CN1907597A - Casting method for exhaust branch pipe of thin-wall ball iron triplet - Google Patents
Casting method for exhaust branch pipe of thin-wall ball iron triplet Download PDFInfo
- Publication number
- CN1907597A CN1907597A CN 200610030287 CN200610030287A CN1907597A CN 1907597 A CN1907597 A CN 1907597A CN 200610030287 CN200610030287 CN 200610030287 CN 200610030287 A CN200610030287 A CN 200610030287A CN 1907597 A CN1907597 A CN 1907597A
- Authority
- CN
- China
- Prior art keywords
- branch pipe
- exhaust branch
- core
- casting
- gate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a casting method for casting the three-way ventilate branch tube of thin-wall iron element, which comprises: (1), using the curvature formed by the central line of C exhaust open and the central line of A exhaust tube, to make the C and A exhaust opens above the parting surface, to be shaped via upper and lower outer moulds; the tube core and sand core are put via the serial number, and it uses pour system that combines side pour and bottom pour with contract cap and cold iron; (2), preparing outer mould, core box, section sheet, pour cap, and the wood mould that checking sample plate; (3), preparing the casting element and sand core; (4), drying the casting element and the sand core, and closing the tank after arranging the sand core; (5), smelting and pouring; (6), cooling and molding; (7), cleaning the casting element; (8), thermally treating; (9), testing the water pressure. The invention can improve the quality of casting element, and improve the producing efficiency.
Description
Technical field
The present invention relates to the casting method of a kind of casting method of complex-shaped foundry goods, particularly a kind of exhaust branch pipe of thin-wall ball iron triplet.
Background technology
Exhaust branch pipe is complex-shaped thin-wall ductile iron threeway tubular cast, and one of them exhaust outlet has the angle of bend of three directions, to mould and moulding, to join in the case process dimension precision requirement very high; The caliber of exhaust branch pipe: Φ 120-200mm, thickness of pipe wall: 6-8mm, pipeline is about 800mm.According to the technical specification of medium seed diesel engine patents company, the material of this foundry goods is: FGS350-22, stokehold coupon performance requirement, tensile strength: 330-390N/mm
2, yield strength: 220-240N/mm
2, percentage elongation: 12-18%, Brinell hardness: 130-180.Foundry goods has higher alloy to become chemical composition requirement, Si:3%, Cr:0.3%, Mo:0.25%.Foundry goods must not have casting flaws such as sand holes, pore, cold shut, shrinkage porosite.
Existing exhaust branch pipe casting production process is: adopt wooden die and the resin sand mode modeling with craft; The center line that does not have the exhaust outlet of curvature of space angle with this foundry goods is die joint (referring to Fig. 1); Angle of bend exhaust outlet with three directions is positioned at nowel, and 2 embedded cores are established in the exhaust outlet both sides; Running gate system is that side is annotated.
Having the following disadvantages of the casting method of existing complex-shaped spheroid three-way pipe:
1. the exhaust outlet that dimensional requirement is the highest is positioned at nowel, by 3 core combination formings, because the angle of bend of three directions of this exhaust outlet band, can't check mould dimension behind the knockout core, the casting dimension deviation is difficult to effective control, foundry goods processing back often finds that tube wall is thin excessively, causes foundry goods water pressure test seepage and scraps, and the eccentric defective in exhaust outlet position is also more serious simultaneously.
2. the die cavity space of nowel is minimum, and the die cavity bending is irregular, can't check in the die cavity when joining case to be
Foreign material such as the loose sand that does not have, dust stratification also can't be cleared up die cavity with cold wind, and the sand holes of foundry goods, defective such as to be mingled with more, has a strong impact on castings material compactness, local leaktightness of wall of tubes during the water pressure test, and foundry goods is scrapped.
3. pipe core and embedded core be at the vertical direction location overlap, when joining case pipe core and embedded core must be simultaneously toward falling, " the colliding with " between the core is very serious, causes loose sand, dust stratification to fall into cavity bottom, increased the weight of foundry goods sand holes, defective such as be mingled with.
4. simultaneously in the dropping process, 1 core wherein has to adopt a dead lift mode for pipe core and embedded core, and embedded core again must be along the moving horizontally of pipe core bending direction when falling, operation inconvenience, and production efficiency is low, and labour intensity is big.
5. foundry goods adopts the side cast, and the molten iron flow process is longer, because molten ductile iron is mobile relatively poor, is easy to generate defectives such as cold shut.
Summary of the invention
The objective of the invention is to overcome the deficiencies in the prior art, a kind of casting method of complex-shaped thin wall nodular iron casting threeway exhaust branch pipe is provided, improve the dimensional accuracy of foundry goods, casting flaws such as the sand holes of minimizing foundry goods, pore, cold shut, foundry goods water pressure test ne-leakage, handled easily has reduced labour intensity, has improved production efficiency.
