The restorative procedure of mechanical machine-lathed compression spring
Affiliated technical field:
Patent of the present invention relates to a kind of restorative procedure of spring, the restorative procedure of particularly a kind of mechanical workout car system rectangle (or trapezoidal) cross section compression spring.
Background technology:
Often need pitch compression springs such as processing in the mechanical workout, this spring power requires big, the specification of quality height, and therefore Hardness Control narrow range behind the heat-treatment quenching is the very strict spring product of performance requriements.At present, divide two kinds etc. the method for the processing of pitch compression spring: a kind of is coiling, and coiling is divided into hot coiling and the cold coiling of starting material under as-annealed condition; Another kind is a mechanical workout car system spring, promptly processing a spring cross section with mechanical means fully on a circular bar is pitch compression springs such as orthogonal, its manufacturing process is:------excising the unnecessary number of turns---two ends circle is also tight to be machined into the spring external form, and------blast---pressed 24 hours---detection to the plain grinding both ends of the surface for heat-treatment quenching, tempering in starting material annealing.After all production process are finished, the preload P the during installation of test spring
1Value, working load P
2Value, rigidity value, free height H
0Deng, as the P that measures
1, P
2Value, rigidity value, free length H
0In have one to have defectively, the spring of processing can only be scrapped, and can't do over again by retirement.Therefore, the whole process of production of mechanical workout car system rectangle (or trapezoidal) cross section compression spring, especially thermal treatment control requires extremely strict.Because rectangle (or trapezoidal) the cross section compression spring production qualification rate of mechanical workout is not high yet, and this manufacturing tooling cost is than higher, technical difficulty is bigger, therefore be easy to generate waste product, the spring how will scrap returns processing, becomes the qualification rate problem demanding prompt solution that improves mechanical machine-lathed compression spring.
Summary of the invention:
Purpose of the present invention provides a kind of restorative procedure of mechanical machine-lathed compression spring.Utilize this method, can improve the qualification rate of mechanical machine-lathed compression spring, reduce production costs greatly.
Technical scheme of the present invention is:
The spring of needs reparation is carried out average tempering again, and temperature is 450 ± 20 ℃, and the time is 90 minutes, and water-cooled 3-5 minute, the tempered temperature determined that according to the material of spring the Hardness Control of tempering rear spring is in the HRC44-HRC48 scope.The afterbody of tiltedly splitting is connected with the head of pressing machine, having tiltedly splitting of little arc surface with head then struts each pitch of spring, when strutting the pitch of spring, set the spacing of each pitch, adjust the pressure of pressing machine, substantially the same to guarantee that each pitch struts spacing, and control is after each pitch of spring is strutted, the length of spring with return processing before heat-treatment quenching before spring length near or equate, even each pitch is all strutted the free length H of rear spring
0Near or be equal to return processing before thermal treatment before free length.In the process that struts the spring pitch, crooked if spring occurs, then support spring again at the direction place of spring bending, make spring in time obtain alignment, to adjust the linearity of spring, it is not crooked to guarantee to be strutted spring.
To carry out the quenching second time, tempering through the compression spring of above-mentioned operation.The temperature of quenching is 880 ℃, and the time is 10 minutes, oil cooling 5-10 minute; Average tempering is adopted in tempering, and temperature is 410-430 ℃, and the time is 90-120 minute.The Hardness Control of quenching, tempering rear spring was pressed the P of test spring 24 hours again between HRC50-HRC53
1, P
2Value, rigidity value, free length H0 meet processing requirement, can obtain qualified product.
Correction struts employed pressure head angle 10 degree-30 degree of tiltedly splitting of pitch, and tiltedly splitting the pressure head surface requirements has 0.8 above smooth finish, struts in the spring pitch process in correction preventing, causes that the spring rectangular surfaces is inboard to be damaged.
The invention has the beneficial effects as follows:
Adopt the inventive method, needs are returned the spring tempering again of processing, to reduce the intensity and the hardness of spring, in hardness HRC44-HRC48 scope the pitch of spring is strutted adjustment, simultaneously the free length of spring is adjusted, spring can return to the state before the mechanical workout postheat treatment Q-tempering substantially.Again spring is heat-treated quenching, tempered processing.During quenching, spring obtains austenite structure behind 880 ℃ of austenitizings on the metallographic.In insulating process, carbon atom and alloying element atom make the austenite of spring steel obtain homogenizing at the austenite crystal internal diffusion, to improve the hardening capacity and the mechanical property of spring steel.After insulation finished, spring steel entered in machinery oil or the conventional quenching oil and cools off fast, austenite took place to martensitic transformation.
