CN1970419A - Elevator operation box panel and its producing method - Google Patents
Elevator operation box panel and its producing method Download PDFInfo
- Publication number
- CN1970419A CN1970419A CN 200610154998 CN200610154998A CN1970419A CN 1970419 A CN1970419 A CN 1970419A CN 200610154998 CN200610154998 CN 200610154998 CN 200610154998 A CN200610154998 A CN 200610154998A CN 1970419 A CN1970419 A CN 1970419A
- Authority
- CN
- China
- Prior art keywords
- panel
- operation box
- elevator operation
- making
- box panel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
It relates to the control panel of a lifer. The integrated panel comprises a panel, slide track at the back, installation holes on the panel for installing display, label and press button, with the panel made of aluminum alloy. It extrudes the heated aluminum alloy bar into a panel with punching holes processed installation holes, through polishing, sand spraying or wire drawing pre processing to the panel surface, then acid dipping or/and alkali washing and finally for oxidation treatment. It is simple, nice looking, convenient in processing and low in cost.
Description
Technical field
The present invention relates to a kind of elevator operation box panel and preparation method thereof.
Background technology
It is material that existing elevator operation box panel adopts stainless steel sheet mostly, make through operations such as shear, laser beam cutting, punching, bending, butt-joint screws then, and it is assembled by multi-sheets, so have cost height, surface working difficulty, appearance forrns mono-shortcoming.
As Chinese utility model patent 93245890.4 disclosed " elevator console cabinet panel ", it is made up of centre panel and both sides panel, panel is a substrate with the aluminium alloy plate of aluminium alloy extrusions system, outside face at aluminium alloy plate is covered with stainless steel faceplate, and centre panel and both sides panel are the connection structures of inlaying of sliding type.This panel is slided by three aluminium alloy plates after the interlocking, the fixing stainless steel faceplate on the surface again, and non-integrative-structure, so have complex structure, the problem that tooling cost is high, and panel appearance can only be the writing board shape of ordinary stainless steel plate.
In addition by retrieval, do not find the prior art of the elevator operation box panel method for making identical with the present invention.
Summary of the invention
Technical matters to be solved by this invention provides a kind of simple in structure, handsome in appearance, easy to process, the elevator operation box panel that cost is low and the method for making of this panel.
The present invention addresses the above problem the technical scheme that is adopted: this panel is structure as a whole, and the slide rail that it comprises panel body and is positioned at the panel body back side has some mounting holes that are used to install telltale, label and button on the panel body; Described panel is an aluminum alloy material.
The method for making of above-mentioned elevator operation box panel, carry out according to the following steps:
Step 1, make mould, select aluminium alloy bars then, utilize extrusion press will be heated to aluminium alloy bars extrusion molding from mould of 400 ℃-540 ℃ as extruding raw material according to required panel shape of cross section;
Step 2, the mode with line cutting or stamping die punching on panel process the mounting hole that telltale, label and button are installed;
Polish on step 3, counter plate surface, sandblast or wire drawing pretreatment, pickling and/or alkali cleaning are carried out in the counter plate surface then, again panel is installed on the anode frame and place the oxidation trough that battery acid is housed, the groove temperature control is 18 ℃-22 ℃ and energising, make panel surface form one deck compact oxidation layer, the panel that will form oxide coating again places staining jar and energising, make the microcellular structure precipitation adsorpting dye molecule of oxide coating, the fine fenestra of the porous oxide coatings that generates after the last antianode oxidation seals.
Described panel can carry out quenching strengthening when extruding; The thickness of described compact oxidation layer is 8-12 μ m.After described oxidation step is finished, stick protective film on the oxide coating surface.
The present invention compared with prior art has following beneficial effect: 1, this panel is by extrusion forming of aluminium alloy bars, and panel body is structure as a whole with the slide rail that is positioned at the panel body back side, and simple in structure, tooling cost is low; 2, can produce mould according to the panel cross sectional shape that designs, utilize the aluminium alloy bars extrusion molding from mould after extrusion press will heat then, so just can produce the panel of various given shapes, and be not limited to the writing board shape of ordinary stainless steel plate; 3, by colored or self-colored anodic oxidation treatment PROCESS FOR TREATMENT, not only corrosion resistance of surface is strong, color and luster is attractive in appearance again for the aluminum alloy behind the extrusion forming, has also improved the shortcoming of common aluminum alloy part corrosion-resistant, surface gloss difference.
