CN1775888A - Method for preparing modified phenolic resin adhesive - Google Patents
Method for preparing modified phenolic resin adhesive Download PDFInfo
- Publication number
- CN1775888A CN1775888A CN 200510010598 CN200510010598A CN1775888A CN 1775888 A CN1775888 A CN 1775888A CN 200510010598 CN200510010598 CN 200510010598 CN 200510010598 A CN200510010598 A CN 200510010598A CN 1775888 A CN1775888 A CN 1775888A
- Authority
- CN
- China
- Prior art keywords
- phenolic resin
- resin adhesive
- modified phenolic
- preparation
- modified
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a method to make modification phenol-formaldehyde resin adhere agent that is made up from using metal element to modify organic silicon resin and takes action to phenolic aldehyde and formaldehyde. It first forms titanium or aluminum modified organic silicon resin than takes reaction with phenolic aldedyde and formaldehyde under the effect of activator to gain phenol-formaldehyde resin adhere agent that has high shear strength and high thermal endurance.
Description
Technical field
A kind of preparation method of modified phenolic resin adhesive, be with the metallic element modified organic silicone resin and with phenol and formaldehyde reaction, make modified phenolic resin adhesive.Belong to the organic high molecular compound preparation field.
Technical background
Resol is industrialized the earliest synthetic resins, from the sixties in 20th century, just is used as the matrix resin of the instantaneous high temperature resistant and ablation resistant material of space vehicle, guided missile, rocket and supersonic plane.But, require the resin of anti-the ablation to have than higher in the past resistance toheat and better ablation resistance along with developing rapidly of aerospace cause.
Polymer-based material has following characteristics: resistance to sudden heating is good, the physical strength height, and relative density is low, and thermal insulation is good, and density is low, and thermal conductivity is little, the specific heat height, and can controlling polymers decompose the gaseous product that produces.Ablation resistant material is widely used to be to be the matrix material (comprising coating, sizing agent) of matrix with the polymkeric substance, this is because fibre reinforced plastics have significant superiority on endothermic effect, mainly use with the form of fibre reinforced plastics and coating, use therein polymkeric substance has epoxy, phenolic aldehyde, organosilicon and urethane.Polymkeric substance mainly is to use as sizing agent in the ablation resistant material manufacturing processed, but the performance of ablation resistant material is played fundamental influence.Main at present having of using: boron modified phenolic resin, phenol triazine (PT) resin, benzoxazine resin, bismaleimide modified resol (BMI) and poly-aryl ethane resin (PAA) etc.The PT resin has the processing characteristics of Resins, epoxy, the high-temperature behavior of BMI and the flame retardant properties of resol, but the used starting material toxicity of its building-up reactions is big, can supply the of less types of RTM process application; Volume does not shrink even expands during the benzoxazine resin solidification, can avoid the stress concentration that produces in the solidification process, but the benzoxazine resin carbon forming rate that is fit to RTM technology is 54% only, is not suitable as the high performance resin of anti-the ablation; The BMI modified phenolic resins has low viscosity, working life is long, temperature tolerance is good advantage, and shortcoming is that the ablation carbon forming rate is low, has only 38.3%; PAA is the performance resins that is applicable to RTM technology, and the high temperature carbon forming rate can reach 85%～90%, and resistance to elevated temperatures excellence, its shortcoming mainly are, when solidifying volumetric shrinkage big and high polymerization exotherms poor with the carbon fiber bonding force.
Study of the Song Dynasty intelligence in " resol ablation property progress " (" engineering plastics application " 2003 the 7th phase 69-71 of magazine page or leaf) literary composition system introduction the kind and the performance of various modified phenolic resinss, comprising boron bakelite resin, molybdenum resol, phosphorous-containing phenolic resin, poly-pheno-ether resin, aryl phenol and modified by alkyl phenol resol, DA modifier modification resol, ring-opening polymerization resol, the phenol cyanate resin, novel phenolic resins S-157 and S-158 and other modified phenolic resins---as adding Cr respectively in mutually at the resin of typical resol/silicon-dioxide ablator
2O
3, Fe and Fe
2O
3Three kinds of additives, in the molecular skeleton of resol, introduce cyano group, boron, aromatic ring organosilicon, trimeric cyanamide and aniline, phenyl or benzyl and carry out modification by copolymerization, also have ammonia resol, ba phenolic resin, magnesium resol, organic silicon modified phenolic resin, dimethylbenzene modified phenolic resins, contain imide-type modified phenolic resins, heavy metal modified phenolic resins and high molecular weight phenolic resin etc.
