CN1947692A - Artificial compound black mud - Google Patents
Artificial compound black mud Download PDFInfo
- Publication number
- CN1947692A CN1947692A CN 200610021156 CN200610021156A CN1947692A CN 1947692 A CN1947692 A CN 1947692A CN 200610021156 CN200610021156 CN 200610021156 CN 200610021156 A CN200610021156 A CN 200610021156A CN 1947692 A CN1947692 A CN 1947692A
- Authority
- CN
- China
- Prior art keywords
- salt
- black mud
- clay
- mineral
- sea
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
An artificial black mud for promoting blood circulation and metabolism, improving immunity, regulating nerve system, relieving inflammation, etc is proportionally prepared from mineral salt and clay.
Description
Technical field
The present invention relates to mineralogy, health science and fine chemical technology field, particularly a kind of black mud of artificial preparation.
Background technology
Contain several mineral materials in the black mud.In the process of using black mud, the patient sees through skin and absorbs a large amount of natural mineral matters, thereby can be made into various types of skin care item and SPA product.Black mud is put on the skin pain that direct ameliorate osteoarthritis disease causes, by arthritic clinical research shows the black mud treatment effectively to kind more than 100.Clinical verification was arranged in 1958 first, and black mud is successfully treated the psoriatic, and effective percentage is 75-90%.
Scientist has confirmed the mineralogical composition in the black mud, can replenish, strengthen and balanced skin in mineralogical composition.With cation and anion classification, these nutritious mineral comprise potassium, sodium, magnesium, calcium and iodine etc., these mineral element porous skin top layers, some in addition can antioxidation, with the oxygen molecule associating, antagonism destroys the free radical of protein and infringement skin gene.The geographical environment of mineral mud and the kind of carrier can make the color of black mud and stickiness different.The color of black mud can be very light, also can be deeply as grey black.Black mud can only obtain by the mud in salt lake, and is well-known, and salt lake resources distributes not extensive in China, how can prepare the development that black mud is perplexing black mud always on a large scale.
China has a large amount of mineral salts, mainly come from natural mineral resource, wherein contain the abundant salts substances that exists with ionic forms as magnesium salt, carbonate, sulfate, potassium salt, oxonium salt, calcium salt, ferrum oxide and aluminium oxide, silicate, bromine salt etc., the black mud composition of these materials and the Dead Sea, the Middle East is closely similar, equally also health is played the very important regulating action of improving.We are by studies show that clay, crystal is generally less than 2 microns in the clay, mainly be the layer silicate mineral of aqueous aluminum, ferrum and magnesium, characteristics such as the dilatancy that the effect of clay mineral and water produced, dispersion and coherency, viscosity, thixotropy and plasticity have obtained extensive use industrial.
Summary of the invention
The object of the present invention is to provide a kind of black mud that utilizes mineral salt and clay preparation, adopt this black mud bog bath can promote the blood circulation of human body, strengthen metabolic function, the irritability of nervous system regulation and process of inhibition, and have effects such as good antiinflammatory, detumescence, calmness, pain relieving and raising immunologic function.
Mineral salt of the present invention comes from natural mineral spring salt, comprises face of land salt lake bittern, dissolves afterwards the well mine salt salt and the natural sea-water of gained to the water filling that is arranged in well mine salt layer mineral deposit.After processing, can obtain solid-state lake salt, well mine salt and sea salt with these natural bitterns.
Clay of the present invention comprises kandite, smectite, Vermiculitum, clay level Muscovitum, illite, glauconite, chlorite and expansion chlorite and relevant mixed layer structure mineral, comprises Paligorskite and meerschaum and amorphous allophane of the cambic layer of tool chain structure in addition.
In order to reach the purpose of foregoing invention, technical scheme of the present invention realizes as follows:
Black mud of the present invention, its preparation characteristics are 20-70% mineral salt and 20-70% clay to be ground be the superfines of granularity＜10 μ m, and the water that adds 5-30% then stirs formulated, and solids content is 40-90% in the prepared black mud.
Black mud component commonly used is a mineral salt 60%, clay 25%, water 15%.
The present invention is that to adopt mineral salt and clay be raw material, specifically is well mine salt or sea salt or lake salt to be mixed with clay prepare black mud.
