CN1760278A - Wax-for preventing rubber - Google Patents
Wax-for preventing rubber Download PDFInfo
- Publication number
- CN1760278A CN1760278A CN 200410080803 CN200410080803A CN1760278A CN 1760278 A CN1760278 A CN 1760278A CN 200410080803 CN200410080803 CN 200410080803 CN 200410080803 A CN200410080803 A CN 200410080803A CN 1760278 A CN1760278 A CN 1760278A
- Authority
- CN
- China
- Prior art keywords
- wax
- paraffin
- rubber
- preventing rubber
- dosage
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A protecting wax for rubber is proportionally prepared through mixing the paraffin wax with 40-70 deg.C for smelting point with microcrystalline wax with 70-90 deg.C for smelting point, and adding polyethene wax and the antioxidizing agent chosen from N-isopropyl-N-phenylbenzodiamine, dimethyl phthalate and 2,6-di-tert-butyl p-cresol. It can prevent ageing and cracking of rubber.
Description
Technical field
The present invention relates to rubber industry, specifically, is a kind of Wax-for preventing rubber.
Background technology
China's rubber industry development at present is swift and violent, but rubber item is in processing, storage and use, be subjected to ' invasion and attack ' of airborne oxygen and ozone, be subjected to the comprehensive action of physical factors such as light, heat, radiation, mechanical force and other chemical factor simultaneously, a series of catabiosis such as the result can make rubber item produce to be clamminess, hardening embrittlement or be full of cracks have had a strong impact on the application of rubber item in the tire industry.At present China's radial output increases year by year, and to take the method caching of air storage, static ozone ageing before dispatching from the factory be a very serious problem more, and it is improper to solve, and then tire is promptly aging before dispatching from the factory, so must take corresponding safeguard procedures.
The protection of rubber item is divided into chemical protection and physical protection.Mostly chemical protection is to add the compound of aniline structure in rubber item.The phenyl amines protective agent has certain toxicity, and must be under dynamic situation the competence exertion protective effect, when static state, chemical antiager is very slow to the migration on surface, can't play the purpose that prevents ozone ageing.Physical protection is to add a certain proportion of protection wax in rubber item, form on the surface one deck continuously, protective membrane uniformly, can prolong work-ing life of rubber in static state, the Reinforced Rubber antioxidant property suppresses the generation of catabiosis effectively.
Other relevant patent is as follows by retrieval:
1 Chinese patent (application number 91111953) rubber protecting agent, a kind of rubber protecting agent is characterized in that, it is by the hydrogenation Microcrystalline Wax, industrial paraffin, new LDPE (film grade), purification ceresine and oxidation inhibitor are formed.
2 Chinese patents (application number 01106005) Wax-for preventing rubber, a kind of Wax-for preventing rubber is characterized in that, it is by low melt point paraffin, inspissated wax, Microcrystalline Wax and polyethylene are formed.
3 Chinese patents (application number 93103399) rubber product protective agent, a kind of Wax-for preventing rubber is characterized in that, it is made up of brazil wax, dispersion agent, emulsifying agent, tinting material, permeate agent, thinner.
4US5296125 Wax-for preventing rubber: paraffin, Microcrystalline Wax.The isoparaffin content of carbon 30-60 is the 16-30% of alkane total amount.
5US4877465 Wax-for preventing rubber: paraffin, Microcrystalline Wax.Content in the isoparaffin should reach 75% at least, and wherein the normal paraffin content of carbon 21-26 is 5-25%, and the normal paraffin content of carbon 36-51 is 20-45%.
6US5242091 air curing cartridge sealing agent: paraffin, Microcrystalline Wax, high viscosity polyisobutene, high viscosity polybutene.
7J05125823 ceramic tile caulking joint hot melt adhesive: natural carnauba wax, paraffin, Microcrystalline Wax, polyethylene wax, Poly Propylene Wax, ammonification wax
8J05025460 decorates and to use mildew resistant sealant: thermoplastic resin: A. polymkeric substance (a. crystalline acrylic resin or/and through sour modification, b. segmented copolymer, c. ethene-(methyl) acrylate copolymer).B. carboxylic compound: rosin ester.C. natural wax (as paraffin, Microcrystalline Wax, polyethylene wax, Poly Propylene Wax, synthetic wax is as amino wax, ester type waxes, polyester wax for carnauba wax, petroleum wax)
9US5063271 is used for the hot melt wax composition of paper etc.: paraffin wax fully refined, the heavy middle distillate wax of recrystallization, Microcrystalline Wax, EVA multipolymer, polypropylene.
