CN1766016A - Aqueous fire-proof coating for growing tree and its preparation method - Google Patents
Aqueous fire-proof coating for growing tree and its preparation method Download PDFInfo
- Publication number
- CN1766016A CN1766016A CN 200410086254 CN200410086254A CN1766016A CN 1766016 A CN1766016 A CN 1766016A CN 200410086254 CN200410086254 CN 200410086254 CN 200410086254 A CN200410086254 A CN 200410086254A CN 1766016 A CN1766016 A CN 1766016A
- Authority
- CN
- China
- Prior art keywords
- trees
- proof coating
- water
- emulsion
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to water-based fire-proof paint for growing tree, which comprises: polyphosphamidon, melamine, pentaerythrite, clorafin, titanium white/ iron oxide red, talcum powder, carboxyethyl cellulose, free water and water-base resin. Wherein, brushing this product on stem of growing tree without effect to tree growth, and playing fire-proof role when there is fire to protect forest resource. This product has no pollution to environment.
Description
Technical field
The invention belongs to chemical industry class frie retardant coating technical field, just be applied to fire prevention the growing period trees.The invention still further relates to grow trees aqueous fire-proof coating and preparation method.
Technical background
Before the present invention,, do not find the patented technology consistent with the technology of the present invention content by retrieval to Chinese national patent and United States Patent (USP).The timber structure frie retardant coating has a plurality of kinds, is applied to building structure.Technical characterictic of the present invention be to grow trees aqueous fire-proof coating and just be brushed on the trunk of growing period trees with this coating does not influence the normal growth of trees, when woods presence of fire, plays the fp effect, protects forest resources.
Summary of the invention
Trees aqueous fire-proof coating and the preparation method of growing of the present invention is achieved through the following technical solutions:
The trees aqueous fire-proof coating of growing of the present invention is characterized in that by following weight part proportioning preparation:
Polyphosphoric acid amine 8-35 trimeric cyanamide 8-15 tetramethylolmethane 3-10
Chlorinated paraffin 3-10 titanium dioxide/red iron oxide 3-10 talcum powder 5-8
Carboxyethyl cellulose 0.5-0.9 tap water 10-30 water-based resin emulsion 15-45
Wherein water-based resin can be water-based acrylic resin, aqueous-based polyamide resin and water base organosilicon acrylic resin, and emulsion can be styrene-propene yogurt liquid, pure acrylic acid emulsion, organosilicon-ACRYLIC EMULSION and vinyl acetate emulsion.
The preparation method of the trees aqueous fire-proof coating of growing of the present invention, undertaken by following step:
Carboxyethyl cellulose is mixed with 1% the aqueous solution, polyphosphoric acid amine, trimeric cyanamide, tetramethylolmethane, chlorinated paraffin, titanium dioxide, the talcum powder carboxyethyl cellulose aqueous solution and tap water is mixed, disperse to stir 20-60 minute with high speed dispersor, slurry after disperseing got in the shredder grind, ground slurry is mixed with water-based resin/emulsion, stir, filter, check.
