CN1962772A - Ink for white board marker and method for manufacturing same - Google Patents
Ink for white board marker and method for manufacturing same Download PDFInfo
- Publication number
- CN1962772A CN1962772A CN 200610097942 CN200610097942A CN1962772A CN 1962772 A CN1962772 A CN 1962772A CN 200610097942 CN200610097942 CN 200610097942 CN 200610097942 A CN200610097942 A CN 200610097942A CN 1962772 A CN1962772 A CN 1962772A
- Authority
- CN
- China
- Prior art keywords
- white board
- pen ink
- board pen
- pigment
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a white-board pen ink and preparing method, which comprises the following parts: 3.5-5.0% dye,1.0-5.0% decapping agent,48.0-71.0% alcohol,15.0-25.0% propanol,5.0- 10.0% erasable agent,3.5-5.0% resin and 1.0-2.0% dispersant. the preparing method comprises the following steps: adding alcohol and propanol in the predispersing stove; stirring to add decapping agent, erasable agent, resin and dispersant until dissolving evenly; adding dye; stirring completely; grinding for 20-30h until the grain size D50 of dye particle reaches 120-200nm; discharging.
Description
Technical field
The present invention relates to white board pen ink, relate in particular to a kind of nano-level pigment-type white board pen ink and manufacture method thereof, belong to the ink technology field.
Background technology
The blank pen is the new class product that a system industry is developed in recent years, the basic dependence on import of supporting with it white board pen ink.Hang Xiao high-grade special-purpose ink is all being changed to pigment style by dye-type in the market.The shortcoming of dye-type white board pen ink is: the easy crystallization of dye component, and cause China ink inhomogeneous, write not smooth; Poisonous, not environmental protection.
The pigment style white board pen ink is to be scattered in the ink system with pigment particles it is effective.Common pigment style white board pen ink pigment particles is big, and dispersion effect is poor, and directly influence is write.A kind of nano-level pigment-type white board pen ink can overcome above-mentioned deficiency effectively.But along with diminishing of particle, specific surface area will increase greatly, and the Van der Waals force between the particle will become greatly, very easily produce cohesion between micropartical, thereby cause producing in storage process layering, precipitation iso-metamorphism phenomenon.General Technology and equipment are difficult to make that pigment particles reaches initial nanometer in the ink system, are difficult to the dispersion stabilization that keeps good.Moreover, keep low viscous stable be again an important index, viscosity is bigger than normal, it is little to use black quantitative change, causes phenomenons such as writing smooth, broken string, wire drawing; Viscosity is too little, the ink leak phenomenon can occur, and keeping low viscosity is another technical barrier of white board pen ink.So, produce desirable high quality nanometer level pigment style white board pen ink, in preparation, must capture above technical problem.
Summary of the invention
The purpose of this invention is to provide a kind of white board pen ink and manufacture method thereof, adopt " superfine grinding technology " and " scientific formula ", be intended to effectively solve particle diameter, viscosity, the cohesion layering of white board pen ink pigment and write erasability, technical problem such as raise one's hat, make it can mate various homemade, import rolled cores and fiber nib.
Purpose of the present invention is achieved through the following technical solutions:
White board pen ink is characterized in that its component has following weight percent: pigment 3.5~5.0%, the agent 1.0~5.0% of raising one's hat, ethanol 48.0~71.0%, propyl alcohol 15.0~25.0%, but liniment 5.0~10.0%, resin 3.5~5.0%, dispersion agent 1.0~2.0%.
Further, a kind of in black, red, blue, green four base colors of pigment of above-mentioned white board pen ink, described pigment; The described agent of raising one's hat is the how pure lipoid of long carbochain; But described liniment is long chain fatty acid fat; Described resin is polyvinyl butyral acetal (PVB); Described dispersion agent is the polymkeric substance macromolecule dispersing agent.
Again further, above-mentioned white board pen ink, its component has following weight percent: pigment 4.25%, the how pure lipoid 3.0% of long carbochain, ethanol 59.5%, propyl alcohol 20.0%, long chain fatty acid fat 7.5%, polyvinyl butyral acetal 4.25%, polymkeric substance macromolecule dispersing agent 1.5%.
Again further, the manufacture method of above-mentioned white board pen ink, it is characterized in that: earlier ethanol, propyl alcohol are added in the pre-dispersed pot, add raise one's hat agent liniment, resin, dispersion agent down successively but stir, even up to whole dissolvings, add pigment at last, after fully mixing, carried out superfine grinding then 20~30 hours, the granularity that makes granules of pigments is the nano level specification, stop to grind discharging.
