CN1861543A - Gypsum base plastering mortar and gypsum base gravity flowing levelling mortar - Google Patents
Gypsum base plastering mortar and gypsum base gravity flowing levelling mortar Download PDFInfo
- Publication number
- CN1861543A CN1861543A CNA2005100691848A CN200510069184A CN1861543A CN 1861543 A CN1861543 A CN 1861543A CN A2005100691848 A CNA2005100691848 A CN A2005100691848A CN 200510069184 A CN200510069184 A CN 200510069184A CN 1861543 A CN1861543 A CN 1861543A
- Authority
- CN
- China
- Prior art keywords
- mortar
- dry
- gypsum
- gypsum base
- mixed mortar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A gypsum-based mortar for plastering is prepared from semi-hydrated gypsum, quartz sand, Ca(OH)2, powdered coal ash, slag, lime stone, hoolamite, volcanic dregs, haydite, polystyrene foam, expanded pearlite, zeolite, and ethene-vinyl acetate copolymer resin. Agypsum-based mortar for automatic leveling is prepared from semi- hydrated gypsum, quartz sand, Ca(OH)2, powdered coal ash, slag, lime stone, ethene-vinyl acetate copolymer resin, methyl hydroxyethyl (or hydroxypropyl) cellulose ether, sulfonated cyanuramide-formaldehyde resin and gluconate.
Description
Technical field
The present invention relates to a kind of gypsum base mortar, be more particularly to a kind of gypsum base motar (or dry-mixed mortar) and a kind of gypsum base gravity flowing levelling mortar or dry-mixed mortar.
Background technology
What at present material of construction used all is the concrete base building material, and voidage is very low in its structure, can not store more water, and the atmospheric moisture in can not surge chamber does not possess fire prevention yet or prolongs the function of catching fire.
Because there is above problem in prior art, so presses on the market and a kind ofly can store more water, the atmospheric moisture in can surge chamber, and can prevent fires or prolong the material of construction of the function of catching fire.
Summary of the invention
Technical problem to be solved by this invention is to overcome deficiency of the prior art, provide a kind of voidage high can absorb airborne moisture, and when dry air, emit the gypsum base motar (or dry-mixed mortar) and the high good fluidity that can absorb airborne moisture of a kind of voidage of moisture content wherein, internal stress is low, is difficult for forming fissured gypsum base gravity flowing levelling mortar (or dry-mixed mortar).
In order to solve the technical problem of above-mentioned existence, the present invention is achieved by the following technical solutions:
A kind of gypsum base motar or dry-mixed mortar is characterized in that it is mortar or the dry-mixed mortar of being made by the raw material of following weight %:
α/β semi-hydrated gypsum 19-20%
Quartz sand 14-16% (granularity is 0-1mm)
14-16% (granularity is 1-2mm)
Ca(OH)
2 4-5%
Flyash (drying) 0.5-1.5%
Slag (levigate) 0.5-2.0%
Wingdale (levigate) 2-3%
Float stone 2-4%
Volcanic cinder 1-2%
Haydite 0.2-0.4%
Polystyrene foam light skeletal 0.3-0.5%
Pearlstone 0.35-0.45%
Zeolite 0.10-0.15%
Vinyl acetate and ethylene copolymer 4-5%
Dimethyl hydroxyethyl/methylhydroxypropylcellulose ether 4-6%
Sulfonated melamine compound resin 0.2-0.3%
Gluconate 0.2-0.3%
Ligninsulfonate 0.2-0.3%
Tartrate 3-4%
Sugar calcium 2-4%
Citric acid 3-4%
Zinc salt 2-4%
Dodecane sulfonate 0.5-1.5%
Fatty alcohol-polyoxyethylene ether 0.5-1.5%
Alkylphenol ethylene oxide condensate 3-4%
Calcium acrylate 1.0-1.5%
Polyacrylonitrile fibre/polyvinyl alcohol fiber 1.0-1.5%
Ordinary Portland cement 3-4%.