10US4772650 sealant composition: the content of wax, polystyrene, rosin and ethylene copolymer.(a) wax is fusing point 44-72 ℃ paraffin, and fusing point is lower than 85 ℃ Microcrystalline Wax; (b) polystyrene, poly alpha methylstyrene, Vinyl toluene/α-Jia Jibenyixigongjuwu; (c) rosin or derivatives thereof; (d) ethylene-acrylic acid copolymer, ethylene-vinyl acetate copolymer or ethylene-acrylate copolymer
11US4684554 container internal layer sealing: consist of the cardboard wax coating, polystyrene resin and ethylene copolymer.Wax is paraffin, Microcrystalline Wax; The polystyrene or derivatives thereof, the rosin or derivatives thereof.Ethylene copolymer is an ethylene-acrylic acid copolymer, ethylene-vinyl acetate copolymer, ethylene-methyl acrylate multipolymer or ethene-vinyl acetate-methacrylic ester terpolymer.
The surrogate of 12US3284279 wax: crystalline polyethylene, unformed Atactic Polypropylene, the petroleum wax of paraffin distillate.Poly number-average molecular weight is 2,000-40, and 000, polyacrylic number-average molecular weight is 2,000-100,000, paraffin melting point is 120-200F.Be used to roll or apply the high-density fiber thin slice, parchment, glassine, or regenerated cellulose.
13CA-776181 is used for the plastics composite of milk preparation container and similar article: petroleum wax contains paraffin and Microcrystalline Wax, solid polyethylene, isotactic polypropylene, solid polyterpene resin.
14DE1250255 is used for the Wax composition of coating or conceived paperboard: fusing point is at the paraffin of 120-180F, and fusing point is at the Microcrystalline Wax of 160-180F, and molecular weight is at the polyolefine of 1500-25000, molecular weight 800-2,000 petrolatum or styrene polymer or multipolymer
15 Chinese patents (application number 88102331) traditional Chinese medicine pill packing wax shell is formed, a kind ofly form by paraffin, beeswax, ceresine, Vaseline, low molecular polyethylene, be used to pack the wax shell of traditional Chinese medicine pill, it is characterized in that: adopting the manual wax method of hanging when carrying out the honeyed bolus packing, the wax shell is by 60-80% paraffin, and 1-10%EVA resin (or EEA resin), 0-6% polyvinyl resin, 15-20% rosin, 3-5% Viscotrol C and 0-5% low molecular polyethylene are formed.
Technology wax and its production and application in 16 Chinese patents (application number 91104019), a kind of craft candle composition is characterized in that said composition comprises (in parts by weight) component title, weight content: paraffin, 2000~3000 parts; Polyethylene wax, 1~5 part; The plastics end, 0.1~10 part; Stearic acid, 0.5~25 part; Pigment, consumption is decided as required.
17 Chinese patents (application number 92108156) dampproof agent for paper products, a kind of dampproof agent for paper products is characterized in that: with low molecular polyethylene and paraffin is main raw material, and sodium hydroxide, stearic acid, rosin, water are mixed the body of heating and stirring into.
18 Chinese patents (application number 95110282) are produced the processing method of series high melting point paraffin, the present invention relates to a kind of processing method of producing series high melting point paraffin, are that the method by upgrading realizes.The present invention is to be raw material with No. 54, No. 56, No. 58 hydrogenation food-grade paraffin wax, with the high-pressure polyethylene is host, with polypropylene, ethene and vinyl acetate copolymer is that assistant agent is made composite additive, after heating up, stirring, under temperature constant state, mix through static mixer, be cooled to below 100 ℃, can produce 66-109 ℃ series high melting point paraffin product.
Chinese patent (application number 91111953) rubber protecting agent, a kind of rubber protecting agent is characterized in that, it is by the hydrogenation Microcrystalline Wax, industrial paraffin, new LDPE (film grade), purification ceresine and oxidation inhibitor are formed.Used oxidation inhibitor is 2,6 two-Butylated Hydroxytoluenes.
