CN1911556A - Water base casting coating material powder for concave convex rod - Google Patents
Water base casting coating material powder for concave convex rod Download PDFInfo
- Publication number
- CN1911556A CN1911556A CN 200610088474 CN200610088474A CN1911556A CN 1911556 A CN1911556 A CN 1911556A CN 200610088474 CN200610088474 CN 200610088474 CN 200610088474 A CN200610088474 A CN 200610088474A CN 1911556 A CN1911556 A CN 1911556A
- Authority
- CN
- China
- Prior art keywords
- water base
- concave
- coating material
- material powder
- casting coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention discloses one kind of water base attapulgite casting paint powder, which is prepared with sodide modified attapulgite, high alumina bauxite, graphite, magnesia, sodium silicate and carboxymethylcellulose sodium in certain weight proportion, and through mixing, grinding in mill and packing. In production site of foundry, the water base attapulgite casting paint powder and water are compounded to form the casting paint with high suspension rate, good brushing performance, high surface smoothness, no precipitate, no caking, good flowability, high sand adhesion resistance and high stability.
Description
Technical field:
The present invention relates to cast paint, be specifically related to a kind of water base casting coating material powder for concave convex rod.
Background technology:
Water base cast paint has production efficiency height, characteristics such as cheap and applied widely, in China's Foundry Production, obtained extensive use, water base cast paint easily produces precipitation in long-term storage and transportation, secondly be that the coating brush mark is serious, influences the surface quality of foundry goods.
The suspending agent of present water base cast paint is selected attapulgite clay or bentonite mostly for use, attapulgite clay of supplying on the market or bentonite are with the product behind the direct abrasive dust of raw ore, do not handle owing to carry out modification, directly have influence on attapulgite clay or bentonitic dispersion suspension and stability.
Chinese patent Granted publication CN1164385, Granted publication day is on September 1st, 2004, name is called: " magnesium-alloy metal-type casting coating and preparation method ", disclose: " a kind of magnesium-alloy metal-type casting coating and preparation method, its chemical constituent mass percent is: talcum powder 3-8%, diatomite 2-5%, binding agent 1.5-4%, suspending agent 0.3-2%, fire retardant 2-7% and water 75-90%.Binding agent can be waterglass, Ludox or aluminum phosphate, and suspending agent can be attapulgite clay, palygorskite clay etc., and fire retardant can be NH ↓ [4] BF ↓ [4], KBF ↓ [4], sodium alkyl sulfonate and boric acid etc.The magnesium-alloy metal-type casting coating of the present invention's preparation, have stronger heat insulating ability, anti-flammability, caking property and coating, and have good suspension, be difficult for precipitation in the use, help obtaining the Mg alloy castings of any surface finish, non-oxidation elephant skin ".
Use the attapulgite clay do not have modification, palygorskite clay primary raw material in the foregoing invention, will reduce the suspension of " magnesium-alloy metal-type casting coating " as suspending agent.
Summary of the invention:
The objective of the invention is to overcome weak point in the prior art, provide a kind of production technology simple, cheap, all reasonable water base casting coating material powder for concave convex rod of suspensibility, plasticity, caking property, thixotropy and heat endurance.
Concave-convex clay rod, graphite, high-aluminium vanadine, magnesia, sodium metasilicate and sodium carboxymethylcellulose after water base casting coating material powder for concave convex rod is handled by modification are formed.
Concave-convex clay rod has unique rod-like fibre crystal shape structure, formed space structure is difficult for being opened, viscosity can be up to more than the 3000mpa.s, dry post-shrinkage ratio is less, dryout or sintering after do not crack, after with sodium carbonate Concave-convex clay rod being carried out modification and handles, be better than other clay with its excellent caking property, suspension and thickening property, the refractoriness performance of Concave-convex clay rod is poor slightly.
Magnesia can improve Concave-convex clay rod and bentonitic dispersion viscosity, suspendability and refractoriness.
Graphite possesses good thermal conductivity, lubricity, acid and alkali-resistance and performance such as high temperature resistant.
High-aluminium vanadine has higher refractoriness, and Heat stability is good.
The sodium metasilicate cementitiousness derives from the silicon gel, so be widely used as binding agent, plays the effect that increases stability in the batching of water base casting coating material powder for concave convex rod.