As previously discussed gypsum base motar or dry-mixed mortar is characterized in that it is mortar or the dry-mixed mortar of being made by the raw material of following weight %:
α/β semi-hydrated gypsum 20%
Quartz sand 15% (granularity is 0-1mm)
15% (granularity is 1-2mm)
Ca(OH)
2 5%
Flyash (drying) 1.0%
Slag (levigate) 1.0%
Wingdale (levigate) 3%
Float stone 2%
Volcanic cinder 2%
Haydite 0.2%
Polystyrene foam light skeletal 0.4%
Pearlstone 0.4%
Zeolite 0.10%
Vinyl acetate and ethylene copolymer 5%
Dimethyl hydroxyethyl/methylhydroxypropylcellulose ether 5%
Sulfonated melamine compound resin 0.3%
Gluconate 0.3%
Ligninsulfonate 0.3%
Tartrate 3%
Sugar calcium 3%
Citric acid 3%
Zinc salt 3%
Dodecane sulfonate 1.0%
Fatty alcohol-polyoxyethylene ether 1.0%
Alkylphenol ethylene oxide condensate 4%
Calcium acrylate 1.0%
Polyacrylonitrile fibre/polyvinyl alcohol fiber 1.0%
Ordinary Portland cement 4%.
Above-mentioned semi-hydrated gypsum is by adding plaster of paris to 150 ± 50 ℃, and dehydration makes;
By adding plaster of paris to 600 ± 50 ℃, can dewater makes dehydrated gyp-.
Its reaction formula is as follows respectively:
The preparation method of a kind of gypsum base motar or dry-mixed mortar, it is characterized in that: fuel-burning power plant institute exhaust gas discharged is carried out high-purity dihydrate gypsum that gained is handled in desulfurization with aqua calcis, at 150 ± 50 ℃ of semi-hydrated gypsums that make after carrying out calcined dehydration 0.5-1 hour, or make dehydrated gyp-after carrying out calcined dehydration 0.5-1 hour at 600 ± 50 ℃; Semi-hydrated gypsum or dehydrated gyp-as main gelling material, are added above-mentioned various chemical additive efficiently and corresponding packing material, the gypsum base motar or the dry-mixed mortar that are configured to according to the above ratio.
A kind of gypsum base gravity flowing levelling mortar or dry-mixed mortar is characterized in that it is mortar or the dry-mixed mortar of being made by the raw material of following weight %:
Semi-hydrated gypsum (the 19-20% of α/β)
Quartz sand 14-16% (granularity is 0-1mm)
14-16% (granularity is 1-2mm)
Ca(OH)
2 4-6%
Flyash (drying) 0.5-1.5%
Slag (levigate) 0.5-1.5%
Wingdale (levigate) 0.3-0.5%
Vinyl acetate and ethylene copolymer 0.5-0.7%
Dimethyl hydroxyethyl/methylhydroxypropylcellulose ether 2-4%
Sulfonated melamine compound resin 3-5%
Gluconate 3-5%
Ligninsulfonate 1-3%
Tartrate 3-5%
Sugar calcium 3-5%
Citric acid 2-4%
Zinc salt 3-5%
Dodecane sulfonate 1-3%
Fatty alcohol-polyoxyethylene ether 1-3%
Alkylphenol ethylene oxide condensate 1-3%
Calcium acrylate 1-3%
Polyacrylonitrile fibre/polyvinyl alcohol fiber 1-3%
Ordinary Portland cement 3-5%.