Chinese patent (application number 01106005) Wax-for preventing rubber, a kind of Wax-for preventing rubber is characterized in that, it is by low melt point paraffin, inspissated wax, Microcrystalline Wax and polyethylene wax are formed.Structure alkane content is between 35-70%, wherein carbon number accounts for the 0.5-3% of alkane total amount less than 27 the alkane of structure, carbon number between 27-35% structure alkane account for the 2-10% of alkane total amount, the structure alkane of carbon number between 36-45% accounts for the 5-25% of alkane total amount, and carbon number accounts for the 20-45% of alkane total amount greater than 45 the alkane of structure.
US5296125 Wax-for preventing rubber: paraffin, Microcrystalline Wax.The isoparaffin content of carbon 30-60 is the 16-30% of alkane total amount.
US4877465 Wax-for preventing rubber: paraffin, Microcrystalline Wax.Content in the normal paraffin should reach 75% at least; wherein the normal paraffin content of carbon 21-26 is 5-25%, and that to be 20-45% be used to protect the elastomerics that contains two keys with auxiliary protection to avoid the infringement of ozone, weather, daylight in paraffin to the normal paraffin content of carbon 36-51 is early well known.This is because most of rubber molecule structures all are undersaturated, destroys original molecular structure with airborne active atomic generation chemical reaction easily.After adding protection wax in the rubber, under the condition of high temperature in sulfidation, wax all is dissolved in the sizing material, but after the cross-linked rubber cooling, has just formed supersaturation wax solution.Owing to exist concentration gradient between cross-linked rubber inside and surface, the wax molecule continuously to surface transport, forms one deck physical protection film at rubber surface.The characteristics of this tunic are to exist minimum thickness on the one hand, to guarantee that rubber surface is had enough protective capacities; Can not surpass a certain thickness again on the other hand, to prevent the rubber surface dirt.And have the airtight structure of homogeneous, have certain elasticity, the surface that is adhered to rubber item is not peelable.
Paraffin is during as rubber antioxidant, its move to cere that the rubber surface bloom forms crystallize into loose, that have hole, with the less fragility cere of sticking power of rubber, this cere comes off from rubber surface easily in the form of sheets, thereby ozone penetrates the two keys of this cere and rubber molecule easily and reacts and the ageing of rubber phenomenon takes place.Contain higher isoparaffin of more relative molecular mass and the naphthenic hydrocarbon that has long side chain in the Microcrystalline Wax molecule, its fusing point height, good toughness, crystallization is tiny, fine and close, viscosity is big, when therefore using Microcrystalline Wax as rubber antioxidant, its speed of moving to rubber surface is slower, and the cere good toughness of formation, densification, tack is good and difficult drop-off.But because of the Microcrystalline Wax travelling speed slower, so form the time of cere long, cere is thinner.If paraffin mixes (being that normal paraffin and isoparaffin are mixed in proportion) by a certain percentage with Microcrystalline Wax, the crystallization meeting forms unbodied, fine and close, thicker cere, can effectively prevent penetrating of ozone, thereby reaches the purpose of favorable protection ozone.
Summary of the invention
The object of the present invention is to provide a kind of high performance Wax-for preventing rubber; it can be applied in natural rubber and the synthetic rubber; and can form the fine and close cere of one deck at rubber surface rapidly; can be in the wide temperature range permanent protection effect that plays prevents that effectively rubber item is influenced by atmospheric ambient factors and aging cracking takes place.
The present invention relates to a kind of Wax-for preventing rubber, it is characterized in that it is to be mixed with the crystallite wax phase by the paraffin that extracts in the crude oil of Kelamayi, Xinjiang to add polyethylene wax and oxidation inhibitor again and make.Isoparaffin content reaches between the 40-70% in the Wax-for preventing rubber described in the invention.Wherein carbon number accounts for the 10-20% of alkane total amount at the isoparaffin content of 27-35, and carbon number accounts for the 10-30% of alkane total amount at the isoparaffin content of 36-45, and carbon number accounts for the 25-50% of alkane total amount greater than 45 isoparaffin content.