Well mine salt of the present invention is the mineral salt that is arranged in well mine salt layer mineral deposit, has the area of well mine salt mineral products by oneself, adopts water filling dissolution method exploitation (concrete Technology is seen " salt chemical industry ", Chemical Industry Press, 1995 editions).After exploitation obtains well mine salt salt, by precipitate, filter, removed secondary element, through solar evaporation or vacuum concentration, obtain solid-state well mine salt.The precipitation of mineral salt salt, filtration, removed secondary element method as described later.
Lake salt of the present invention and sea salt are natural minerals salt, take from salt lake, the face of land, various places and coastal waters, obtain (concrete Technology see " salt industry handbook, China Light Industry Press's in February, 1994 version) with the mode of solar evaporation or vacuum concentration.
The filtration clarification mode of described mineral salt salt is will be through sedimentary salt through being equipped with the filtering layer of filtrate (as anthracite, quartz sand), interception larger particles material wherein, and the salt permeate mainly be less than the hydrone of 1nm and calcium, magnesium, potassium, sodium, ferrum, chlorine, (concrete Technology is seen " salt chemical industry " to the sulfate radical plasma, Chemical Industry Press, 1995 editions).
The method of removal excessive bromo element, strontium element and barium element in sedimentation and filtration rock salt salt is that (concrete Technology is seen " salt industry chemical engineering science " for industrial chlorine oxidation chemical replacement method commonly used, ammonium bicarbonate method, mirabilite method etc., Tianjin publishing house of Academy of Social Sciences, 1994 editions; " inorganic chemical product ", Chemical Industry Press, 2004 the 4th edition).
Described mineral salt is the mixture of well mine salt and lake salt also, the mixture of sea salt and well mine salt, the mixture of sea salt and lake salt, the mixture of well mine salt and lake salt and sea salt.
The main component of described clay is a silicate, and generally adopting the few kaolinite of impurity content is raw material, and its processing technique is that clay is levigate to＜10 μ m with its granularity with ultra-fine grinding mill.
Described water is fresh water or salt lake bittern or well mine salt salt or sea water.
The present invention has following outstanding advantage:
1, the present invention adopts mineral salt and clay manually to prepare black mud, and the mineral salt resource is widely distributed in China, and clay also obtains easily simultaneously.Thereby overcome the limitation that natural black mud is subjected to the region factor, the problem that the black mud stock number is few has found the road of an artificial preparation black mud, and it is low to have a cost, use wide, characteristics that processing technique is easy.
2, black mud of the present invention is owing to contain the mineral salt composition, its main component and the Dead Sea, Middle East black mud, the composition of salt lake black mud is identical, has the circulation of the blood of human body of promotion equally, strengthen metabolic function, the irritability of nervous system regulation and process of inhibition, and have effects such as good antiinflammatory, detumescence, calmness, pain relieving and raising immunologic function, so be the good succedaneum of natural black mud.
What 3, black mud of the present invention adopted is the natural minerals element, so have to the skin nonirritant characteristics without any side effects.The crowd of any age, skin matter can use this black mud, and the people who especially is fit to allergic skin uses.
The specific embodiment
Black mud of the present invention is mainly prepared according to percentage by weight.Different according to the kind that adopts mineral salt and water, process for preparation is distinguished to some extent.Be further described below in conjunction with embodiment.
Embodiment 1:
Prepare 1000 kilograms of black muds: earlier that clay is levigate to＜10 μ m with its granularity with ultra-fine grinding mill, get the lake salt that accounts for total weight percent 60% then, account for the clay of total weight percent 25%, with the abundant mixing of the fresh water that accounts for total weight percent 15%, with ultra-fine grinding mill that the granularity of mixture is levigate to 5 μ m, obtain solid-state mineral content and be 85% black mud.
Embodiment 2:
Prepare 1000 kilograms of black muds: earlier that clay is levigate to＜10 μ m with its granularity with ultra-fine grinding mill, get the well mine salt that accounts for total weight percent 58% then, account for the clay of total weight percent 32%, with the abundant mixing of the fresh water that accounts for total weight percent 10%, with ultra-fine grinding mill that the granularity of mixture is levigate to 5 μ m, obtain solid-state mineral content and be 90% black mud.