As previously discussed gypsum base gravity flowing levelling mortar or dry-mixed mortar is characterized in that it is mortar or the dry-mixed mortar of being made by the raw material of following weight %:
(α/β) 20% for semi-hydrated gypsum
Quartz sand 15% (granularity is 0-1mm)
15% (granularity is 1-2mm)
Ca(OH)
2 5%
Flyash (drying) 1.0%
Slag (levigate) 1.0%
Wingdale (levigate) 0.4%
Vinyl acetate and ethylene copolymer 0.6%
Dimethyl hydroxyethyl/methylhydroxypropylcellulose ether 3%
Sulfonated melamine compound resin 4%
Gluconate 4%
Ligninsulfonate 2%
Tartrate 4%
Sugar calcium 4%
Citric acid 3%
Zinc salt 4%
Dodecane sulfonate 2%
Fatty alcohol-polyoxyethylene ether 2%
Alkylphenol ethylene oxide condensate 2%
Calcium acrylate 2%
Polyacrylonitrile fibre/polyvinyl alcohol fiber 2%
Ordinary Portland cement 4%.
The preparation method of a kind of gypsum base gravity flowing levelling mortar or dry-mixed mortar, it is characterized in that: fuel-burning power plant institute exhaust gas discharged is carried out high-purity dihydrate gypsum that gained is handled in desulfurization with aqua calcis, at 150 ± 50 ℃ of semi-hydrated gypsums that carry out making behind the calcined dehydration, or carry out making dehydrated gyp-behind the calcined dehydration at 600 ± 50 ℃; With semi-hydrated gypsum or dehydrated gyp-as main gelling material, add various aggregates and various chemical additive efficiently according to the above ratio in factory-configured, mix and a kind of dry-mix that is specifically designed to floor leveling of making: gypsum base gravity flowing levelling mortar or dry-mixed mortar.
This mortar has good flowing property, and the energy Automatic Levelling can be used for interior architecture thing floor leveling, as is used to fill the uneven of ground, micro-cavity and crack etc.The levelling that can be widely used in ground such as indoor laying carpet, PVC floor, timber floor is handled, and is specially adapted to floor heating system (hot-water heating or electricity are warm).
More than in other raw material except flyash, slag be when each power station is bought by levigate excessively, other raw material is all from various markets, especially buy on the building materials market, for example: Wingdale is the Wingdale of the levigate mistake bought from the building materials market, remaining again other raw material is bought from various markets, is not just enumerating one by one herein.
The pore structure that an important feature of the present invention is the gypsum base mortar is crystallizated into the needle-like crystal intersection by dihydrate gypsum and forms, so in needle-shaped crystal structure, exist a large amount of freeboards, be that voidage is very high, so when humidity is too high in the air, the gypsum base mortar can absorb airborne moisture content by the pore structure, that is to say: in its internal pore structure of gypsum base mortar, can store a large amount of moisture content, and when outside atmosphere is dry gradually, the moisture content of these storages can be evaporated in the room air gradually along the pore structure and go, thereby further reduce atmospheric moisture, come atmospheric moisture in the surge chamber with this, that is to say: gypsum-based construction material has certain " breathing " function, well the atmospheric moisture in the surge chamber;
Another important feature of the present invention is that the gypsum base mortar has good performance in fire, and this mainly is because dihydrate gypsum (CuSO
4.2H
2O) chemically contain two crystal water, just contain about 21% crystal water (so-called " fire extinguishing water "), when high temperature, crystal water in the energy discharging structure, (its reaction formula is face as follows), these moisture content can be diffused in the air of surface of wall rapidly, and then at materials for wall surface formation one deck " aqueous vapor film ", should " aqueous vapor film " can reduce the temperature on materials for wall surface, and can play the effect of isolating oxygen again, stop and delayed the further burning of materials for wall/buildings with this.