Although wherein mentioned the organic silicon modified phenolic resin, described organosilicon is not the organosilicon of metallic element modification.
Summary of the invention
The invention discloses a kind of preparation method of modified phenolic resin adhesive, promptly adopt metallic element that silicone resin is carried out modification earlier, prepare low-viscosity resol by catalyzed reaction again, thereby reach adhesiveproperties and the solubility property that improves resin.Since metallic element at high temperature can with the mineral filler generation chemical reaction in the high temperature resistant gluing agent of moment, form have good heat resistance can inorganic materials, thereby can be used as the raw material of the resin of anti-the ablation.
Preparation process of the present invention comprises the steps:
With organosilane monomer, containing metal compound and an amount of solvent, organosilane monomer can be one or more in dialkyl dialkoxy silicane, the diaryl dichlorosilane, and wherein, alkyl or alkoxyl group carbochain are C
1～C
5It can be straight or branched, aryl can use phenyl, tolyl or benzyl, metallic element can be a titanium, also can be aluminium, metallic compound can use isopropyl titanate, tetrabutyl titanate, iso-butyl titanate, pure aluminium silicate or Tai-Ace S 150, solvent is an ethanol, Virahol, butanols, primary isoamyl alcohol, benzene, toluene or water, the mass ratio of organosilane monomer and containing metal compound is 5～10: 1, reacted 1～5 hour down at 70～110 ℃, underpressure distillation removes and desolvates, add phenol then successively, formaldehyde and zinc oxide, the mass ratio of three kinds of materials are 1: 1～2: 0.01～0.05, react 8～12h down at 80～120 ℃, then at 100～135 ℃, 0.08～0.09MPa pressure decompression down removes water and small-molecule substance, makes metallic element modified organic silicon resol.This resin also can be dissolved in the organic solvent, organic solvent can be a kind of or blending ingredients in ethanol, Virahol, acetone, ethyl acetate, butylacetate or the industrial naptha, the final metallic element modified organic silicon phenolic resin adhesive that obtains to contain organic solvent.
The prepared phenolic resin adhesive of present method has higher shearing resistance under normal temperature and hot conditions, because metallic element oxide compounds such as titanium and aluminium are again the anti-aging agent of silicone resin, thereby the resistance toheat of this resin can improve greatly, is more suitable for the matrix resin as high temperature resistant gluing agent of moment.
Embodiment
A kind of preparation method of modified phenolic resin adhesive, be with organosilane monomer, containing metal compound and an amount of solvent, organosilane monomer can be one or more in dialkyl dialkoxy silicane, the diaryl dichlorosilane, and wherein, alkyl or alkoxyl group carbochain are C
1～C
5It can be straight or branched, aryl can use phenyl, tolyl or benzyl, metallic element can be a titanium, also can be aluminium, metallic compound can use isopropyl titanate, tetrabutyl titanate, iso-butyl titanate, pure aluminium silicate or Tai-Ace S 150, solvent is an ethanol, Virahol, butanols, primary isoamyl alcohol, benzene, toluene or water, the mass ratio of organosilane monomer and containing metal compound is 5～10: 1, reacted 1～5 hour down at 70～110 ℃, underpressure distillation removes and desolvates, add phenol then successively, formaldehyde and zinc oxide, the mass ratio of three kinds of materials are 1: 1～2: 0.01～0.05, react 8～12h down at 80～120 ℃, then at 100～135 ℃, 0.08～0.09MPa pressure decompression down removes water and small-molecule substance, makes metallic element modified organic silicon resol.This resin also can be dissolved in the organic solvent, organic solvent can be a kind of or blending ingredients in ethanol, Virahol, acetone, ethyl acetate, butylacetate or the industrial naptha, the final metallic element modified organic silicon phenolic resin adhesive that obtains to contain organic solvent.
