CN1768938A - Mesopore structured heteropoly acid/silicon dioxide catalyst - Google Patents
Mesopore structured heteropoly acid/silicon dioxide catalyst Download PDFInfo
- Publication number
- CN1768938A CN1768938A CN 200410067849 CN200410067849A CN1768938A CN 1768938 A CN1768938 A CN 1768938A CN 200410067849 CN200410067849 CN 200410067849 CN 200410067849 A CN200410067849 A CN 200410067849A CN 1768938 A CN1768938 A CN 1768938A
- Authority
- CN
- China
- Prior art keywords
- heteropoly acid
- catalyst
- acid
- silicon dioxide
- heteropoly
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a middle-pore heteropoly acid/silica dioxide catalyst, which can mainly solve the problems of present catalyst which uses solid silica dioxide as carrier to load heteropoly acid on surface, therefore, the heteropoly acid is lost easily to affect the property of catalyst. The invention uses average diameter at 80-150nm, the specific surface at 100-300 m2/g, the heteropoly acid in 1-40% (weight), and the silica dioxide in 60-99% (weight) while the silica dioxide is the catalyst formed by porous non-crystalline silica dioxide. The invention can be used to produce C9-12 long chain olefin and carbolic acid.
Description
Technical field
The present invention relates to a kind of heteropoly acid/silicon dioxide catalyst of central hole structure.
Background technology
Heteropoly acid is a kind of important catalysis material, can be widely used in the reactions such as acid catalysis and redox catalysis.In order to make catalyst be easy to separate with product, it is a main path that heteropoly acid is prepared into a kind of support type heterogeneous catalyst.The existing employed method of patent report be by heteropoly acid solution impregnation method with loaded by heteropoly acid on the solid silica carrier surface, Chinese patent CN1265940A wherein, CN1264941A has introduced various loaded by heteropoly acid at silica gel, aerosil, on HZSM-5 molecular sieve, activated carbon, atlapulgite, diatomite and the titanium dioxide surface, be used for the esterification of etherification reaction and the ethylene glycol and the acetate of oxirane and methyl alcohol as catalyst.CN1184797A has introduced phosphorus heteropoly tungstic acid and has been carried on the solid silica, is used for the catalytic reaction that alkane is converted into alkene; CN1185992A has introduced and has been carried on solid silica surface phosphotungstic acid and is used for the catalytic reaction that ether is converted into isobutene; US5856575A5 has introduced the catalytic reaction that the phosphotungstic acid that is carried on the solid silica surface is used for phenol and acid amides; EP955284A1 has introduced heteropolyacid salt and has been carried on the solid silica surface and is used for the alkene hydrolysis catalysis reaction.WO2000074842, WO2002020157, WO200200589 and JP2000342980 have introduced heteropoly acid respectively or heteropolyacid salt loads on the esterification that silica surface is used for the acid of low-carbon ester fat.
Heteropoly acid/silicon dioxide catalyst in the above-mentioned patent report since adopt solid silica do carrier with loaded by heteropoly acid in the surface, but the heteropoly acid/silicon dioxide catalyst that obtains does not thus have big hole dimension (＜＜100 ) and the uniform central hole structure feature of pore-size distribution.EP1123956, JP2002110597 have reported that the aqueous dispersion that phosphorus heteropoly tungstic acid and Ludox mix is used for chemical method machine glazed finish, but do not prepare the heteropoly acid/silicon dioxide of solid.
Summary of the invention
Technical problem to be solved by this invention be solve catalyst in the conventional art since adopt solid silica do carrier with loaded by heteropoly acid in the surface, heteropoly acid easily runs off and causes stability in use poor, and the problem that does not have uniform intermediate pore size provides a kind of heteropoly acid/silicon dioxide catalyst of new central hole structure.This catalyst has good stable, and active high, the advantage that selectivity is good.
For solving the problems of the technologies described above, the technical solution used in the present invention is as follows: a kind of heteropoly acid/silicon dioxide catalyst of central hole structure, average pore size are 80～150 , and specific area is 100～300 meters
2/ gram comprises following component by weight percentage:
A) 1～40% heteropoly acid, wherein heteropoly acid is selected from phosphorus heteropoly tungstic acid or phosphato-molybdic heteropolyacid;
B) 60～99% silica, wherein silica is the noncrystal silica of porous.
