CN1947802A - Slow release type testis prosthesis and its application - Google Patents
Slow release type testis prosthesis and its application Download PDFInfo
- Publication number
- CN1947802A CN1947802A CN 200610117622 CN200610117622A CN1947802A CN 1947802 A CN1947802 A CN 1947802A CN 200610117622 CN200610117622 CN 200610117622 CN 200610117622 A CN200610117622 A CN 200610117622A CN 1947802 A CN1947802 A CN 1947802A
- Authority
- CN
- China
- Prior art keywords
- silicone rubber
- slow
- androgen
- releasing
- medicine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A slow-release artificial testis for slowly releasing androgen is prepared from silicon rubber and testosterone in weight ratio of (2-4):1. It can be used to replace human testis for androgen therapy.
Description
Technical field
The present invention relates to a kind of prosthese, specifically about a kind of slow-releasing testicular prosthesis and application thereof.
Background technology
Absence of testis and male castration are concerning the patient, be not only the forfeiture of organ, also can produce psychological defective, a lot of patients can pass through or wish by selecting ectogenic testis substitute---testicular prosthesis (testicular prosthesis, false testis, artificial testis) remedy on this health and psychological loss, testicular prosthesis treatment commonly used clinically at present, though be a kind of alternative to male gonad shaping in appearance, and the physiological function of anorchia (endocrine and spermatogenesis), but it but is that androgen treatment institute is irreplaceable to the patient in the effect aspect the mental health.
Testicular prosthesis is the synthetic of a kind of outer appearnce like testis, has experienced in development from the inorganic material goods to the organic compound Tetramune, by the process of low molecular material to macromolecular material.The evolution of testicular prosthesis is inseparable with modern biomaterial for medical purpose progress of research.Early stage testicular prosthesis adopts alloy, pottery, organic plastics etc. as prosthetic material, because the defective of aspects such as its texture, weight, toxicity and histocompatibility, be eliminated gradually now, the substitute is the organosilicon material that nineteen forties puts goods on the market.
Silicone rubber is one of main member of organosilicon family, it is most popular novel high polymer synthetic material in organ prosthese and the tissue substitute clinically at present, compare with early stage prosthetic material, silicone rubber has possessed many requisite advantages on the organism that are applied in:
1, chemical inertness and physiology inertia: silastic material is having advantages of higher stability aspect chemistry and the physiology, after implanting, body fluid can not make the characteristic of its this respect change, body can not implanted the variation that blood and tissue fluid composition take place because of prosthese yet simultaneously, no foreign body surface blood agglutination.
2, histocompatibility: remove the influence of infective agent, organize not and can demonstrate the favorable tissue compatibility to silica gel prosthese be inflamed reaction, anaphylaxis and foreign body rejection.
3, non-carcinogenesis: silicone rubber be applied to the clinical history that has had more than 40 year, and its whole history as biomaterial for medical purpose has exceeded over half a century as bioprosthetic material, but does not still have silicone rubber and carcinogenic definite relevant report so far.
4, physical and mechanical properties is stable: silastic material implants for a long time, and its tensile strength, elasticity etc. can not be lost or minimum forfeiture only arranged, and aspect clinical practices such as shaping, orthopedic and beauty treatment, has the characteristics of appearance stablity, can not be out of shape.
5, adaptive temperature scope wide (60 ℃～+ 200 ℃): heat-resisting, cold-resistant, can stand necessary disinfectant measure.
6, processing and moulding are easy: can be processed into the outward appearance and the form of various complexity according to the specific requirement of clinical treatment and scientific research, to satisfy the actual needs of different operating.
7, avirulence.
8, tool physiology inertia, anti-biological aging.
The above-mentioned advantage of silicone rubber makes it become in the medical macromolecular materials the most the typical case, also be to use maximum organosilicon macromolecule materials, obtains application more and more widely aspect clinical treatment, medical research.
Now generally adopt the material of silicone rubber clinically as testicular prosthesis, clinically use and improve through secular, develop series of products, comprised the solid-state compression moulding testicular prosthesis of silicone rubber, and liquid (normal saline of gelatinous silica gel or liquid) filling testicular prosthesis.On concrete the selection, can be according to the different development conditions of individuality, individual preference to the testis quality is selected different sizes for use, dissimilar testicular prosthesises, or change prosthese (as individual growth) according to practical situation, satisfy patient's requirement.