About 21% (weight)
Compared with prior art, the invention has the beneficial effects as follows:
1, compares with the concrete base building material, the voidage of gypsum mortar is very high, when humidity is too high in the air, can absorbs airborne moisture content, and store a large amount of moisture content, when outside atmosphere is dry gradually, the moisture content of these storages can be evaporated in the room air gradually and go, and reduces atmospheric moisture, the atmospheric moisture in the surge chamber, that is to say, well the atmospheric moisture in the surge chamber;
2, the gypsum base mortar has good performance in fire, when high temperature, crystal water in the energy discharging structure, moisture content can be diffused in the air of surface of wall rapidly, form one deck " aqueous vapor film " on the materials for wall surface, both can reduce the temperature on materials for wall surface, and can play the effect of isolating oxygen again, stop and delayed the further burning of materials for wall/buildings with this;
3, can guarantee the quality of sand-cement slurry: this is because the performance of gypsum base mortar itself: the common quality defect of sand-cement slurry such as for example its surface compressed crack, hollowing can not occur, come off;
4, nontoxic, tasteless, harmless to skin, workability is good, and easy construction is fit to the mechanical execution fast drying, the intensity height, and wear resistance is good, can disposablely carry out the metope levelling;
5, good heat insulation and preservation effect is arranged, fire line is good, has certain " breathing " function, well the atmospheric moisture in the surge chamber;
6, adaptability is strong: be easy to bond wallpaper and ceramic tile, can make the kinds of surface decorating structure.
Narrate the performance of gypsum base gravity flowing levelling mortar below again:
Gypsum base gravity flowing levelling mortar good fluidity, and internal stress is low, is difficult for forming the crack;
(concrete thickness is relevant with the prescription of gypsum base gravity flowing levelling mortar but one-off construction is from 1mm-60mm! );
Can be used for thin layer floor heating system (electrically heated and water heating system);
But about 30min of engineering time;
Available mechanical means is carried out auxiliary construction, can further improve operating efficiency and construction quality;
Gypsum base gravity flowing levelling mortar rate of set is fast, can go up about 4~24h between man-hour;
The about 15-30N/mm of mortar ultimate compression strength (28 days);
The about 5-10N/mm of mortar folding strength (28 days);
The about 1.6kg/m of mortar consumption
2Mm (concrete consumption is relevant with the surface pore structure/crude degree of substrate and the denseness of mortar etc.);
The gypsum base gravity flowing levelling mortar meets German hazardous material regulations of rules (GefStoff V), does not contain hazardous material;
Fire-protection rating A1 (with reference to 96/603/EG).
All under laboratory condition, room temperature is 20 ℃ to above data, and 65% relative air humidity records.
Embodiment
Embodiment 1
A kind of gypsum base motar or dry-mixed mortar is characterized in that it is mortar or the dry-mixed mortar of being made by the raw material of following weight % (also can represent with parts by weight):
α/β semi-hydrated gypsum 20%
Quartz sand 16% (granularity is 0-1mm)
14% (granularity is 1-2mm)
Ca(OH)
2 5%
Flyash (drying) 1.5%
Slag (levigate) 0.5%
Wingdale (levigate) 3%
Float stone 3%
Volcanic cinder 1%
Haydite 0.2%
Polystyrene foam light skeletal 0.5%
Pearlstone 0.35%
Zeolite 0.15%
Vinyl acetate and ethylene copolymer 5%
Dimethyl hydroxyethyl/methylhydroxypropylcellulose ether 5%
Sulfonated melamine compound resin 0.3%
Gluconate 0.2%
Ligninsulfonate 0.3%
Tartrate 4%
Sugar calcium 2%
Citric acid 4%
Zinc salt 2%
Dodecane sulfonate 1.5%
Fatty alcohol-polyoxyethylene ether 0.5%
Alkylphenol ethylene oxide condensate 4%
Calcium acrylate 1.0%
Polyacrylonitrile fibre/polyvinyl alcohol fiber 1.5%
Ordinary Portland cement 3.5%.
