CN1865339A - Bamboo/plastic surface crusting composite material and its preparation method - Google Patents
Bamboo/plastic surface crusting composite material and its preparation method Download PDFInfo
- Publication number
- CN1865339A CN1865339A CNA2006100353719A CN200610035371A CN1865339A CN 1865339 A CN1865339 A CN 1865339A CN A2006100353719 A CNA2006100353719 A CN A2006100353719A CN 200610035371 A CN200610035371 A CN 200610035371A CN 1865339 A CN1865339 A CN 1865339A
- Authority
- CN
- China
- Prior art keywords
- bamboo
- matrix material
- foam matrix
- moulded
- mould
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a bamboo-plastic composite material and its preparing process, wherein the composite material comprises the following constituents (by weight portions): PVC 100, bamboo powder 30-80, coupling agent 0.5-2%, heat stabilizer 0.5-4, lubricating agent 0.2-2%, foaming agent 0.2-0.8, and foaming regulation agent 3-12.
Description
Technical field
The present invention relates to bamboo and mould the field, be specifically related to a kind of bamboo and mould foam matrix material and production method thereof.
Background technology
The bamboo molding technology is to develop a kind of faster type material processing technology in recent years at home and abroad.Plastics, material that this two classes nature difference of timber is bigger are mixed mutually and be processed into goods by rational technology, equipment.With its novel idea, novel design, novel product, the appearance of bamboo molding technology will greatly advance the development of new material industry.As everyone knows, when 21 century arrived, people constantly pursued and yearn for novel material, new technology industrial expansion, put from this, and the development and application of bamboo molding technology has great vitality and development prospect.
Bamboo is moulded foam material and compares with general bamboo moulding material, have in light weight, advantage such as the raw material consumption is few, and the outward appearance woodiness touch is good, and is with low cost.But, problem such as existing foamed products ubiquity hardness is strong, toughness is not enough, rub resistance is not strong.The adding of bamboo powder then can effectively improve the surface hardness and the antifriction performance of goods.Simultaneously can reclaim a large amount of waste and old bamboo products, have great environment protection significance and economic outlook.
Summary of the invention
The objective of the invention is to overcome the problem that existing bamboo moulding material exists, provide a kind of hardness height, good-toughness, rub resistance strong, and bamboo with low cost is moulded the foam matrix material.
Another object of the present invention provides the production method that above-mentioned bamboo is moulded the foam matrix material.
To achieve these goals, the present invention adopts following technical scheme:
Bamboo of the present invention is moulded the foam matrix material, contains following component and parts by weight:
PVC 100 bamboo powder 30～80
Coupling agent 0.5～2 thermo-stabilizer 0.5～4
Lubricant 0.2～2 whipping agent 0.2～0.8
Foaming control agent 3～12.
Mould in the foam matrix material in above-mentioned bamboo, also comprise photostabilizer UV-531 (Octabenzone), parts by weight are 0.05～0.5.
Mould in the foam matrix material in above-mentioned bamboo, described foaming control agent is acrylics foaming control agent (commodity is called ZB530).
Mould in the foam matrix material in above-mentioned bamboo, described coupling agent is silane coupling agent γ-An Jibingjisanyiyangjiguiwan (commodity are called KH550) or γ-Racemic glycidol oxygen propyl trimethoxy silicane (commodity are called KH560).
Mould in the foam matrix material in above-mentioned bamboo, described PVC is SG type (suspension method is universal), can be that virgin material also can be a reclaimed materials.
Mould in the foam matrix material in above-mentioned bamboo, described thermo-stabilizer is general complex lead salt stabilizer (as the PF18 of bear board SMS318 or three beneficial companies), also calcium zinc (as the CZ-93 or the CZ-968 of three beneficial companies) or organotin non-toxic stabilizers such as (as the T-191 of Atofina).Annotate: SMS318, PF18, CZ-93, CZ-968, T-191 are trade name.
Mould in the foam matrix material in above-mentioned bamboo, described lubricant is internal lubricant or external lubricant or its mixture, wherein internal lubricant is a kind of or combination in calcium stearate, lead stearate, barium stearate, the Zinic stearas, and external lubricant is a kind of or combination in paraffin, PE wax, EBS (ethylene bis stearamide), the OPE wax.
Mould in the foam matrix material in above-mentioned bamboo, described whipping agent is azo two formyl ammonia (common name AC whipping agent) or 4,4-OBSH (common name OBSH whipping agent).
Above-mentioned bamboo powder is that various bamboo plants are pulverized the particulate that obtains.
The production method that above-mentioned PVC bamboo is moulded the foam matrix material is made up of following steps:
(1) with coupling agent treatment bamboo powder;
(2) add the polyvinyl chloride resin powder earlier, add thermo-stabilizer, lubricant, foaming control agent, whipping agent more successively, be mixed evenly;
(3) add a watercooling jacket that is connected with mould mouth mould, cut the length of having lacked core in mouthful mould simultaneously.Design has the water route in the watercooling jacket that adds, and has water inlet and water outlet.Feeding the water route water jacket when extruding starts working.The purpose of water jacket is for cooling material surface, to obtain slick outside surface.Simultaneously, cut the length of short mouthful of model core, make the structure of the inner no core of water jacket to provide good space for the inside foaming.For the heat of preventing seam mould well heater imports water jacket into by connection, cause jacket water temperature too high, cause cooling performance to descend, water jacket has been made grooved with the joint face of mouthful mould, to reduce contact area to greatest extent, reduces the thermal conductance effect.