In the technique scheme, the preferable range of average pore size is 100～110 , and the specific area preferable range is 150～200 meters
2/ gram.Heteropoly acid is heteropoly acids such as phosphorus heteropoly tungstic acid or phosphato-molybdic heteropolyacid in heteropoly acid/silicon dioxide catalyst, and the consumption preferable range of heteropoly acid is 5～35% by weight percentage.
The central hole structure heteropoly acid/silicon dioxide catalyst is to be feedstock production with the Ludox, in water one alcohol/acetone soln, prepare by the collosol and gel coprecipitation, wherein alcohol can be low-carbon alcohols such as ethanol or isopropyl alcohol, and wherein Ludox can be the aqueous solution of silica gel of 20～40 weight %.
The heteropoly acid/silicon dioxide catalyst of above-mentioned central hole structure is used for C
9～C
12The alkylated reaction of long-chain olefin and phenol, reaction condition be phenol/benzene mole than 2/1～4/1, be reflected at 100 ℃ of temperature, reaction velocity WHSV.2.0 hour
-1Under carry out, olefin conversion＞95% is up to more than 99%.
This catalyst has the central hole structure of the bigger hole dimension that general heteropoly acid/silicon dioxide lacks and good stability in use, has significant application value.
The concrete preparation process of the heteropoly acid/silicon dioxide catalyst of central hole structure of the present invention is as follows:
(1) is made into the aqueous solution of alcohol or acetone by a certain percentage, and is metered into the heteropoly acid dissolving by required.Ludox filters the back use through 500 mesh filter screens simultaneously.
(2) in flask, add above-mentioned heteropoly acid solution,, about 60～80 ℃, handle forming white jelly in 2 hours under agitation by the required Ludox that is metered into.
(3) evaporation removes and desolvates, and dry below 120 ℃, obtains white solid, again 180～200 ℃ of following preliminary treatment 2 hours, obtains the heteropoly acid/silicon dioxide catalyst of central hole structure.
Among the present invention owing to be raw material with the Ludox, in containing the aqueous solution of alcohol/acetone, by the collosol and gel coprecipitation, heteropoly acid and silica bound are formed together the heteropoly acid/silicon dioxide material of central hole structure, make the body of material all have heteropoly acid with the surface, material property is stable, and heteropoly acid is difficult for running off.This catalyst has bigger hole dimension and better catalytic stability than the heteropoly acid/silicon dioxide catalyst of general area load, and pore-size distribution is more even, the catalysis or the adsorbing separation that can be used for big molecule or biomolecule, this catalyst has important use and is worth, and has obtained better technical effect.
The invention will be further elaborated below by embodiment.
The specific embodiment
[embodiment 1]
The concrete preparation process of 10 weight % phosphorus heteropoly tungstic acid/SiO 2 catalysts of central hole structure is as follows:
(1) is made into 40 milliliters of the aqueous solution of ethanol/acetone in 50 weight % ratios, and adds 2.0 gram phosphorus heteropoly tungstic acids dissolvings.Simultaneously 40 weight % Ludox being filtered the back through 500 mesh filter screens uses.
(2) in flask, add above-mentioned heteropoly acid solution, under agitation by preparation 10 weight % phosphorus heteropoly tungstic acid/silica required be metered into Ludox, about 60～80 ℃, handle forming white jelly in 2 hours.
(3) evaporation removes and desolvates, and, obtain white solid, again 180～200 ℃ of following preliminary treatment 2 hours dry below 120 ℃, the 10 weight % phosphorus heteropoly tungstic acid/SiO 2 catalyst A that obtain have the central hole structure that average pore size flows 104 , and its surface area is 176 meters
2/ gram.
[embodiment 2]
The concrete preparation process of 35 weight % phosphorus heteropoly tungstic acid/SiO 2 catalysts of central hole structure is as follows:
(1) is made into 40 milliliters of the aqueous solution of ethanol in 50 weight % ratios, and adds 3.0 gram phosphorus heteropoly tungstic acids dissolvings.Simultaneously 30 weight % Ludox being filtered the back through 500 mesh filter screens uses.
