CN1840500A - 镁钙碳中间包干性工作衬料 - Google Patents

镁钙碳中间包干性工作衬料 Download PDF

Info

Publication number
CN1840500A
CN1840500A CN 200510059787 CN200510059787A CN1840500A CN 1840500 A CN1840500 A CN 1840500A CN 200510059787 CN200510059787 CN 200510059787 CN 200510059787 A CN200510059787 A CN 200510059787A CN 1840500 A CN1840500 A CN 1840500A
Authority
CN
China
Prior art keywords
working lining
dry working
accounts
magnesium calcium
tundish dry
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 200510059787
Other languages
English (en)
Inventor
高兴奎
吴鹏程
杨晓芳
秦雪琳
易飞舟
曾庆兵
朱勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 200510059787 priority Critical patent/CN1840500A/zh
Publication of CN1840500A publication Critical patent/CN1840500A/zh
Pending legal-status Critical Current

Abstract

本发明镁钙碳中间包工作衬料。是一种施工时不加水,不用搅拌机械,低温烘烤2小时后就可使用。在烘烤过程中不爆裂,不剥落,同永久衬粘附性好,不回落坍塌,用后清除残钢渣壳容易方便,且不损坏永久衬。抗侵蚀性好。本发明其组份为:电熔镁砂、镁钙砂、石墨、复合添加剂,酚醛树脂等均匀混合物。该料施工性能使用寿命均优于目前应用的中间包涂料。

Description

镁钙碳中间包干性工作衬料
技术领域
本发明属于耐火材料领域,更具体地说本发明涉及不定形耐火材料,它适用于做连铸中间包工作衬料。
背景技术
在我国大力发展高效连铸的今天,中间包冶金技术日益受到重视,它已成为钢铁冶炼过程中在最后阶段最主要的精炼容器,并向大型化发展。它位于钢包与结晶器中间,因此中间包工作衬的耐火材料质量,对保证洁净炼钢,多炉连浇及中间包向大型化发展至关重要。
而现普遍使用的中间包工作衬涂料,材质主要是镁质。它具使用寿命相对较长、不污染钢水等优点。但它在施工时需要加入15%-20%的水。需用搅拌机充分搅拌才能应用,使现场施工比较复杂,由于涂料使用时加入水,降低了涂料的使用强度及抗渣侵蚀性能,增加了烘烤时间,加长了中间包的周转期,同时加水涂料容易与中间包永久衬粘连,造成渣壳清除困难。
发明内容:
为了克服上述涂料的缺陷,我们经过精心研究,合理地选择工作衬料各组份及配比,完成了本发明。
本发明的目的是提供一种施工时不加水,不用搅拌机械,低温烘烤2小时后就可使用。在烘烤过程中不爆裂,不剥落,同永久衬粘附性好,不回落坍塌,用后清除残钢渣壳容易方便,且不损坏永久衬。抗侵蚀性好,使用寿命有较大的提高。也使钢水注余量及铸坯的切头相应减少,而且也符合洁净炼钢的需要,因此镁钙碳中间包干性振捣工作衬在一定程度上降低了钢材生产成本。
本发明的镁钙碳中间作包干性工衬料是由电熔镁砂镁钙砂,鳞片石墨为主体,由以下各组份组成的不定形均匀混合物;其组份按重量百分比计为:
电熔镁砂15-20%,镁钙砂70-80%,鳞片石墨1.5-4%,复合添加剂占8-5%,酚醛树脂5-9%。以上各组份重量之和为100%。
本发明镁钙碳中间包干性工作衬料一个优选实施方案是,其组份按重量百分比计为:
电熔镁砂≤0.088mm占16%,镁钙砂1mm-3mm占27%,0.5mm-1mm占35%,鳞片石墨占3%,复合添加剂占12%,酚醛树脂占7%。以上各组份重量之和为100%。
本发明镁钙碳中间包干性工作衬料的生产工艺是:将上述各组份原料按优选方案比例称量,投入到搅拌机中混合5分钟后出料,装入双层防潮包装袋备用。
本发明中间包干性振捣工作衬料施工方法如下:
1、清理中间包原残余工作衬料。
2、将干性料投入中间包内,铺平后捣实,其厚度为60-80mm。
3、将胎模吊入中间包内并调整胎模与永久衬之间距离,保证其间距为50mm-80mm,之后将干性料投入永久衬与胎模之间,用风镐打实。
4、将施工体用200-300℃温度煤气火烘烤2小时,等胎模冷却至室温后吊出即可投入使用。
本发明实施例
按照本发明优选方案原料组份,制备了一批工作衬料、工作衬料所采用各原料质量技术指标检测结果如下:
电熔镁砂,其质量指标为MgO≥97.1%,SiO2<0.92%,Fe2O3<0.45%,烧失<0.18,体积密度>3.45g/cm3
镁钙砂:MgO65.2%、CaO31.8%、Al2O30.39%、SiO20.8%、Fe2O30.52%、体积密度3.25g/cm3
鳞片石墨的质量技术指标为:固定碳≥93.00%、挥发分≤1.5%、水分≤1.0%。
复合添加剂为:SiO2微粉2%、α-Al2O3微粉3%、金属硅2%,炭墨3%,软质粘土2%,共五种材料的均匀混合物。
酚醛树脂软化点60℃-100℃。
所生产的干性工作衬料的质量指标为:化学成份MgO58.9%、CaO19.8%、C8.5%;物理性能为300℃×3h,耐压强度48.6MPa、抗折强度8.6MPa、体积密度2.52g/cm3。1500℃×3h烧后耐压强度58.47MPa,抗折强度>12MPa,体积密度2.41g/cm3
用本发明产品在某钢铁企业中间包上使用,施工方式如前所述包底厚度为60mm,边厚度50mm,连续拉钢72小时,连拉炉数为131炉,因其它因素停用。渣线残余厚度13-18mm,脱包容易。
综上所述,本发明提供了一种优质镁钙碳中间包干性工作衬料,通过本发明产品的实施,提高了工作衬的使用寿命,使吨钢耐材消耗量降低;同时也使注余量及铸坯切头相应减少。降低了钢材生产成本。