(4) forcing machine is matched with mould, cooling and shaping device, towing mechanism, cutting unit;
(5) setting machine barrel, die head temperature are 100～180 ℃, open watercooling jacket, cooling and shaping device, towing mechanism and cutting unit, mixed ingredients is put in the forcing machine, setting dump temperature is 80～100 ℃, the two extruder screw rotating speed 20～150rpm of awl, reinforced rotating speed 10～80rpm can obtain to have the smooth surface of not foaming of skinning and mould foam composite material with the loose inner bamboo of foaming.
Compared with prior art, the present invention has following beneficial effect:
1, bamboo of the present invention mould foam material have in light weight, hardness is high, good-toughness, rub resistance is strong, water tolerance and good weatherability have woodiness touch, and with low cost.Can be used for fields such as building decoration section bar, floor, baseboard, handrail, gardens chair stool, fence; Be to mould the new generation product of Dai Mu.
2, bamboo of the present invention is moulded one step of foam material employing and extrudes production, need not the bamboo powder is anticipated, and has reduced production stage, has improved efficient; Add watercooling jacket, cool off the material surface effectively, and the core of cutting after short cooperates with a mouthful mould,, mould the foam material thereby obtain the smooth PVC bamboo of foaming with inside of not foaming of surface skining for foaming provides enough foaming spaces.
Embodiment
At first the bamboo plant fiber process is become micro mist, then the bamboo powder is rendered in the mixer, the outer drying that heats up that heats, remove the large quantity of moisture in the bamboo powder, add coupling agent again and carry out surface treatment, add the polyvinyl chloride resin powder then, be docile and obedient preface again and add thermo-stabilizer, lubricant, foaming control agent, whipping agent, be mixed evenly; Add a watercooling jacket that is connected with mould mouth mould, cut short mouthful of model core 10cm; Forcing machine is matched with mould, cooling and shaping device, towing mechanism, cutting unit; Set machine barrel, die head temperature, open watercooling jacket, cooling and shaping device, towing mechanism and cutting unit, mixed ingredients is put in the two forcing machines of awl, set dump temperature, the two extruder screw rotating speeds of awl, reinforced rotating speed can be produced and has do not foam smooth surface and the loose inner bamboo of foaming of skinning and mould foam material.According to this preparation method, each embodiment is as shown in table 1.
Table 1
Annotate: "-" expression is not added.
Claims (9)
1, a kind of bamboo is moulded the foam matrix material, it is characterized in that containing following component and parts by weight:
PVC 100 bamboo powder 30～80
Coupling agent 0.5～2 thermo-stabilizer 0.5～4
Lubricant 0.2～2 whipping agent 0.2～0.8
Foaming control agent 3～12.
2, bamboo as claimed in claim 1 is moulded the foam matrix material, it is characterized in that also comprising photostabilizer UV-531, and parts by weight are 0.05～0.5.
3, bamboo as claimed in claim 1 or 2 is moulded the foam matrix material, it is characterized in that described foaming control agent is the acrylics foaming control agent.
4, bamboo as claimed in claim 1 or 2 is moulded the foam matrix material, it is characterized in that described coupling agent is silane coupling agent γ-An Jibingjisanyiyangjiguiwan or γ-Racemic glycidol oxygen propyl trimethoxy silicane or its mixture.
5, bamboo as claimed in claim 1 or 2 is moulded the foam matrix material, it is characterized in that described PVC is that suspension method is universal.
6, bamboo as claimed in claim 1 or 2 is moulded the foam matrix material, it is characterized in that described thermo-stabilizer is complex lead salt stabilizer or calcium zinc stabilizer or organotin stabilizer.
7, bamboo as claimed in claim 1 or 2 is moulded the foam matrix material, it is characterized in that described lubricant is internal lubricant or external lubricant or its mixture, wherein internal lubricant is a kind of or combination in calcium stearate, lead stearate, barium stearate, the Zinic stearas, and external lubricant is a kind of or combination in paraffin, PE wax, ethylene bis stearamide, the OPE wax.
8, bamboo as claimed in claim 1 or 2 is moulded the foam matrix material, it is characterized in that described whipping agent is azo two formyl ammonia or 4,4 ' OBSH.
9, claims 1 described bamboo production method of moulding the foam matrix material is characterized in that comprising the steps:
(1) with coupling agent treatment bamboo powder;
(2) add the polyvinyl chloride resin powder earlier, add thermo-stabilizer, lubricant, foaming control agent, whipping agent more successively, be mixed evenly;
(3) add a watercooling jacket that is connected with mould mouth mould, and cut the core in the short mouthful mould;
(4) forcing machine is matched with mould, cooling and shaping device, towing mechanism, cutting unit;
(5) setting machine barrel, die head temperature are 100～180 ℃, open watercooling jacket, cooling and shaping device, towing mechanism and cutting unit, mixed ingredients is put in the forcing machine, setting dump temperature is 80～100 ℃, extruder screw rotating speed 20～150rpm, reinforced rotating speed 10～80rpm can obtain bamboo and mould the foam matrix material.