CN1798498A - 有机屏蔽材料 - Google Patents
有机屏蔽材料 Download PDFInfo
- Publication number
- CN1798498A CN1798498A CN 200410093232 CN200410093232A CN1798498A CN 1798498 A CN1798498 A CN 1798498A CN 200410093232 CN200410093232 CN 200410093232 CN 200410093232 A CN200410093232 A CN 200410093232A CN 1798498 A CN1798498 A CN 1798498A
- Authority
- CN
- China
- Prior art keywords
- organic
- shielding material
- material according
- parts
- organic shielding
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及能够吸收强电磁波的屏蔽材料，特别是一种有机屏蔽材料。它主要由有机基材、改性配料和导电屏蔽功能材料混合组成，该基材为高分子材料，该改性配料是有机化工原料；当上述材料按照重量份数合计180份时，基材100份、改性配料25－55份、导电屏蔽功能材料25－55份。本发明在强电磁波的情况下也能达到很好的屏蔽能力，而且制造方便、成本低。
Description
技术领域：
本发明涉及能够吸收强电磁波的屏蔽材料，特别是一种有机屏蔽材料。
背景技术：
中国实用新型专利说明书(CN 2629395Y)公开了一种复合电磁屏蔽材料，它用来抑制电子产品电磁辐射的复合电磁屏蔽材料，其包括本体和导电体，所述导电体覆盖在所述本体上。本实用新型中的复合电磁屏蔽材料由于整个截面上只有外面较薄的一层为导电体，所以导电体的用料很少，材料成本较低。由于所述本体为较软的硅橡胶，并且外层硬度较大的导电体层较薄，所以材料整体上仍然具有很好拉伸性能和压缩性能，同时具有良好的防水性能。由于导电体层可以做到很薄，即使发生电化学腐蚀，也只是腐蚀外露表面的导电体层，其腐蚀不会很严重，并且作为所述本体的硅橡胶不会腐蚀。但是，它对于强电磁波的屏蔽能力不能达到理想的效果。
发明内容：
本发明的目的是提供一种有机屏蔽材料，在强电磁波的情况下也能达到很好的屏蔽能力，而且制造方便、成本低。
为解决上述技术问题，本发明是这样实现的：
一种有机屏蔽材料，其特征在于：它主要由有机基材、改性配料和导电屏蔽功能材料混合组成，该基材为高分子材料，该改性配料是有机化工原料；当上述材料按照重量份数合计180份时，基材100份、改性配料25-55份、导电屏蔽功能材料25-55份。
该高分子材料是丙烯腈-丁二烯-苯乙烯共聚物或聚乙烯或聚丙烯或HP-PVC。
该有机化工原料包括二盐/三盐、醚类、硬脂类、软脂类、抗静电增塑剂和光敏化促进剂。
该二盐/三盐是三氧化二锑或氧化锌。
该醚类是十溴二苯醚。
该硬脂类是硬脂酸钡或硬脂酸。
该软酯类是石腊或液化石腊。
该抗静电增塑剂是邻苯二甲酸二辛酯或邻苯二甲酸二丁酯。
该光敏化促进剂是N-(乙氧基羰基苯基)-N’-甲基-N’-苯基甲醚或N-(乙氧基羰基苯基)-N’-乙基-N’-苯基甲醚。
该导电屏蔽功能材料包括乙炔碳黑、聚碳酸酯废料真空热处理变性碳黑、茂金属催化处理高分子材料和有机碳催化处理后再纳米化形成超细颗粒粉剂。