Spring is in average tempering technology, and the metallographic structure that is obtained is a tempering troostite, and this tissue is a matrix with the acicular ferrite, and is distributed with the mixed structure of disperse sheet globular cementite, and wherein the sheet globular cementite is the main strengthening phase of average tempering spring steel.Behind the spring average tempering, the internal stress in the steel significantly reduces, and therefore, can make steel keep high elastic limit, higher-strength and high safe range of stress, and enough toughness.
This restorative procedure can improve the manufacturing qualification rate of mechanical machine-lathed compression spring energetically, and the inventive method is used for the reparation of buffer spring through Chang'an company, and delivery-check qualified rate brings up to 95% by original 65%, year saves ten thousand yuan of starting material 6-8.
Below in conjunction with accompanying drawing and enforcement patent of the present invention is further specified.
Description of drawings
Fig. 1 struts the synoptic diagram of pitch at the correcting spring of doing over again for the present invention.
Among the figure: 1 is press ram, and 2 for tiltedly splitting, and 3 neutralize the spring that contracts for car, and 4 is copper cushion block.
Embodiment
Below to select 65Si for use
2The MnWA material is an example, and the restorative procedure with mechanical machine-lathed compression spring is described.
The spring rotation direction of present embodiment be dextrorotation to, number of active coils n=13, number of total coils n
1=14.5, the external diameter Φ 33.6h12 of spring, internal diameter Φ is 13.6H12, the inside and outside rounded corner of spring is 1 * 45 °, free length
Rigidity
Preload when spring is installed
Working load P when spring is installed
2=15640.6N, the height H when spring is installed
1=140mm, the height H during spring work
2=121mm.
With the spring tempering again that needs are repaired, tempering in the tempering electric furnace, 450-470 ℃ of tempered temperature, the time is 90 minutes, water-cooled 3-5 minute, with the Hardness Control that guarantees the tempering rear spring in the HRC44-HRC48 scope.To prevent that when strutting pitch and alignment tiny crack appears in spring breakage or spring.
Referring to Fig. 1.Spring 1 is put on the copper cushion block 4, when strutting pitch, be not damaged with the surface that guarantees spring.Tiltedly split 2 pitches of putting spring 1 into, tiltedly split 2 with 3 pairs of press rams and exert pressure, to strut spring pitch t, when strutting each pitch of spring, should note adjusting 3 pairs of press rams at any time and tiltedly split 2 pressure, equate with the spacing of each pitch of keeping spring.When the one side pitch of spring strut adjust after, again with spring along axle line Rotate 180 ℃, repeat above-mentioned steps, spring another side pitch is strutted.The free length H of adjusted spring
0Should with return processing before heat-treatment quenching before free length H
0Approaching or equal.In the process that struts the spring pitch, crooked if spring occurs, then support spring again at the direction place of spring bending, make spring in time obtain alignment, to adjust the linearity of spring, it is not crooked to guarantee to be strutted spring.
The pressure head of tiltedly splitting has little arc surface, and its angle 10 degree-30 are spent, and tiltedly split smooth finish 〉=0.8 on pressure head surface, prevent to strut in the spring pitch process in correction, cause the inboard damage of spring rectangular surfaces.
To carry out the quenching second time, tempering through the compression spring of above-mentioned operation.The temperature of quenching is 880 ℃, and the time is 10 minutes, and quenching was finished in cooling in 5-10 minute in the oil.Enter the next process average tempering, tempering temperature is 410-430 ℃, and the time is 90-120 minute.The Hardness Control of Q-tempering rear spring is between HRC50-HRC53, and tempering enters water cooling after finishing, and the refrigerative time is 2-5 minute, presses the P of test spring again 24 hours
1, P
2Value, rigidity value, free length H
0, all meet
Rigidity
P
2=15640.6N enters last operation---blast, obtains qualified product.
The inventive method is used to adopt 60Si
2MnA, 65Si
2MnWA, 55Si
2MnA, 60Si
2The reparation of the mechanical machine-lathed compression spring of material such as CrVA, 65Mn can reach above-mentioned same effect.