Silastic material is except the advantage of being addressed above having, also has unique Penetration Signature to gas and solution, make thin film and can be widely used in and make permeable membrane on the medical apparatus and instruments, in medical treatment, also can be used as the medicine controlled release carrier material of some implant into body.
Nineteen fifty-seven, silastic material began the lapping as the sustained release medicine.Folkman in 1964 and Long have proved that at first medicine can slowly release in the silicone rubber tube of sealing, keep certain drug level in the quite a long time in vivo.Along with scientific research personnel's continuous research with grope, it is found that silicone rubber has good penetration and permeability, make it become ideal medicament slow release material, thereby make it become the simple pathway that solves this problem.Medicine has utilized this specific character of silicone rubber just, sees through silicone rubber and carries out effective sustained release and slowly diffusion.
Utilize silicone rubber to come the mode of control drug release to mainly contain two kinds: (1) lock-in type, promptly with medicine as core, the external silicon rubber film is sealed.This medicine carrying mode is equivalent to " warehouse " of macromolecule membrane vesicle as medicine, therefore also claims bank agent or film preparation.(2) microdispersed form, promptly in the substrate of silicone rubber, its drug releasing rate diminishes with the growth of release time medicine with microparticulate, but its manufacturing is fairly simple, as long as medicine and silicone rubber mixing, molding.
Now, utilize the silicone rubber biomaterial to be applied in contraceptive and the anticarcinogen for the controllable sustained-release agent of substrate, and obtain good effect, this delivery system also is used for the sustained release of other many medicines and domestic animal growth hormone, as promoting the hormone hormone preparation of Niu Shengchang.In male testical forfeiture and the low androgen replacement therapy of gonad function, be that the controllable sustained-release preparation such as the slow-releasing androgen preparation capable of permeating skin of substrate also begins to apply clinically with silicone rubber, as gel card film.But also do not have in the market to discharge androgen, can satisfy the testicular prosthesis of patient's needs aspect mental health again.
Summary of the invention
The objective of the invention is to:
(1) provides a kind of and can discharge androgen, can satisfy the testicular prosthesis of patient's needs aspect mental health again.
(2) provide the application of a kind of testicular prosthesis in the slow-release medicine of preparation treatment absence of testis disease.
The objective of the invention is to realize by following technical method:
A kind of slow-releasing testicular prosthesis is made up of silicone rubber, androgen, and silicone rubber, androgen weight ratio are: 2: 1-4: 1.Androgen is selected from testosterone or testosterone undecanoate or dihydrotestosterone.Androgen is a testosterone.Silicone rubber, androgen weight ratio are: 2.5: 1-3.5: 1.Silicone rubber, androgen weight ratio can for: 3: 1.The application of slow-releasing testicular prosthesis in the slow-release medicine of preparation treatment absence of testis disease.
The present invention mixes androgen raw material medicine mutually with silicone rubber, and mold pressing is made and contained androgenic slow-releasing testicular prosthesis.This prosthese belongs to the homogeneous phase slow-releasing system of drug microparticles decentralized, and the rate of releasing drug under its perfect condition (solid-liquid interface) can be used the Noyes-Whithey The Representation Equation:
dc/dt＝k
DA(c
a-c
t)
Wherein dc/dt is the release rate of medicine, and A is effective release surface area, k
DBe medicine dissolution rate constant, c
aBe medicine concentration when saturated, c
tBe Periprosthetic medium Chinese medicine concentration when the time t.In prosthese, there is solid drugs, then c
a＞＞c
t, false intravital solid drugs can carry out zero-order release by dissolving, and the rate of releasing drug that draws prosthese this moment thus is relevant with effective release surface area of its medicament contg and prosthese.
Yet, slow-releasing testicular prosthesis among the present invention is not to be in perfect condition (solid-liquid interface) to carry out release in actual applications, medicine androgen in the while prosthese is water-insoluble medicine also, but fat-soluble steroidal steroid hormone preparation, comparatively complicated in in-house diffusion process, (in prosthese, there is solid drugs, c during high concentration
a＞＞c
tThe time) saturated phenomenon may appear, improve medicament contg can't make the testosterone release rate what increase in the prosthese this moment, and in this state, effectively release surface area A variation can become the influence factor that prosthese testosterone release rate is had decisive action.