The trees aqueous fire-proof coating of growing of the present invention has following technical feature:
Viscosity, (being coated with 4 glasss): 20-60 second
Time of drying, 23 ℃, RH55%
Surface drying time: 2 hours
Do solid work the time: 24 hours
Snappiness: 2-3 millimeter
Flame resistivity: one-level 30 minutes; Secondary 20 minutes; Three grades 10 minutes
Ratio: one-level 0-20 is propagated in the fire combustion; Secondary 25-50; Three grades of 55-70
Weightlessness, g: one-level 5; Secondary 10; Three grade 15
Fire retardance, char volume, cm
3: one-level 25; Secondary 50; Three grade 75
The trees aqueous fire-proof coating of growing of the present invention, its construction feature is directly to be brushed on the trunk of trees, can adopt the constructional method of brushing, also can adopt the constructional method of spraying.Coat-thickness should be between 2-5mm
Embodiment
Embodiment 1 polyphosphoric acid amine 22 trimeric cyanamides 7 tetramethylolmethanes 6
Chlorinated paraffin 5 titanium dioxides 5 talcum powder 4
Carboxyethyl cellulose 0.6 tap water 20 water-based acrylic resins 30
Embodiment 2 polyphosphoric acid amine 22 trimeric cyanamides 7 tetramethylolmethanes 6
Chlorinated paraffin 5 titanium dioxides 5 talcum powder 4
Carboxyethyl cellulose 0.6 tap water 20 aqueous-based polyamide resins 30
Embodiment 3 polyphosphoric acid amine 22 trimeric cyanamides 7 season tetramethylolmethane 6
Chlorinated paraffin 5 titanium dioxides 5 talcum powder 4
Carboxyethyl cellulose 0.6 tap water 20 water base acid-organosilicon crylic acid resins 30
Embodiment 4 polyphosphoric acid amine 22 trimeric cyanamides 7 tetramethylolmethanes 6
Chlorinated paraffin 5 titanium dioxides 5 talcum powder 4
Carboxyethyl cellulose 0.6 tap water 20 pure acrylic acid breasts tuck in 30
Embodiment 5 polyphosphoric acid amine 22 trimeric cyanamides 7 tetramethylolmethanes 6
Chlorinated paraffin 5 titanium dioxides 5 talcum powder 4
Carboxyethyl cellulose 0.6 tap water 20 benzene emulsions 30
Embodiment 6 polyphosphoric acid amine 22 trimeric cyanamides 7 tetramethylolmethanes 6
Chlorinated paraffin 5 titanium dioxides 5 talcum powder 4
Carboxyethyl cellulose 0.6 tap water 20 organosilicon crylic acid latexs 30
Embodiment 7 polyphosphoric acid amine 22 trimeric cyanamides 7 tetramethylolmethanes 6
Chlorinated paraffin 5 titanium dioxides 5 talcum powder 4
Carboxyethyl cellulose 0.6 tap water 20 vinyl acetate emulsions 30
Embodiment 8 polyphosphoric acid amine 22 trimeric cyanamides 7 tetramethylolmethanes 6
Chlorinated paraffin 5 red iron oxides 6 talcum powder 4
Carboxyethyl cellulose 0.5 tap water 20 organosilicon crylic acid latexs 30
Claims (5)
1 growing trees aqueous fire-proof coating and preparation method is characterized in that using the following weight parts proportioning, through the trees of the growth aqueous fire-proof coating of physical process preparation:
Polyphosphoric acid amine 8-35 trimeric cyanamide 8-15 tetramethylolmethane 3-10
Chlorinated paraffin 3-10 titanium dioxide/red iron oxide 3-10 talcum powder 5-8
Carboxyethyl cellulose 0.5-0.9 tap water 10-30 water-based resin/emulsion 15-45
Described trees aqueous fire-proof coating and the preparation method of growing of 2 claims 1 is characterized in that described water-based resin/emulsion, and wherein water-based resin can be water-based acrylic resin, aqueous-based polyamide resin and water base organosilicon acrylic resin.Emulsion can be styrene-propene yogurt liquid, pure acrylic acid emulsion, organosilicon-ACRYLIC EMULSION and vinyl acetate emulsion.
3 trees aqueous fire-proof coating and the preparation methods of growing according to claim 1, the content that it is characterized in that described water-based resin/emulsion is 15-45.
4 trees aqueous fire-proof coating and the preparation methods of growing according to claim 1, the content that it is characterized in that described polyphosphoric acid amine is 8-35; The content of trimeric cyanamide is 8-15; The content of tetramethylolmethane is 3-110; The content of chlorinated paraffin is 3-9.
5 trees aqueous fire-proof coating and the preparation methods of growing according to claim 1 is characterized in that described trees aqueous fire-proof coating and preparation process and the construction process of growing, non-environmental-pollution.