Further, the manufacture method of above-mentioned white board pen ink, the particle diameter after described granules of pigments grinds is D
50=100~200 nanometers.
Further, the manufacture method of above-mentioned white board pen ink, earlier ethanol, propyl alcohol are added in the pre-dispersed pot, stir and add the how pure lipoid of long carbochain, long chain fatty acid fat, polyvinyl butyral acetal (PVB), polymkeric substance macromolecule dispersing agent down successively, even up to whole dissolvings, add pigment at last, after fully mixing, carried out superfine grinding then 25 hours, and made the granularity D of granules of pigments
50=160 nanometers stop to grind discharging.
The outstanding substantive distinguishing features and the obvious improvement of technical solution of the present invention is mainly reflected in:
1. adopt advanced " superfine grinding technology ", make the pigment particles median size reach 100~200 nanometers, method is easy, and technology is reasonable;
2. the uses advanced scientific formula all can keep low viscosity under high temperature, low temperature, normal temperature;
3. bright in colour, go out China ink evenly, write delicate and smooth, no wire drawing sense, neat in edge;
4. long-term storage steady quality, not stratified, do not precipitate, have good dispersion stabilization, still can normally write after raising one's hat 8 hours;
5. erasability is good, writes afterwards still very easily to wipe more than 30 days, and leaves no trace;
6. be adapted at writing on any smooth clean planes such as blank, glass, plastics, can mate various homemade, import rolled cores and fiber nib, effect is good.
Embodiment:
The manufacturing prescription of white board pen ink: pigment 3.5~5.0%, the agent 1.0~5.0% of raising one's hat, ethanol 48.0~71.0%, propyl alcohol 15.0~25.0%, but liniment 5.0~10.0%, resin 3.5~5.0%, dispersion agent 1.0~2.0%.A kind of in black, red, blue, green four base colors of pigment of pigment wherein; The agent of raising one's hat is the how pure lipoid of long carbochain; But liniment is long chain fatty acid fat; Resin is polyvinyl butyral acetal (PVB); Dispersion agent is the polymkeric substance macromolecule dispersing agent.
The formula optimization of ideal white board pen ink: pigment 4.25%, the how pure lipoid 3.0% of long carbochain, ethanol 59.5%, propyl alcohol 20.0%, long chain fatty acid fat 7.5%, polyvinyl butyral acetal 4.25%, polymkeric substance macromolecule dispersing agent 1.5%.
The manufacturing process of white board pen ink: earlier ethanol, propyl alcohol are added in the pre-dispersed pot, add raise one's hat agent liniment, resin, dispersion agent down successively but stir, even up to whole dissolvings, add pigment at last, after fully mixing, carried out superfine grinding then 20~30 hours, and made the granularity of granules of pigments reach D
50=100~200 nanometers stop to grind discharging.
Adopt the superfine grinding technology, make the granules of pigments median size reach 100~200 nanometers; Adopt the polymkeric substance macromolecule dispersing agent to be dissolved in fast in the solvent, obviously reduce the viscosity of dispersion system in the particulate process of lapping, improve the pigment particles wetting property, adopt the PVB resin, increase the then property of ink and blank, make write more smooth, also increased simultaneously dispersing of pigments and with the mutual solubility of other resins, improve pigment dispersion and tie up to dispersion stabilization in the long-time storage process.
Embodiment 1:
Earlier 71kg ethanol, 15kg propyl alcohol are added in the pre-dispersed pot, but stir and to add 1.0kg raise one's hat agent, 5.0kg liniment, 3.5kg resin, 1.0kg dispersion agent down successively, even up to whole dissolvings, add the 3.5kg black pigment at last, after fully mixing, carried out superfine grinding then 20 hours, the granularity that makes granules of pigments is the nano level specification, stop to grind discharging.
Embodiment 2:
Earlier 48kg ethanol, 25kg propyl alcohol are added in the pre-dispersed pot, but stir and to add 5.0kg raise one's hat agent, 10kg liniment, 5.0kg resin, 2.0kg dispersion agent down successively, even up to whole dissolvings, add the 5.0kg black pigment at last, after fully mixing, carried out superfine grinding then 30 hours, the granularity that makes granules of pigments is the nano level specification, stop to grind discharging.
Embodiment 3:
Earlier 59.5kg ethanol, 20kg propyl alcohol are added in the pre-dispersed pot, stir and add the how pure lipoid of the long carbochain of 3.0kg, the long chain fatty acid fat of 7.5kg, 4.25kg polyvinyl butyral acetal, 1.5kg polymkeric substance macromolecule dispersing agent down successively, even up to whole dissolvings, add the 4.25kg black pigment at last, after fully mixing, carried out superfine grinding then 25 hours, and made the granularity D of granules of pigments
50=160 nanometers stop to grind discharging.
