CN1858270A - 一种菱镁矿石煅烧法 - Google Patents
一种菱镁矿石煅烧法 Download PDFInfo
- Publication number
- CN1858270A CN1858270A CN 200510070386 CN200510070386A CN1858270A CN 1858270 A CN1858270 A CN 1858270A CN 200510070386 CN200510070386 CN 200510070386 CN 200510070386 A CN200510070386 A CN 200510070386A CN 1858270 A CN1858270 A CN 1858270A
- Authority
- CN
- China
- Prior art keywords
- low
- coal
- powder
- giobertite
- small pellets
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种菱镁矿石煅烧法属于菱镁矿石煅烧技术领域，其特征是用氧化镁粉作粘结剂并加粒径0.2mm以下优质高纯度焦炭粉或低灰分、低硫、低磷无烟煤粉和水调拌成具有粘性的煤糊状，把粒径5～10mm菱镁矿石小粒料放入煤糊内搅拌，菱镁矿石小粒料颗粒外面润湿并粘覆一层煤衣，又倒入氧化镁粉与粒径0.2mm以下优质高纯度焦炭粉或低灰分、低硫、低磷无烟煤煤粉混合的干燥粉体内滚动，使其再粘覆一层煤衣，然后用人工或自然干燥入窑内煅烧，本发明优点：1.节能20％以上；2.产量提高25％以上；3.质量提高20％以上；4.既适宜普通立窑又适宜回转窑、隧道窑；5.无昂贵设备投资和维护费用；6.操作简单运行成本低。
Description
技术范畴
本发明属于菱镁矿石煅烧技术领域。
技术背景
据中国化学工业出版社2004年3月第一版《镁化合物生产与应用》载明，工业煅烧菱镁矿石主要有两类：一大类是采用大块料粒径80MM～120MM在立窑内煅烧，存在煅烧时间长，煅烧温度高，而造成的欠烧和过烧现象严重，产品质量不稳定；另一小类是采用将菱镁矿石粉碎成100～200目粉状入窑煅烧，但又存在着设备投资昂贵、运行成本过高、操作技术要求太严、维护费用大、单位产能低；并且，前两类煅烧法均是烧煤制煤气或烧油等气体类、液体类燃料加热的方式，既燃料昂贵又热效率利用低下。
发明内容
本发明针对上述提供新的菱镁矿石煅烧法。
本菱镁矿石煅烧法是这样实现的：用氧化镁粉作粘结剂并加粒径0.2mm以下优质高纯度焦炭粉或低灰分、低硫、低磷无烟煤粉和水调拌成具有粘性的煤糊状，把粒径5～10mm菱镁矿石小粒料放入煤糊内搅拌，菱镁矿石小粒料颗粒外面润湿并粘覆一层煤衣，所形成菱镁矿石粘覆式小粒料，又倒入氧化镁粉与粒径0.2mm以下优质高纯度焦炭粉或低灰分、低硫、低磷无烟煤煤粉混合的干燥粉体内滚动，使其再粘覆一层煤衣，然后用人工或自然的方式将菱镁矿石粘覆式小粒料颗粒上的煤衣干燥或凝固后直接投入窑内煅烧。
本发明具有下列优点：1、节能20％以上；2、产量提高25％以上；3、质量提高20％以上；4、既能适宜普通立窑手工生产又能适应机立窑或非立窑形的其它窑体的机械化生产：如回转窑、隧道窑等；5、无昂贵设备投资和维护费用；6、固体燃料便宜且直接加热形式热效率高、单位产能大；7、操作简单运行成本低。
具体实施方式
下面将结合非限定性实施例作进一步说明：
用通常的碎石机将菱镁矿石块料破碎成粒径为5mm～10mm的小粒料堆放在料库内，用粉煤机将优质高纯度焦炭或低灰分、低硫、低磷无烟煤块粉碎成粒径0.2mm以下的精粉，添加用20％氧化镁粉作的粘结剂和80％高纯度焦煤炭精粉，再加入适量的水调拌成具有粘性的煤糊状倒入搅拌机，将菱镁矿石小粒料也倒入搅拌机内搅拌，使菱镁矿石小粒料颗粒外面润湿并粘附一层煤衣，所形成的粘覆式菱镁矿石小粒料再倒入15％氧化镁粉与85％高纯度的粒径0.2MM焦炭粉或低灰分、低硫、低磷无烟煤粉所混合成的干燥粉体内滚动，使其再粘覆一层煤衣，然后，用自然的方式或人工方进行干燥或凝固，本实施例是用窑内的废余热气体将菱镁矿石粘覆式小粒料颗粒上的煤衣干燥、凝固后，用输送带直接入窑内煅烧。当然，氧化镁粉与焦炭粉或无烟煤粉配比比例是按实际情况进行调节。通常情况下氧化镁粉作为粘结剂比例为10～20％。本实施例中焦炭粉(热值7000千卡/千克)与菱镁矿石小粒料配比额为1∶12.5，综合结算，每吨氧化镁粉耗标煤在160公斤以下。另外，就是由于小粒料通风性相对降低，应在窑底下部加装通风机进行强制通风，但同时也达到了菱镁矿石急烧急冷效果，增强氧化镁煅烧后的活性度。
理论和实践证明：当菱镁矿石料粒径从80～120mm减小到5～10mm，其受热面积增加几番，烧成时间大大缩短，本发明燃料燃烧直接加热矿石热效率显著提高，从而提高了产量25％以上、节标煤20％以上；由于每一小粒料均粘附了一层煤衣，相当于窑内均匀分布了燃料，其石料与燃料达到最佳架构，窑内的预热段、燃烧烧成段、冷却段等各窑段温度均匀稳定又极易控制，尤其重要的是本粘覆式小粒料外煅烧后形成一层保护膜，煅烧过程中的过烧和欠烧大大降低，品质从而提高20％以上；本发明既适宜普通立手工生产又适宜其它窑形机械化作业，现有的水泥立窑、回转窑等设施不需改造，就可用本发明煅烧氧化镁产品。
当然，本发明在煅烧高纯或重质氧化镁砂时，对焦炭或无烟煤粉的纯度与低灰分、低杂质要求更高。
Claims (1)
1、一种菱镁矿石煅烧法，其特征是：用氧化镁粉作粘结剂并加粒径0.2mm以下优质高纯度焦炭粉或低灰分、低硫、低磷无烟煤粉和水调拌成具有粘性的煤糊状，把粒径5～10mm菱镁矿石小粒料放入煤糊内搅拌，菱镁矿石小粒料颗粒外面润湿并粘覆一层煤衣，所形成菱镁矿石粘覆式小粒料，又倒入氧化镁粉与粒径0.2mm以下优质高纯度焦炭粉或低灰分、低硫、低磷无烟煤煤粉混合的干燥粉体内滚动，使其再粘覆一层煤衣，然后用人工或自然的方式将菱镁矿石粘覆式小粒料颗粒上的煤衣干燥或凝固后直接投入窑内煅烧。