CN1775930A - Coal-firing efficient additive for dry cement process and its use - Google Patents
Coal-firing efficient additive for dry cement process and its use Download PDFInfo
- Publication number
- CN1775930A CN1775930A CN 200510020002 CN200510020002A CN1775930A CN 1775930 A CN1775930 A CN 1775930A CN 200510020002 CN200510020002 CN 200510020002 CN 200510020002 A CN200510020002 A CN 200510020002A CN 1775930 A CN1775930 A CN 1775930A
- Authority
- CN
- China
- Prior art keywords
- coal
- new type
- efficient additive
- type nonaqueous
- firing efficient
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention belongs to coal additive field, especially a dry method concrete technology burning high efficiency additive. The feature is that it is made up of 20-30 portions of steel ground slag, 10-30 portions of barium slag, 5-10 portions of potassium permanganate, 1-2 portions of modification paper making sewage, 5-10 portions of citric acid, and 30-50 portions of high calcium fly ash. It could enhance the fire feature, and decline the firing temperature and no negative effect to concrete clinker aggregate.
Description
Technical field
The invention belongs to the additive for fire coal field, be specifically related to a kind of new type nonaqueous cement technology coal-firing efficient additive and application thereof.
Background technology
China's cement total output reached 9.7 hundred million tons in 2004, and the cement total energy consumption is up to more than 100,000,000 tons of mark coals, and coal consumption accounts for 10% of national coal ultimate production.Therefore, under situation about being becoming tight various countries' energy consumption day, the cement industry development of hanging down output as high energy consumption will be restricted.At present, though the coal resources of China are quite abundant, proven reserve have surpassed 45,000 hundred million t, account for the No. 1 in the world, and resource distribution is very unbalanced, and eastern Shaoxi is many, Nan Shaobei is many.The distribution of coal in China kind is also very unbalanced, and about 76% hard coal concentrates on Shanxi and Guizhou two provinces, and 80% of coking coal is distributed in several provinces and cities in North China, and inferior coal 90% above richness is stored in the each province, northwest.On ature of coal, the difficult separation coal of China is more, and the ratio of high ash, high sulphur coal is great, and most of pit ash is more than 25%, and medium-high sulfur coal and the high sulphur coal of sulphur content more than 2% accounts for 1/3 of total reserves in the coal.Western part of China and southern areas high-quality bituminous coal are less, are hard coal more than 98% as Fujian; Yunnan 75% brown coal; The hard coal of Guizhou, Hunan and Guangxi San Sheng all accounts for about 75%; Guangdong hard coal and brown coal respectively account for 45%; Jiangxi and Zhejiang soft coal account for about 80%.
Yet new dry process is produced cement and is generally used bituminous coal, and fugitive constituent (〉=25%), ash content (about≤20%), sulphur content etc. are required relatively strictness, causes low-quality coal resources to fail to make full use of in Cement industry.And along with China's economic construction and social development, increasing to the demand of the energy.Be difficult to guarantee that at present power supply deficiency, coal supply most of cement mill often change with the coal of coal under the ature of coal situation of Cement industry needs.Therefore, advance any coal often and just burn what coal, be difficult to guarantee the economical operation of production line.
In order to improve the burning of coal situation, extensive work was carried out in the research of additive for fire coal and use both at home and abroad, had applied for many patents, but had been the efficient utilization at China's boiler of power plant and civilian coal basically, and mostly be band K
+, Mg
2+, Na
+, Cl
-The ignition dope that negative impact is arranged Deng cement clinker.And commercially available ignition dope majority exists the volume height, price is expensive and to the shortcomings such as selectivity of coal.
Summary of the invention
The object of the present invention is to provide a kind of can overheavy firing effect, reduce igniting temperature of pulverized-coal, improve coal dust after-flame degree and the performance of cement clinker do not had the new type nonaqueous cement technology coal-firing efficient additive and the application thereof of negative impact.
To achieve these goals, the present invention proposes to form coal-firing efficient additive by the combustion-supporting composition of oxidation, catalyticcombustion composition, grinding aid composition and high reactivity carrier.Technical scheme of the present invention is: a kind of new type nonaqueous cement technology coal-firing efficient additive, it is characterized in that: formed by steel-making slag powder, barium slag, potassium permanganate, modification paper waste, citric acid and high-calcium fly ass raw material mixed grinding, wherein the weight percentage of each raw material is:
Steel-making slag powder 20-30, barium slag 10-30, potassium permanganate 5-10, modification paper waste 1-2, citric acid 5-10, high-calcium fly ass 30-50.
Above-mentioned potassium permanganate and citric acid are potassium permanganate and the citric acid that is applicable to that industrial production is used, and as the combustion-supporting component of oxidation, potassium permanganate and degradation production thereof also have katalysis to burning.
