CN1850295A - De-calcificated bone carriage and its making method - Google Patents
De-calcificated bone carriage and its making method Download PDFInfo
- Publication number
- CN1850295A CN1850295A CN 200610080609 CN200610080609A CN1850295A CN 1850295 A CN1850295 A CN 1850295A CN 200610080609 CN200610080609 CN 200610080609 CN 200610080609 A CN200610080609 A CN 200610080609A CN 1850295 A CN1850295 A CN 1850295A
- Authority
- CN
- China
- Prior art keywords
- bone
- spongy bone
- calcificated
- carriage
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention discloses a decalcified bone support material and its preparation method. Said decalcified bone support material is a product obtained by using animal spongy bone as raw material and making it undergo the treatment processes successively by using acetone, hydrochloric acid, hydrogen dioxide solution and pancreatin. Said invention also provides the concrete steps of its preparation method.
Description
Technical field
The present invention relates to timbering material that is used for the bone injury reparation and preparation method thereof, particularly relate to a kind of de-calcificated bone carriage and preparation method thereof.
Background technology
The treatment that bone is damaged is one of difficult problem of facing of orthopaedics, its curative effect is good with autologous bone transplanting, but because of bone source deficiency, clinical practice is restricted, therefore seek from the ideal substitution material of body bone is the direction (Kokubo that research worker is carried out bone tissue engineer research always, S., Fujimoto, R., Yokota, S., Fukushima, S., Nozaki, K., Takahashi, K., and Miyata, K. (2003) .Bone regeneration by recombinant humanbone morphogenetic protein-2 and a novel biodegradable carrier in a rabbitulnar defect model.Biomaterials 24,1643-1651.; Shors, E.C. (1999) .Corallinebone graft substitutes.Orthop Clin North Am 30,599-613.).Studies show that, a kind of timbering material that is suitable for the bone reparation should possess following characteristics: (1) certain mechanical strength is to keep specific modality, (2) good cell and histocompatibility, (3) suitable pore size is beneficial to the osteocyte growth, (4) suitable (Damien such as degradation rate, C.J., and Parsons, J.R. (1991) .Bone graft and bone graftsubstitutes:a review of current technology and applications.J Appl Biomater2,187-208.).At present, bone holder material commonly used comprises: bone cement, polymeric material (as PLGA, titanium alloy etc.) etc., but all there is the cell compatibility difference more or less in above-mentioned material and cause problem (Mastrogiacomo such as local inflammation because of degraded, M., Scaglione, S., Martinetti, R., Dolcini, L., Beltrame, F., Cancedda, R., and Quarto, R. (2006) .Role of scaffold internal structureon in vivo bone formation in macroporous calcium phosphate bioceramics.Biomaterials 27,3230-3237.).
Decalcified bone matrix is a kind of timbering material (Chakkalakal, D.A., Strates commonly used in clinical at present and the scientific research, B.S., Garvin, K.L., Novak, J.R., Fritz, E.D., Mollner, T.J., and McGuire, M.H. (2001) .Demineralized bone matrix as a biological scaffoldfor bone repair.Tissue Eng 7,161-177.).This material has kept the trabecularism and the organic principle of nature bone, thereby is a kind of good filling material of bone.Decalcified bone matrix material commonly used at present adopts the form of granule or gel more; though it is damaged that such form can be good at filling irregular bone; but because it does not have mechanical strength; can not keep a fixed form; thereby regular meeting causes moving of material and lost; the inhomogeneity and the unpredictability that cause bone to be repaired; and existing processing method can't effectively be controlled immunogen; bring risk to transplanting, these defectives have greatly limited the application of existing decalcified bone matrix material in treatment is damaged than DAGU.Therefore, press for a kind of have good cell and histocompatibility, suitable aperture and the de-calcificated bone carriage of certain mechanical strength.
Summary of the invention
The purpose of this invention is to provide a kind of have good cell and histocompatibility, the de-calcificated bone carriage of suitable aperture and certain mechanical strength.
De-calcificated bone carriage provided by the present invention is the product that obtains after the animal spongy bone is handled with acetone, hydrochloric acid, hydrogen peroxide and pancreatin successively.
The concentration of described hydrochloric acid is 0.5-0.7M; The mass percentage concentration of hydrogen peroxide is 10-15%; The mass percentage concentration of pancreatin is 0.4-0.6%.
Second purpose of the present invention provides a kind of preparation method of de-calcificated bone carriage.
The preparation method of de-calcificated bone carriage provided by the present invention may further comprise the steps:
1) gets the animal spongy bone, remove adhering tissues such as cartilage and fat;
2) clean spongy bone;
3) spongy bone is used acetone treatment 48-72 hour;
4) spongy bone is placed hydrochloric acid decalcification 24-48 hour of 0.5-0.7M, loose structure occurs, and do not have tangible inorganic constituents again and washed out until the spongy bone material;
5) with decalcification spongy bone mass percentage concentration be hydrogen peroxide bleaching 10-30 minute of 10-15%;
6) clean spongy bone, balance 12-24 hour;
7) under the room temperature, be that the pancreatin of 0.4-0.6% was handled 6-8 hour with the spongy bone mass percentage concentration;
8) clean spongy bone, balance 12-24 hour;
9) with after the lyophilizing of decalcification spongy bone, the sterilization, obtain can be used for the de-calcificated bone carriage that bone injury is repaired.
