CN1831147A - Method for producing slag forming agent contg. high calcium and low silicone by corundum arc furnace - Google Patents
Method for producing slag forming agent contg. high calcium and low silicone by corundum arc furnace Download PDFInfo
- Publication number
- CN1831147A CN1831147A CN 200610051006 CN200610051006A CN1831147A CN 1831147 A CN1831147 A CN 1831147A CN 200610051006 CN200610051006 CN 200610051006 CN 200610051006 A CN200610051006 A CN 200610051006A CN 1831147 A CN1831147 A CN 1831147A
- Authority
- CN
- China
- Prior art keywords
- raw material
- arc furnace
- high calcium
- drops
- stove
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a method to make high calcium low silicon fluxing medium by corundum arc furnace that includes the following steps: mixture that crushing raw material and mixing 42-45% wrought aluminium bauxite, 48%-53% calcium oxide, 3-4% calcite and 1-2% coke; melting that adding the raw material into furnace adding 10-30% of the total quantity before blowing on, and the rest would be added for 3-4 times after current and voltage stabilizing for 20-30min, after the material totally melted, and soft cover is formed, the furnace could be shut down; turning down, fetching, and cooling; classifying; taking crashing, testing, packaging, storing to the qualified product. The invention has good chemical stability, high CaO content, strong activity, good performance.
Description
Technical field
The invention belongs to technical field of smelting, relate in particular to a kind of method of producing the high calcium and low silicone slag former.
Background technology
The high calcium and low silicone slag former that iron and steel metallurgical industry uses, traditional production method is the rotary kiln calcination, raw material make a living bauxitic clay and Wingdale, the subject matter of its existence is: because the rotation of kiln body, material is the high temperature motion in kiln, adds that raw material constantly drop into, the temperature difference big (reaching about 500 ℃) in the kiln, make the product poor chemical stability, the performance index instability; CaO, Al
2O
3Begin fusing at 1200 ℃, stop up easily in the kiln when furnace temperature surpasses 1400 ℃, usually produce and to stop the kiln cleaning week; Take off S, P effect relatively poor (S, P take off to a certain degree and just can't improve again, directly influence the high-quality Iron and Steel Production), product main chemical CaO content≤30%, poor activity, detrimental impurity component content height, thereby product performance are not good.
Summary of the invention
A kind of chemical reaction that the objective of the invention is to overcome above-mentioned shortcoming and provide is thorough, and chemical stability is good, products C aO content height, and active strong, it is effective to take off S, P, the method with corundum arc furnace production high calcium and low silicone slag former of good product performance.
A kind of method of producing the high calcium and low silicone slag former with corundum arc furnace of the present invention may further comprise the steps:
(1) batching: raw material crushing to 2-15mm, is pressed following proportioning mix then
Wrought aluminium alumina 42～45%, unslaked lime 48%～53%, calcite 3～4%, coke 1～2%;
(2) melting: the raw material gradation drops in the stove, drops into the 10-30% of total stuff amount before the blow-on, and 3-4 throwing of clout average mark drops into after current/voltage is stablized 20-30min, the whole fusions of the bed of material to the stove that finish that feed intake, and charge level is rubescent and form soft lid and get final product blowing out;
(3) fall stove, connect bag, cool off;
(4) classification: stand-by behind the underproof 0-15mm of being crushed to of crystallization (be mixed together batching with raw material, add-on is the 10-20% of raw material total amount, like this can save energy, reduce the input of material quantity, thereby reduce product cost);
(5) qualified through the split pole post crystallization, carry out fragmentation, check, packing, warehouse-in.
The present invention has compared with prior art overcome the interior big shortcoming of the temperature difference of stove that rotary kiln exists, and raw material adopts wrought aluminium alumina, unslaked lime, calcite and removes silicon additive, and Al in the product can be stablized and control to the wrought aluminium alumina
2O
3Composition strengthens product slag making performance; CaO composition in the product can be stablized and control to unslaked lime, strengthens the product activity and take off P, S ability; Calcite and coke participate in chemical reaction, reduce Fe in the product
2O
3, SiO
2Content is removed detrimental impurity composition in the product, improves product performance.And furnace temperature reaches 1800 ℃-1900 ℃, and chemical reaction is thorough, and chemical stability is good; Because chemical reaction is abundant, products C aO content height, active strong, take off S, P is effective, performance index are stable, can satisfy various steel and smelt demands.
Description of drawings
Accompanying drawing is a process flow sheet of the present invention.