本发明具有如下技术效果：
1、本发明在10MHz-3000MHz频率范围内达到屏蔽强电磁波能力为98％以上。
2、本发明可以在宽带线束方面应用达到无误码现象控制在10-12比特之内。
3、本发明可以在信息产业中的手机、个人数字助理机和智能产品的方高强频率的电磁波干扰即屏蔽作用。
4本发明可以达到吸收强电磁波，因为它是用有机材料，密度仅在0.8-0.9之间，比采用无机材料的密度低且产品呈现内部分子结构的疏松性，电磁波不能达到反射现象，在产品内部分子的布朗运动形式下，将强电磁波的能量消耗和吸收。
具体实施方式：
实施例1
一种有机屏蔽材料，它主要由有机基材、改性配料和导电屏蔽功能材料混合组成。按照重量份数计，基材100份、改性配料55份、导电屏蔽功能材料25份。该基材为高分子材料丙烯腈-丁二烯-苯乙烯共聚物(简称：ABS)，该改性配料由三氧化二锑、十溴二苯醚、硬脂酸钡、石腊、邻苯二甲酸二辛酯和N-(乙氧基羰基苯基)-N’-甲基-N’-苯基甲醚组成，该导电屏蔽功能材料由乙炔碳黑、聚碳酸酯废料真空热处理变性碳黑、茂金属催化处理高分子材料和有机碳催化处理后再纳米化形成超细颗粒粉剂组成。
上述材料制成后，加工至0.07mm厚度用于IC卡上，经测试，在10MHz的频率范围内达到屏蔽强电磁波能力为98.80％。
实施例2
一种有机屏蔽材料，它主要由有机基材、改性配料和导电屏蔽功能材料混合组成。按照重量份数计，基材100份、改性配料40份、导电屏蔽功能材料40份。该基材为高分子材料聚丙烯(简称：PP)，该改性配料由三氧化二锑、十溴二苯醚、硬脂酸钡、石腊、邻苯二甲酸二辛酯和N-(乙氧基羰基苯基)-N’-甲基-N’-苯基甲醚组成，该导电屏蔽功能材料由乙炔碳黑、聚碳酸酯废料真空热处理变性碳黑、茂金属催化处理高分子材料和有机碳催化处理后再纳米化形成超细颗粒粉剂组成。
上述材料制成后，加工至0.07mm厚度用于光卡上，经测试，在10MHz的频率范围内达到屏蔽强电磁波能力为98.83％。
实施例3
一种有机屏蔽材料，它主要由有机基材、改性配料和导电屏蔽功能材料混合组成。按照重量份数计，基材100份、改性配料25份、导电屏蔽功能材料55份。该基材为高分子材料聚乙烯(简称：PE)，该改性配料由三氧化二锑、十溴二苯醚、硬脂酸钡、石腊、邻苯二甲酸二辛酯和N-(乙氧基羰基苯基)-N’-甲基-N’-苯基甲醚组成，该导电屏蔽功能材料由乙炔碳黑、聚碳酸酯废料真空热处理变性碳黑、茂金属催化处理高分子材料和有机碳催化处理后再纳米化形成超细颗粒粉剂组成。
上述材料制成后，加工至0.07mm厚度用于磁卡上，经测试，在10MHz的频率范围内达到屏蔽强电磁波能力为98.85％。
实施例4
一种有机屏蔽材料，它主要由有机基材、改性配料和导电屏蔽功能材料混合组成。按照重量份数计，基材100份、改性配料55份、导电屏蔽功能材料25份。该基材为高分子材料丙烯腈-丁二烯-苯乙烯共聚物(简称：ABS)，该改性配料由氧化锌、十溴二苯醚、硬脂酸、液化石腊、邻苯二甲酸二丁酯和N-(乙氧基羰基苯基)-N’-乙基-N’-苯基甲醚组成，该导电屏蔽功能材料由乙炔碳黑、聚碳酸酯废料真空热处理变性碳黑、茂金属催化处理高分子材料和有机碳催化处理后再纳米化形成超细颗粒粉剂组成。
上述材料制成后，加工至0.07mm，经测试，在10MHz的频率范围内达到屏蔽强电磁波能力为98.83％，适用于X射线防护服。
实施例5
