CN1844278A - Black polyethylene anticorrosion adhesive for buried steel pipeline - Google Patents
Black polyethylene anticorrosion adhesive for buried steel pipeline Download PDFInfo
- Publication number
- CN1844278A CN1844278A CN 200610043777 CN200610043777A CN1844278A CN 1844278 A CN1844278 A CN 1844278A CN 200610043777 CN200610043777 CN 200610043777 CN 200610043777 A CN200610043777 A CN 200610043777A CN 1844278 A CN1844278 A CN 1844278A
- Authority
- CN
- China
- Prior art keywords
- buried steel
- steel pipeline
- parts
- external anticorrosive
- polar monomer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses an anti-corrosion material for ground buried steel pipes, which comprises high-density polyethylene, linear ethane-high carbon-alpha-olefin, anti-oxidant, light stabilizing agent, carbon black, silicane coupling agent, polar monomer and peroxidate.
Description
Technical field
The present invention relates to a kind of external anticorrosive material that is used for buried steel pipeline.Specifically, relate to a kind of black polyethylene anticorrosion adhesive for buried steel pipeline.Described buried steel pipeline comprises oil and gas pipeline, petroleum pipe line, gas line, water supply pipe etc.
Background technology
Begin from the eighties of last century the eighties, occurred the buried steel pipeline anticorrosion process of three-decker in the world.So-called three-decker refers to that the first layer (innermost layer) is a sintered powder; The second layer (middle layer) is a copolymer adhesive, is divided into polyethylene glue stick and polypropylene adhesive again; The 3rd layer (outermost layer) is external anticorrosive material, and wherein the black external anticorrosive material is divided into two kinds of polyethylene external anticorrosive material and polypropylene external anticorrosive materials again, and white external anticorrosive material is generally the polypropylene external anticorrosive material.
Facts have proved that three-decker is anticorrosion to exist following defective: at first, complex process; Secondly, production cost is higher; The 3rd, in making processes because unexpected fracture appears in the middle layer tackiness agent, or because the steel pipe deflection sometimes and the mouth of pipe reason such as circle cause the tackiness agent holiday, can make between the first layer and the 3rd layer bonding badly, reduce even destroy the pipeline operating safety.
Summary of the invention
Purpose of the present invention just provides a kind of black polyethylene anticorrosion adhesive for buried steel pipeline, technical problem to be solved is: intermediate layer polyethylene adhesive layer and outer black polyethylene external anticorrosive material layer are integrated, form a kind of bonding and novel material anti-corrosion function of having simultaneously, thereby simplify complicated three-decker anticorrosion process.
Technical scheme of the present invention is as follows:
A kind of external anticorrosive material that is used for buried steel pipeline is characterized in that: it is made of following component:
High density polyethylene(HDPE) (m
1=1～30): 60～80 parts
Linear structure ethene-high-carbon-alpha-olefin: 17.5～37.5 parts
Oxidation inhibitor: 0.1～0.5 part
Photostabilizer: 0.1～0.5 part
Carbon black: 2.0～3.0 parts
Silane coupling agent: 0.2～0.4 part
Polar monomer: 1～2 part
Superoxide: 0.1～0.4 part
Described part is weight part.
Described polar monomer is preferably the derivative of unsaturated carboxylic acid or unsaturated carboxylic acid.Such as vinylformic acid or toxilic acid or maleic anhydride.
Described superoxide is preferably benzoyl peroxide or peroxidation diethyl propyl benzene.
The present invention has following positively effect: (1), on the basis of original three layers of impregnating material, by introducing modified with polar, material of the present invention can be reacted with epoxy group(ing), the hydroxyl in the epoxy layer, produce firm chemically crosslinked combination, thereby remove the middle layer tackiness agent, make the anticorrosion two-layer structure (two PE) that is reduced to of three-decker (three PE) anticorrosion.(2), save the forcing machine production line and the expressing technique that are used to extrude tackiness agent, and simplified coating processes, reduced production cost.(3), this material is through machine test on the impregnating plant, the stripping strength under 20 ℃ is greater than 150N/cm, the stripping strength under 50 ℃ is greater than 100N/cm.
Embodiment
Further specify the present invention below in conjunction with specific embodiment.
Embodiment one
High density polyethylene(HDPE) (m
1=1～30): 60 parts, m
1Be melting index
Linear structure ethene-high-carbon-alpha-olefin: 17.5 parts
Oxidation inhibitor: 0.1 part
Photostabilizer: 0.1 part
Carbon black: 2.0 parts
Silane coupling agent: 0.2 part
Vinylformic acid: 1 part
Benzoyl peroxide: 0.1～0.4 part
Described part is weight part.
By above-mentioned prescription batching, mix, in stirrer, stir, to extrude by extruder then, the forcing machine extrusion temperature is: 170～220 ℃, the head temperature out is 195 ℃.
Embodiment two
High density polyethylene(HDPE) (m
1=1～30): 70 parts
Linear structure ethene-high-carbon-alpha-olefin: 28 parts
Oxidation inhibitor: 0.3 part
Photostabilizer: 0.3 part
Carbon black: 2.5 parts
Silane coupling agent: 0.3 part
Maleic anhydride: 1.5 parts
Dicumyl peroxide: 0.3 part
Described part is weight part.
By above-mentioned prescription batching, mix, in stirrer, stir, to extrude by extruder then, the forcing machine extrusion temperature is: 170～220 ℃, the head temperature out is 195 ℃.
Embodiment three
High density polyethylene(HDPE) (m
1=1～30): 80 parts
Linear structure ethene-high-carbon-alpha-olefin: 37.5 parts
Oxidation inhibitor: 0.5 part
Photostabilizer: 0.5 part
Carbon black: 3.0 parts
Silane coupling agent: 0.4 part
Silane coupling agent: 0.4 part
Toxilic acid: 2 parts
Described part is weight part.
By above-mentioned prescription batching, mix, in stirrer, stir, to extrude by extruder then, the forcing machine extrusion temperature is: 170～220 ℃, the head temperature out is 195 ℃.
Claims (4)
1, a kind of external anticorrosive material that is used for buried steel pipeline, it is characterized in that: it is made of following component:
High density polyethylene(HDPE) (m
1=1～30): 60～80 parts
Linear structure ethene-high-carbon-alpha-olefin: 17.5～37.5 parts
Oxidation inhibitor: 0.1～0.5 part
Photostabilizer: 0.1～0.5 part
Carbon black: 2.0～3.0 parts
Silane coupling agent: 0.2～0.4 part
Polar monomer: 1～2 part
Superoxide: 0.1～0.4 part
Described part is weight part.
2, the external anticorrosive material that is used for buried steel pipeline as claimed in claim 1 is characterized in that: described polar monomer is the derivative of unsaturated carboxylic acid or unsaturated carboxylic acid.
3, the external anticorrosive material that is used for buried steel pipeline as claimed in claim 2 is characterized in that: described polar monomer is vinylformic acid or toxilic acid or maleic anhydride.
4, as claim 1 or the 2 or 3 described external anticorrosive materials that are used for buried steel pipeline, it is characterized in that: described superoxide is benzoyl peroxide or dicumyl peroxide.