CN1851384A - Preparing method for paper-made fireworks-firecrackers tube, roket head, seat and fireworks shell - Google Patents
Preparing method for paper-made fireworks-firecrackers tube, roket head, seat and fireworks shell Download PDFInfo
- Publication number
- CN1851384A CN1851384A CN 200610031687 CN200610031687A CN1851384A CN 1851384 A CN1851384 A CN 1851384A CN 200610031687 CN200610031687 CN 200610031687 CN 200610031687 A CN200610031687 A CN 200610031687A CN 1851384 A CN1851384 A CN 1851384A
- Authority
- CN
- China
- Prior art keywords
- firework
- fireworks
- seat
- paper
- tube
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a fireworks and rocket head, base and fireworks spring making method. It uses paper pulp or dry paper pieces or starch as raw material, adds water to mix to equal, takes shaping on pressing shaping machine, and heating to dry for figuration to gain the product. The pressure is 2-20kg/square centimeter, heating temperature is 100-300 degree centigrade and the figuration time is 30-200 seconds. The invention has simple technology, few process, high efficiency, good quality, etc.
Description
Technical field:
The present invention relates to a kind of firework and display shell preparation method, particularly relate to a kind of papery firework tube and rocket head, seat and cartridge case of firework preparation method.
Background technology:
The traditional fabrication method of the cartridge case of firework of the firework tube of making firework and making display shell is to be raw material with paper at present, to open paper earlier greatly and plant into corresponding fritter pattern by the cartridge case of firework difformity, then the multilayer pattern is successively affixed to certain thickness, after drying, hot forming, be modified to cartridge case of firework after cut edge.There are many disadvantages in this cartridge case of firework preparation method, and operation is loaded down with trivial details, needs through tens of procedures to finished product from planting paper, and work efficiency is low, and speed is slow, waste material, and the paper utilization rate has only about 70%.Existing firework tube and rocket head are plastic products, cost an arm and a leg, and environmental protection is brought very big influence.
Summary of the invention: the above-mentioned disadvantage that the objective of the invention is to overcome existing firework tube and rocket head, seat and cartridge case of firework manufacturing technology; provide a kind of efficient, quick, be beneficial to environmental protection, the firework tube of saving paper material and the preparation method of rocket head, seat and cartridge case of firework.
The technical solution of the utility model is a kind of papery firework tube and rocket head, seat and cartridge case of firework preparation method, adopt paper pulp or dried paper is broken into cotton-shaped fragment and starch is raw material, mix with water, on form-pressing machine through the pressing mold press forming, heating, drying typing simultaneously, finally demould obtains finished product;
Moulding pressure is: 2kg/cm
2-20kgcm
2
Heating-up temperature is: 100 ℃-300 ℃
Fixing time is: 30 seconds-200 seconds
Can add the string stiffener in the raw material to increase product strength.Also can add appropriate amount of auxiliary materials in the raw material, auxiliary material is talcum powder, the plaster of paris, white clay, bentonite, fine particle calcium carbonate, calcium chloride.
Advantage of the present invention is:
1, manufacture craft is simple, compares with existing traditional handicraft method, does not need the sample of cutting a sheet of paper, and multilayer is pasted, and the correction multiple working procedure is cut on the limit; And save and beat fairlead.Base, fairlead and cup tube bottom all can be through pressing molds press forming in the lump;
2, raw material paper stock utilization rate height particularly, raw material paper almost 100% obtain utilizing also recyclable firework tube, seat and cartridge case of firework waste-material-preparing;
3, work efficiency height, operation are few, and 1 people can operate an above form-pressing machine, finish firework tube, and rocket head, seat and the tens of people's of cartridge case of firework making conventional method workload, the part costliness that desirable seville orange flower big gun is used mould the product of making not environmental protection.
4, firework tube of Zhi Zuoing and rocket head, seat and cartridge case of firework quality are good, can change shape, size, thickness and the intensity of firework tube, cartridge case of firework as required flexibly and easily.