Embodiment 2
A kind of gypsum base motar or dry-mixed mortar is characterized in that it is mortar or the dry-mixed mortar of being made by the raw material of following weight %:
α/β semi-hydrated gypsum 19%
Quartz sand 14% (granularity is 0-1mm)
16% (granularity is 1-2mm)
Ca(OH)
2 4%
Flyash (drying) 0.5%
Slag (levigate) 2.0%
Wingdale (levigate) 2%
Float stone 4%
Volcanic cinder 2%
Haydite 0.4%
Polystyrene foam light skeletal 0.35%
Pearlstone 0.45%
Zeolite 0.1%
Vinyl acetate and ethylene copolymer 4%
Dimethyl hydroxyethyl/methylhydroxypropylcellulose ether 6%
Sulfonated melamine compound resin 0.2%
Gluconate 0.3%
Ligninsulfonate 0.2%
Tartrate 3%
Sugar calcium 4%
Citric acid 3%
Zinc salt 3.5%
Dodecane sulfonate 1.0%
Fatty alcohol-polyoxyethylene ether 1.5%
Alkylphenol ethylene oxide condensate 3%
Calcium acrylate 1.0%
Polyacrylonitrile fibre/polyvinyl alcohol fiber 1.5%
Ordinary Portland cement 3%.
Embodiment 3
A kind of gypsum base motar or dry-mixed mortar is characterized in that it is mortar or the dry-mixed mortar of being made by the raw material of following weight %:
α/β semi-hydrated gypsum 20%
Quartz sand 15% (granularity is 0-1mm)
15% (granularity is 1-2mm)
Ca(OH)
2 5%
Flyash (drying) 1.0%
Slag (levigate) 1.0%
Wingdale (levigate) 3%
Float stone 2%
Volcanic cinder 2%
Haydite 0.2%
Polystyrene foam light skeletal 0.4%
Pearlstone 0.4%
Zeolite 0.10%
Vinyl acetate and ethylene copolymer 5%
Dimethyl hydroxyethyl/methylhydroxypropylcellulose ether 5%
Sulfonated melamine compound resin 0.3%
Gluconate 0.3%
Ligninsulfonate 0.3%
Tartrate 3%
Sugar calcium 3%
Citric acid 3%
Zinc salt 3%
Dodecane sulfonate 1.5%
Fatty alcohol-polyoxyethylene ether 1.0%
Alkylphenol ethylene oxide condensate 3.5%
Calcium acrylate 1.0%
Polyacrylonitrile fibre/polyvinyl alcohol fiber 1.0%
Ordinary Portland cement 4%.
Embodiment 4
The preparation method of a kind of gypsum base motar or dry-mixed mortar, it is characterized in that: fuel-burning power plant institute exhaust gas discharged is carried out high-purity dihydrate gypsum that gained is handled in desulfurization with aqua calcis, at the semi-hydrated gypsum that carries out about 150 ℃ making behind the calcined dehydration, or carrying out making dehydrated gyp-behind the calcined dehydration about 600 ℃; Semi-hydrated gypsum or dehydrated gyp-as main gelling material, are aided in above-mentioned various chemical additives efficiently and corresponding packing material, the gypsum base dry-mixed mortar that evenly is configured to by the material use properties: gypsum base motar.
Embodiment 5
A kind of gypsum base gravity flowing levelling mortar or dry-mixed mortar is characterized in that it is mortar or the dry-mixed mortar of being made by the raw material of following weight %:
(α/β) 20% for semi-hydrated gypsum
Quartz sand 15% (granularity is 0-1mm)
15% (granularity is 1-2mm)
Ca(OH)
2 5%
Flyash (drying) 1.0%
Slag (levigate) 1.0%
Wingdale (levigate) 0.4%
Vinyl acetate and ethylene copolymer 0.6%
Dimethyl hydroxyethyl/methylhydroxypropylcellulose ether 3%
Sulfonated melamine compound resin 4%
Gluconate 4%
Ligninsulfonate 2%
Tartrate 4%
Sugar calcium 4%
Citric acid 3%
Zinc salt 4%
Dodecane sulfonate 2%
Fatty alcohol-polyoxyethylene ether 2%
Alkylphenol ethylene oxide condensate 2%
Calcium acrylate 2%
Polyacrylonitrile fibre/polyvinyl alcohol fiber 2%
Ordinary Portland cement 4%.
