CN1962257A - NbTiAl series laminate structure intermetallic compound composite material and its preparation method - Google Patents
NbTiAl series laminate structure intermetallic compound composite material and its preparation method Download PDFInfo
- Publication number
- CN1962257A CN1962257A CN 200610164922 CN200610164922A CN1962257A CN 1962257 A CN1962257 A CN 1962257A CN 200610164922 CN200610164922 CN 200610164922 CN 200610164922 A CN200610164922 A CN 200610164922A CN 1962257 A CN1962257 A CN 1962257A
- Authority
- CN
- China
- Prior art keywords
- layer
- nbtial
- intermetallic compound
- composite material
- alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a laminated metal composite of NbTiAl group, and relative production, wherein said composite is formed by one layer of Nb group flexible metal alloy layer, above one layer of Nb group metal compound, and above one layer of Nb group flexible metal alloy. The invention is made from laser deposition method, while the metal compound layer is directly composed on the flexible metal alloy layer via said method; the flexible metal layer and metal compound layer are smelt, while their thickness and ratio can be controlled. The invention has high flexibility in room temperature and high temperature.
Description
Technical field
The present invention relates to a kind of laminated construction high temperature NbTiAl series intermetallic compound composite, belong to the intermetallic compound based composite material field.
Background of invention
Intermetallic compound has architectural characteristic, good high-temperature intensity and non-oxidizability, high specific strength, high-melting-point, high thermal conductivity, the low heat expansion coefficient of long-range order, is a kind of desirable, high-temperature structural material that good potential using value is arranged.But architectural features such as the slip system deficiency of intermetallic compound, sliding vector be big, hand over that slippage is limited, crystal boundary slippage difficulty and crystal boundary hydrogen embrittlement cause its very big room temperature fragility, high brittle-ductile transition temperature and the very poor characteristic that shapes, and make its difficulty that practical application be arranged.Compound-material is its development trend between research and development room temperature toughness, elevated temperature strength/creep resistant combination property good metal.
The main method of intermetallic compound malleablization has element alloyed and complex technique.Element alloyedly mainly improve the crystal boundary bond strength, suppress polycrystalline fragility intercrystalline fracture, improve room temperature toughness by the optimization of microstructure by adding trace element.Composite toughening mainly improves toughness by fiber, particle, structure optimization such as stacked.Patent 200310115547.8 has proposed the new method of a kind of laser synthetic preparation intermetallic compound and particulate reinforced composite.With respect to toughness reinforcing modes such as fiber, particles, stepped construction can play more effectively composite toughening effect.The stepped construction material is the multilayer material that two kinds of different materials are formed in certain interlamellar spacing and bed thickness ratio intermeshing, fragility when unique stepped construction can make some hard brittle materials overcome monomer, possess superior anti-fracture, shock resistance, when keeping high strength, high antioxidant, might increase substantially the toughness and the reliability of material.
Several stepped construction inter-metallic compound materials of existing bibliographical information are from spreading method preparations such as hot forming or plasma powder sintering by magnetron sputtering, vapour deposition, thin plate.Between these lamination metals the common trait of compound-material be between the lamination for non-metallurgical binding, interfacial bonding strength a little less than, laminated thickness and bed thickness ratio are difficult to flexible variation, thereby the room temperature yield strength and the fracture toughness of compound-material is lower between these lamination metals.
Summary of the invention
The object of the present invention is to provide a kind of NbTiAl is laminated construction intermetallic compound composite material and preparation method thereof, it is very high promptly to prepare a kind of interfacial bonding strength, have good room temperature obdurability and high-temperature behavior, the bed thickness of ductile metal layer and intermetallic compounds layer and bed thickness are the laminated construction intermetallic compound composite material than NbTiAl that can odd jobs control, to adapt to the needs of this composite in high-tech sectors such as Aeronautics and Astronautics, the energy and military projects.
Technical scheme of the present invention is as follows:
A kind of NbTiAl is the laminated construction intermetallic compound composite material, it is characterized in that: this intermetallic compound composite material alternately is formed by stacking by one deck NbTiAl ductile metal alloy-layer and one deck Nb3Al intermetallic compound successively, is metallurgical binding between described ductile metal alloy-layer and the intermetallic compounds layer.