Technical scheme provided by the invention is a kind of casting method of thin wall nodular iron casting threeway exhaust branch pipe, comprise analogue formation, smelting and pouring, cooling forming, the cleaning check, adopt the mode analogue formation of curved surface somatotype, adopt the mode analogue formation of curved surface somatotype, with the curved surface formed with the center line of the center line of the C exhaust branch pipe of three angle of bend and A exhaust branch pipe is the curved surface die joint of last drag box, make on the described curved surface die joint that is positioned at sandbox with the C exhaust branch pipe and the A exhaust branch pipe of three angle of bend, by last, the external mold direct forming of drag box, the B exhaust branch pipe is positioned at drag box; Adopt the running gate system that side is annotated and rising pouring combines, first side is set in the end of A exhaust branch pipe annotates cast gate, at C exhaust branch pipe sidepiece second side is set and annotates cast gate, described first side annotates cast gate and second side notes cast gate all is arranged in cope, the elongated end first embedded core place in the B exhaust branch pipe bottom that is positioned at drag box is provided with a down-pour gate, be positioned at " L " shape structure of the cross gate of cope for the bending of band arc, described cross gate one end is parallel to the center line of A exhaust branch pipe and annotates cast gate with the down-pour gate and first side and is communicated with, the other end of cross gate is annotated cast gate with second side and is communicated with, down gate is communicated with perpendicular to cross gate place face and with cross gate, and on C exhaust branch pipe flange, first feeding head is set, second feeding head is set on the flange of A exhaust branch pipe, place first chill and second chill (8) in the platform subordinate symmetry that B exhaust branch pipe front end is outstanding, place the 3rd chill in the platform portion that C exhaust branch pipe front end is outstanding.
Described casting process mainly comprises following several steps:
1. according to curved surface classifying method establishment casting technique;
2. make the wooden model of external mold, core box, template, dead head and inspection template according to the requirement of casting technique;
3. wooden model is positioned on the template, makes casting mold, and utilize core box to make core;
4. dry casting mold and core, descend core in order, remove mould assembling behind loose sand, the dust stratification in the casting mold;
5. smelting and pouring;
6. cooling forming;
7. clear up foundry goods, remove cast gate, rising head, fash;
8. casting stress is eliminated in conventional heat treatment;
9. to after the spray line processing, carry out the water pressure test.
Described casting mold and core adopt furan resin self curing sand to make.
Described down core for being first embedded core down earlier, descend pipe core in proper order then, second embedded core down at last, and whenever next core all will be checked mould dimension with inspection template, clears up casting mold interior loose sand and dust stratification then.
The weight proportion of the furnace charge in the described smelting and pouring process is the new pig iron 80%, steel scrap 20%, fusion temperature is 1520 ± 10 ℃, tapping temperature is 1510 ± 10 ℃, the rare earth magnesium nodularizer addition is 1.6 ± 0.2% of a furnace charge gross weight, the ferrosilicon innoculant adding quantity is 1.0 ± 0.2% of a furnace charge gross weight, the spheroidization and inoculation temperature is 1435 ± 15 ℃, and pouring temperature is 1340 ± 10 ℃.
Cooling procedure must be incubated behind the described casting pouring, holding temperature≤200 ℃, temperature retention time 〉=12 hour.
The pressure that carries out the water pressure test in the checkout procedure of described foundry goods is 0.6MPa.
The present invention compared with prior art has following technique effect:
1. owing to adopt the curved surface somatotype, C exhaust outlet with 3 angle of bend is positioned on the die joint, by the external mold direct forming, can directly control the size of casting mold when joining case with inspection template, guarantee the locus of casting section thickness and exhaust outlet, obviously improved the dimensional accuracy of foundry goods.
2. pipe core and embedded core can play core in order one by one when joining case, be convenient to operation, can carry out handling to pipe core and embedded core with driving during following core, reduce artificial labour intensity, enhance productivity, eliminated " colliding with " phenomenon between the core simultaneously, minimizing loose sand, dust stratification fall into die cavity, the B exhaust outlet that is positioned at nowel does not have angle of bend, can check to direct convenience the wall thickness of die cavity when joining case.
3. die cavity is inner if there are foreign material such as loose sand, dust stratification directly to clean out with cold wind, foundry goods sand holes, inclusion defect have effectively been prevented, guaranteed the dense materials of foundry goods, after adopting the foundry goods of new method casting to carry out the water pressure test, seldom find the leaktightness of wall of tubes phenomenon that causes because of loose sand and dust stratification.
4. owing to adopt the gate system of side notes and rising pouring combination, improve the mold-filling capacity of molten iron, reduced the cold shut defective of thin-wall part.