Embodiment 6
A kind of gypsum base gravity flowing levelling mortar or dry-mixed mortar is characterized in that it is mortar or the dry-mixed mortar of being made by the raw material of following weight %:
(α/β) 19% for semi-hydrated gypsum
Quartz sand 15.5% (granularity is 0-1mm)
14.5% (granularity is 1-2mm)
Ca(OH)
2 5.5%
Flyash (drying) 0.5%
Slag (levigate) 1.5%
Wingdale (levigate) 0.3%
Vinyl acetate and ethylene copolymer 0.5%
Dimethyl hydroxyethyl/methylhydroxypropylcellulose ether 2.5%
Sulfonated melamine compound resin 4.5%
Gluconate 3.5%
Ligninsulfonate 3%
Tartrate 4.7%
Sugar calcium 3.5%
Citric acid 2%
Zinc salt 3%
Dodecane sulfonate 3%
Fatty alcohol-polyoxyethylene ether 1%
Alkylphenol ethylene oxide condensate 3%
Calcium acrylate 3%
Polyacrylonitrile fibre/polyvinyl alcohol fiber 1%
Ordinary Portland cement 5%.
Embodiment 7
A kind of gypsum base gravity flowing levelling mortar or dry-mixed mortar is characterized in that it is mortar or the dry-mixed mortar of being made by the raw material of following weight %:
(α/β) 20% for semi-hydrated gypsum
Quartz sand 14.5% (granularity is 0-1mm)
16% (granularity is 1-2mm)
Ca(OH)
2 4%
Flyash (drying) 1.5%
Slag (levigate) 0.5%
Wingdale (levigate) 0.5%
Vinyl acetate and ethylene copolymer 0.7%
Dimethyl hydroxyethyl/methylhydroxypropylcellulose ether 4%
Sulfonated melamine compound resin 3.3%
Gluconate 5%
Ligninsulfonate 1%
Tartrate 3%
Sugar calcium 5%
Citric acid 4%
Zinc salt 5%
Dodecane sulfonate 1%
Fatty alcohol-polyoxyethylene ether 3%
Alkylphenol ethylene oxide condensate 1%
Calcium acrylate 1%
Polyacrylonitrile fibre/polyvinyl alcohol fiber 3%
Ordinary Portland cement 3%.
Embodiment 8
The preparation method of a kind of gypsum base gravity flowing levelling mortar or dry-mixed mortar, it is characterized in that: fuel-burning power plant institute exhaust gas discharged is carried out high-purity dihydrate gypsum that gained is handled in desulfurization with aqua calcis, 150 ± 50 ℃ calcine dehydration in 0.5-1 hour after the semi-hydrated gypsum that makes, or make dehydrated gyp-after calcining dehydration in 0.5-1 hour at 600 ± 50 ℃; Semi-hydrated gypsum or dehydrated gyp-as main gelling material, are aided in above-mentioned various chemical additives efficiently and corresponding packing material, the gypsum base dry-mixed mortar that is configured to by the material use properties: gypsum base gravity flowing levelling mortar.
Claims (4)
1, a kind of gypsum base motar or dry-mixed mortar is characterized in that it is mortar or the dry-mixed mortar of being made by the raw material of following weight %:
α/β semi-hydrated gypsum 19-20%
Quartz sand size is 0-1mm:14-16%
Granularity is 1-2mm:14-16%
Ca(OH)
2 4-5%
Exsiccant flyash 0.5-1.5%
Levigated slag 0.5-2.0%
Levigated Wingdale 2-3%
Float stone 2-4%
Volcanic cinder 1-2%
Haydite 0.2-0.4%
Polystyrene foam light skeletal 0.3-0.5%
Pearlstone 0.35-0.45%
Zeolite 0.10-0.15%
Vinyl acetate and ethylene copolymer 4-5%
Dimethyl hydroxyethyl/methylhydroxypropylcellulose ether 4-6%
Sulfonated melamine compound resin 0.2-0.3%
Gluconate 0.2-0.3%
Ligninsulfonate 0.2-0.3%
Tartrate 3-4%
Sugar calcium 2-4%
Citric acid 3-4%
Zinc salt 2-4%
Dodecane sulfonate 0.5-1.5%
Fatty alcohol-polyoxyethylene ether 0.5-1.5%
Alkylphenol ethylene oxide condensate 3-4%
Calcium acrylate 1.0-1.5%
Polyacrylonitrile fibre/polyvinyl alcohol fiber 1.0-1.5%
Ordinary Portland cement 3-4%.