NbTiAl of the present invention is the laminated construction intermetallic compound composite material, it is characterized in that: described NbTiAl ductile metal alloy-layer is β/B2 structure, described Nb
3The Al intermetallic compound is the A15 structure.
NbTiAl of the present invention is the laminated construction intermetallic compound composite material, it is characterized in that: intermetallic compounds layer is 1: 5~2: 1 with the bed thickness ratio of ductile metal alloy-layer.The thickness of described ductile metal alloy-layer is for being preferably 0.1~3mm, and the thickness of intermetallic compounds layer is preferably 0.1~1.5mm.
The invention provides a kind of method that described NbTiAl is the laminated construction intermetallic compound composite material for preparing, it is characterized in that this method carries out as follows:
1) is base material with the Ti6Al4V alloy sheets, puts into the inert gas shielding chamber after cleaning up;
2) adopting pure Nb, pure Al, pure Ti element powders is raw material, prepares NbTiAl ductile metal alloy and Nb respectively by atomic percent
3The mixed-powder of Al intermetallic compound;
3) adopt the inert gas shielding chamber, the inert gas shielding chamber is vacuumized, charge into Ar gas again and form the protective gas atmosphere, in laser deposition process, replenish Ar gas always and form the positive pressure protection environment;
4) adopt high power CO
2Laser, the irradiation substrate material surface forms local molten bath; Adopt powder-feeding method that the toughness mixed powder for alloy is sent into the molten bath, the metallurgical deposition of the Chemical Physics in the molten bath forms the toughness NbTiAl alloy-layer of β/B2 structure:
5) on toughness NbTiAl alloy-layer, use high power CO
2Laser, irradiation form local molten bath, with powder-feeding method intermetallic compound powder are sent into the molten bath, utilize Physical Metallurgy and chemical metallurgy in the molten bath to react the Nb that forms the A15 structure
3The Al intermetallic compound coating; Intermetallic compounds layer is 1: 5~2: 1 with the bed thickness ratio of ductile metal alloy-layer;
6) repeat 4), 5) step, alternately stack, layer by layer deposition obtains the intermetallic compound composite material that NbTiAl is a laminated construction.
The present invention compared with prior art, having the following advantages is the high-lighting effect: NbTiAl provided by the invention is the laminated construction intermetallic compound composite material, by one deck toughness NbTiAl alloy-layer, on it the stack Nb
3The Al intermetallic compound, one deck ductile metal alloy-layer that superposes again on it, so alternately stack and forming.Between ductile metal alloy-layer and the Nb series intermetallic compound layer is metallurgical binding, interfacial bonding strength is very high, has good room temperature obdurability and high-temperature behavior, and its room temperature yield strength reaches 1000MPa, 900 ℃ of high-temperature yield strengths reach 300MPa, and fracture toughness can reach 30MPa
, this material has broad application prospects in high-tech sectors such as Aeronautics and Astronautics, the energy and military projects.This composite is prepared by laser deposition technique, has very big design flexibility, its composition, microstructure, bed thickness can accurately design and realize, ductile metal layer can odd jobs be controlled with the bed thickness and the bed thickness ratio of intermetallic compounds layer, not only can realize the uniform quality material of composition, can also realize heterogeneous materials such as function-graded material.Can solve the black brittleness of inter-metallic compound material and the contradiction between the elevated temperature strength preferably, have the advantage that obviously is different from laminated material.
Description of drawings
Fig. 1 is laminated construction Nb
3The macrostructure of Al/NbTiAl intermetallic compound composite material.
Fig. 2 is laminated construction Nb
3Nb in the Al/NbTiAl intermetallic compound composite material
3The microstructure of Al intermetallic compounds layer.
Fig. 3 laminated construction Nb
3The microstructure of NbTiAl ductile layers in the Al/NbTiAl intermetallic compound composite material.