5, compare with existing firework tube and rocket head, a seat plastic production method, low price not only, and help environmental protection.
Description of drawings:
Fig. 1 is firework rocket head 1 schematic diagram
Fig. 2 is cup-shaped firework 2 schematic diagrames
Fig. 3 is cone barrel firework 3 schematic diagrames
Fig. 4 is hemispherical cartridge case of firework 4 schematic diagrames
Fig. 5 is dish type rocket seat 5 schematic diagrames
The specific embodiment:
The present invention further specifies as follows in conjunction with specific embodiments referring to accompanying drawing:
A kind of papery firework tube and rocket head, seat and cartridge case of firework preparation method, it is characterized in that adopting paper pulp or dried paper to be broken into cotton-shaped fragment and starch is that raw material and water mix, on form-pressing machine through the pressing mold press forming, heating, drying typing simultaneously, finally demould obtains finished product;
Moulding pressure is: 2kg/cm
2-20kgcm
2
Heating-up temperature is: 100 ℃-300 ℃
Fixing time is: 30 seconds-200 seconds
Papery firework tube and rocket head, seat and cartridge case of firework preparation method, this method can add the string stiffener to increase the intensity of goods in raw material.
Wherein raw material paper needs be broken into cotton-shaped fragment if when opening paper greatly on disintegrating machine.
Adhesive is made in the modulation of starch water.
String is cotton, numb short fiber, plays booster action.Consumption does not wait.
In the raw material, by weight percentage, the paper pulp consumption is 25～50%, if cotton-shaped a scrap of paper should be modulated into paper pulp.The starch consumption is 25～50%.
Specific embodiment sees the following form:
| Embodiment | Name of product | Firework tube, cartridge case of firework | Material composition (percentage by weight) | Moulding pressure kg/cm 2 | Heating-up temperature (℃) | Heat time heating time | |||
| Shape | Wall thickness | Size | Paper pulp water content/paper pulp amount | Amylum adhesive | |||||
| 1 | The fireworks display eggshell | Hemispherical (seeing accompanying drawing 1) | 5mm | Diameter 120mm | 18％/45％ | 30％ | 6-12 | 200-250 | 50 |
| 2 | The firework rocket head | Bullet-headed (seeing accompanying drawing 2) | 3mm | The high 60mm of diameter 50mm | 20％/25％ | 50％ | 4-12 | 170-250 | 30 seconds |
| ? ? 3 | The firework tube | Circular cone tubular (seeing accompanying drawing 3) | ? ? 6mm | The high 60mm of diameter 60mm under the last diameter 40mm | ? ? 15％/30％ | ? ? 45％ | ? ? 8-15 | ? ? 200-260 | 150 seconds |
| ? 4 | The firework tube | Cup-shaped (seeing accompanying drawing 4) | ? 7mm | The high 150mm of diameter 80mm | ? 25％/35％ | ? 35％ | ? 9-18 | 210-280 | 200 seconds |
| ? 5 | Firework rocket seat | Dish type (seeing accompanying drawing 5) | ? 3m | Diameter 50mm 15mm | ? 25％/25％ | ? 50％ | ? 3-10 | ? 120-250 | 50-100 second |
Amylum adhesive is to be 50% starch and 50% water hybrid modulation with weight ratio.
Claims (2)
1, a kind of papery firework tube and rocket head, seat and cartridge case of firework preparation method, it is characterized in that adopting paper pulp or dried paper to be broken into cotton-shaped fragment and starch is that raw material and water mix, on form-pressing machine through the pressing mold press forming, heating, drying typing simultaneously, finally demould obtains finished product;
Moulding pressure is: 2kg/cm
2-20kg/cm
2
Heating-up temperature is: 100 ℃-300 ℃
Fixing time is: 30 seconds-200 seconds.
2, papery firework tube according to claim 1 and rocket head, seat and cartridge case of firework preparation method is characterized in that adding in the raw material string stiffener.