises the cup 18 of a holding liquid, the material of cup 18 is the same with prior art, it can be metallic substance, also can be non-metallic material (as pottery, glass, plastics etc.), whole surfaces externally and internally at cup 18 adopts vacuum magnetic-control sputtering technology, plate the silvered film 19 of one deck 2-5 micron thickness, be coated with the water white toughened paint layer 20 of one deck on the surface of silvered film 19.In the inside of cup 18, remain with the silver layer 21 that has pattern of protruding dew, do not sprayed toughened paint on the silver layer 21 that has pattern of protruding dew, to keep the gas defence function of silver.
7, according to claim 1 a kind of adopt vacuum magnetic-control sputtering silvered film technology and macromolecular material curing technology to combine to produce prevent the medical vessels that Chinese medicinal materials is poisoned, it is characterized in that it comprises a medical vessels 22 of containing Chinese medicinal materials, the material of medical vessels 22 is the same with prior art, it can be metallic substance, also can be that non-metallic material are (as pottery, glass, plastics etc.), whole surfaces externally and internally at medical vessels 22 adopts vacuum magnetic-control sputtering technology, plate the silvered film 23 of one deck 2-5 micron thickness, be coated with the water white toughened paint layer 24 of one deck on the surface of silvered film 23, the inside at medical vessels 22, remain with the silver layer 25 that has pattern of protruding dew, do not sprayed toughened paint on the silver layer 25 that has pattern of protruding dew, to keep the gas defence function of silver.