CN1817817A - 铁水包透气砖用耐火材料的制造方法 - Google Patents

铁水包透气砖用耐火材料的制造方法 Download PDF

Info

Publication number
CN1817817A
CN1817817A CN 200610020363 CN200610020363A CN1817817A CN 1817817 A CN1817817 A CN 1817817A CN 200610020363 CN200610020363 CN 200610020363 CN 200610020363 A CN200610020363 A CN 200610020363A CN 1817817 A CN1817817 A CN 1817817A
Authority
CN
China
Prior art keywords
corundum
brown corundum
hot metal
brown
fire
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN 200610020363
Other languages
English (en)
Other versions
CN1328220C (zh
Inventor
蓝亭
钱学义
文龙
陈奇龙
熊伟
陈清泉
王雪冬
李其中
曹维
吴远斌
陈汀水
邓光明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
CHENGDUFU TIANXIN MATERIAL TECHNOLOGY Co Ltd
Original Assignee
CHENGDUFU TIANXIN MATERIAL TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by CHENGDUFU TIANXIN MATERIAL TECHNOLOGY Co Ltd filed Critical CHENGDUFU TIANXIN MATERIAL TECHNOLOGY Co Ltd
Priority to CNB2006100203637A priority Critical patent/CN1328220C/zh
Publication of CN1817817A publication Critical patent/CN1817817A/zh
Application granted granted Critical
Publication of CN1328220C publication Critical patent/CN1328220C/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

发明提供的铁水包透气砖制造方法的特征在于该铁水包透气砖材料由棕刚玉8－5mm、棕刚玉5－3mm、棕刚玉3－1mm、棕刚玉1－0mm、棕刚玉320目、氮化硅、炭化硅200目、石墨电极粉、97硅微粉、AL2O3微粉，纯铝酸钙水泥、六偏磷酸钠和水构成。本铁水包透气砖材料骨料以刚玉为主，利用刚玉的耐高温、强度高、硬度大、耐腐蚀、韧性好的优良特性；同时引入较宽粒度范围的高纯度炭化硅骨料，充分利用了它在比较宽的温度范围内具有高强度、高热震性、优良的耐磨性，较高的热导率、耐化学腐蚀性；引入石墨，使气孔率提高，烘干强度和烧后强度较高，材料烧后线性变化率小，对保持透气砖透气性的稳定性十分有利，从而使生产出的铁水包透气砖耐高温、耐腐蚀、耐热震、气孔率高、稳定性好。

Description

铁水包透气砖用耐火材料的制造方法
技术领域
本发明涉及一种生产耐火材料的制造方法，特别是一种脱硫铁水包透气砖用耐火材料的制造方法。
背景技术
欧洲人首先提出在铁水包里精练铁水，此后，日本人提出了具有划时代意义的铁水包透气砖，其使用效果得到了肯定。国内一些企业也在已有机械搅拌脱硫法的基础上提出了脱硫铁水罐吹气精炼的冶炼思想。
透气砖是用于炼铁时在铁水包底部通过透气砖向铁水包里鼓入氮气，可以均匀铁水温度及成分，去除夹杂并且避免挂渣。经过精炼可以提高铁水洁净度，减轻转炉以及钢包精炼炉的压力，降低冶炼成本，减少铁损。
发明内容
为了配合国内钢铁联合企业的需要，本发明的目的是设计一种适合铁水精炼需要的透气砖材料的制造方法。
本发明提供的铁水包透气砖制造方法达到了上述发明目的，其特征在于该铁水包透气砖材料由棕刚玉8-5mm、棕刚玉5-3mm、棕刚玉3-1mm、棕刚玉1-0mm、棕刚玉320目、氮化硅、炭化硅200目、石墨电极粉、97硅微粉、AL2O3微粉、纯铝酸钙水泥、六偏磷酸钠和水构成；他们的重量份分别是：
棕刚玉8-5mm     18-19        棕刚玉5-3mm             20
棕刚玉3-1mm     18           棕刚玉1-0mm             11-12
棕刚玉320目     6-10         氮化硅                  1-2
炭化硅200目     8-10         石墨电极粉              2-5
97硅微粉        2            AL2O3微粉            5
纯铝酸钙水泥    3            六偏磷酸钠              0.15
水              4.9-5.4。
本铁水包透气砖材料采用多级配料制成，将各种组分材料按照配方比例备料，先把颗粒状材料倒入搅拌机中，开动搅拌机，再加入微粉搅拌2-3分钟，然后缓缓加入水继续搅拌，直到混合均匀为止。接着，将混合好的材料置入透气砖模具，通过震动，紧密堆积而成。由于所选用的材料性能各异，因此功能也有所不同。97硅微粉表面活性大，分散作用强，纯铝酸钙水泥与水产生水化反应而结合用。
本铁水包透气砖材料的骨料以刚玉为主，利用刚玉的耐高温、强度高、硬度大、耐腐蚀、韧性好的优良特性；同时引入较宽粒度范围的高纯度炭化硅骨料，充分利用了它在比较宽的温度范围内具有高强度、高热震性、优良的耐磨性，较高的热导率、耐化学腐蚀性；引入石墨，使气孔率提高，烘干强度和烧后强度较高，材料烧后线性变化率小，对保持透气砖透气性的稳定性十分有利，从而使生产出的铁水包透气砖耐高温、耐腐蚀、耐热震、气孔率高、稳定性好。
具体实施方式
实施例1-4
表1
表1是本发明的四组实施例数据。
将各种组分材料按照各实施例配方数据备料。先把颗粒状材料倒入搅拌机中，开动搅拌机，再加入微粉搅拌2-3分钟，然后缓缓加入水继续搅拌，直到混合均匀为止，即得到本发明的铁水包透气砖用耐火材料。接着，将混合好的材料置入透气砖模具，通过震动，紧密堆积而成。

Claims (1)

1、一种铁水包透气砖用耐火材料的制造方法，其特征在于该铁水包透气砖材料由棕刚玉8-5mm、棕刚玉5-3mm、棕刚玉3-1mm、棕刚玉1-0mm、棕刚玉320目、氮化硅、炭化硅200目、石墨电极粉、97硅微粉、AL2O3微粉、纯铝酸钙水泥、六偏磷酸钠和水构成；他们的重量份分别是：
棕刚玉8-5mm  18-19      棕刚玉5-3mm    20
棕刚玉3-1mm  18         棕刚玉1-0mm    11-12
棕刚玉320目  6-10       氮化硅         1-2
炭化硅200目  8-10       石墨电极粉     2-5
97硅微粉     2          AL2O3微粉   5
纯铝酸钙水泥 3          六偏磷酸钠     0.15
水           4.9-5.4。
CNB2006100203637A 2006-02-27 2006-02-27 铁水包透气砖用耐火材料的制造方法 Expired - Fee Related CN1328220C (zh)