Description of drawings
Fig. 1 is the plane somatotype schematic diagram in the casting method of exhaust branch pipe of thin-wall ball iron triplet in the prior art.
Fig. 2 is the front view of the casting method mean camber somatotype of exhaust branch pipe of thin-wall ball iron triplet of the present invention.
Fig. 3 is the vertical view of the casting method mean camber somatotype of exhaust branch pipe of thin-wall ball iron triplet of the present invention.
Fig. 4 for the F of exhaust branch pipe of thin-wall ball iron triplet casting method mean camber somatotype of the present invention to view.
Wherein:
The 1-curved surface die joint 2-first feeding head 3-second feeding head 4-down gate
The 5-cross gate 6-down-pour gate 7-first chill 8-second chill
9-the 3rd chill 10-first side is annotated cast gate 11-second side and is annotated cast gate
12-A exhaust branch pipe 13-B exhaust branch pipe 14-C exhaust branch pipe 15-first embedded core
16-pipe core 17-second embedded core
The specific embodiment
Below in conjunction with specific embodiment the present invention is described in further detail, but should not limit protection scope of the present invention with this.
See also Fig. 2, Fig. 3 and Fig. 4, the front view of Fig. 2 threeway exhaust branch pipe of the present invention casting method mean camber somatotype, the vertical view of Fig. 3 threeway exhaust branch pipe of the present invention casting method mean camber somatotype, the F of Fig. 4 threeway exhaust branch pipe of the present invention casting method mean camber somatotype is to view.With the curved surface formed with the center line of the center line of the C exhaust branch pipe 14 of three angle of bend and A exhaust branch pipe 12 is the curved surface die joint 1 of last drag box, make on the described curved surface die joint 1 that is positioned at sandbox with the C exhaust branch pipe 14 and the A exhaust branch pipe 12 of three angle of bend, by the external mold direct forming of upper and lower sandbox, B exhaust branch pipe 13 is positioned at drag box; Adopt the running gate system that side is annotated and rising pouring combines, first side is set in the end of A exhaust branch pipe 12 annotates cast gate 10, at C exhaust branch pipe 14 sidepieces second side is set and annotates cast gate 11, described first side annotates cast gate 10 and second side notes cast gate 11 all is arranged in cope, elongated end first embedded core 15 places in B exhaust branch pipe 13 bottoms that are positioned at drag box are provided with a down-pour gate 6, be positioned at " L " shape structure of the cross gate 5 of cope for the bending of band arc, described cross gate 5 one ends are parallel to the center line of A exhaust branch pipe 12 and annotate cast gate 10 with the down-pour gate 6 and first side and are communicated with, the other end of cross gate 6 is annotated cast gate 11 with second side and is communicated with, down gate 4 is communicated with perpendicular to cross gate 6 place faces and with cross gate 6, and first feeding head 2 is set on C exhaust branch pipe 14 flanges, second feeding head 3 is set on the flange of A exhaust branch pipe 12, place first chill 7 and second chill 8 in the platform subordinate symmetry that B exhaust branch pipe 13 front ends are outstanding, place the 3rd chill 9 in the platform portion that C exhaust branch pipe 14 front ends are outstanding.
Fig. 2, Fig. 3 and Fig. 4 are most preferred embodiments of the casting method of exhaust branch pipe of thin-wall ball iron triplet of the present invention, threeway exhaust branch pipe with the PA6 medium seed diesel engine is an example, utilizes the design of Fig. 2, Fig. 3 and Fig. 4 to specify the process of thin-wall ductile iron exhaust branch pipe casting method of the present invention:
1) according to the casting technique of the method for above-mentioned curved surface somatotype establishment exhaust branch pipe.
2) make wooden model by the requirement of casting technique drawing, comprise external mold, core box, template, dead head and a complete set of inspection template, and wooden model is positioned on the template.
3) adopt furan resin self curing sand to make casting mold, core, put chill by the sign on the external mold during moulding.
4) behind employing spray gun oven dry casting mold and the core, core under the order that gets on, get off by spatial distribution, whenever next core all will check whether mould dimension meets the requirements with inspection template, clean out loose sand, dust stratification in the casting mold behind the following core, check and cleaning back mould assembling.
5) smelting and pouring.Furnace charge carries out being positioned over the melting of 1.5t intermediate frequency furnace after the proportioning according to the new pig iron 80% and steel scrap 20%, smelting temperature is 1520 ± 10 ℃, the fusing tapping temperature is 1510 ± 10 ℃, nodulizer is F-2P, addition is 1.6% of a total iron and steel weight, and inovulant is 75SiFe, 1.0% of the iron and steel weight that addition is total, the spheroidization and inoculation temperature is 1435 ± 15 ℃, and pouring temperature is 1340 ± 10 ℃.