Above-mentioned barium slag is a raw material with the barite, at high temperature with carbon it is reduced into barium sulphide, and water leaches reprocessing and produces barium salt then, and leaching the residual solid that stays is the barium slag, wherein solubility in acid barium salt BaCO
3And BaSO
4Shared weight percent 25-70 altogether, barium slag and steel-making slag powder are as the catalyticcombustion composition.
Above-mentioned modification paper waste is to add sulphonating agent at black liquid, and black liquid and sulphonating agent are by 20-30ml: 1g chooses, 25-40 minute sulfonation reaction time, condensation reaction time 1.5-2.5 hour and make.The modification paper waste is as the grinding aid composition of coal dust.
Above-mentioned high-calcium fly ass is that the coal-burning power plant adopts and to increase the collected dry powder flyash of fly-ash separator after the calcium technology, and the shared weight percent of its f-CaO is 10-70, and high-calcium fly ass is as the high reactivity carrier.
A kind of preparation of new type nonaqueous cement technology coal-firing efficient additive, with the weight percentage of raw material be: steel-making slag powder 20-30, barium slag 10-30, potassium permanganate 5-10, modification paper waste 1-2, citric acid 5-10, the steel-making slag powder of high-calcium fly ass 30-50, barium slag, potassium permanganate, modification paper waste, citric acid and high-calcium fly ass add grinding machine and mix, grind to form 180-200 purpose powder material, promptly get product (abbreviation coal-firing efficient additive).
A kind of application of new type nonaqueous cement technology coal-firing efficient additive: after the adding weight percent is the new type nonaqueous cement technology coal-firing efficient additive of 1-10 (wt%) in raw coal, mix, dry, the standard particle size that is crushed to coal dust, send into by transport pipe or burner in the decomposing furnace and rotary kiln of cement industry.
Ultimate principle of the present invention is: coal-firing efficient additive is mainly formed by industrial chemicals and the trade waste processing reaction that grades of the combustion-supporting composition of oxidation, catalyticcombustion composition, grinding aid composition and high reactivity vehicle group,, catalyticcombustion combustion-supporting based on oxidation, reduce the point of ignition of coal, accelerate burning of coal speed, improve burner hearth and kiln temperature, strengthening heat transfer impels raw coal combustion and after-flame; Add the grinding aid composition to reach the raising mill efficiency, reduce coal abrasive dust mill energy consumption, simultaneously can be by improving the fineness overheavy firing effect of coal dust; The trace element that contains in the coal-firing efficient additive (Mn, Ba, Fe etc.), reducing raw material burns till fusing point on the one hand, and liquid phase is occurred in advance, reduces grog greatly and forms activation energy, has accelerated the speed of response of clinker mineral, makes C in the grog
3S is a large amount of fast at low temperatures to be formed, on the other hand because the crystal inducing action of trace element promotes newborn C in the grog
3The high reactivityization of S, thus burning till hear rate and improving the intensity of grog of cement clinker reduced.
The new type nonaqueous cement technology coal-firing efficient additive that the present invention proposes adds in the coal with trace (the adding weight percent is 1-10), can reduce the coal-fired sulfurous gas that discharges in air, flue dust and NOx (NO, NO in the consumption reduction of economizing on coal again
2) wait principal pollutant, to the promoter action of having burnt till of cement clinker, this has obvious practical significance to solving China's Cement industry energy dilemma simultaneously.
Of the present invention also have following characteristics:
1, make full use of trade waste and prepare additive for fire coal, the treatment of wastes with processes of wastes against one another is turned waste into wealth, and cost is low, the efficient height.
2, the starting material of additive for fire coal are easy to get, and are applicable to multiple coals such as bituminous coal, ash coal, lambskin.
3, the technology of the present invention is applicable to particularly new type nonaqueous cement kiln of various kiln types, because addition is few, additive contains K in addition
+, Mg
2+, Na
+, Cl
-Amount very little, so can not cause exceeding standard and also can suitably improving the intensity of cement clinker of magnesium and alkali content in the grog, improve clinker strength 2-5MPa, reduce the unit grog and burn till hear rate, the performance of cement clinker is not had negative impact.
4, new type nonaqueous cement technology coal-firing efficient additive provided by the invention have that preparation technology is simple, processing ease and be easy to advantage such as popularization.
5, play the comprehensive action of economizing on coal and reducing the pollution substance discharging, 5-20% economizes on coal.
Embodiment
In order to understand the present invention better, further illustrate content of the present invention below in conjunction with embodiment, but content of the present invention not only is confined to the following examples.