This release control action of this prosthese conforms to maturation process with organism growing development, and the androgen level all is different in preadolescence and the postpubertal animals and human beings, its testis size and body.At preadolescence, testis is less, and androgen is in low-level, and after adolescing, testicular volume increases rapidly, the also corresponding rising of androgen level.Therefore on prosthese is selected, can pass through little prosthese, little release surface area provides the testosterone of low release rate, to satisfy prepuberal needs, and for postpubertal animal or patient, by selecting for use big testicular prosthesis obtaining bigger release area, thereby increase the medicine release rate of testosterone in the prosthese, required for body.This illustrates the reasonability of slow-releasing testicular prosthesis in concrete application the in this research, this reasonability not only is embodied in the prosthese size can be needed consistent with body, be also embodied in prosthese rate of releasing drug can with body need consistent, and the adjusting of rate of releasing drug exactly the size of testicular prosthesis be directly proportional.
Disclosed slow-releasing testicular prosthesis of the present invention and application thereof, its advantage shows: the present invention is by combining silastic material with testosterone, the testicular prosthesis that preparation has the androgen slow-release capability, thus the treatment that the replacement therapy and the androgen of testicular prosthesis are treated these two aspects is united effectively.Effective release surface area of prosthese has determined its rate of releasing drug, and the two can be united harmoniously with the needs (apparent size, hormonal readiness) of individuality.Therefore, this silica gel testicular prosthesis with slow-release function has very big potentiality in the clinical practice afterwards.
Description of drawings
Fig. 1: slow-releasing testicular prosthesis outward appearance pictorial diagram of the present invention (macropinacoid view, major diameter 2.5cm)
Fig. 2: slow-releasing testicular prosthesis outward appearance pictorial diagram of the present invention (brchypinacoid view, minor axis 2.0cm)
The specific embodiment
Below in conjunction with embodiment the present invention is further described.
Embodiment 1
The slow-releasing testicular prosthesis preparation
One. medicine and preparation:
1, androgen: testosterone crude drug (Zhejiang celestial jade pendant raw material pharmaceutical factory supply).
2, silicone rubber compounds: purchase in Shanghai Rubber Products Insitute.The silicone rubber that the present invention selects for use is two-component room-temperature-vulcanized silicone rubber, before not vulcanizing, divide two components of A, B to exist, wherein contain catalyst in the A component, contain cross-linking agent in the B component, both do not react mutually at ordinary times, mix because of catalyst and cross-linking agent after mutual blend, can carry out polyreaction.
Two. equipment
1, pressure forming machine:
Product type: XLB-D400-400
Working fluid pressure: 19.6MPa
Gross pressure: 500kN
Range: 250mm
Manufacturer: east, Huzhou, Chinese Zhejiang machinery company limited manufacturing.
2, rubber mixing machine
Model: JTC-752A
Pattern: open
Specification: φ 160*320
Friction ration: 1: 1.22
Power: 7kw
Cylinder preliminary roller speed: 22.09 rev/mins
Roller rotating speed behind the cylinder: 27 rev/mins
Maximum feeding quantity: 2kg
Net weight: 1100kg
Manufacturer: Zhanjiang Machine Factory, Guangdong Prov.
3, electronic platform scale
Model: TSC-6
Maximum capacity: 6kg
Minimum weighing: 0.04kg
Calibrating scale division value: 2g/5g
Power supply: 9VDC/200mA
Manufacturer: METTLER-TOLERDO (Changzhou) weighing equipment System Co., Ltd
4, electric drying oven with forced convection
Model: 101A-1B
Maximum operating temperature: 300 ℃
Rated power: 5kw
Rated voltage: 200V
Manufacturer: Shanghai experimental apparatus Co., Ltd., Factory
5, drying baker
Model: 101-3 type
Maximum temperature: 300 ℃
Thermostat sensitivity: ± 1 ℃
Voltage: 220V
Operating room's size: 50*60*75cm
Heating power: 6.6kw
Manufacturer: Shanghai experimental apparatus factory
6, three-roll grinder
Model: SG-150 type
Manufacturer: the good mechanical company limited of Qinhuangdao gold
7, the display instrument of weighing
Model: XK3130
Specification: KTGN-1000-023
Power supply: 220VAC/50Hz
Electric current: 60Ma
Manufacturer: METTLER TOLEDOC (Changzhou) Weight Equipment System Co., Ltd
Three. the preparation of silica gel prosthese:
1, the mould design: the Half mould, for being spheroid (olive shape spheroid) design in axle center with the major diameter, its major diameter is 2.5cm by profile, minor axis is 2.0cm.
2, take by weighing silicone rubber compounds 100g.