Claims (6)

1.镁钙碳中间包干性工作衬料,其特征是其组份按重量百分比计为:电熔镁砂≤0.088mm占16%,镁钙砂1mm-3mm占27%,0.5mm-1mm占35%,鳞片石墨占3%,复合添加剂占12%,酚醛树脂占7%。以上各组份重量之和为100%。
2.根据权利要求1所述的镁钙碳中间包干性工作衬料,其特征是所述的电熔镁砂,其质量指标为MgO≥97.1%,SiO2<0.92%,Fe2O3<0.45%,烧失<0.18,颗粒体积密度>3.45g/cm3
3.根据权利要求1所述的镁钙碳中间包干性工作衬料,其特征是所述的镁钙砂,其质量指标为:MgO≥65.2%,CaO≥31.8%,Al2O3≥0.39%,SiO2≤0.8%,Fe2O3<0.52%,体积密度>3.25%g/cm3
4.根据权利要求1所述的镁钙碳中间包干性工作衬料,其特征在于鳞片石墨的质量技术指标为:固定碳≥93.00%、挥发分≤1.5%、水分≤1.0%。
5.根据权利要求1所述的镁钙碳中间包干性工作衬料,给添加剂为:SiO2微粉2%、α-Al2O3微粉3%、金属硅2%,炭墨3%,软质粘土2%,共五种材料的均匀混合物。
6.根据权利要求1所述的镁钙碳中间包干性工作衬料,其特征是所述的酚醛树脂软化点为:60℃-100℃。
CN 200510059787 2005-04-01 2005-04-01 镁钙碳中间包干性工作衬料 Pending CN1840500A (zh)