CN1884193A - Porous mullite ceramic materials and method for preparing same - Google Patents
Porous mullite ceramic materials and method for preparing same Download PDFInfo
- Publication number
- CN1884193A CN1884193A CN 200610019552 CN200610019552A CN1884193A CN 1884193 A CN1884193 A CN 1884193A CN 200610019552 CN200610019552 CN 200610019552 CN 200610019552 A CN200610019552 A CN 200610019552A CN 1884193 A CN1884193 A CN 1884193A
- Authority
- CN
- China
- Prior art keywords
- mullite
- ceramic materials
- powder
- preparation
- mullite ceramic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a porous mullite ceramic material and preparing method, which comprises the following steps: dispensing 10-50 percent coal gangue powder, 50-90 percent Al (OH) 3, 2-10 percent water and 0-10 percent addictive; stirring; moulding; drying the mould at 110 deg.c for 4-24 h; sintering at 1400-1600 deg.c for 1-8 h. The chemical component of product is SiO2 and Al2O3, wherein the main crystal phase is mullite or mullite-alumina, which can be high-strength and light-quality insulating flame-proof material.
Description
One, technical field
The invention belongs to the porous ceramic film material field.Relating in particular to a kind of is light thermal insulation fire-resistant material of main phase composition and preparation method thereof with mullite, corundum.
Two, background technology
Present lagging material mostly belongs to Al
2O
3-SiO
2Based material (Wang Weibang. fire-proof material technology. metallurgical industry press, 2003), main thing is corundum, mullite, quartzy thing phase and glassy phase mutually.These lagging material apertures are bigger, and pore distribution is inhomogeneous.From the pore-creating technological angle, the method for preparing porous ceramic film material and light thermal insulation fire-resistant material at present mainly contains two kinds:
1, adds the combustiblematerials method
In pottery or refractory materials powder, add combustiblematerials, as sawdust, coal dust, coke powder, polystyrene foamed ball etc., after moulding, burning till, the combustiblematerials burning-off forms pore in material.As " development of light-weight mullite brick and application " (" ceramic engineering ", 2002,12) technology, be raw material with mullite grog, commercial alumina, kaolin, be additive with saw dust, styrofoam bead, prepared the light-weight mullite brick.The shortcoming of this method is: when combustiblematerials burns not to the utmost, easily form " black core " in material; The combustiblematerials powder is easily reunited in powder, causes uneven, the unequal shortcoming of gas cell distribution of material inner air vent size, and the amount that adds the combustiblematerials powder is received restriction, can not prepare the very high material of void content.
2, foaming process
Pottery or refractory materials powder are made mud, in mud, add whipping agents such as rosined soap and solidifying agent and make through stirring and in mud, form bubble.Mud promptly obtains porous ceramic film material behind casting, curing and sintering.As " a kind of light fire brick " technology (CN03100439.3), disclosing with kyanite and calcining coal gangue is raw material, adopts the foaming process moulding, and having prepared with the mullite is that principal crystalline phase, lime feldspar are the light fire brick in conjunction with phase.Pore opening in the porous ceramic film material that this method makes is subjected to the influence of factors such as whipping agent and stirring very big with distribution.Be difficult to obtain the material that even air hole distribution and air vent aperture are evenly distributed.
More than in the porous material of two kinds of methods preparation, the material (composing the hole material) that produces pore all is the material beyond the stupalith raw material.The influence of being composed the forming of hole material, particle diameter or foaming condition by the pore that they produced is very big, is difficult to make even air hole distribution, and the porous material of microstructure and stable performance particularly is difficult to make poromerics.
From using the raw material angle, the raw material of existing preparation porous mullite material comprises: clay, bauxitic clay, kyanite, mullite, coal gangue, commercial alumina and some additives.Wherein use bauxitic clay in the majority, so just occupy bauxite resource in a large number, produce resource contention with the aluminium metallurgy industry.
Though document " research of coal gangue mullite synthesizing grog " (" mineral rock ", the 18th volume, the 4th phase) has been reported with coal gangue and Al (OH)
3For feedstock production the mullite grog, but its preparation is dense material, unit weight＞2.51g/cm
3
Three, summary of the invention
The purpose of this invention is to provide that a kind of void content height, mean pore size are little, even air hole distribution, intensity are high is light thermal insulation fire-resistant material of principal crystalline phase and preparation method thereof with mullite, corundum.
For achieving the above object, the technical solution used in the present invention is: percentage composition is with 10～50% colliery powder, 50～90% Al (OH) by weight
3Powder is prepared burden, and adds 2～10% water of above-mentioned compound weight and 0～10% additive, through stir, after the moulding, again with molding blank 110 ℃ dry 4～24 hours down.Under 1400～1600 ℃ of temperature, burn till then, be incubated 1～8 hour.