Below only provide three embodiment of the white board pen ink of black pigment, and basic identical with its implementation condition of white board pen ink of red/orchid/phthalocyanine, no longer repeat.
After testing, the various inks that adopt technical solution of the present invention to obtain, its Main physical performance index see Table 1.
Table 1
Color | Black | Red | Blue | Green |
Granularity (D50) (nm) | 100~200 | 100~200 | 100~200 | 100~200 |
Viscosity (cps) | 5.5~14.0 | 5.5~14.0 | 5.5~14.0 | 5.5~14.0 |
Surface tension (d/cm) | 20~32 | 20~32 | 20~32 | 20~32 |
PH value | 3.0~5.0 | 3.0~5.0 | 3.0~5.0 | 3.0~5.0 |
Time of drying (blank) | <30s | <30s | <30s | <30s |
Proportion (g/cm 3) | 0.83~0.85 | 0.83~0.85 | 0.83~0.85 | 0.83~0.85 |
Erasability | Fabulous, the no vestige in wiping back | Fabulous, the no vestige in wiping back | Fabulous, the no vestige in wiping back | Fabulous, the no vestige in wiping back |
Ink smell gentleness of the present invention, by EN-71.3 and ASTMD-4236 authentication.Adopt advanced " superfine grinding technology ", make the pigment particles median size reach 100~200 nanometers, method is easy, and technology is reasonable; The uses advanced scientific formula all can keep low viscosity under high temperature, low temperature, normal temperature; Bright in colour, go out China ink evenly, write delicate and smooth, no wire drawing sense, neat in edge; The long-term storage steady quality, not stratified, do not precipitate, have good dispersion stabilization; Reach 8 hours after raising one's hat and still can normally write; Erasability is good, writes afterwards still very easily to wipe more than 30 days, and leaves no trace; Be adapted at writing on any clean planes such as blank, glass, plastics, can mate various homemade, import rolled cores and fiber nib.
More than specifically described the application example of technical solution of the present invention, they only provide as an example, are not considered as application limitations of the present invention.All operational conditions be equal to replacement, all drop within protection scope of the present invention.
Claims (10)
1. white board pen ink, it is characterized in that: the component and the weight percent of this ink are pigment 3.5~5.0%, the agent 1.0~5.0% of raising one's hat, ethanol 48.0~71.0%, propyl alcohol 15.0~25.0%, but liniment 5.0~10.0%, resin 3.5~5.0%, dispersion agent 1.0~2.0%.
2. white board pen ink according to claim 1 is characterized in that: a kind of in black, red, blue, green four base colors of pigment of described pigment.
3. white board pen ink according to claim 1 is characterized in that: the described agent of raising one's hat is the how pure lipoid of long carbochain.
4. white board pen ink according to claim 1 is characterized in that: described resin is a polyvinyl butyral acetal.
5. white board pen ink according to claim 1 is characterized in that: but described liniment is long chain fatty acid fat.
6. white board pen ink according to claim 1 is characterized in that: described dispersion agent is the polymkeric substance macromolecule dispersing agent.
7. white board pen ink according to claim 1, it is characterized in that: the component and the weight percent of this ink are pigment 4.25%, the how pure lipoid 3.0% of long carbochain, ethanol 59.5%, propyl alcohol 20.0%, long chain fatty acid fat 7.5%, polyvinyl butyral acetal 4.25%, polymkeric substance macromolecule dispersing agent 1.5%.
8. make the method for the described white board pen ink of claim 1, it is characterized in that: earlier ethanol, propyl alcohol are added in the pre-dispersed pot, add raise one's hat agent liniment, resin, dispersion agent down successively but stir, even up to whole dissolvings, add pigment at last, after fully mixing, carried out superfine grinding then 20~30 hours, making the granularity of granules of pigments is the nano level specification, stops to grind discharging.
9. the manufacture method of white board pen ink according to claim 8 is characterized in that: the particle diameter after described granules of pigments grinds is D
50=100~200 nanometers.
10. the manufacture method of white board pen ink according to claim 8, it is characterized in that: earlier ethanol, propyl alcohol are added in the pre-dispersed pot, stir and add the how pure lipoid of long carbochain, long chain fatty acid fat, polyvinyl butyral acetal, polymkeric substance macromolecule dispersing agent down successively, even up to whole dissolvings, add pigment at last, after fully mixing, carried out superfine grinding then 25 hours, make the granularity D of granules of pigments
50=160 nanometers stop to grind discharging.