In above-mentioned preparation method, the source of spongy bone is widely in the described step 1), as large mammals such as cattle, sheep, horse or pigs.
Step 2), available deionized water cleans spongy bone in step 6) and the step 8); The balance water is a deionized water in step step 6) and the step 8).
Can earlier spongy bone be divided into suitable size according to actual needs in the step 3), reuse acetone is handled.
The concentration of pancreatin is preferably 0.5% in the step 7).
The available rays irradiation is sterilized to the decalcification spongy bone in the step 9), as shining with cobalt 60 (Co60).
The invention provides a kind of de-calcificated bone carriage and preparation method thereof.After testing, de-calcificated bone carriage of the present invention has the aperture of suitable osteocyte growth, good physical characteristic and cell and histocompatibility, and non-immunogenicity, total protein content is 93-94%, and water content is 6-7%, and collagen content is 85-92%, ignition residue is 0.4-0.5%, has removed inorganic constituents effectively.In the preparation method of this de-calcificated bone carriage, adopting acetone is to remove fatty tissue to its purpose of handling; Using the purpose of hydrochloric acid is decalcification; The purpose of using hydrogen peroxide is bleaching; Using the purpose of pancreatin is to remove non-collagen albuminoid as much as possible.This preparation method is simple, low for equipment requirements, with low cost, can be applicable to large-scale industrial production, thereby satisfies in bone tissue engineer research and the clinical treatment (particularly treating the damaged and bone does not connect of bone) demand to the bone injury repair materials.The present invention has higher actual application value at medical domain.
Below in conjunction with specific embodiment the present invention is described in further detail.
Description of drawings
Figure 1A is the mode of appearance observed result of de-calcificated bone carriage
Figure 1B is the scanning electron microscopic observation result of de-calcificated bone carriage
Fig. 2 growing state of former generation fibroblast on de-calcificated bone carriage of behaving
Fig. 3 A is the photomacrograph of back de-calcificated bone carriage around the subcutaneous embedding
Fig. 3 B is the slice map of back de-calcificated bone carriage around the subcutaneous embedding of 10 times of amplifications
Fig. 3 C is the slice map of back de-calcificated bone carriage around the subcutaneous embedding of 20 times of amplifications
The specific embodiment
Method therefor is conventional method if no special instructions among the following embodiment, and described percent concentration is mass percentage concentration.
The preparation of embodiment 1, de-calcificated bone carriage and evaluation thereof
One, preparation de-calcificated bone carriage
Spongy bone with cattle is the raw material preparing de-calcificated bone carriage, and concrete preparation process comprises the steps:
1) gets bovine cancellous bone, remove adhering tissues such as cartilage and fat;
2) with deionized water spongy bone is cleaned up;
3) spongy bone is pressed every about 0.5-5cm
3Size cut apart, and in acetone, handled 48 hours;
4) spongy bone is placed the hydrochloric acid decalcification 24 hours of 0.5M, can see that loose structure appears in the spongy bone material, and do not have tangible inorganic constituents again and washed out;
5) spongy bone that will handle through decalcification was with 10% hydrogen peroxide bleaching 30 minutes;
6) use deionized water rinsing, balance 12-24 hour;
7) under the room temperature, handled 8 hours with 0.4% pancreatin;
8) use deionized water rinsing, balance 12-24 hour;
9) with the lyophilizing of decalcification spongy bone, the Co60 radiation sterilization is used in packing, obtains de-calcificated bone carriage.
Two, identify
1, mode of appearance and scanning electron microscopic observation
At first the de-calcificated bone carriage that step 1 is obtained carries out the mode of appearance observation, shown in Figure 1A, and this material porous, and possess hydrophilic property.Under lyophilised state, this material has mechanical strength preferably; Under the situation of moistening, this material then has higher elasticity, can keep certain form when therefore being transplanted to it in body.With scanning electron microscope its morphosis is observed further then, the scanning electron microscope observation result has shown the loose structure and the pore size of this material from microcosmic angle shown in Figure 1B, and the aperture is suitable for the growth of osteocyte between 400-600 μ m.Above-mentioned observed result shows that de-calcificated bone carriage of the present invention has suitable aperture and good physical characteristic.
2, collagen content is measured
The collagen content of the de-calcificated bone carriage that determination step one obtains, total protein content is 94% in this material as a result, and water content is 7%, and collagen content is 92%, ignition residue is 0.5%, shows that the removal of inorganic constituents in the de-calcificated bone carriage of the present invention is very effective.
