CN1817640A - Production of laminated composite plate without copper powder sintering layer - Google Patents
Production of laminated composite plate without copper powder sintering layer Download PDFInfo
- Publication number
- CN1817640A CN1817640A CN 200610049793 CN200610049793A CN1817640A CN 1817640 A CN1817640 A CN 1817640A CN 200610049793 CN200610049793 CN 200610049793 CN 200610049793 A CN200610049793 A CN 200610049793A CN 1817640 A CN1817640 A CN 1817640A
- Authority
- CN
- China
- Prior art keywords
- copper powder
- composite plate
- laminated composite
- groove
- powder sintering
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A process for preparing the laminated plate without sintered copper powder layer includes such steps as making slots on the surface of a metallic substrate, spreading a layer of non-metallic antifriction material, sintering, rolling, and smoothing.
Description
Technical field
The present invention relates to a kind of manufacturing of composite board, relate in particular to a kind of on metal material the manufacture method of the laminated composite plate of sintering nonmetallic materials.
Background technology
Metal material, macromolecular material and ceramic material etc. all possess some good points on serviceability and are not enough, and the range of application of oneself is respectively arranged.Along with science and technology development, also more and more higher to the requirement of material, use single material to satisfy various requirement and seem more and more difficult and uneconomical.Therefore, composite board has appearred, at present, the general laminated composite plate of Shi Yonging, oil-free lubrication sliding bearing composite board as steel-copper-nonmetallic materials, the general manufacturing process of these composite boards is: the sheet material of specific thickness is smoothed in cutting steel plate one surface of steel plate shop copper powder sintering one smoothing one surface nonmetal antifriction material sintering one rolling in shop, make the blank of making sliding bearing, formation of parts as requested again, because the inconsistency of steel and nonmetallic materials physical property, as the thermal expansion factor difference, at high temperature work, crease easily or the material faying face between separate; Plate material is in the process of bending forming, because the curvature difference of material ectonexine also can cause the separation between the material faying face.Therefore, generally spread the spherical copper powder sintering in the production,, improve the adhesive force of nonmetal antifriction material and base steel material surface, make both not easily separated with roughness and the formation space that increases steel material primary surface at the material primary surface of steel.And copper powder sintering process complexity, difficult quality control consumes copper powder again, and product cost greatly improves.
Summary of the invention
The object of the present invention is to provide a kind of technology simple, can exempt copper powder sintering layer, make the manufacture method of metal material and nonmetallic materials laminated composite plate.
In order to achieve the above object, the manufacture method of exempting from the laminated composite plate of copper powder sintering layer is: on metal base by cutting and/or be suppressed with groove, spread nonmetal antifriction material sintering in flute surfaces, rolling again, as to smooth specific thickness sheet material becomes finished product.
According to the above-mentioned manufacture method of exempting from the laminated composite plate of copper powder sintering layer, can be melted to nonmetal antifriction material in the groove of metallic substrate surface by sintering, traction-increasing surface is long-pending, especially the big groove in section configuration little bottom surface suitable for reading, can be engaged in nonmetal antifriction material in the groove securely, have extremely strong adhesive force, do not separate with nonmetal antifriction material no matter in processing or use, all can not produce metal base; Exempt the technology of sintered copper powder, save copper powder, reduce energy resource consumption, product cost, be beneficial to environmental protection again.
Description of drawings
Fig. 1 is the front view that has staggered trapezoidal groove on the metal base;
Fig. 2 is the A-A profile of Fig. 1;
Fig. 3 is the B-B profile of Fig. 1;
Fig. 4 is the front view that groove is arranged in parallel;
Fig. 5 is the front view that groove becomes miter angle on the metal base with the base material sideline;
Fig. 6 is the triangular groove profile;
Fig. 7 is the rectangle groove profile;
Fig. 8 is the semi-circular grooves profile;
Fig. 9 is the groove profile of triangle and rectangle combination;
Figure 10 is the groove profile of semicircle and rectangle combination;
Figure 11 is the profile that sintering has nonmetal antifriction material on the metal base.
Wherein: 1, metal base; 2, surface; 3, groove; 4, sideline; 5, nonmetal antifriction material.
The specific embodiment
The invention will be further described below in conjunction with accompanying drawing.
Fig. 1, Fig. 2, Fig. 3 are the structural representations that has staggered trapezoidal groove on metal base.There is longitudinal and transverse staggered trapezoidal groove 3 on surface 2 at metal base 1 by cutting and/or press process.The arrangement of groove 3 can also be to be arranged in parallel as shown in Figure 4.Groove 3 can become certain included angle with the sideline 4 of base material 1, and as 30 degree, 60 degree etc., shown in Figure 5 is groove 1 and 4 one-tenth miter angles in sideline of base material 1.The shape of groove 3 sections can by cutting and/or press process triangularity as shown in Figure 6 or rectangle as shown in Figure 7 semicircle as shown in Figure 8 or the combination of triangle and rectangle as shown in Figure 9 or the combination of semicircle and rectangle wait the combination of other geometries as shown in figure 10.After the metal base 1 of with groove 3 makes, spread nonmetal antifriction material 5 sintering again on the surface 2 of base material 1 by traditional handicraft, rolling again, as to smooth specific thickness sheet material becomes the finished product of laminated composite plate.Nonmetal antifriction material 5 can be embedded in the groove 3 by such method, groove 3 shapes especially as shown in Figure 3, bonding strength is higher.Can exempt the technology of sintered copper powder, the performance of gained composite board is suitable with the composite board that had copper powder sintering layer originally.
Claims (3)
1, a kind of manufacture method of exempting from the laminated composite plate of copper powder sintering layer, it is characterized in that on metal base by cutting and/or be suppressed with groove, spread nonmetal antifriction material sintering in flute surfaces, rolling again, as to smooth specific thickness sheet material becomes finished product.
2, the manufacture method of exempting from the laminated composite plate of copper powder sintering layer according to claim 1 is characterized in that the groove of opening is to be arranged in parallel or to be staggered on described metal base.
3, the manufacture method of exempting from the laminated composite plate of copper powder sintering layer according to claim 1, the shape that it is characterized in that described trench section is that triangle or rectangle are semicircle or trapezoidal, or triangle, rectangle, semicircle, trapezoidal any combined shaped.