Fig. 4 is Nb
3Metallurgical bonding interface between Al intermetallic compounds layer and the NbTiAl toughness alloy-layer
The specific embodiment
The Nb series intermetallic compound is with the Nb of the A15 structure that contains the NbTiAl composition in the intermetallic composite of the present invention
3The Al intermetallic compound is main, particularly contains the intermetallic compound of Nb12Ti22Al, also comprises the Nb of 15 structures that contain the NbAl composition
3The Al intermetallic compound;
The ductile metal alloy is based on the niobium titanium solid solution alloy, particularly Nb40Ti15Al alloy of β/B2 structure in the intermetallic composite of the present invention;
Fig. 1 illustrates laminated construction Nb
3The macrostructure of Al/NbTiAl intermetallic compound composite material, this composite is the Nb that is gone up stack layer of brittle A15 structure by the NbTiAl toughness alloy-layer of one deck β/B2 structure (dark layer among Fig. 1, microstructure such as Fig. 3)
3Al intermetallic compounds layer (bleached bed among Fig. 1, microstructure such as Fig. 2), the NbTiAl toughness alloy-layer of one deck β/B2 structure that superposes again, the laminated construction Nb that alternately is formed by stacking
3The Al/NbTiAl intermetallic compound composite material, Nb
3Realize metallurgical binding (Fig. 4) between Al intermetallic compounds layer and NbTiAl toughness alloy-layer.Intermetallic compounds layer is 1: 5~2: 1 with the bed thickness ratio of ductile metal alloy-layer.The thickness of described ductile metal alloy-layer is preferably 0.1~3mm, and the thickness of intermetallic compounds layer is preferably 0.1~1.5mm.
Laminated construction Nb of the present invention
3The Al/NbTiAl intermetallic compound composite material is prepared by laser deposition technique.Laser deposition is to utilize the high power focused laser beam irradiation metallic substrate surface of certain power density scope to form local molten bath, by powder feed system the alloy powder of the required composition of certain powder feeding rate scope is sent into the molten bath simultaneously, deposition formation single track alloy-layer is solidified in fusing under laser action; Laterally the multi-track overlapping deposition forms the larger area flexible coating by a certain percentage, and control laser power density, sweep speed and powder feeding rate obtain certain thickness coating, can obtain different bed thickness by the multilayer deposition.By the laminated material of laser deposition method preparation, can realize metallurgical binding completely between its lamination, each laminated thickness and bed thickness ratio can odd jobs be controlled, the laminated composite materials that obtained performance changes.
Laminated construction Nb of the present invention
3The detailed preparation process of Al/NbTiAl intermetallic compound composite material is as follows:
(1) choose the Ti6Al4V alloy sheets as base material, thickness of slab 2mm, size can be 50mm * 50mm, and the surface cleans up with acetone and alcoholic solution, and blowing is dry, puts into the inert gas shielding chamber;
(2) adopting pure Nb, pure Al, pure Ti element powders is raw material, according to the atomic percent proportioning of Nb40Ti15Al with preparation NbTiAl toughness alloy, according to the atomic percent preparation Nb of Nb12Ti22Al
3The Al intermetallic compound; Powder size is-150 orders~+ 250 orders.Above-mentioned powder mixes through mechanical agitation, and moisture was removed in insulation in 1 hour in 100 ℃ vacuum drying oven;
(3) adopt the inert gas shielding chamber, the inert gas shielding chamber is vacuumized, charge into Ar gas again and form the protective gas atmosphere, in laser deposition process, replenish Ar gas always and form the positive pressure protection environment;
(4) adopt high power CO
2Laser, laser power 2500W is focused into the hot spot that diameter is 3mm, and with the sweep speed of 0.3m/min, irradiation Ti-6Al-4V substrate material surface forms local molten bath; Adopt powder-feeding method that the Nb40Ti15Al mixed-powder is sent into the molten bath, the powder quality flow rate is 30g/min, make the mixed-powder carrier gas with He gas, gas flow is 3L/min, the metallurgical deposition of Chemical Physics in the molten bath forms single track B/B2 structure toughness NbTiAl layer, and the overlapping rate lateral deposition with 50% forms the toughness NbTiAl alloy-layer of larger area β/B2 structure; Bed thickness is 0.7mm;
(4) on Nb40Ti15Al toughness alloy-layer, use high power CO
2Laser, laser power 2500W, be focused into the hot spot that diameter is 3mm, form local molten bath with O.3m/min sweep speed irradiation, to send into the molten bath by the Nb12Ti22Al powder with powder-feeding method, the powder quality flow rate is 35g/min, makes the mixed-powder carrier gas with He gas, gas flow is 3.5L/min, utilizes Physical Metallurgy and chemical metallurgy reaction in the molten bath to form single track Nb
3The Al intermetallic compounds layer; Form larger area Nb with the horizontal multi-track overlapping deposition of 50% overlapping rate
3The Al intermetallic compound coating; Bed thickness is 0.5mm
(5) at Nb
3Use high power CO on the Al intermetallic compound coating
2Laser, laser power 2500W is focused into the hot spot that diameter is 3mm, and with the sweep speed of 0.3m/min, irradiation forms local molten bath; Adopt powder-feeding method that the Nb40Ti15Al mixed-powder is sent into the molten bath, the powder quality flow rate is 30g/min, make the mixed-powder carrier gas with He gas, gas flow is 3L/min, the metallurgical deposition of Chemical Physics in the molten bath forms single track β/B2 structure toughness NbTiAl layer, and the overlapping rate lateral deposition with 50% forms the toughness NbTiAl coating of larger area β/B2 structure; Bed thickness is 0.7mm
(6) repeat (4), (5) step, alternately stack, layer by layer deposition can obtain laminated construction Nb
3The Al/NbTiAl intermetallic compound composite material, intermetallic compound and toughness alloy-layer thickness rate are 0.7mm.