一种有机屏蔽材料，它主要由有机基材、改性配料和导电屏蔽功能材料混合组成。按照重量份数计，基材100份、改性配料40份、导电屏蔽功能材料40份。该基材为高分子材料聚丙烯(简称：PP)，该改性配料由氧化锌、十溴二苯醚、硬脂酸、液化石腊、邻苯二甲酸二丁酯和N-(乙氧基羰基苯基)-N’-乙基-N’-苯基甲醚组成，该导电屏蔽功能材料由乙炔碳黑、聚碳酸酯废料真空热处理变性碳黑、茂金属催化处理高分子材料和有机碳催化处理后再纳米化形成超细颗粒粉剂组成。
上述材料制成后，加工至0.07mm，经测试，在10MHz的频率范围内达到屏蔽强电磁波能力为98.85％，适用于孕妇防电磁服装。
实施例6
一种有机屏蔽材料，它主要由有机基材、改性配料和导电屏蔽功能材料混合组成。按照重量份数计，基材100份、改性配料25份、导电屏蔽功能材料55份。该基材为高分子材料聚乙烯(简称：PE)，该改性配料由氧化锌、十溴二苯醚、硬脂酸、液化石腊、邻苯二甲酸二丁酯和N-(乙氧基羰基苯基)-N’-乙基-N’-苯基甲醚组成，该导电屏蔽功能材料由乙炔碳黑、聚碳酸酯废料真空热处理变性碳黑、茂金属催化处理高分子材料和有机碳催化处理后再纳米化形成超细颗粒粉剂组成。
上述材料制成后，加工至0.07mm，经测试，在10MHz的频率范围内达到屏蔽强电磁波能力为98.83％，适用于儿童防电磁书包。
实施例7
一种有机屏蔽材料，它主要由有机基材、改性配料和导电屏蔽功能材料混合组成。按照重量份数计，基材100份、改性配料35份、导电屏蔽功能材料45份。该基材为高分子材料HP-PVC，该改性配料由氧化锌、十溴二苯醚、硬脂酸、液化石腊、邻苯二甲酸二丁酯和N-(乙氧基羰基苯基)-N’-乙基-N’-苯基甲醚组成，该导电屏蔽功能材料由乙炔碳黑、聚碳酸酯废料真空热处理变性碳黑、茂金属催化处理高分子材料和有机碳催化处理后再纳米化形成超细颗粒粉剂组成。
上述材料制成后，加工至0.07mm，经测试，在10MHz的频率范围内达到屏蔽强电磁波能力为98.87％，适用于儿童防电磁书包。
Claims (10)
1、一种有机屏蔽材料，其特征在于：它主要由有机基材、改性配料和导电屏蔽功能材料混合组成，该基材为高分子材料，该改性配料是有机化工原料；当上述材料按照重量份数合计180份时，基材100份、改性配料25-55份、导电屏蔽功能材料25-55份。
2、根据权利要求1所述的有机屏蔽材料，其特征在于：该高分子材料是丙烯腈-丁二烯-苯乙烯共聚物或聚乙烯或聚丙烯或HP-PVC。
3、根据权利要求1或2所述的有机屏蔽材料，其特征在于：该有机化工原料包括二盐/三盐、醚类、硬脂类、软脂类、抗静电增塑剂和光敏化促进剂。
4、根据权利要求3所述的有机屏蔽材料，其特征在于：该二盐/三盐是三氧化二锑或氧化锌。
5、根据权利要求3所述的有机屏蔽材料，其特征在于：该醚类是十溴二苯醚。
6、根据权利要求3所述的有机屏蔽材料，其特征在于：该硬脂类是硬脂酸钡或硬脂酸。
7、根据权利要求3所述的有机屏蔽材料，其特征在于：该软酯类是石腊或液化石腊。
8、根据权利要求3所述的有机屏蔽材料，其特征在于：该抗静电增塑剂是邻苯二甲酸二辛酯或邻苯二甲酸二丁酯。
9、根据权利要求3所述的有机屏蔽材料，其特征在于：该光敏化促进剂是N-(乙氧基羰基苯基)-N’-甲基-N’-苯基甲醚或N-(乙氧基羰基苯基)-N’-乙基-N’-苯基甲醚。
10、根据权利要求1或2所述的有机屏蔽材料，其特征在于：该导电屏蔽功能材料包括乙炔碳黑、聚碳酸酯废料真空热处理变性碳黑、茂金属催化处理高分子材料和有机碳催化处理后再纳米化形成超细颗粒粉剂。