(2) in flask, add above-mentioned heteropoly acid solution, under agitation by preparation 35 weight % phosphorus heteropoly tungstic acid/silica required be metered into Ludox, about 60～80 ℃, handle forming white jelly in 2 hours.
(3) evaporation removes and desolvates, and, obtain white solid, again 180～200 ℃ of following preliminary treatment 2 hours dry below 120 ℃, the 35 weight % phosphorus heteropoly tungstic acid/SiO 2 catalyst B that obtain have the central hole structure that average pore size flows 91 , and its surface area is 132 meters
2/ gram.
[embodiment 3]
The concrete preparation process of 20 weight % phosphato-molybdic heteropolyacid/SiO 2 catalysts of central hole structure is as follows:
(1) is made into 30 milliliters of the aqueous solution of acetone in 50 weight % ratios, and adds 1.0 gram phosphato-molybdic heteropolyacids dissolvings.Simultaneously 20 weight % Ludox being filtered the back through 500 mesh filter screens uses.
(2) in flask, add above-mentioned heteropoly acid solution, under agitation by preparation 20 weight % phosphato-molybdic heteropolyacid/silica required be metered into Ludox, about 60～80 ℃, handle forming white jelly in 2 hours.
(3) evaporation removes and desolvates, and, obtain white solid, again 180～200 ℃ of following preliminary treatment 2 hours dry below 120 ℃, the 20 weight % phosphato-molybdic heteropolyacid/SiO 2 catalyst C that obtain have the central hole structure that average pore size flows 109 , and its surface area is 157 meters
2/ gram.
[embodiment 4]
The concrete preparation process of 5 weight % phosphato-molybdic heteropolyacid/SiO 2 catalysts of central hole structure is as follows:
(1) is made into 30 milliliters of the aqueous solution of acetone in 50 weight % ratios, and adds 1.0 gram phosphato-molybdic heteropolyacids dissolvings.Simultaneously 20 weight % Ludox being filtered the back through 500 mesh filter screens uses.
(2) in flask, add above-mentioned heteropoly acid solution, under agitation by preparation 5 weight % phosphato-molybdic heteropolyacid/silica required be metered into Ludox, about 60～80 ℃, handle forming white jelly in 2 hours.(3) evaporation removes and desolvates, and, obtain white solid, again 180～200 ℃ of following preliminary treatment 2 hours dry below 120 ℃, the 5 weight % phosphato-molybdic heteropolyacid/SiO 2 catalyst C that obtain have the central hole structure that average pore size flows 142 , and its surface area is 256 meters
2/ gram.
[embodiment 5]
With phosphato-molybdic heteropolyacid/SiO 2 catalyst A～D that embodiment 1～3 makes, on the fixed bed reaction evaluating apparatus, carry out reactivity and investigate.Be used for C
9～C
12The alkylation reaction of long-chain olefin and phenol, loaded catalyst be 5.0 the gram catalyst, reaction condition be phenol/benzene mole than 2/1～4/1, be reflected at 100 ℃ of temperature, reaction velocity WHSV.2.0 hour
-1Down, the reaction result olefin conversion is: catalyst A～97.6%, catalyst B～99.2%, catalyst C～95.6%, catalyst D～94.3%.
Claims (4)
1, a kind of heteropoly acid/silicon dioxide catalyst of central hole structure, average pore size are 80～150 , and specific area is 100～300 meters
2/ gram comprises following component by weight percentage:
A) 1～40% heteropoly acid, wherein heteropoly acid is selected from phosphorus heteropoly tungstic acid or phosphato-molybdic heteropolyacid;
B) 60～99% silica, wherein silica is the noncrystal silica of porous.
2,, it is characterized in that average pore size is 100～110 according to the heteropoly acid/silicon dioxide catalyst of the described central hole structure of claim 1.
3,, it is characterized in that specific area is 150～200 meters according to the heteropoly acid/silicon dioxide catalyst of the described central hole structure of claim 1
2/ gram.
4,, it is characterized in that the consumption of heteropoly acid is 5～35% by weight percentage according to the heteropoly acid/silicon dioxide catalyst of the described central hole structure of claim 1.