After tested, the average microhardness of B2 structure Nb40Ti15Al toughness alloy-layer is HV
0.2450, the room temperature compressive strength reaches 691Mpa, and 900 ℃ of high temperature compressed intensity are 67MPa.The Nb12Ti22Al composition Nb of A15 structure
3The average microhardness of Al intermetallic compounds layer is HV
0.21020,900 ℃ of elevated temperature strengths reach 470MPa.The Nb of laminated construction
3The room temperature compression yield strength of Al/NbTiAl intermetallic compound composite material reaches 1030MPa, and 900 ℃ of high temperature compressed yield strengths are 301MPa.The Nb of laminated construction
3The fracture toughness of Al/NbTiAl intermetallic compound composite material reaches 30MPa
Claims (5)
1. a NbTiAl is the laminated construction intermetallic compound composite material, it is characterized in that: this intermetallic compound composite material is successively by one deck NbTiAl ductile metal alloy-layer and one deck Nb
3The Al intermetallic compound alternately is formed by stacking, and is metallurgical binding between described ductile metal alloy-layer and the intermetallic compounds layer.
2. be the laminated construction intermetallic compound composite material according to the described NbTiAl of claim 1, it is characterized in that: described NbTiAl ductile metal alloy-layer is β/B2 structure, described Nb
3The Al intermetallic compound is the A15 structure.
3. be the laminated construction intermetallic compound composite material according to claim 1 or 2 described NbTiAl, it is characterized in that: intermetallic compounds layer is 1: 5~2: 1 with the bed thickness ratio of ductile metal alloy-layer.
4. be the laminated construction intermetallic compound composite material according to the described NbTiAl of claim 3, it is characterized in that: the thickness of described ductile metal alloy-layer is 0.1~3mm, and the thickness of intermetallic compounds layer is 0.1~1.5mm.
5. one kind prepares according to claim 1 that NbTiAl is the method for laminated construction intermetallic compound composite material, it is characterized in that this method carries out as follows:
1) is base material with the Ti6A14V alloy sheets, puts into the inert gas shielding chamber after cleaning up;
2) adopting pure Nb, pure Al, pure Ti element powders is raw material, prepares NbTiAl ductile metal alloy and Nb respectively by atomic percent
3The mixed-powder of Al intermetallic compound;
3) adopt the inert gas shielding chamber, the inert gas shielding chamber is vacuumized, charge into Ar gas again and form the protective gas atmosphere, in laser deposition process, replenish Ar gas always and form the positive pressure protection environment;
4) adopt high power CO
2Laser, the irradiation substrate material surface forms local molten bath; Adopt powder-feeding method that the toughness mixed powder for alloy is sent into the molten bath, the metallurgical deposition of the Chemical Physics in the molten bath forms the toughness NbTiAl alloy-layer of β/B2 structure;
5) on toughness NbTiAl alloy-layer, use high power CO
2Laser, irradiation form local molten bath, with powder-feeding method intermetallic compound powder are sent into the molten bath, utilize Physical Metallurgy and chemical metallurgy in the molten bath to react the Nb that forms the A15 structure
3The Al intermetallic compound coating; Intermetallic compounds layer is 1: 5~2: 1 with the bed thickness ratio of ductile metal alloy-layer;
6) repeat 4), 5) step, alternately stack, layer by layer deposition obtains the intermetallic compound composite material that NbTiAl is a laminated construction.