Embodiment 1
Dimethyldiethoxysilane, each 10g of phenylbenzene diethoxy silane are added tetrabutyl titanate 3g and an amount of alcohol solvent, after the reflux 3 hours, washing, then phenol 100g, formaldehyde 120g and zinc oxide 2g are added successively, be warmed up to 100 ℃, reaction 8h is at 10～135 ℃, pressure 0.08～0.09MPa decompression down removes water and small-molecule substance, makes titanium modified organic silicon phenolic resin adhesive.
This sizing agent is warming up to 180 ℃ and solidifies down 1h, records the normal temperature shearing resistance greater than 12MPa, and 200 ℃ of shearing resistances are greater than 8MPa, and 300 ℃ of shearing resistances are greater than 5MPa, and has good toughness and resistance toheat, and maximum operation (service) temperature can reach 300 ℃.
Embodiment 2
Diphenyl dichlorosilane 20g, pure aluminium silicate 3g, toluene and distilled water is an amount of, after reacting 2 hours under 90～100 ℃, moisture and toluene are removed in decompression, add phenol 94g, formaldehyde 162g and zinc oxide 2g then, after reacting 8h under 100 ℃, decompression removes water and small-molecule substance under 100～135 ℃, 0.08～0.09MPa pressure, at last with resin dissolves in ethyl acetate, make aluminium modified organic silicon resol.
After this resin is made sizing agent, solidify 2h down at 180 ℃, the normal temperature shearing resistance that records sizing agent is greater than 15MPa, and 300 ℃ of shearing resistances are greater than 6MPa, and 350 ℃ of shearing resistances are greater than 2MPa, and 400 ℃ of shearing resistances are greater than 1MPa.Owing to contain aluminium element in the sizing agent, at high temperature has better moment resistance toheat.
Adopt the prepared phenolic resin adhesive of the present invention under normal temperature and hot conditions, to have higher shearing resistance, because metallic element oxide compounds such as titanium and aluminium are again the anti-aging agent of silicone resin, thereby the resistance toheat of this resin can improve greatly, is more suitable for the matrix resin as high temperature resistant gluing agent of moment.
Claims (5)
1. the preparation method of a modified phenolic resin adhesive, it is characterized in that organosilane monomer, containing metal compound and an amount of solvent, the mass ratio of organosilane monomer and containing metal compound is 5～10: 1, reacted 1～5 hour down at 70～110 ℃, washing, underpressure distillation removes and desolvates, add phenol then successively, formaldehyde and zinc oxide, the mass ratio of three kinds of materials is 1: 1～2: 0.01～0.05, react 8～12h down at 80～120 ℃, then at 100～135 ℃, 0.08～0.09MPa pressure decompression down removes water and small-molecule substance, makes metallic element modified organic silicon resol.
2. the preparation method of modified phenolic resin adhesive according to claim 1, it is characterized in that employed organosilane monomer can be one or more in dialkyl dialkoxy silicane, the diaryl dichlorosilane, wherein, alkyl or alkoxyl group carbochain are C
1～C
5, can be straight or branched, aryl can use phenyl, tolyl or benzyl.
3. the preparation method of modified phenolic resin adhesive according to claim 1 is characterized in that employed metallic element can be a titanium, also can be aluminium, metallic compound can use isopropyl titanate, tetrabutyl titanate, iso-butyl titanate, pure aluminium silicate, Tai-Ace S 150.
4. the preparation method of modified phenolic resin adhesive according to claim 1 is characterized in that employed solvent is ethanol, Virahol, butanols, primary isoamyl alcohol, benzene, toluene or water.
5. the preparation method of modified phenolic resin adhesive according to claim 1 is characterized in that modified organic silicon resol also can be dissolved in the organic solvent, the final metallic element modified organic silicon phenolic resin adhesive that obtains to contain organic solvent; Employed organic solvent is a kind of or blending ingredients in ethanol, Virahol, acetone, ethyl acetate, butylacetate or the industrial naptha.