Embodiment 3:
Prepare 1000 kilograms of black muds: earlier that clay is levigate to＜10 μ m with its granularity with ultra-fine grinding mill, get the sea salt that accounts for total weight percent 42% then, account for the clay of total weight percent 31%, with the abundant mixing of the fresh water that accounts for total weight percent 27%, with ultra-fine grinding mill that the granularity of mixture is levigate to 5 μ m, obtain solid-state mineral content and be 73% black mud.
Embodiment 4:
Prepare 1000 kilograms of black muds: earlier that clay is levigate to＜10 μ m with its granularity with ultra-fine grinding mill, get the sea salt that accounts for total weight percent 52% then, account for the clay of total weight percent 25%, with the fresh water that accounts for total weight percent 23% or sea water or the abundant mixing of salt, with ultra-fine grinding mill that the granularity of mixture is levigate to 5 μ m, obtain solid-state mineral content and be 77% black mud.
Embodiment 5:
Prepare 1000 kilograms of black muds: earlier that clay is levigate to＜10 μ m with its granularity with ultra-fine grinding mill, get the sea salt that accounts for total weight percent 30% then, account for the lake salt of total weight percent 38%, account for the clay of total weight percent 20%, with the fresh water that accounts for total weight percent 9% or sea water or the abundant mixing of salt, with ultra-fine grinding mill that the granularity of mixture is levigate to 5 μ m, obtain solid-state mineral content and be 88% black mud.
Embodiment 6:
Prepare 1000 kilograms of black muds: earlier that clay is levigate to＜10 μ m with its granularity with ultra-fine grinding mill, get the well mine salt that accounts for total weight percent 21% then, account for the lake salt of total weight percent 29%, account for the clay of total weight percent 20%, with the fresh water that accounts for total weight percent 30% or sea water or the abundant mixing of salt, with ultra-fine grinding mill that the granularity of mixture is levigate to 5 μ m, obtain solid-state mineral content and be 70% black mud.
Embodiment 7:
Prepare 1000 kilograms of black muds: earlier that clay is levigate to＜10 μ m with its granularity with ultra-fine grinding mill, get the sea salt that accounts for total weight percent 16% then, account for the well mine salt of total weight percent 32%, account for the clay of total weight percent 25%, with the fresh water that accounts for total weight percent 27% or sea water or the abundant mixing of salt, with ultra-fine grinding mill that the granularity of mixture is levigate to 5 μ m, obtain solid-state mineral content and be 73% black mud.
Embodiment 8:
Prepare 1000 kilograms of black muds: earlier that clay is levigate to＜10 μ m with its granularity with ultra-fine grinding mill, get the sea salt that accounts for total weight percent 12% then, account for the well mine salt of total weight percent 22%, account for the lake salt of total weight percent 20%, account for the clay of total weight percent 20%, with the fresh water that accounts for total weight percent 26% or sea water or the abundant mixing of salt, with ultra-fine grinding mill that the granularity of mixture is levigate to 5 μ m, obtain solid-state mineral content and be 74% black mud.
Claims (7)
1, a kind of black mud of artificial preparation is characterized in that, it is made by following weight percentages:
Mineral salt 20-70% clay 20-70% water 5-30%.
2, the black mud of a kind of artificial preparation according to claim 1, it is characterized in that: it is made by following weight percentages:
Mineral salt 40-60% clay 30-50% water 15-20%.
3, the black mud of a kind of artificial preparation according to claim 1, it is characterized in that: it is made by following weight percentages:
Mineral salt 60% clay 25% water 15%.
4, according to the black mud of claim 1 to 3 each described artificial preparation, it is characterized in that: mineral salt is well mine salt or sea salt or lake salt.
5, according to the black mud of claim 1 to 3 each described artificial preparation, it is characterized in that: mineral salt is the mixture of well mine salt and lake salt, the mixture of sea salt and well mine salt, the mixture of sea salt and lake salt, the mixture of well mine salt and lake salt and sea salt.
6, according to the black mud of claim 1 to 3 each described artificial preparation, it is characterized in that: the clay main component is a silicate.
7, according to the black mud of claim 1 to 3 each described artificial preparation, it is characterized in that: water is fresh water or salt lake bittern or well mine salt salt or sea water.