CN1253607C - Surface treatment method for making metal container surface indicating two kinds of color and/or surface effect - Google Patents
Surface treatment method for making metal container surface indicating two kinds of color and/or surface effect Download PDFInfo
- Publication number
- CN1253607C CN1253607C CN 03122798 CN03122798A CN1253607C CN 1253607 C CN1253607 C CN 1253607C CN 03122798 CN03122798 CN 03122798 CN 03122798 A CN03122798 A CN 03122798A CN 1253607 C CN1253607 C CN 1253607C
- Authority
- CN
- China
- Prior art keywords
- metal vessel
- kinds
- color
- treatment method
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention discloses a surface treatment method for making metal container surfaces indicate two color and/or surface effects. Part of a molded and polished metal container is covered and protected; the exposure part is corroded or sandblasted; then, the whole metal container is electroplated to form two surface effects of a smooth coating surface and patterns with the same color or a sandblast coating surface; or firstly, the molded and polished metal container is electroplated; part of the molded and polished metal container is covered and protected; after the exposure part is stripped, a coating with a new color is electroplated to make the surface of the metal container form surface coatings with the two different colors; the surface treatment method can be used for obtaining more than two surface colours and more than two surface effects to make the surface colours of the metal container abundant. The patterns can change in various modes. The surface effects are also diverse. The present invention largely enhances the decorative function of the metal container.
Description
Technical field
The present invention relates to a kind of surface treatment method of metal vessel, particularly a kind of surface treatment method that makes the metal vessel surface present two kinds of colors and/or surface effect.
Background technology
At present, metal vessel is used for the splendid attire household objects and has obtained more and more widely application, because metal vessel is corrosion-resistant, anti-ly beat, collide with, and the color that presents is various, splendid, can be used as kettle, teacup or sugar handleless cup etc., attractive and durable, play certain decorative effect simultaneously.But common in the market metal vessel has only single color and surface treatment effect usually, and color is single, form is stiff, does not have best decoration function, can not satisfy the modern to the ornamental requirement of household objects.
Summary of the invention
The object of the present invention is to provide a kind of surface treatment method that makes the metal vessel surface present two kinds of colors and/or surface effect.
The technical solution adopted for the present invention to solve the technical problems is:
A kind of surface treatment method that makes the metal vessel surface present two kinds of colors and/or surface effect, its treatment step is as follows: (1) carries out electroplating processes with the metal vessel behind the plastic polishing, makes it to present the color of coating; (2) will be wherein a part by rubberizing paper, spray paint or mode covering protection such as printing; (3) metal vessel is carried out strip and handle, make the appearance part take off coating; (4) metal vessel is different from the electroplating processes of step (1) color, makes the metallic surface that is not capped protection present new coating color; (5) remove the coverture that is capped the surface, form surface effect on the metal vessel surface thus with two kinds of different colours overlay coatings.
For the surface effect that makes metal vessel abundanter, can between step (3) and step (4), increase a step: promptly increase the printing or the sandblast of appearance part or melt to paste and handle, so just can make the metal vessel surface present two kinds of colors and two kinds of surface effects---smooth plating layer surperficial and floral designs or sandblast face coating surface.
Electroplating processes described in the above-mentioned steps is chromium plating, gold-plated, silver-plated or copper etc.; Adopting aforesaid method to carry out surface-treated metal vessel material is iron, stainless steel, aluminium etc.
The invention has the beneficial effects as follows: metal vessel surface after treatment can present two kinds of colors and/or surface effect, and analogize by this method and can obtain two or more surface color and polishes and/or surface effect, can adopt different colors such as gold, silver color to come the decorative vessel surface, also can adopt minute surface and two kinds of surface effects of sandblast face of same color to form sharp contrast, make the surface color and polish of metal vessel abundanter, and floral designs change various, surface effect is splendid, has strengthened its decoration function greatly; Before the metal of electroplating another color, the appearance part is carried out strip simultaneously and handle, can guarantee the pure unanimity of color of metal plating, thereby make surface form stronger striking contrast with two kinds of different colors.
Description of drawings
The present invention is further described below in conjunction with drawings and Examples.
Fig. 1 is first embodiment synoptic diagram of the present invention;
Fig. 2 is second embodiment synoptic diagram of the present invention;
Fig. 3 is the 3rd an embodiment synoptic diagram of the present invention;
Fig. 4 is the 4th an embodiment synoptic diagram of the present invention.