Sodium carboxymethylcellulose can improve suspensibility, plasticity and the stability of water base casting coating material powder for concave convex rod.
The present invention is achieved by following technical proposals:
1, the batching of water base casting coating material powder for concave convex rod comprises following component by weight percentage: Concave-convex clay rod 55～85%, high-aluminium vanadine 5～25%, graphite 5～20%, magnesia 2～10%, sodium metasilicate 1～5% and sodium carboxymethylcellulose 1～3% after modification is handled.
2, the production method of water base casting coating material powder for concave convex rod is:
After at first Concave-convex clay rod and sodium carbonate being mixed according to the requirement of batching, import jointly and add water in the fermentation vat and carry out sodium and handle, the sodium processing time was controlled at 24～72 hours; Push in the Concave-convex clay rod input extruder after sodium is handled, and be compressed to tablet by twin rollers, the THICKNESS CONTROL of tablet is at 0.5～2.0 millimeter, tablet is transported to and carries out airing on the cement threshing ground, tablet after the airing is the Concave-convex clay rod after sodium modification is handled, its dispersion viscosity 〉=2200mPa.s, water content≤13%; Concave-convex clay rod, high-aluminium vanadine, graphite, magnesia, sodium metasilicate, sodium carboxymethylcellulose after again sodium modification being handled mixes according to the requirement of preparing burden and stirs, the back input grinding machine that stirs carries out abrasive dust, grain fineness≤0.044 millimeter is packaged as finished product.
In the Foundry Works production scene, water base casting coating material powder for concave convex rod and water are mixed with the water-based concave-convex stick cast paint according to specification requirement, have the suspensibility height, the brushing performance is good, surface smoothness is good, do not precipitate, do not lump, good fluidity, anti-stick grittiness is strong and the characteristics of good stability.
The suspensibility of water base casting coating material powder for concave convex rod in water 8 hours 〉=99.0%, 24 hour 〉=98.5%, 72 hour 〉=98.0%, 15 day 〉=95.0%.
Water base casting coating material powder for concave convex rod is applicable to makes water base cast paint.
The specific embodiment:
Below in conjunction with embodiment, the invention will be further described:
1, the batching of water base casting coating material powder for concave convex rod comprises following component by weight percentage: Concave-convex clay rod 70%, high-aluminium vanadine 14%, graphite 9%, magnesia 3%, sodium metasilicate 3% and sodium carboxymethylcellulose 1% after modification is handled.
2, the production method of water base casting coating material powder for concave convex rod is:
After at first Concave-convex clay rod and sodium carbonate being mixed according to the requirement of batching, import jointly and add water in the fermentation vat and carry out sodium and handle, the sodium processing time was controlled at 48 hours; Push in the Concave-convex clay rod input extruder after sodium is handled, and be compressed to tablet by twin rollers, the THICKNESS CONTROL of tablet is at 0.5～1.5 millimeter, tablet is transported to and carries out airing on the cement threshing ground, tablet after the airing is the Concave-convex clay rod after sodium modification is handled, its dispersion viscosity 〉=2200mPa.s, water content≤13%; Concave-convex clay rod, high-aluminium vanadine, graphite, magnesia, sodium metasilicate, sodium carboxymethylcellulose after again sodium modification being handled mixes according to the requirement of preparing burden and stirs, the back input grinding machine that stirs carries out abrasive dust, grain fineness≤0.044 millimeter is packaged as finished product.
Claims (2)
1, a kind of water base casting coating material powder for concave convex rod, it is characterized in that, the batching of water base casting coating material powder for concave convex rod comprises following component by weight percentage: Concave-convex clay rod 55～85%, high-aluminium vanadine 5～25%, graphite 5～20%, magnesia 2～10%, sodium metasilicate 1～5% and sodium carboxymethylcellulose 1～3% after modification is handled.
2, the production method of water base casting coating material powder for concave convex rod according to claim 1: the Concave-convex clay rod after sodium modification handled, high-aluminium vanadine, graphite, magnesia, sodium metasilicate, sodium carboxymethylcellulose mix according to the requirement of batching and stir, the back input grinding machine that stirs carries out abrasive dust, grain fineness≤0.044 millimeter is packaged as finished product.