CN1868708A - Production method of carbonizing wood floor board - Google Patents
Production method of carbonizing wood floor board Download PDFInfo
- Publication number
- CN1868708A CN1868708A CN 200610051117 CN200610051117A CN1868708A CN 1868708 A CN1868708 A CN 1868708A CN 200610051117 CN200610051117 CN 200610051117 CN 200610051117 A CN200610051117 A CN 200610051117A CN 1868708 A CN1868708 A CN 1868708A
- Authority
- CN
- China
- Prior art keywords
- timber
- temperature
- floor board
- hours
- production method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A technology for manufacturing carbonization wooden floor board includes such steps as drying raw wooden board, charring, curing, polishing, abrading, making tongue and groove, sealing edges, coating and packing the charred wooden floor board has high stability, weatherability and resistance to corrosion.
Description
Technical field
The present invention relates to a kind of production method of carbonizing wood floor board, belong to the woodwork technical field of producing.
Background technology
Timber floor is natural with it, environmental protection and have beautiful texture and become the interior decoration main material.But, distortion such as cracking, infested and arch camber, tile usually appear when timber floor makes, cause quality problems, and therefore, timber floor also is to complain one of higher commodity.How to improve timber floor dimensional stability, prevent timber floor use in cracking, damage by worms, be the problem that timber floor production faces.
At present, the general operation of the production of solid wooden floor board is: drying → health → four sides light → sanding → tongue and groove → edge sealing → application → finished product packing.Common solid wooden floor board is produced the plate body of rectangle, adopts air drying then, directly is processed into finished product after the health.This shows that this common process is not owing to carry out any processing to solid wooden floor board, therefore, moisture content can change with the humidity of environment for use in the solid wooden floor board use of producing.Moisture content is changed to and makes the floor produce defectives such as cracking, distortion.In addition, for the timber of some easy infested moths because baking temperature is low, the worm's ovum of timber can be in timber growth and breeding, in addition, the timber of air drying still contains required nutritional labelings such as worm, ant, is subject to the infringement of extraneous worm, ant.
Summary of the invention
The objective of the invention is to: the timber floor quality that provides a kind of processing to obtain is good, the raising timber floor is stable and the production method of carbonizing wood floor board of the corrosion resistant weather resistance of raising timber, to overcome the deficiencies in the prior art.
The present invention is achieved in that the timber floor blank of producing rectangle, and blank through super-dry, charing processing, health, four sides light, sanding, tongue and groove, edge sealing, application, finished product packing, is obtained carbonizing wood floor board.
Above-mentioned production method of carbonizing wood floor board, charing is handled and is comprised the steps,
A, press 1t/m with the neat piling of timber and at timber heap top
2Standard compression steel plate frame pouring concrete briquetting, in the carbonization of wood equipment of packing into then;
B, in carbonization of wood equipment, adopt the continuous temperature-rising method of staged, temperature is warming up to 120~140 ℃ by the speed that improved 3~7 ℃ in per 4~6 hours;
C, adopt the continuous temperature-rising method of staged, the speed that improved 8~12 ℃ by per 1~3 hour is warming up to 160~240 ℃, and keeps under maximum temperature 3~6 hours, and the charing processing procedure finishes; When temperature raises, improve 8~12 ℃ rapidly and kept 2 hours later on.
D, treat that the charing processing procedure finishes, stop heating, adopt atomization water method to allow timber slowly be cooled to 100 ℃, the saturated steam that feeds 100 ℃ then carries out damping moisture regain processing to timber, in 6~8 hours processing times, the moisture content of timber is adjusted back 4~6%;
E, timber are cooled to temperature under field conditions (factors) and are higher than kiln discharge after 15~30 ℃ of the room temperatures.
Above-mentioned production method of carbonizing wood floor board in step b, adopts the continuous temperature-rising method of staged in carbonization of wood equipment, temperature is warming up to 130 ℃ by the speed that improved 5 ℃ in per 5 hours.
Above-mentioned production method of carbonizing wood floor board in step c, adopts the continuous temperature-rising method of staged, and the speed that improved 10 ℃ by per 2 hours is warming up to 160~240 ℃, and keeps under maximum temperature 4~5 hours, and the charing processing procedure finishes.