Basic comprising of the present invention:
Mainly form by the paraffin and the Microcrystalline Wax that extract in the crude oil of Kelamayi, Xinjiang;
A adds polyethylene wax
B adds oxidation inhibitor
The difference of the present invention and prior art:
Isoparaffin content reaches between the 40-70% in the Wax-for preventing rubber described in the invention.Wherein carbon number accounts for the 10-20% of alkane total amount at the isoparaffin content of 27-35, and carbon number accounts for the 10-30% of alkane total amount at the isoparaffin content of 36-45, and carbon number accounts for the 25-50% of alkane total amount greater than 45 isoparaffin content.
The oxidation inhibitor that adds in the Wax-for preventing rubber described in the invention is N-sec.-propyl-N-phenyl phenylenediamine, dimethyl phthalate, 2,6-ditertbutylparacresol.
Characteristics of the present invention:
Wax-for preventing rubber provided by the invention, it is to be mixed with the crystallite wax phase by the paraffin that extracts in the crude oil of Kelamayi, Xinjiang to add polyethylene wax and oxidation inhibitor again and make.Good anti-flex crack and anti-ozone ageing performance are arranged, and especially anti-flex crack performance is better than the high-grade rubber protection wax of Compaynie Francaise des Petroles.
Described paraffin, fusing point are 40-70 ℃.
Described Microcrystalline Wax, fusing point are 70-90 ℃.
In the described preventing rubber Wax composition, add polyethylene wax, molecular weight can be between 1000-20000.
In the described preventing rubber Wax composition, add N-sec.-propyl-N-phenyl phenylenediamine, dimethyl phthalate, 2,6-ditertbutylparacresol.
The dosage of described paraffin is 20-70%, and preferred addition is 30-50%.
The dosage of described Microcrystalline Wax is 30-80%, and preferred addition is 40-60%.
The dosage of described polyethylene wax is 0-20%, and preferred addition is 5-10%.
The dosage of described this basic phenylenediamine of N-propyl group-N-is 0-15%, and preferred addition is 0.5-10%.
The dosage of described dimethyl phthalate is 0-15%, and preferred addition is 0.5-12%.
Dosage described 2, the 6-ditertbutylparacresol is 0-20%, and preferred addition is 0.5-15%.
Described isoparaffin content reaches between the 40-70%.
The isoparaffin content of described carbon number little 27 accounts for the 1-3.5% of alkane total amount.
Described carbon number accounts for the 10-20% of alkane total amount at the isoparaffin content of 27-35.
Described carbon number accounts for the 10-30% of alkane total amount at the isoparaffin content of 36-45.
Described carbon number accounts for the 25-50% of alkane total amount greater than 45 isoparaffin content.
Wax-for preventing rubber of the present invention is to be mixed with the crystallite wax phase by the paraffin that extracts in the crude oil of Kelamayi, Xinjiang to add polyethylene wax and oxidation inhibitor again and make.Wherein paraffin accounts for 20-60%, and Microcrystalline Wax accounts for 40-80%, and polyethylene wax accounts for 5-10%, and oxidation inhibitor accounts for 1-10%.
Used paraffin is 52-60 paraffin, and oleaginousness is less than 1.5%.
Used Microcrystalline Wax is the 70-80 Microcrystalline Wax, and oleaginousness is less than 3.5%.
Used polyethylene wax molecular weight is between the 1000-20000.
The index of the Wax-for preventing rubber that the present invention makes is as follows:
Melt drop temperature, ℃ 60~68
Oleaginousness, % 0.5-3.5
Kinematic viscosity (25 ℃), mm
2/ s 5~7
Ash content, % is not more than 0.1
The main crystallite of microscopic examination
Refractive index 1.428-1.45
The preparation method of product of the present invention:
By proportioning weighing paraffin, Microcrystalline Wax, polyethylene wax and oxidation inhibitor.Load weighted polyethylene wax and Microcrystalline Wax are joined in the reactor, slowly be heated to 130-140 ℃, start agitator after the thawing, stirred 15-25 minute, add industrial paraffin then, mixed 20-30 minute, add oxidation inhibitor at last, stirred 40-50 minute.Through filter, impurity screening, cooling forming is promptly made product of the present invention again.