2, gypsum base motar as claimed in claim 1 or dry-mixed mortar is characterized in that it is mortar or the dry-mixed mortar of being made by the raw material of following weight %:
α/β semi-hydrated gypsum 20%
Quartz sand size is 0-1mm:15%
Granularity is 1-2mm:15%
Ca(OH)
2 5%
Exsiccant flyash 1.0%
Levigated slag 1.0%
Levigated Wingdale 3%
Float stone 3%
Volcanic cinder 1%
Haydite 0.2%
Polystyrene foam light skeletal 0.5%
Pearlstone 0.35%
Zeolite 0.15%
Vinyl acetate and ethylene copolymer 5%
Dimethyl hydroxyethyl/methylhydroxypropylcellulose ether 5%
Sulfonated melamine compound resin 0.3%
Gluconate 0.2%
Ligninsulfonate 0.3%
Tartrate 3%
Sugar calcium 3%
Citric acid 3%
Zinc salt 3%
Dodecane sulfonate 1.0%
Fatty alcohol-polyoxyethylene ether 1.0%
Alkylphenol ethylene oxide condensate 4%
Calcium acrylate 1.0%
Polyacrylonitrile fibre/polyvinyl alcohol fiber 1.0%
Ordinary Portland cement 4%.
3, a kind of gypsum base gravity flowing levelling mortar or dry-mixed mortar is characterized in that it is mortar or the dry-mixed mortar of being made by the raw material of following weight %:
α/β semi-hydrated gypsum 19-20%
Quartz sand size is 0-1mm:14-16%
Granularity is 1-2mm:14-16%
Ca(OH)
2 4-6%
Exsiccant flyash 0.5-1.5%
Levigated slag 0.5-1.5%
Levigated Wingdale 0.3-0.5%
Vinyl acetate and ethylene copolymer 0.5-0.7%
Dimethyl hydroxyethyl/methylhydroxypropylcellulose ether 2-4%
Sulfonated melamine compound resin 3-5%
Gluconate 3-5%
Ligninsulfonate 1-3%
Tartrate 3-5%
Sugar calcium 3-5%
Citric acid 2-4%
Zinc salt 3-5%
Dodecane sulfonate 1-3%
Fatty alcohol-polyoxyethylene ether 1-3%
Alkylphenol ethylene oxide condensate 1-3%
Calcium acrylate 1-3%
Polyacrylonitrile fibre/polyvinyl alcohol fiber 1-3%
Ordinary Portland cement 3-5%.
4, gypsum base gravity flowing levelling mortar as claimed in claim 3 or dry-mixed mortar is characterized in that it is mortar or the dry-mixed mortar of being made by the raw material of following weight %:
α/β semi-hydrated gypsum 20%
Quartz sand size is 0-1mm:15%
Granularity is 1-2mm:15%
Ca(OH)
2 5%
Exsiccant flyash) 1.0%
Levigated slag 1.0%
Levigated Wingdale 0.4%
Vinyl acetate and ethylene copolymer 0.6%
Dimethyl hydroxyethyl/methylhydroxypropylcellulose ether 3%
Sulfonated melamine compound resin 4%
Gluconate 4%
Ligninsulfonate 2%
Tartrate 4%
Sugar calcium 4%
Citric acid 3%
Zinc salt 4%
Dodecane sulfonate 2%
Fatty alcohol-polyoxyethylene ether 2%
Alkylphenol ethylene oxide condensate 2%
Calcium acrylate 2%
Polyacrylonitrile fibre/polyvinyl alcohol fiber 2%
Ordinary Portland cement 4%.