The carbonization of wood is handled and to be meant and to allow timber pyrolysis processing for a long time under 160~240 ℃ hot conditions, by reducing the concentration of hydroxyl in the wood components, reduces the hygroscopicity and the internal stress of timber, thus reach increase Wood Dimensional Stability can purpose; Complicated chemical reaction has taken place in wood components in the charing heat treatment process simultaneously, changed some composition of timber, reduced the nutriment of wood-decaying fungus, suppress the growth of mushroom timber from this link of food chain, the complex chemical reaction that takes place in the timber also produces some toxin harmful to rot fungi, can kill rot fungi, improve the corrosion resistant weather resistance of timber.The present invention is applicant's long-term experiment research, on the basis of existing timber floor production method, carbonization of wood treatment technology is applied in the production of timber floor, and at the material and the characteristics of timber floor, sums up the best carbonizing treatment method that is suitable for timber floor.Therefore the present invention has the timber floor of raising stability and corrosion resistant weather resistance, improves the timber floor product quality, prolongs advantages such as timber floor useful life, can be used for the making of various timber floors.
The specific embodiment
Embodiments of the invention: the present invention produces the timber floor blank of rectangle, and blank through super-dry, charing processing, health, four sides light, sanding, tongue and groove, edge sealing, application, finished product packing, is obtained carbonizing wood floor board.
Each step of the present invention can adopt common process to finish, and wherein, the carbonizing treatment method of employing is:
A, press 1t/m with the neat piling of timber and at timber floor heap top
2Standard compression steel plate frame pouring concrete briquetting, in the carbonization of wood equipment of packing into then.
B, timber floor are packed into behind the charing equipment, begin to heat up.The continuous temperature-rising method of the phase I employing staged that heats up, temperature is warming up to 130 ℃ by the speed that improved 5 ℃ in per 5 hours, promptly keep 5h after 5 ℃ heating up on the original temperature basis rapidly, temperature is raised to high 130 ℃ with identical method then, be incubated 5h under 130 ℃ of conditions, first temperature rise period finished.The timber floor kind difference of processing, its maximum temperature is determined according to timber floor density size, the density temperature height, the big temperature of density is low, and the maximum temperature of various timber floors is set according to prior art.
After c, first temperature rise period finish, entered for second temperature rise period.Second temperature rise period was adopted the continuous temperature-rising method of staged, speed by 10 ℃ of raisings in per 2 hours is warming up to 210 ℃, promptly keep 2h after 10 ℃ heating up on the original temperature basis rapidly, temperature is raised to high 210 ℃ with identical method then, and under 210 ℃ of temperature, kept 4 hours, the charing processing procedure finishes.
D, treat that the charing processing procedure finishes after, close the heating valve of charing treatment facility, stop heating, opening the atomized water device valve, jet atomization water in charing equipment is cooled to 100 ℃ to timber floor with atomization water, and the saturated steam that feeds 100 ℃ then in charing equipment carries out damping moisture regain processing to timber floor, in 6 hours processing times, the moisture content of timber floor is got damp again 6%.
E, timber floor is naturally cooled to temperature at last in charing equipment and be higher than kiln discharge after 15~30 ℃ of the room temperatures.
Claims (4)
1, a kind of production method of carbonizing wood floor board is characterized in that: produce the timber floor blank of rectangle, blank through super-dry, charing processing, health, four sides light, sanding, tongue and groove, edge sealing, application, finished product packing, is obtained carbonizing wood floor board.
2, production method of carbonizing wood floor board according to claim 1 is characterized in that: charing is handled and is comprised the steps,
A, press 1t/m with the neat piling of timber and at timber heap top
2Standard compression steel plate frame pouring concrete briquetting, in the carbonization of wood equipment of packing into then;
B, in carbonization of wood equipment, adopt the continuous temperature-rising method of staged, temperature is warming up to 120~140 ℃ by the speed that improved 3~7 ℃ in per 4~6 hours;
C, adopt the continuous temperature-rising method of staged, the speed that improved 8~12 ℃ by per 1~3 hour is warming up to 160~240 ℃, and keeps under maximum temperature 3~6 hours, and the charing processing procedure finishes;
D, treat that the charing processing procedure finishes, stop heating, adopt atomization water method to allow timber slowly be cooled to 100 ℃, the saturated steam that feeds 100 ℃ then carries out damping moisture regain processing to timber, in 6~8 hours processing times, the moisture content of timber is adjusted back 4~6%;
E, timber are cooled to temperature under field conditions (factors) and are higher than kiln discharge after 15~30 ℃ of the room temperatures.
3, production method of carbonizing wood floor board according to claim 2 is characterized in that: in step b, adopt the continuous temperature-rising method of staged in carbonization of wood equipment, temperature is warming up to 130 ℃ by the speed that improved 5 ℃ in per 5 hours.
4, production method of carbonizing wood floor board according to claim 2, it is characterized in that: in step c, adopt the continuous temperature-rising method of staged, the speed that improved 10 ℃ by per 2 hours is warming up to 160~240 ℃, and under maximum temperature, kept 4~5 hours, the charing processing procedure finishes.