Wherein: additive or be MgCO
3, or be CaCO
3, or be MgCO
3And CaCO
3Mixture, particle diameter all≤88 μ m; Colliery powder, Al (OH)
3The particle diameter of powder is 10～88 μ m; Moulding or mechanical compaction or manual ramming, the pressure of mechanical compaction are 10～400Mpa.
Owing to adopt technique scheme, with coal gangue and Al (OH)
3Powder is a raw material, utilizes it to decompose original position and produces pore, synthesizing porous mullite material (void content＞38%, unit weight＜2.00g/cm
3).The material even air hole distribution that this method obtained, and the waste material coal gangue that can utilize the colliery to produce help environment protection.
The product chemical ingredients of the present invention's preparation mainly is SiO
2With Al
2O
3, its principal crystalline phase is mullite or mullite-corundum.It is the light thermal insulation fire-resistant material that a kind of mean pore size is 100nm～15 μ m, even air hole distribution, intensity is high.
Four, embodiment
Embodiment 1
A kind of porous mullite ceramic materials and preparation method thereof: with particle diameter is colliery powder and the Al (OH) of 53～75 μ m
3Powder respectively by weight percentage composition be 32～16%, 68～84% to prepare burden, add 2～10% water of above-mentioned compound weight, mix and stir.Ageing mixture 18～24 hours is a mechanical pressing under 30～50Mpa condition at pressure, molding blank seasoning 24 hours in air, again 110 ℃ dry 8～16 hours down, under 1500 ℃, burn till, soaking time is 3～5 hours.
With the product that the preparation method obtained of present embodiment, can obtain apparent porosity and be 54～62%, unit weight is 1.42～1.50g/cm
3, mean pore size is mullite-corundum light heat insulation material of 400～600nm.
Embodiment 2
A kind of porous mullite ceramic materials preparation method: with particle diameter is colliery powder and the Al (OH) of 10～88 μ m
3Powder respectively by weight percentage composition be 46～32%, 54～68% to prepare burden, add 2～10% water of above-mentioned compound weight, 1.5～2.5% MgCO
3With 1.0～2.0% CaCO
3Mix and stir.Ageing mixture 18～24 hours, mechanical pressing under 80～100Mpa pressure.Seasoning is 16～24 hours in air, descends dry 8～16 hours at 110 ℃ again, burns till under 1500 ℃, and soaking time is 3～5 hours.
With the product that the preparation method obtained of present embodiment, can obtain apparent porosity 40～50%, unit weight is at 1.74～1.91g/cm
3, mean pore size is that 3.273～4.475 μ m, compressive strength are corundum-mullite light heat insulation material of 54～60Mpa.
Embodiment 3
A kind of porous mullite ceramic materials preparation method: with colliery powder and the Al (OH) of particle diameter between 10～88 μ m
3Powder, percentage composition is 46～50%, 54～50% to prepare burden by weight respectively, adds 2～10% water of above-mentioned compound weight and 1.9～2.9% MgCO
3Mix and stir.Ageing mixture 16～24 hours, mechanical pressing under 30～50Mpa pressure.Seasoning is 24～32 hours in air, descends dry 16～24 hours at 110 ℃ again, burns till under 1500 ℃, and soaking time is 3～5 hours.
With the product that the preparation method obtained of present embodiment, can obtain apparent porosity 44～48%, unit weight is at 1.88～1.92g/cm
3, mean pore size is that 2.202～3.247 μ m, compressive strength are mullite-corundum light heat insulation material of 52～58Mpa.
Claims (4)
1, a kind of porous mullite ceramic materials and preparation method thereof is characterized in that percentage composition is with 10～50% colliery powder, 50～90% Al (OH) by weight
3Powder is prepared burden, and adds 2～10% water of above-mentioned compound weight and 0～10% additive, through stir, moulding, molding blank 110 ℃ dry 4～24 hours down, under 1400～1600 ℃ of temperature, burn till then, be incubated 1～8 hour.
2, porous mullite ceramic materials according to claim 1 and preparation method thereof is characterized in that described colliery powder, Al (OH)
3The particle diameter of powder is 10～88 μ m.
3, porous mullite ceramic materials according to claim 1 and preparation method thereof is characterized in that described additive or is MgCO
3, or be CaCO
3, or be MgCO
3And CaCO
3Mixture, particle diameter all≤88 μ m.
4, porous mullite ceramic materials according to claim 1 and preparation method thereof is characterized in that described moulding or mechanical compaction or manual ramming, and the pressure of mechanical compaction is 10～400Mpa.