3, cell compatibility detects
For verifying whether de-calcificated bone carriage of the present invention is fit to the growth of cell, now with former generation human fibroblasts and de-calcificated bone carriage carry out common cultivation, the result is (scale=100 μ m) as shown in Figure 2, the inside and outside growth that a large amount of cells are all arranged of material, along stock support, cell is attached to surperficial cluster growth, does not have tangible rejection, shows that de-calcificated bone carriage of the present invention has the good cell compatibility.
4, immunogenicity detects
The immunogenicity evaluation is an important indicator that detects graft materials.Now detect the immunogenicity of de-calcificated bone carriage of the present invention with subcutaneous investment, concrete grammar is: material is transplanted to subcutaneous rat, and tissues observed is for the reaction of this material.The photomacrograph of this material does not have the sign of tangible immunologic rejection as shown in Figure 3A after around the embedding, and surrounding tissue is inwardly grown, and edge of materials begins degraded.Slice map after around the subcutaneous embedding is shown in Fig. 3 B (amplification 10 *) and Fig. 3 C (amplification 20 *), a large amount of fiber-like tissue filling are among the space of material, based on fibroblast and hemocyte, the immunocyte that around material, does not have hyper-proliferative, and material begin to become loose, the degraded.Above-mentioned testing result shows that de-calcificated bone carriage of the present invention does not cause significantly reaction of tissue, proves that this bone material has the favorable tissue compatibility, and non-immunogenicity, can be used for the bone injury reparation.
The preparation of embodiment 2, de-calcificated bone carriage and evaluation thereof
One, preparation de-calcificated bone carriage
Spongy bone with pig is the raw material preparing de-calcificated bone carriage, and concrete preparation process comprises the steps:
1) gets the pig spongy bone, remove adhering tissues such as cartilage and fat;
2) with deionized water spongy bone is cleaned up;
3) spongy bone is pressed every about 0.5-5cm
3Size cut apart, and in acetone, handled 72 hours;
4) spongy bone is placed the hydrochloric acid decalcification 48 hours of 0.7M, can see that loose structure appears in the spongy bone material, and do not have tangible inorganic constituents again and washed out;
5) spongy bone that will handle through decalcification was with 15% hydrogen peroxide bleaching 10 minutes;
6) use deionized water rinsing, balance 12-24 hour;
7) under the room temperature, handled 6 hours with 0.5% pancreatin;
8) use deionized water rinsing, balance 12-24 hour;
9) with the lyophilizing of decalcification spongy bone, the Co60 radiation sterilization is used in packing, obtains de-calcificated bone carriage.
Detect with the de-calcificated bone carriage of the method identical preparation with embodiment 1, testing result shows that de-calcificated bone carriage of the present invention has suitable aperture, good physical characteristic and cell and histocompatibility, and non-immunogenicity, total protein content are 93%, and water content is 6%, collagen content is 87%, ignition residue is 0.4%, and the removal of inorganic constituents is very effective, can be used for the bone injury reparation.
Claims (10)
1, a kind of de-calcificated bone carriage is the product that obtains after the animal spongy bone is handled with acetone, hydrochloric acid, hydrogen peroxide and pancreatin successively.
2, de-calcificated bone carriage according to claim 1 is characterized in that: the concentration of described hydrochloric acid is 0.5-0.7M.
3, de-calcificated bone carriage according to claim 1 and 2 is characterized in that: the mass percentage concentration of described hydrogen peroxide is 10-15%.
4, de-calcificated bone carriage according to claim 1 and 2 is characterized in that: the mass percentage concentration of described pancreatin is 0.4-0.6%.
5, a kind of preparation method of de-calcificated bone carriage may further comprise the steps:
1) gets the animal spongy bone, remove cartilage and adhering tissue;
2) clean spongy bone;
3) spongy bone is used acetone treatment 48-72 hour;
4) spongy bone is placed hydrochloric acid decalcification 24-48 hour of 0.5-0.7M;
5) with the spongy bone mass percentage concentration be hydrogen peroxide bleaching 10-30 minute of 10-15%;
6) clean spongy bone, balance 12-24 hour;
7) under the room temperature, be that the pancreatin of 0.4-0.6% was handled 6-8 hour with the spongy bone mass percentage concentration;
8) clean spongy bone, balance 12-24 hour;
9) with after the lyophilizing of decalcification spongy bone, the sterilization, obtain de-calcificated bone carriage.
6, preparation method according to claim 5 is characterized in that: the spongy bone in the described step 1) derives from cattle, sheep, horse or pig.
7, preparation method according to claim 5 is characterized in that: described step 2), with deionized water spongy bone is cleaned in step 6) and the step 8); The balance water is a deionized water in step step 6) and the step 8).
8, preparation method according to claim 5 is characterized in that: earlier spongy bone is cut apart in the described step 3), reuse acetone is handled.
9, preparation method according to claim 5 is characterized in that: the concentration of pancreatin is 0.5% in the described step 7).
10, preparation method according to claim 5 is characterized in that: carry out radiation sterilization with 60 pairs of decalcification spongy bone of cobalt in the described step 9).