Embodiment
Embodiment 1
Paraffin (No. 56) 22%
Microcrystalline Wax (No. 70) 69%
Polyethylene wax 5%
N-propyl group-N-phenyl phenylenediamine 1%
Dimethyl phthalate 0.5%
2, the 6-ditertbutylparacresol 0.5%
Press embodiment 1 proportioning weighing paraffin, Microcrystalline Wax, polyethylene wax and oxidation inhibitor.Polyethylene wax with load weighted 5% and 69% 70
#Microcrystalline Wax joins in the reactor, slowly is heated to 130-145 ℃, starts agitator after the thawing, stirs 15-25 minute, add then 22% 56
#Paraffin mixed 20-30 minute, add at last N-propyl group-N-phenyl phenylenediamine of 1%, 0.5% dimethyl phthalate 0.5% and 0.5% 2,6-ditertbutylparacresol 0.5%, stirred 40-60 minute.Through filter, impurity screening, cooling forming is promptly made product of the present invention again.
Embodiment 2
Paraffin (No. 54) 25%
Microcrystalline Wax (No. 75) 68%
Polyethylene wax 6.5%
2, the 6-ditertbutylparacresol 0.5%
Press embodiment 2 proportioning weighing paraffin, Microcrystalline Wax, polyethylene wax and oxidation inhibitor.Polyethylene wax with load weighted 6.5% and 68% 75
#Microcrystalline Wax joins in the reactor, slowly is heated to 130-150 ℃, starts agitator after the thawing, stirs 20-25 minute, add then 25% 54
#Paraffin mixed 20-30 minute, add at last 0.5% 2,6-ditertbutylparacresol 0.5%, stirred 40-50 minute.Through filter, impurity screening, cooling forming is promptly made product of the present invention again.
Embodiment 3
Paraffin (No. 58) 31%
Microcrystalline Wax (No. 75) 60%
Polyethylene wax 8.5%
Dimethyl phthalate 0.5%
Press embodiment 3 proportioning weighing paraffin, Microcrystalline Wax, polyethylene wax and oxidation inhibitor.Polyethylene wax with load weighted 7% and 60% 75
#Microcrystalline Wax joins in the reactor, slowly is heated to 130-140 ℃, starts agitator after the thawing, stirs 15-25 minute, add then 31% 58
#Paraffin mixed 20-35 minute, added 0.5% dimethyl phthalate at last, stirred 40-55 minute.Through filter, impurity screening, cooling forming is promptly made product of the present invention again.
Embodiment 4
Paraffin (No. 60) 31%
Microcrystalline Wax (No. 75) 68%
Polyethylene wax 8%
N-propyl group-N-phenyl phenylenediamine 0.5%
2, the 6-ditertbutylparacresol 0.5%
Press example 4 proportioning weighing paraffin, Microcrystalline Wax, polyethylene wax and oxidation inhibitor.With 75 of load weighted 8% polyethylene wax and 68%
#Microcrystalline Wax joins in the reactor, slowly is heated to 130-140 ℃, starts agitator after the thawing, stirs 15-25 minute, add then 31% 60
#Paraffin mixed 20-30 minute, add at last 0.5%N-propyl group-N-phenyl phenylenediamine 0.5% and 0.5% 2, the 6-ditertbutylparacresol, stirred 50-60 minute.Through filter, impurity screening, cooling forming is promptly made product of the present invention again.
Embodiment 5
Paraffin (No. 52) 38%
Microcrystalline Wax (No. 80) 50%
Polyethylene wax 9%
N-propyl group-N-phenyl phenylenediamine 0.5%
Dimethyl phthalate 0.5%
2, the 6-ditertbutylparacresol 1%
Press example 5 proportioning weighing paraffin, Microcrystalline Wax, polyethylene wax and oxidation inhibitor.With 80 of load weighted 9% polyethylene wax and 50%
#Microcrystalline Wax joins in the reactor, slowly is heated to 140-150 ℃, starts agitator after the thawing, stirs 15-25 minute, add then 38% 52
#Paraffin mixed 20-30 minute, add at last N-propyl group-N-phenyl phenylenediamine of 0.5%, 0.5% dimethyl phthalate 0.5% and 1% 2,6-ditertbutylparacresol 1%, stirred 40-50 minute.Through filter, impurity screening, cooling forming is promptly made product of the present invention again.
