CN1935736A - 磷石膏高强度墙体砖及其生产方法 - Google Patents

磷石膏高强度墙体砖及其生产方法 Download PDF

Info

Publication number
CN1935736A
CN1935736A CNA2006100545210A CN200610054521A CN1935736A CN 1935736 A CN1935736 A CN 1935736A CN A2006100545210 A CNA2006100545210 A CN A2006100545210A CN 200610054521 A CN200610054521 A CN 200610054521A CN 1935736 A CN1935736 A CN 1935736A
Authority
CN
China
Prior art keywords
phosphogypsum
ardealite
quantitative
wall brick
make
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CNA2006100545210A
Other languages
English (en)
Other versions
CN100364917C (zh
Inventor
杨金平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chongqing Jincanglong New Building Material Co.,Ltd.
Original Assignee
杨金平
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 杨金平 filed Critical 杨金平
Priority to CNB2006100545210A priority Critical patent/CN100364917C/zh
Publication of CN1935736A publication Critical patent/CN1935736A/zh
Application granted granted Critical
Publication of CN100364917C publication Critical patent/CN100364917C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开一种磷石膏高强度墙体砖及其生产方法，其组成成份的重量比是：半水磷石膏70－85：无水磷石膏12－20：粉煤灰15－20：凝结剂15－25；凝结剂是12－20％的硅溶胶水溶液。用喷淋方式拌合均匀，经机械装模高压成型，机械脱模，自然水化后完成。本发明首次将其磷石膏原料大量用于建筑材料，其综合利用达80％；可完全替代实心粘土红砖，且无毒无害。其成本低、又节约土地资源。经处理后符合国家规定的核放射指标、硬度高，还减少了设备投资；降低了产品成本。

Description

磷石膏高强度墙体砖及其生产方法
技术领域
本发明涉及磷石膏全干法高强度墙体砖及其生产方法，具体涉及一种全干法生产的高度墙体砖，属于建筑材料技术领域。
背景技术
实心粘土红砖因消耗大量不可再生土地资源，在现今建筑设计中，国家针对各地区具体情况已经作了法律性或政策性的规定：禁止和限期使用实心粘土红砖。因此，建筑行业纷纷寻求替代品，如煤干砖、烧结普通砖、加气砌块和普通化学石膏砌块应运而生，传统的墙体砖是蒸气养护或烧结而成的。但这些砖块存在强度不好、核放射超标问题；现有的墙体材料生产，相当部分是浇注法“湿法”生产，湿法生产需耗用大量的能源，每吨煤的万元产值极低，不符合国家政策；另一方面，解决工业废渣磷石膏所造成的环境污染，是当前急待解决的难题，如何利用工业废渣磷石膏，是所属领域技术人员待解决的问题。
经专利检索，目前还没有全干法工艺方法、利用磷石膏生产的磷石膏墙体砖。
发明内容：
针对现有技术存在的上述不足，本发明的目的是提供一种合理利用工业废渣磷石膏，并且强度高、无干收缩特性、耐水性能好的磷石膏墙体砖。
本发明另一目的是提供所述墙体砖的生产方法。
本发明的目的是这样实现的：磷石膏高强度墙体砖，其组成成份是：半水磷石膏，硬石膏、粉煤灰、凝结剂、凝结剂，硅溶胶水溶液。
所述磷石膏高强度墙体砖，按以下方法制得：
(1)原料处理：弃掉磷石膏中附着水水份，使其结晶含水量小于15％；同时，除弃磷石膏中的磷、酸等有害物质，氟含量≤0.3mg/L，放射性活性比为0.25，达到环保建材要求。
(2)将定量半水磷石膏与定量无水磷石膏与凝结剂配合混合搅拌，将凝结剂用喷淋方式使之成雾状；
(3)使运动的粉与凝接剂结合，使之成为不结团的湿粉状；
(4)将定量的拌合粉，送入定量的供应模筐；
(5)用机械压力≥10Mpa/C m2使之成型；
(6)脱模后通过自然水化完成后，便可堆垛使用。
相比现有技术，本发明具有如下优点：
1、首次将其磷石膏原料大量用于建筑材料，并综合利用达80％；可完全替代实心粘土红砖，且无毒无害；其成本低、又节约土地资源。
2、耐水性好，强度高，表面平整，尺寸偏差小，不变形，不开裂，吸水率少，无干收缩特性；在水中连续浸泡60天后均无裂痕、不分层、不掉皮、不掉角。
3、自然养护，脱模4小时后即可使用。
4、经处理后符合国家规定的核放射指标；除弃了磷、酸，解决了氟等有害物质，达到了环保建材≤1的要求，氟含量0.3mg/L；放射性活性比为0.25，符合GB6566-2001《建筑材料放射性核素限量》。
5、本发明全干法生产工艺的优点是：节约了生产用水；减少了烘干的后工序；减少了设备投资；降低了产品成本。
具体实施方式
本发明磷石膏高强度墙体砖，其组成成份的重量比按下述配方即可：
    配方1     配方2     配方3     配方4     配方5
半水磷石膏     70     75     80     82     85
无水磷石膏     20     15     10     8     10
粉煤灰     10     12     10     8     6
凝结剂     15     18     20     22     25
凝结剂是硅溶胶水溶液，凝结剂用于增强耐水性。
本发明按以下方法制得：
(1)原料处理：采用干燥煅烧法(180℃-500℃，分段处理)弃掉磷石膏中附着水水份，使其结晶含水量小于15％；同时，除弃磷石膏中的磷、酸等有害物质，氟含量≤0.3mg/L，放射性活性比为0.25，达到了环保建材的要求；
(2)将定量半水石膏与定量无水石膏与凝结剂配合混合搅拌，将凝结剂用喷淋方式使之成雾状；
(3)使运动的粉与凝接剂结合，使之成为湿润的不结团的湿粉状；
(4)将定量的拌合粉，送入定量的供应模筐；
(5)用机械压力≥10Mpa/C m2使之成型；
(6)脱模后通过自然水化，完成后便可堆垛使用。
本发明研制的全干法生产磷石膏产品技术，磷石膏利用率为80％，是在二水石膏结晶的水量内，不加入多于的水量；在80％半水磷石膏里加入水硅溶胶，用喷淋方式拌合均匀，经机械装模高压成型，机械脱模，自然水化后完成；产品各项质量技术指标经重庆质量监督检验均已符合了国家标准。
特别是冻融实验砖样完好，质量损失为0.12％。另在水中连续浸泡60天后均无开裂、不分层、不掉皮、不掉角。

Claims (2)

1、磷石膏高强度墙体砖，其组成成份的重量比是：半水磷石膏70-85∶无水磷石膏12-20∶粉煤灰10-20∶凝结剂15-25；凝结剂是12-20％的硅溶胶水溶液。
2、磷石膏高强度墙体砖，按以下方法制得：
(1)原料处理：弃掉磷石膏中附着水水份，使其结晶含水量小于15％；同时，除弃磷石膏中的磷、酸等有害物质，氟含量≤0.3mg/L，放射性活性比为0.25；
(2)将定量半水磷石膏与定量无水磷石膏与粉煤灰按上述配方混合搅拌，将凝结剂用喷淋方式使之成雾状；
(3)使运动的粉与凝接剂结合，使之成为不结团的湿粉状；
(4)将定量的拌合粉，送入定量的供应模筐；
(5)用机械压力≥10Mpa/Cm2使之成型；
(6)脱模后通过自然水化，完成后便可堆垛使用。
CNB2006100545210A 2006-10-21 2006-10-21 磷石膏高强度墙体砖及其生产方法 Expired - Fee Related CN100364917C (zh)