Description of drawings
Fig. 1 is the front view of the embodiment of the invention.
Fig. 2 is the cross sectional drawing of Fig. 1.
The specific embodiment
Referring to Fig. 1, Fig. 2, panel in the present embodiment is structure as a whole, two slide rails 2 that it comprises panel body 1 and is positioned at panel body 1 back side have some mounting holes 3 that are used to install telltale, label and button etc. on the panel body 1, and this panel integral body are aluminum alloy material.During installation, can slip into screw in the slide rail 2, be used for fixing the panel block parts such as telltale, communication board, interphone at panel body 1 back side.
The method for making of the panel in the present embodiment is made according to the following steps:
Step 1, elder generation make extrusion dies according to panel shape of cross section shown in Figure 2, the shape of mold cavity is identical with the shape of panel cross-sectional plane, selecting the trade mark then is that 6063 aluminium alloy bars is as extruding raw material, at the extruding tonnage is to squeeze out the panel of shape of cross section as shown in Figure 2 on 200 tons the extrusion press, temperature with aluminium alloy bars during extruding is controlled between 400 ℃-540 ℃, the temperature of mould is carried out air-blast hardening, with stiffened panel intensity in extruding about 420 ℃.
Step 2, the mode with the stamping die punching on panel process some mounting holes 3 that are used to install telltale and button as shown in Figure 1.
Step 3: 1, sandblast pretreatment is carried out on the counter plate surface, makes the surface produce frosted finish effect, and pickling is carried out on the counter plate surface earlier then, alkali cleaning again, grease or other impurity of removal panel surface; 2, panel is installed on the anode frame and place the oxidation trough that battery acid is housed, panel is vertical with the energising direction, and the groove temperature control makes panel surface form one deck compact oxidation layer 18 ℃-22 ℃ and energising, and the thickness of compact oxidation layer is 8-12 μ m; 3, the panel that will form oxide coating places staining jar and energising, makes the microcellular structure precipitation adsorpting dye molecule of oxide coating; 4, the fine fenestra of the porous oxide coatings that generates after the antianode oxidation seals processing, and dye molecule is fixed in the oxide coating, makes oxide coating anti-pollution simultaneously, improves its against corrosion and wear resisting property.
After finishing oxidation step, it is to be installed to stick protective film on the oxide coating surface.
In the above-mentioned steps one the quenching mode also can be water smoke cooling or tank cooling.
Also available line cutting mode processing mounting holes 3 in the above-mentioned steps two.
In the above-mentioned steps three the counter plate surface also can polish, pretreatment such as wire drawing, make the surface produce effects such as minute surface, wire drawing respectively; The counter plate surface also can be carried out pickling or alkali cleaning separately.
Claims (6)
1, a kind of elevator operation box panel is characterized in that: this panel is structure as a whole, and the slide rail that it comprises panel body and is positioned at the panel body back side has some mounting holes that are used to install telltale, label and button on the panel body.
2, elevator operation box panel according to claim 1 is characterized in that: described panel is an aluminum alloy material.
3, the method for making of the described elevator operation box panel of a kind of claim 1 is characterized in that: carries out according to the following steps,
Step 1, make mould, select aluminium alloy bars then, utilize extrusion press will be heated to aluminium alloy bars extrusion molding from mould of 400 ℃-540 ℃ as extruding raw material according to required panel shape of cross section;
Step 2, the mode with line cutting or stamping die punching on panel process display aperture and button hole:
Polish on step 3, counter plate surface, sandblast or wire drawing pretreatment, pickling and/or alkali cleaning are carried out in the counter plate surface then, again panel is installed on the anode frame and place the oxidation trough that battery acid is housed, the groove temperature control is 18 ℃-22 ℃ and energising, make panel surface form one deck compact oxidation layer, the panel that will form oxide coating again places staining jar and energising, make the microcellular structure precipitation adsorpting dye molecule of oxide coating, the fine fenestra of the porous oxide coatings that generates after the last antianode oxidation seals.
4, the method for making of elevator operation box panel according to claim 3 is characterized in that: described panel can carry out quenching strengthening when extruding.
5, the method for making of elevator operation box panel according to claim 3 is characterized in that: the thickness of described compact oxidation layer is 8-12 μ m.
6, the method for making of elevator operation box panel according to claim 3 is characterized in that: after described oxidation step is finished, stick protective film on the oxide coating surface.