Embodiment 1:
Get the steel-making slag powder 25kg of wuhan iron ﹠ steel croup co. company, the collected dried high-calcium fly ass 40kg of Wuchang plant dust catcher, barium slag 20kg, commercially available potassium permanganate 5kg, modification paper waste 2kg, citric acid 8kg, mixing also grinds to form 180-200 purpose powder material, makes coal-firing efficient additive.The modification paper waste is in black liquid 250ml, adds sulphonating agent (vitriol oil) 10g, 30 minutes sulfonation reaction time, condensation reaction time 2 hours.
Is research object with ash content up to 40% ash coal, and the kindling temperature of ash coal (Ta) is 458.5 ℃, and when this coal-firing efficient additive of being mixed with 3% in the coal dust sample, the kindling temperature of coal is reduced to 402.8 ℃.Grog burns till the result and shows: use time of coagulation, alkali content, the stability of additive for fire coal grog of the present invention normal, intensity (28d) has improved 5MPa, economizes on coal 12%.
Embodiment 2:
Get the steel-making slag powder 25kg of wuhan iron ﹠ steel croup co. company, the collected dried high-calcium fly ass 35kg of Wuchang plant dust catcher, barium slag 20kg, commercially available potassium permanganate 8kg, modification paper waste 2kg, citric acid 10kg, mixing also grinds to form 180-200 purpose powder material, makes coal-firing efficient additive.The modification paper waste is in black liquid 250ml, adds sulphonating agent (vitriol oil) 10g, 30 minutes sulfonation reaction time, condensation reaction time 2h and making.
With ash content up to 30%, volatile matter is research object less than 8% lambskin, the kindling temperature of ash coal (Ta) is 496.5 ℃, and when this additive for fire coal of being mixed with 4% in the coal dust sample, the kindling temperature of coal is reduced to 422.8 ℃.Grog burns till the result and shows: use time of coagulation, alkali content, the stability of additive for fire coal grog of the present invention normal, intensity (28d) has improved 5MPa, economizes on coal 10%.
Embodiment 3:
Get the steel-making slag powder 30kg of wuhan iron ﹠ steel croup co. company, the collected dried high-calcium fly ass 50kg of Wuchang plant dust catcher, barium slag 12kg, commercially available potassium permanganate 5kg, modification paper waste 1kg, citric acid 5kg, mixing also grinds to form 180-200 purpose powder material, makes coal-firing efficient additive.The modification paper waste is in black liquid 250ml, adds sulphonating agent (S-WAT) 10g, 30 minutes sulfonation reaction time, condensation reaction time 2h and making.
With bituminous coal is research object, and the kindling temperature of bituminous coal (Ta) is 420 ℃, and when this additive for fire coal of being mixed with 4% in the coal dust sample, the kindling temperature of coal is reduced to 400 ℃.Grog burns till the result and shows: use time of coagulation, alkali content, the stability of additive for fire coal grog of the present invention normal, intensity (28d) has improved 5MPa, economizes on coal 15%.
The upper limit, lower limit and the interval value of steel-making slag powder of the present invention, barium slag, potassium permanganate, modification paper waste, citric acid and each raw material of high-calcium fly ass can both be realized the present invention, just differ one for example at this.
Claims (6)
1. new type nonaqueous cement technology coal-firing efficient additive, it is characterized in that: formed by steel-making slag powder, barium slag, potassium permanganate, modification paper waste, citric acid and high-calcium fly ass raw material mixed grinding, wherein the weight percentage of each raw material is:
Steel-making slag powder 20-30, barium slag 10-30, potassium permanganate 5-10, modification paper waste 1-2, citric acid 5-10, high-calcium fly ass 30-50.
2. a kind of new type nonaqueous cement technology coal-firing efficient additive according to claim 1 is characterized in that: solubility in acid barium salt BaCO in the described barium slag
3And BaSO
4Shared weight percent be 20-28.
3. a kind of new type nonaqueous cement technology coal-firing efficient additive according to claim 1 is characterized in that: Fe in the described steel-making slag powder
2O
3Shared weight percent is 25-70.
4. a kind of new type nonaqueous cement technology coal-firing efficient additive according to claim 1, it is characterized in that: described modification paper waste is for adding sulphonating agent at black liquid, black liquid and sulphonating agent are by 20-30ml: 1g chooses, 25-40 minute sulfonation reaction time, condensation reaction time 1.5-2.5 hour and make.
5. a kind of new type nonaqueous cement technology coal-firing efficient additive according to claim 1 is characterized in that: described high-calcium fly ass is that the shared weight percent of f-CaO is 10-70 in the fire coal.
6. the application of a kind of new type nonaqueous cement technology coal-firing efficient additive as claimed in claim 1, it is characterized in that: after the adding weight percent is the new type nonaqueous cement technology coal-firing efficient additive of 1-10 in raw coal, mix, dry, the standard particle size that is crushed to coal dust, send into by transport pipe or burner in the decomposing furnace and rotary kiln of cement industry.