Take by weighing testosterone 25g.
Two kinds of raw materials are put into the rubber mixing machine blend, make sizing material and medicine mixing even, draw thin-pass 10 times, medicine more is evenly dispersed in the sizing material.
Blanking, take by weighing the 7.5g material, put into the mould mold pressing
140 ℃ of temperature, time 12min, pressure 9.5MPa
Depanning is taken out product, deburring.
Encapsulation, ethylene oxide gas sterilization back is standby.
Embodiment 2
The slow-releasing testicular prosthesis preparation
One. medicine and preparation:
1, androgen: testosterone crude drug (Zhejiang celestial jade pendant raw material pharmaceutical factory supply).
2, silicone rubber compounds: purchase in Shanghai Rubber Products Insitute.The silicone rubber that the present invention selects for use is two-component room-temperature-vulcanized silicone rubber, before not vulcanizing, divide two components of A, B to exist, wherein contain catalyst in the A component, contain cross-linking agent in the B component, both do not react mutually at ordinary times, mix because of catalyst and cross-linking agent after mutual blend, can carry out polyreaction.
Two. equipment
Equipment with embodiment 1
Three. the preparation of silica gel prosthese:
1, the mould design: the Half mould, for being spheroid (olive shape spheroid) design in axle center with the major diameter, its major diameter is 2.5cm by profile, minor axis is 2.0cm.
2, take by weighing liquid silastic 100g
Take by weighing testosterone 50g
Put into three-roll grinder and grind, make liquid sizing material and medicated powder mixing, until, the viscosity of whole material system increases, blanking.
Take by weighing 9 gram sizing materials, put into the mould mold pressing
150 ℃ of temperature, time 20min, pressure 10MPa
Membrane takes out product, deburring
Encapsulation, ethylene oxide gas sterilization back is standby.
Embodiment 3
The slow-releasing testicular prosthesis preparation
One. medicine and preparation:
1, androgen: testosterone crude drug (Zhejiang celestial jade pendant raw material pharmaceutical factory supply).
2, silicone rubber compounds: purchase in Shanghai Rubber Products Insitute.The silicone rubber that the present invention selects for use is two-component room-temperature-vulcanized silicone rubber, before not vulcanizing, divide two components of A, B to exist, wherein contain catalyst in the A component, contain cross-linking agent in the B component, both do not react mutually at ordinary times, mix because of catalyst and cross-linking agent after mutual blend, can carry out polyreaction.
Two. equipment
Equipment with embodiment 1
Three. the preparation of silica gel prosthese:
1, the mould design: the Half mould, for being spheroid (olive shape spheroid) design in axle center with the major diameter, its major diameter is 2.5cm by profile, minor axis is 2.0cm.
2, take by weighing silicone rubber compounds 100g.
Take by weighing testosterone 33g.
Two kinds of raw materials are put into the rubber mixing machine blend, make sizing material and medicine mixing even, draw thin-pass 10 times, medicine more is evenly dispersed in the sizing material.
Blanking, take by weighing the 7.5g material, put into the mould mold pressing
130 ℃ of temperature, time 15min, pressure 8MPa
Depanning is taken out product, deburring.
Encapsulation, ethylene oxide gas sterilization back is standby.
Embodiment 4
The slow-releasing testicular prosthesis preparation
One. medicine and preparation:
1, androgen: testosterone undecanoate crude drug (Zhejiang celestial jade pendant raw material pharmaceutical factory supply).
2, silicone rubber compounds: purchase in Shanghai Rubber Products Insitute.The silicone rubber that the present invention selects for use is two-component room-temperature-vulcanized silicone rubber, before not vulcanizing, divide two components of A, B to exist, wherein contain catalyst in the A component, contain cross-linking agent in the B component, both do not react mutually at ordinary times, mix because of catalyst and cross-linking agent after mutual blend, can carry out polyreaction.
Two. equipment
Equipment with embodiment 1
Three. the preparation of silica gel prosthese:
1, the mould design: the Half mould, for being spheroid (olive shape spheroid) design in axle center with the major diameter, its major diameter is 2.5cm by profile, minor axis is 2.0cm.
2, take by weighing silicone rubber compounds 100g.
Take by weighing testosterone undecanoate 50g.
Two kinds of raw materials are put into the rubber mixing machine blend, make sizing material and medicine mixing even, draw thin-pass 10 times, medicine more is evenly dispersed in the sizing material.