Product of the present invention can be verified by the test colloid is carried out every comparison test the physicals influence and the protection effect thereof of rubber item:
Table 2 test colloid flavoring (by weight)
Natural rubber | 70 |
Cis-1,4-polybutadiene rubber | 30 |
Zinc oxide | 5 |
Lipid acid | 1 |
Titanium dioxide | 5 |
Sulfur | 1.5 |
Accelerant CZ | 1 |
Altax | 1 |
Antioxidant 264 | 0 |
White carbon black T-S3 | 20 |
Lime carbonate | 65 |
Spindle oil | 3 |
Polyoxyethylene glycol | 0.5 |
Protection wax | 2 |
Add up to | 205 |
The contrast of table 3 test colloid physicals
Project | Unit | Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 | Embodiment 5 | Certain rubber plant's wax | B-10 (France) |
Hardness | Shao A | 46 | 49 | 52 | 50 | 51 | 50 | 49 |
Tensile strength at yield | MPa | 9.3 | 9.3 | 9.6 | 10.1 | 9.8 | 7.3 | 7.9 |
Elongation | % | 800 | 748 | 744 | 768 | 772 | 796 | 768 |
Tension set | % | 44 | 40 | 38 | 40 | 40 | 44 | 42 |
As can be seen from Table 3, use embodiment 1,2,3,4, the colloid of 5, five kinds of Wax-for preventing rubbers and use the gel phase ratio of other wax class, their every physical indexs all show better performance.
Anti-flex crack of table 4 and anti-ozone ageing test
Numbering | Flex crack (subduing number of times) | Ozone ageing (breach time min) |
Embodiment 1 | 70000 | 45 |
Embodiment 2 | 75000 | 120 |
Embodiment 3 | 60000 | 90 |
Embodiment 4 | 45000 | 90 |
Embodiment 5 | 55000 | 60 |
B-10 (France) | 45000 | 40 |
Certain rubber plant's wax | 40000 | 60 |
As can be seen from Table 4, use embodiment 1,2,3,4, the anti-flex crack of 5 five kinds of Wax-for preventing rubbers and anti-ozone ageing performance are better than other wax class.
Claims (8)
1, a kind of Wax-for preventing rubber is characterized in that: by the fusing point that extracts in the crude oil of Kelamayi, Xinjiang is that 40~70 ℃ of paraffin are that 70~90 ℃ of crystallite wax phases mix with fusing point, adds polyethylene wax and oxidation inhibitor again and makes;
The polyethylene wax that is added, molecular weight is between 1000~20000;
The oxidation inhibitor that is added is N-sec.-propyl-N-phenyl phenylenediamine, dimethyl phthalate, 2,6 ditertiary butyl p cresol, and addition is 0-20%;
The dosage of paraffin is 20-70%;
The dosage of Microcrystalline Wax is 30-80%;
The dosage of polyethylene wax is 0-20%.
2 according to the described Wax-for preventing rubber of claim 1, it is characterized in that, used paraffin, Microcrystalline Wax extract from the crude oil of Kelamayi, Xinjiang.
3 according to the described Wax-for preventing rubber of claim 1, it is characterized in that: the dosage of paraffin is 20-70%, and preferred addition is 30-50%.
4 according to the described Wax-for preventing rubber of claim 1, it is characterized in that: the dosage of Microcrystalline Wax is 30-80%, and preferred addition is 40-60%.
5 according to the described Wax-for preventing rubber of claim 4, it is characterized in that: the dosage of polyethylene wax is 0-20%, and preferred addition is 5-10%.
6 according to the described Wax-for preventing rubber of claim 1, it is characterized in that: the dosage of oxidation inhibitor N-sec.-propyl-N-phenyl phenylenediamine is 0-15%, and preferred addition is 0.5-10%.The dosage of oxidation inhibitor dimethyl phthalate is 0-15%, and preferred addition is 0.5-12%, and the dosage of oxidation inhibitor 2,6 ditertiary butyl p cresol is 0-20%, and preferred addition is 0.5-15%.
7 according to the described Wax-for preventing rubber of claim 1, and it is characterized in that: isoparaffin content reaches between the 40-70% in this Wax-for preventing rubber.
8 according to the described Wax-for preventing rubber of claim 1, it is characterized in that: carbon number accounts for the 1-3.5% of alkane total amount less than 27 isoparaffin content, carbon number accounts for the 10-20% of alkane total amount at the isoparaffin content of 27-35, carbon number accounts for the 10-30% of alkane total amount at the isoparaffin content of 36-45, and carbon number accounts for the 25-50% of alkane total amount greater than 45 isoparaffin content.