Embodiment
Embodiment 1:
Referring to accompanying drawing, a kind of method of producing the high calcium and low silicone slag former with corundum arc furnace may further comprise the steps:
(1) batching: raw material crushing to 2-15mm, is pressed following proportioning mix, wrought aluminium alumina 4200kg, unslaked lime 5300kg, calcite 4kg, coke 1kg then;
(2) melting: the raw material gradation drops into the 3000KVA corundum to be toppled in the electric arc furnace, drops into 1000kg before the blow-on, and the clout average mark is thrown for 3 times, after stablizing 20-30min, drops into current/voltage, each 3000kg that throws, the whole fusions of the bed of material to the stove that finish that feed intake, charge level is rubescent and form soft lid and get final product blowing out;
(3) fall stove, connect bag, cool off;
(4) classification: stand-by behind the underproof 0-15mm of being crushed to of crystallization (reach to return with raw material after a certain amount of be mixed together batching, add-on is the 10-20% of raw material total amount);
(5) qualified through the split pole post crystallization, carry out fragmentation, check, packing, warehouse-in.
Embodiment 2:
Referring to accompanying drawing, a kind of method of producing the high calcium and low silicone slag former with corundum arc furnace may further comprise the steps:
(1) batching: raw material crushing to 2-15mm, is pressed following proportioning mix, wrought aluminium alumina 4300kg, unslaked lime 5200kg, calcite 3kg, coke 2kg then;
(2) melting: the raw material gradation drops into the 3000KVA corundum to be toppled in the electric arc furnace, drops into 2000kg before the blow-on, and the clout average mark is thrown for 4 times, after stablizing 20-30min, drops into current/voltage, each 2000kg that throws, the whole fusions of the bed of material to the stove that finish that feed intake, charge level is rubescent and form soft lid and get final product blowing out;
(3) fall stove, connect bag, cool off;
(4) classification: stand-by behind the underproof 0-15mm of being crushed to of crystallization (reach to return with raw material after a certain amount of be mixed together batching, add-on is the 10-20% of raw material total amount);
(5) qualified through the split pole post crystallization, carry out fragmentation, check, packing, warehouse-in.
Embodiment 3:
Referring to accompanying drawing, a kind of method of producing the high calcium and low silicone slag former with corundum arc furnace may further comprise the steps:
(1) batching: raw material crushing to 2-15mm, is pressed following proportioning mix, wrought aluminium alumina 4500kg, unslaked lime 5000kg, calcite 3kg, coke 2kg then;
(2) melting: the raw material gradation drops into the 3000KVA corundum to be toppled in the electric arc furnace, drops into 3000kg before the blow-on, and the clout average mark is thrown for 3 times, after stablizing 20-30min, drops into current/voltage, each 2333kg that throws, the whole fusions of the bed of material to the stove that finish that feed intake, charge level is rubescent and form soft lid and get final product blowing out;
(3) fall stove, connect bag, cool off;
(4) classification: stand-by behind the underproof 0-15mm of being crushed to of crystallization (reach to return with raw material after a certain amount of be mixed together batching, add-on is the 10-20% of raw material total amount);
(5) qualified through the split pole post crystallization, carry out fragmentation, check, packing, warehouse-in.
Through checking the foregoing description products obtained therefrom:
1, Chemical Composition such as following table:
| Chemical Composition | Al 2O 3 | CaO | SiO 2 |
| Average content % | 40-45 | 45-53 | ≤2.0 |
| 30-40 | 40-45 | ≤4.2 |
2, color is an orange, crystallization gloss obviously, oily luster arranged.
The above, it only is preferred embodiment of the present invention, be not that the present invention is done any pro forma restriction, any technical solution of the present invention content that do not break away from,, all still belong in the scope of technical solution of the present invention any simple modification, equivalent variations and modification that above embodiment did according to technical spirit of the present invention.
Claims (2)
1, a kind of method of producing the high calcium and low silicone slag former with corundum arc furnace may further comprise the steps:
(1) batching: raw material crushing to 2-15mm, is pressed following proportioning mix then,
Wrought aluminium alumina 42～45%, unslaked lime 48%～53%, calcite 3～4%, coke 1～2%;
(2) melting: the raw material gradation drops in the stove, drops into the 10-30% of total stuff amount before the blow-on, and 3-4 throwing of clout average mark drops into after current/voltage is stablized 20-30min, the whole fusions of the bed of material to the stove that finish that feed intake, and charge level is rubescent and form soft lid and get final product blowing out;
(3) fall stove, connect bag, cool off;
(4) classification: crystallization is underproof be crushed to behind the 0-15mm stand-by;
(5) qualified through the split pole post crystallization, carry out fragmentation, check, packing, warehouse-in.
2, method of producing the high calcium and low silicone slag former as claimed in claim 1 with corundum arc furnace, wherein: through sub-polar crystal is underproof be crushed to 0-15mm after, be mixed together batching with raw material, add-on is the 10-20% of raw material total amount.