Blanking, take by weighing the 7.5g material, put into the mould mold pressing
130 ℃ of temperature, time 10min, pressure 8MPa
Depanning is taken out product, deburring.
Encapsulation, ethylene oxide gas sterilization back is standby.
Embodiment 5
The slow-releasing testicular prosthesis preparation
One. medicine and preparation:
1, androgen: testosterone undecanoate crude drug (Zhejiang celestial jade pendant raw material pharmaceutical factory supply).
2, silicone rubber compounds: purchase in Shanghai Rubber Products Insitute.The silicone rubber that the present invention selects for use is two-component room-temperature-vulcanized silicone rubber, before not vulcanizing, divide two components of A, B to exist, wherein contain catalyst in the A component, contain cross-linking agent in the B component, both do not react mutually at ordinary times, mix because of catalyst and cross-linking agent after mutual blend, can carry out polyreaction.
Two. equipment
Equipment with embodiment 1
Three. the preparation of silica gel prosthese:
1, the mould design: the Half mould, for being spheroid (olive shape spheroid) design in axle center with the major diameter, its major diameter is 2.5cm by profile, minor axis is 2.0cm.
2, take by weighing silicone rubber compounds 100g.
Take by weighing testosterone undecanoate 33g.
Two kinds of raw materials are put into the rubber mixing machine blend, make sizing material and medicine mixing even, draw thin-pass 10 times, medicine more is evenly dispersed in the sizing material.
Blanking, take by weighing the 7.5g material, put into the mould mold pressing
140 ℃ of temperature, time 12min, pressure 10MPa
Depanning is taken out product, deburring.
Encapsulation, ethylene oxide gas sterilization back is standby.
Embodiment 6
The slow-releasing testicular prosthesis preparation
One. medicine and preparation:
1, androgen: hydrogen testosterone crude drug (Zhejiang celestial jade pendant raw material pharmaceutical factory supply).
2, silicone rubber compounds: purchase in Shanghai Rubber Products Insitute.The silicone rubber that the present invention selects for use is two-component room-temperature-vulcanized silicone rubber, before not vulcanizing, divide two components of A, B to exist, wherein contain catalyst in the A component, contain cross-linking agent in the B component, both do not react mutually at ordinary times, mix because of catalyst and cross-linking agent after mutual blend, can carry out polyreaction.
Two. equipment
Equipment with embodiment 1
Three. the preparation of silica gel prosthese:
1, the mould design: the Half mould, for being spheroid (olive shape spheroid) design in axle center with the major diameter, its major diameter is 2.5cm by profile, minor axis is 2.0cm.
2, take by weighing silicone rubber compounds 100g.
Take by weighing hydrogen testosterone 50g.
Two kinds of raw materials are put into the rubber mixing machine blend, make sizing material and medicine mixing even, draw thin-pass 10 times, medicine more is evenly dispersed in the sizing material.
Blanking, take by weighing the 7.5g material, put into the mould mold pressing
140 ℃ of temperature, time 12min, pressure 9.5MPa
Depanning is taken out product, deburring.
Encapsulation, ethylene oxide gas sterilization back is standby
Used slow-releasing testicular prosthesis is initial stage zoopery articles for use among the present invention, what adopt in preparation technology is easy operating process, processes such as the pressing mold of the mixing and prosthese of sizing material and medicine and deburring are only tentatively operated and are processed, as seen the finished product that makes is dispersed in equally distributed tiny testosterone drug particles, prosthetic surface is slightly coarse, be the fine, soft fur glass appearance and (see Fig. 1, Fig. 2).
Claims (6)
1, a kind of slow-releasing testicular prosthesis is made up of silicone rubber, androgen, and silicone rubber, androgen weight ratio are 2: 1-4: 1.
2, slow-releasing testicular prosthesis according to claim 1 is characterized in that: androgen is selected from testosterone or testosterone undecanoate or dihydrotestosterone.
3, slow-releasing testicular prosthesis according to claim 2 is characterized in that: androgen is a testosterone.
4, according to the arbitrary described slow-releasing testicular prosthesis of claim 1-3, it is characterized in that: silicone rubber, androgen weight ratio are 2.5: 1-3.5: 1.
5, slow-releasing testicular prosthesis according to claim 4 is characterized in that: silicone rubber, androgen weight ratio are 3: 1.
6, the application of slow-releasing testicular prosthesis according to claim 1 in the slow-release medicine of preparation treatment absence of testis disease.