CN1854248A - Nanometer fire-retardant material for refrigerator - Google Patents
Nanometer fire-retardant material for refrigerator Download PDFInfo
- Publication number
- CN1854248A CN1854248A CN 200510039195 CN200510039195A CN1854248A CN 1854248 A CN1854248 A CN 1854248A CN 200510039195 CN200510039195 CN 200510039195 CN 200510039195 A CN200510039195 A CN 200510039195A CN 1854248 A CN1854248 A CN 1854248A
- Authority
- CN
- China
- Prior art keywords
- refrigerator
- retardant material
- fire
- nano
- flame retardant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A sort of nanophase flame retardant material used in refrigerator which consists of acrylonitrile, butadiene, cinnamene terpolymer, ABS powder,PVC,CPE,SiO2, Al2O3 ,and DBP. Source of This material is aboard and cost is low. It shows well fire retardant property and is safe to use.
Description
Technical field:
The present invention relates to fire retardant material, more specifically saying so is applied in fire retardant material in the refrigerator.
Background technology:
Fire-retardant that is applied in the refrigerator should have safety in utilization, but materials such as fire-retardant flame-proof ABS that upward uses of present refrigerator, flame-retarding HIPS, fire-retardant PP, fire retardation PC, though cost is not high, flame retardant effect is good, but the fire retardant that it adopted is poly-bromo biphenyl PBB and poly-dibromodiphenyl ether PBDE, because the hazardous property of this based flame retardant progressively is being familiar with, therefore, the use for this based flame retardant must obtain restriction.
Summary of the invention:
The present invention is for avoiding above-mentioned existing in prior technology weak point, and a kind of nano flame retardant material that is applied in the refrigerator safe in utilization is provided.
Material of the present invention raw material by weight consists of:
Propylene is fine, divinyl, styrene copolymer (ABS) powder 90,
Polyvinyl chloride (PVC) 50,
Chlorinatedpolyethylene (CPE) 8,
Nano silicon (SiO
2) 6,
Nano-aluminium oxide (Al
2O
3) 10,
Calcium stearate 3,
Plasticizer DBP 5.
Material of the present invention is with nanometer SiO
2And Al
2O
3Be major ingredient, SiO
2And Al
2O
3Can from flyash, extract, with nanometer SiO
2And Al
2O
3With mixed with resin together, not only can improve the heat-resisting decomposability of resin, when on fire, also can impel resin carbonation.Experiment showed, and in resin, add about 10% nanometer SiO
2And Al
2O
3Just can reach fire retardant material standard UL specification (V-0/1.5mm) requirement of the U.S..
Compared with the prior art, beneficial effect of the present invention is embodied in:
1, material source of the present invention is extensive, can use the byproduct flyash of heat power station to be raw material production nanometer SiO
2And Al
2O
3, with low cost.
2, flame retardant properties of the present invention is good, and is safe in utilization.
Embodiment:
Present embodiment raw material by weight constitutes:
Propylene is fine, divinyl, styrene copolymer (ABS) powder 90,
Polyvinyl chloride (PVC) 50,
Chlorinatedpolyethylene (CPE) 8,
Nano silicon (SiO
2) 6,
Nano-aluminium oxide (Al
2O
3) 10,
Calcium stearate 3,
DBP softening agent 5.
Carry out granulation with above-mentioned raw materials according to the method for routine.
Claims (1)
1, be applied in nano flame retardant material in the refrigerator, it is characterized in that raw material by weight consists of:
Propylene is fine, divinyl, styrene copolymer (ABS) powder 90,
Polyvinyl chloride (PVC) 50,
Chlorinatedpolyethylene (CPE) 8,
Nano silicon (SiO
2) 6,
Nano-aluminium oxide (Al
2O
3) 10,
Calcium stearate 3,
Plasticizer DBP 5.