Embodiment
With reference to Fig. 1, metal pot lid surface presents gold, there is the concavo-convex pattern of similar " returning " font at the pot lid edge, the rest part of pot lid presents the coating surface of smooth mirror surface, " 1 " expression has the coating surface of " returning " font concavo-convex pattern among the figure, and " 2 " expression presents the coating surface of smooth mirror surface.In order to reach two kinds of such surface effects, need through following surface treatment step: (1) is with the part that indicates " 2 " of the metal pot lid behind the plastic polishing mode covering protection by rubberizing paper; (2) to the appearance part, promptly illustrate the part that indicates " 1 " and carry out corrosion treatment, the cubic stick that has " returning " word flower shape that just will make in advance is attached to the surface that pot lid is marked with " 1 ", other parts of pot lid are carried out putting into corrosive fluid behind the corrosionproof protection, only make the pot lid that exposes " returning " word flower shape depression that partly is corroded, thereby formation has the metallic surface of " going back to " word floral designs; (3) remove the paster that is capped the surface; (4) metal vessel is carried out gold-plated processing, make the pot lid surface present gold.So far, smooth plating layer surface 2 with golden minute surface and two kinds of surface effects of " returning " font decorative pattern coating surface 1 have just been formed in the metallic surface.
With reference to Fig. 2, for the surface effect that makes pot lid shown in Figure 1 abundanter, thereby increase its decorative effect, sandblasting can be carried out in the smooth plating layer surface that indicates " 3 " among Fig. 2, form frosted finish effect.This just need increase a surface treatment step afterwards in above-mentioned step (2): the part that is about to indicate " 1 ", " 2 " is by mode covering protections such as rubberizing paper, and exposing the part that indicates " 3 " carries out sandblasting; Remove the paster that is capped the surface according to step (3), (4) at last, metal vessel is carried out gold-plated processing, make the pot lid surface present gold.Through such surface treatment, the surface of metal pot lid has just had three kinds of surface effects---the coating surface 3 of smooth plating layer surface 2, " returning " font decorative pattern coating surface 1 and the frosted finish effect of golden minute surface.
With reference to Fig. 3, metal kettle body is made up of six faces, and these six intervals present silvery white and golden two kinds of colors, and with " 1 " expression silver color surface, " 2 " represent golden surface among the figure.It is as follows to make the kettle surface present the surface treatment method step of two kinds of colors: (1) is put into electroplate liquid with metal kettle body and is carried out chromium plating and handle, make it the surface and present argenteous coating color; (2) surface color and polish according to design in advance distributes, and the kettle body of six faces is chosen the mode covering protection of three faces by rubberizing paper at interval; (3) metal kettle body is carried out strip and handle, make other three faces that expose take off argenteous coating; (4) metal kettle body is put into electroplate liquid and carry out gold-plated processing, make three appearance parts present golden coating color; (5) remove gummed paper on three faces that are capped in the abovementioned steps.So far, just formed in the metallic surface and had argenteous coating surface 1 and golden coating surface 2.
With reference to Fig. 4, for the surface effect that makes kettle body shown in Figure 3 abundanter, thereby increase its decorative effect, sandblasting can be carried out in the smooth plating layer surface that indicates " 2 " among Fig. 3, form frosted finish effect.This just need increase a step between above-mentioned step (3) and step (4): promptly sandblasting is partly carried out in the appearance behind the strip, thereby formed frosted finish effect at the coating surface that indicates " 2 "; At last metal kettle body is put into electroplate liquid and carry out gold-plated processing, make the appearance part present golden coating color, remove the gummed paper on three faces that indicate " 1 " that are capped in the abovementioned steps again.Through such surface treatment, the surface of metal kettle body just presents two kinds of colors---gold and silver color, and two kinds of surface effects---smooth plating layer surface 1 and frosted coating surface 2.
Metal kettle body in the foregoing description can adopt metallic substance such as iron, stainless steel or aluminium.Embodiments of the present invention are not limited to the above embodiments, obtain two or more surface color and polishes and two or more surface effects if desired and need only similar the foregoing description and equally increase corresponding step and just can obtain.
Adopt surface treatment method of the present invention to make the surface color and polish of metal vessel abundanter, surface effect is more splendid, has improved its decorative effect greatly.
Claims (4)
1. surface treatment method that makes the metal vessel surface present two kinds of colors and/or surface effect is characterized in that the step of this surface treatment method is as follows:
(1) metal vessel behind the plastic polishing is carried out electroplating processes, make it to present the color of coating;
(2) with the part of metal vessel by rubberizing paper, spray paint or print covering protection;
(3) metal vessel is carried out strip and handle, make the appearance part take off coating;
(4) metal vessel is different from the electroplating processes of step (1) color, makes the metallic surface of appearance part present new coating color;
(5) remove the coverture that is capped the surface, form overlay coating on the metal vessel surface thus with two kinds of different colours.
2. the surface treatment method that makes the metal vessel surface present two kinds of colors and/or surface effect according to claim 1, it is characterized in that between step (3) and step (4), can increase a step: the appearance part is corroded or sandblasting, make it to form metallic surface with floral designs or sandblast face.
3. the surface treatment method that makes the metal vessel surface present two kinds of colors and/or surface effect according to claim 1 is characterized in that the electroplating processes described in the above-mentioned steps is chromium plating, gold-plated, silver-plated or copper.
4. the surface treatment method that makes the metal vessel surface present two kinds of colors and/or surface effect according to claim 1, it is characterized in that adopting aforesaid method to carry out surface-treated metal vessel material is iron, stainless steel or aluminium.