6) unpack after the foundry goods behind the moulding by casting is incubated 12 hours in casting mold.
7) foundry goods of cleaning casting is removed cast gate, rising head, fash.
8) foundry goods carries out conventional heat treatment, eliminates stress.
9) spray is processed after the assay was approved, carries out the water pressure test, test pressure 0.6MPa.
Undoubtedly, the value in the described embodiment of casting method of thin wall nodular iron casting threeway exhaust branch pipe of the present invention all also has other similar modes with being connected.In a word, protection scope of the present invention should comprise that those those of ordinary skills are conspicuous conversion or substitute.
Claims (7)
1. the casting method of an exhaust branch pipe of thin-wall ball iron triplet, comprise analogue formation, smelting and pouring, cooling forming, the cleaning check, it is characterized in that adopting the mode analogue formation of curved surface somatotype, with the curved surface formed with the center line of the center line of the C exhaust branch pipe (14) of three angle of bend and A exhaust branch pipe (12) is the curved surface die joint (1) of last drag box, make on the described curved surface die joint (1) that is positioned at sandbox with the C exhaust branch pipe (14) and the A exhaust branch pipe (12) of three angle of bend, by last, the external mold direct forming of drag box, B exhaust branch pipe (13) is positioned at drag box; Adopt the running gate system that side is annotated and rising pouring combines, first side is set in the end of A exhaust branch pipe (12) annotates cast gate (10), at C exhaust branch pipe (14) sidepiece second side is set and annotates cast gate (11), described first side annotates cast gate (10) and second side notes cast gates (11) all are arranged in cope, elongated end first embedded core (15) in B exhaust branch pipe (13) bottom that is positioned at drag box locates to be provided with a down-pour gate (6), be positioned at " L " shape structure of the cross gate (5) of cope for the bending of band arc, described cross gate (5) one ends are parallel to the center line of A exhaust branch pipe (12) and annotate cast gate (10) with the down-pour gate (6) and first side and are communicated with, the other end of cross gate (6) is annotated cast gate (11) with second side and is communicated with, down gate (4) is communicated with perpendicular to cross gate (6) place face and with cross gate (6), and on C exhaust branch pipe (14) flange, first feeding head (2) is set, second feeding head (3) is set on the flange of A exhaust branch pipe (12), place first chill (7) and second chill (8) in the platform subordinate symmetry that B exhaust branch pipe (13) front end is outstanding, place the 3rd chill (9) in the platform portion that C exhaust branch pipe (14) front end is outstanding.
2. according to the casting method of the described exhaust branch pipe of thin-wall ball iron triplet of claim 1, it is characterized in that described casting process mainly comprises following several steps:
1. according to curved surface classifying method establishment casting technique;
2. make the wooden model of external mold, core box, template, dead head and inspection template according to the requirement of casting technique;
3. wooden model is positioned on the template, makes casting mold, and utilize core box to make core;
4. dry casting mold and core, descend core in order, remove mould assembling behind loose sand, the dust stratification in the casting mold;
5. smelting and pouring;
6. cooling forming;
7. clear up foundry goods, remove cast gate, rising head, fash;
8. casting stress is eliminated in conventional heat treatment;
9. to after the spray line processing, carry out the water pressure test.
3. according to the casting method of the described exhaust branch pipe of thin-wall ball iron triplet of claim 2, it is characterized in that described casting mold and core adopt furan resin self curing sand to make.
4. according to the casting method of the described exhaust branch pipe of thin-wall ball iron triplet of claim 2, it is characterized in that described core down is first embedded core (15), pipe core (16) and second embedded core (17) in proper order, every next core all will be checked mould dimension with inspection template, clears up loose sand and dust stratification in the casting mold then.
5. according to the casting method of the described exhaust branch pipe of thin-wall ball iron triplet of claim 2, the weight proportion that it is characterized in that the furnace charge in the described smelting and pouring process is the new pig iron 80%, steel scrap 20%, fusion temperature is 1520 ± 10 ℃, tapping temperature is 1510 ± 10 ℃, the rare earth magnesium nodularizer addition is 1.6 ± 0.2% of a furnace charge gross weight, the ferrosilicon innoculant adding quantity is 1.0 ± 0.2% of a furnace charge gross weight, and the spheroidization and inoculation temperature is 1435 ± 15 ℃, and pouring temperature is 1340 ± 10 ℃.
6. according to the casting method of the described exhaust branch pipe of thin-wall ball iron triplet of claim 2, it is characterized in that described cooling forming process must be incubated, holding temperature≤200 ℃, temperature retention time 〉=12 hour.
7. according to the casting method of the described exhaust branch pipe of thin-wall ball iron triplet of claim 2, it is characterized in that the pressure in the described foundry goods water pressure test is 0.6MPa.